活性炭负载纳米TiO2对腐殖酸光催化降解动力学

采用溶胶-凝胶法制备了以颗粒活性炭(GAC)为载体的纳米TiO2/AC复合催化剂,并将其用于腐殖酸的光催化降解.动力学研究表明,TiO2/AC光催化降解腐殖酸过程可用Langmuir-Hinshelwood(L-H)动力学模式表示.L-H表观反应速率常数KLH=0.1124mg·L-·1min-1,吸附平衡常数K*=0.3402L·mg-1.活性炭负载TiO2对腐殖酸的光催化降解过程,体现了活性炭与TiO2的协同作用,活性炭的吸附作用提高了光催化反应速率.     

负载型TiO2/活性炭的制备及光催化降解罗丹明B研究

通过溶胶-凝胶方法以活性炭(AC)为载体,制备负载型TiO2/AC,利用SEM、BET、XRD、Ranme、XPS对TiO2/AC的组成、结构、尺寸等特征进行分析和表征,并用紫外灯为光源,通过TiO2/AC、TiO2粉末和活性炭与TiO2粉末的混合物对可溶性罗丹明B的光催化降解效果的比较,探讨了TiO2/AC的光催化性能.结果表明,负载体中的TiO2是由30～60nm的球形颗粒组成,含有Ti,O,C等3种元素,颗粒间不发生团聚,其中一些C元素是由活性炭载体扩散到TiO2颗粒中的.由于活性炭载体与TiO2的协同作用以及高浓度Ti3+的影响,负载型TiO2/AC的光催化活性大.当TiO2/AC在250℃空气中热处理2h,再在氮气保护下500℃热处理2 h,TiO2的质量分数为(18±0.3)%时,负载型TiO2/AC对罗丹明B的光催化降解的表观反应常数k最大,为0.0077 min-1.     

活性炭负载型TiO_2光催化降解采油废水的研究

采用溶胶-凝胶法制备了活性炭负载型的TiO2复合光催化剂,通过SEM和XRD对其进行表征,并利用采油废水的COD去除率来考察自制TiO2/AC复合催化剂对采油废水的处理效果。结果表明:活性炭表面负载了均匀的纯锐钛矿型TiO2薄膜,其晶粒尺寸为24.0 nm;TiO2/AC复合催化剂对采油废水中大多数有机物有不同程度的光催化降解;处理后采油废水COD去除率可达65.3%。     

TiO_2/ACFs催化剂光催化降解染料废水活性研究

以活性炭纤维为载体,采用溶胶-凝胶法制备得到了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs),并且以亚甲基蓝为模型化合物模拟研究了活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)对染料废水的光催化活性。通过扫描电镜(SEM)、XRD等表征方法对活性炭纤维负载二氧化钛光催化剂(TiO2/ACFs)的结构进行了研究。SEM表征显示,大部分二氧化钛以膜的形式均匀地包裹在活性炭纤维丝上,二氧化钛膜层的厚度大约为330 nm,还有一部分TiO2是以颗粒的形式负载在活性炭纤维上。FT-IR分析可知,ACF与TiO2之间有Ti—O—C键生成,说明TiO2与ACF结合牢固,TiO2不易脱落。通过对亚甲基蓝降解可知当煅烧温度为500℃时,TiO2/ACF的光催化性能最好,通过对比发现500℃煅烧制备的催化剂也具有最好的循环使用性能,经过4次循环后该催化剂对亚甲基蓝的去除率仍达到90.2%。     

溶胶-凝胶掺杂铁对微弧氧化TiO_2膜光催化性能影响

以磷酸钠为电解液,采用微弧氧化技术在钛片上直接制备TiO2膜,利用溶胶-凝胶法和硝酸铁掺杂方法对该膜表面进行修饰处理,以罗丹明B溶液模拟废水来评价TiO2膜光催化降解水中有机污染物的能力。利用EDX对微弧氧化膜表面成分进行分析。实验结果表明:微弧氧化TiO2膜具有一定的光催化活性。溶胶-凝胶法负载TiO2且硝酸铁掺杂处理后可以使铁离子进入微弧氧化TiO2负载膜,改善膜的光催化性能。溶胶-凝胶法负载TiO2膜对废水的光催化降解效率由13.8%提高到42.5%;铁离子掺杂1%可以使负载TiO2膜对废水的光催化效率由42.5%提高到68.9%。     

微波干燥制备Ag/TiO2的光催化活性试验研究

利用钛酸丁酯溶胶—凝胶法制备TiO2凝胶,通过光化学沉积法在TiO2凝胶表面负载Ag,采用微波对凝胶进行干燥制备TiO2光催化剂。以甲基橙为模拟污染物进行光催化降解试验,结果表明该方法制备的Ag/TiO2催化剂光催化活性明显提高。     

