铂铈共掺杂纳米TiO2的制备、表征及光催化性能

以钛酸四丁酯为前驱体,过氧化氢为氧化剂,采用简单易行的低温氧化法制备出晶粒尺寸较小(平均尺寸25 nm)的二氧化钛纳米粒子。通过贵金属Pt掺杂TiO₂(Pt-TiO₂)、稀土元素Ce掺杂TiO₂(Ce-TiO₂)和Pt、Ce共掺杂TiO₂(Pt/Ce-TiO₂)的掺杂的方法对二氧化钛进行改性。通过XRD,XPS,TEM,紫外漫反射等表征手段对制备的样品进行表征。通过可见光下降解罗丹明B来测试其光催化活性。实验结果表明,由Ce掺杂的TiO₂光催化剂对有机污染物的最大降解能力略大于Pt掺杂的TiO₂,2种元素进行共同掺杂时对应的TiO₂光催化剂降解能力最大。     

V/Ce共掺杂TiO2光催化降解甲醛的实验研究

采用溶胶-凝胶法制备了不掺杂、V掺杂、Ce掺杂、V/Ce共掺杂纳米TiO2光催化剂,并将其分别负载于瓷砖上,利用X射线衍射分析（XRD）和扫描电镜分析（SEM）技术对薄膜样品的结构和形貌进行了表征。通过对甲醛的降解实验评价光催化剂的光催化活性。实验结果表明,光催化剂的负载量、共掺杂离子的掺杂量、掺杂配比、煅烧温度影响纳米TiO2的光催化活性。V/Ce共掺杂TiO2光催化剂产生了协同效应,其光催化活性优于纯TiO2和单掺杂TiO2样品。     

Ce掺杂纳米TiO2光催化剂的制备及降解甲醛的研究

介绍了溶胶-凝胶法制备Ce离子掺杂纳米TiO2的工艺流程。采用X射线衍射（XRD）、紫外可见分光光度法（UV-Vis）等方法表征了Ce掺杂TiO2的相组成、紫外可见漫反射率与掺杂量的关系。结果表明，掺杂的TiO2在520℃．650℃焙烧2h呈锐钛矿结构，在520℃焙烧2h的TiO2的晶粒尺寸大约为20nm，而掺杂Ce后其晶粒尺寸均减小，大约为12nm。UV-Vis吸光度分析表明，掺Ce后吸收带边明显发生红移，但随着Ce掺杂浓度的增大，其对可见光的吸收影响不大。光催化降解反应表明，未掺杂Ce的TiO2反应2h后对甲醛的没有降解作用，而Ce掺杂TiO2反应2h后甲醛降解率达15％。     

B,N和Ce共掺杂TiO2催化剂光催化活性研究

采用溶胶-凝胶法制备出B,N和Ce共掺杂TiO2光催化剂,并用XRD、SEM等表征了其结构特征。以酸性大红染料溶液的光催化降解为探针反应,考察了制备条件对共掺杂TiO2催化剂活性的影响。结果表明,在400℃,当B,N和Ce的原子比为1∶2∶0.1,焙烧3 h时,光催化剂活性最大,大红染料的降解率达到98%。     

B,N和Ce共掺杂TiO_2催化剂光催化活性研究

采用溶胶-凝胶法制备出B,N和Ce共掺杂TiO2光催化剂,并用XRD、SEM等表征了其结构特征。以酸性大红染料溶液的光催化降解为探针反应,考察了制备条件对共掺杂TiO2催化剂活性的影响。结果表明,在400℃,当B,N和Ce的原子比为1∶2∶0.1,焙烧3 h时,光催化剂活性最大,大红染料的降解率达到98%。     

复合型CoO／TiO2光催化剂降解亚甲基蓝动力学研究

以钛酸四丁酯为前驱体，采用溶胶凝胶法，制备了CoO掺杂的TiO2光催化剂。利用X射线衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）、紫外可见漫反射（UV—visDRS）对催化剂进行了分析、表征。以中压汞灯为光源，研究了亚甲基蓝（MB）在CoO／TiO2微粒水悬浮液中的降解动力学。结果表明：所制备的催化剂活性组分主要是锐钛矿型的二氧化钛和CoO固溶体，粒径为25～30nm，分布均匀。亚甲基蓝的光催化降解动力学满足一级动力学，在一定的浓度范围内，反应速率常数随初始浓度增大而减少，适当的掺钴量可以有效地提高TiO2光催化活性，其最佳掺杂量重量百分比为0．25％。     

Ce掺杂纳米TiO2光催化剂的制备及降解甲醛的研究

介绍了溶胶-凝胶法制备Ce离子掺杂纳米TiO2的工艺流程.采用X射线衍射(XRD)、紫外可见分光光度法(UV-Vis)等方法表征了Ce掺杂TiO2的相组成、紫外可见漫反射率与掺杂量的关系.结果表明,掺杂的TiO2在520℃、650℃焙烧2 h呈锐钛矿结构,在520℃焙烧2 h的TiO2的晶粒尺寸大约为20 nm,而掺杂Ce后其晶粒尺寸均减小,大约为12nm.UV-Vis吸光度分析表明,掺Ce后吸收带边明显发生红移,但随着Ce掺杂浓度的增大,其对可见光的吸收影响不大.光催化降解反应表明,未掺杂Ce的TiO2反应2 h后对甲醛的没有降解作用,而Ce掺杂TiO2反应2 h后甲醛降解率达15%.     

V/Ce共掺杂TiO2光催化降解甲醛的实验研究

采用溶胶凝胶法制备了不掺杂、V 掺杂、Ce掺杂、V/Ce共掺杂纳米TiO₂光催化剂，并将其分别负载于瓷砖上，利用X射线衍射分析（XRD）和扫描电镜分析（SEM）技术对薄膜样品的结构和形貌进行了表征。通过对甲醛的降解实验评价光催化剂的光催化活性。实验结果表明，光催化剂的负载量、共掺杂离子的掺杂量、掺杂配比、煅烧温度影响纳米TiO₂的光催化活性。V/Ce共掺杂TiO₂光催化剂产生了协同效应，其光催化活性优于纯TiO₂和单掺杂TiO₂样品。     

模拟可见光下掺杂TiO_2对甲醛溶液光催化降解

模拟自然条件下的可见光,以甲醛的光催化降解为探针反应,评价了通过溶胶-凝胶法分别制备的8种（银Ag、铜Cu、铁Fe、钨W、铈Ce、镧La、硫S、氯Cl）掺杂TiO2纳米晶体的光催化活性及对甲醛水溶液的去除效果。用X射线衍射、激光粒度分析和紫外-可见分光光谱表征了掺杂纳米TiO2的微晶尺寸、晶体结构与光学性能。结果表明：Ce离子尽管有较大的半径但是主要还是掺杂到晶格中,Ce掺杂可以促进TiO2由非正分锐钛矿相向锐钛矿相和金红石相的转变,抑制载流子复合,使TiO2的光吸收带边发生红移且有利于对可见光的吸收,从而使Ce掺杂TiO2在模拟可见光下光催化甲醛水溶液的能力得到明显提高。     

模拟室内环境下掺杂TiO_2纳米晶体的光催化性能

采用环境测试舱模拟可见光下的室内环境,以甲醛气体的光催化降解为探针反应,评价了通过溶胶-凝胶法分别制备的8种（银Ag、铜Cu、铁Fe、钨W、铈Ce、镧La、硫S和氯C l）掺杂TiO2纳米晶体的光催化活性及对甲醛气体的去除效果。用X射线衍射、激光粒度分析和紫外-可见分光光谱表征了掺杂钠米TiO2的微晶尺寸、晶体结构与光学性能。结果表明,Cu掺杂可以提高TiO2对氧的吸附能力,减少纳米粒子表面光生电子与光生空穴的复合,使TiO2的光吸收带边发生红移且有利于对可见光的吸收,从而使Cu掺杂TiO2在模拟室内环境下光催化甲醛气体的能力得到明显提高。     

Comparison of catalytic activity of two platinised TiO2 films towards the oxidation of organic pollutants

Two types of platinised TiO2 films, i.e., Pt-TiO2/ITO and Pt(TiO2)/ITO, were prepared by a procedure of dip-coating and subsequent photo-deposition, and photo-deposition and subsequent dip-coating, respectively. They were well characterized by DRS, XRD spectra, SEM microscopy and photoelectrochemical measurement. Their photocatalytic, dark catalytic and photoelectrocatalytic activities were investigated using formic acid as a model organic pollutants. Compared with pure TiO2/ITO film, the photocatalytic activity of the platinised TiO2 films were apparently improved. However, the improvement was considerably dependent on the preparation method of these films. Pt-TiO2/ITO not only possessed higher photocatalytic activity but also showed a dark catalytic activity towards HCOOH degradation. As a sequence, it was first emphasized that the dark catalytic effect of Pt-TiO2/ITO was partly responsible for degradation of formic acid in the photocatalytic oxidation process. Although the Pt(TiO2)/ITO film does not exhibit the dark catalytic activity, its photocatalytic degradation efficiencies towards HCOOH are higher than that of Pt-TiO2/ITO film. Therefore, in view of enhanced photocatalytic activity, the Pt(TiO2)/ITO was more favored than Pt-TiO2/ITO film.     

Ozone facilitated degradation of caffeine using Ce-TiO2 catalyst

The ozone initiated oxidation of 1,3,7-trimethylxanthine (caffeine), commonly found in wastewaters as model compound is reported using cerium (Ce)/titanium dioxide (TiO₂) as catalyst. The effect of pH and loading of ceria on titania were investigated. Effect of reaction conditions on degradation of caffeine based on their pseudo first-order rate constants were compared. The combination of catalyst Ce-TiO₂ and ozone aeration significantly enhanced the degradation of caffeine compared to uncatalysed ozonation. The oxidation of caffeine ensued via the free radical mechanism, through enhanced ozone decomposition into OH radicals. Ce/TiO₂(0.5?wt%) showed good activity in degradation of caffeine at pH 6, in both natural stream and river water samples showing about 60% total organic carbon removal in 2?h ozonation period. Using liquid chromatography-mass spectroscopy, degradation products were analysed. A reaction intermediate and one final product were positively identified. Nano-catalysts with different loadings of Ce on TiO₂ synthesized by sol-gel route were characterized by scanning electron microscope, transmission electron microscopy, BET and powder X-ray diffraction spectrum techniques. The results showed that the material retained a highly ordered mesoporous structure and possessed large surface area.     

粉煤灰沸石负载Ce^3＋／TiO2光催化降解水中的菲和荧蒽

以钛酸四丁酯为前驱体，粉煤灰合成沸石为载体，采用溶胶-凝胶方法，在低温条件下制备了稀土铈掺杂的TiO2光催化剂。利用SEM—EDS、XRD、FTIR对催化剂进行了分析和表征。以高压汞灯为灯源，对多环芳烃菲、荧蒽的降解进行了研究。实验考查了稀土铈掺杂质量分数、催化剂用量、溶液pH、目标物初始质量浓度等因素对光催化降解的影响，研究了其光降解动力学。结果表明，当稀土铈含量为0．5％，催化剂用量为3g／L，pH偏碱性时，催化效果最佳。光催化反应符合Langmuir—Hinshelwood动力学规律，菲、荧蒽的降解过程符合一级反应动力学，反应速率常数分别为0．0126min^-1，0．0099min^-1。     

Photocatalytic degradation of AZO dyes by supported TiO2 + UV in aqueous solution

The photocatalytic degradation performance of photocatalysts TiO2 supported on 13-X, Na-Y, 4A zeolites with different loading content was evaluated using the photocatalytic oxidation of dyes direct fast scarlet 4BS and acid red 3B in aqueous medium. The results showed that the best reaction dosage of TiO2-zeolite catalysts is about 2 g/l and the photocatalytic kinetics follows first order for all supported catalysts. The photocatalytic activity order of the three series catalysts is 13X type >Y type >4A type. The physical state of titanium dioxide on the supports is evaluated by X-ray photoelectron spectra (XPS), powder X-ray diffraction (XRD), BET, and FTIR.     

Photocatalytic degradation of amoxicillin from aqueous solutions by titanium dioxide nanoparticles loaded on graphene oxide

Environmental Science and Pollution Research - The photocatalytic degradation of amoxicillin (AMX) by titanium dioxide nanoparticles loaded on graphene oxide (GO/TiO2) was evaluated under UV light....     

A comprehensive systematic review of photocatalytic degradation of pesticides using nano TiO2

Environmental Science and Pollution Research - This study has systematically reviewed all of the research articles about the photocatalytic degradation of pesticides using titanium dioxide (TiO2)...     

Effect of adsorbents coated with titanium dioxide on the photocatalytic degradation of propoxur

Photocatalytic oxidation of pesticides in aqueous media irradiated by UV light is a rapidly growing field of research. Therefore, the treatment technology for degradation of propoxur (an insecticide) using titanium dioxide coated on the supports such as activated carbon, zeolite, brick, quartz and glass beads, was performed in this research. Results show that GAC/TiO2 is the best complexing agent for oxidizing propoxur because of its adsorption properities. The others follow the sequence: plain TiO2 > glass beads > zeolite > brick > quartz. The degradation rate of propoxur with plain TiO2 is higher than that with TiO2/GAC complexing agent. But the mineralization rate of propoxur with plain TiO2 is lower than that with TiO2/GAC complexing agent. However, it can be concluded that using GAC as the support can improve the photocatalytic efficiency.