WO3和PEG改性TiO2的制备及光催化性能研究

首次使用PEG作为TiO2改性的主要物质，用溶胶凝胶法制备TiO2-WO3颗粒，TiO2-PEG颗粒、TiO2-PEG-WO3颗粒和TiO2颗粒。通过对甲基橙光催化的研究表明：在同样条件下，TiO2-PEG400颗粒的甲基橙光降解效果明显优于其他颗粒，甲基橙光降解率最高达到97．5％。     

Fe~(3+)-TiO_2/AC光催化剂的制备及其光催化性能

以活性炭(AC)为载体,通过溶胶-凝胶法制备了Fe3+离子掺杂的TiO2/活性炭(Fe3+-TiO2/AC)负载型光催化剂,通过SEM、XRD、UV-Vis等手段对光催化剂进行了表征。以125W高压汞灯作为光源,通过对罗丹明B的光降解反应,主要考察了温度对Fe3+-TiO2/AC复合体的光催化活性的影响。结果表明,温度在600℃条件下焙烧的Fe3(+0.15%)-TiO2/AC具有最好的光催化活性。     

天然麦饭石负载TiO2的光催化性能研究

采用溶胶-凝胶法制备了二氧化钛负载于天然麦饭石表面热处理后得到复合光催化剂TiO2/麦饭石,并通过N2吸附-脱附、XRD及IR对其进行表征。探讨了以天然麦饭石为载体制备具有较高光催化活性的负载型TiO2/天然麦饭石复合物的各种影响因素:焙烧温度,加投量,pH值等。研究结果表明:200℃焙烧条件下TiO2/麦饭石复合物具有最大的光催化活性,达到了纯TiO2的光催化效果:对罗丹明B脱色率随着光催化剂增多而增大;对罗丹明B在pH值7～9时具有最大的降解率,开拓和优化TiO2光催化效能的新途径。     

Ce-TiO_2/ACF型催化剂低温降解柴油机醛酮的研究

介绍了溶胶-凝胶法制备负载于活性炭纤维的Ce掺杂TiO2催化剂工艺流程;利用TiO2光催化和ACF吸附的协调技术,分析了表征参数、Ce掺杂量、煅烧条件、光照条件、负载次数和重复使用性等因素对降解醛酮污染物的影响。采用液相色谱技术,对生物柴油发动机尾气中的醛酮污染物进行了采样和分析。结果表明:Ce与TiO2的最佳物质的量比为0.25,最佳煅烧温度为400℃,煅烧时间为4.0 h,醛酮最大降解效率为90%,优化后的Ce-TiO2/ACF型催化剂光催化性能好,具有较强的低温降解生物柴油发动机尾气中醛酮污染物的能力。     

TiO2催化剂薄膜背光催化的研究

利用TiO₂催化剂薄膜进行光催化反应时,根据光照方式的不同可分为正光催化和背光催化.两者相比,背光催化可以避免光在溶液中的衰减而造成的光能损失.本文研究了背光催化时薄膜的厚度,光源波长的选择,及其非均掺杂V对催化效率的影响,同时与正光催化的情况作了比较.结果表明:与正光催化明显不同,背光催化时催化剂薄膜厚度对应于光源波长有一个最佳值,光源波长也只能选择大约在30 0～388nm之间;非均匀掺杂情况与正光催化相同,能提高薄膜的催化效率.     

纳米Au/TiO2薄膜真空紫外光催化降解甲醛

为提高真空紫外光催化对甲醛的去除率并降低副产物O3的浓度,采用低温吸附法在TiO2薄膜上负载纳米Au.研究比较了UV254nm光催化(TiO2/UV)、真空紫外光降解(VUV)、真空紫外光催化(TiO2/VUV)等3种方法对低浓度甲醛的降解效果.结果表明,TiO2/VUV对甲醛的去除率显著高于VUV和TiO2/UV.TiO2表面负载纳米Au粒子能促进光生电子和空穴的分离.因此,在真空紫外光催化降解过程中, Au/TiO2不仅提高甲醛的降解率,还显著分解副产物臭氧,使尾气臭氧浓度降低32%.而且Au/TiO2薄膜在真空紫外光催化过程中具有很好的稳定性.     

Preparations of TiO2 film coated on foam nickel substrate by sol-gel processes and its photocatalytic activity for degradation of acetaldehyde

Anatase TiO2 films were successfully prepared on foam nickel substrates by sol-gel technique using tetrabutyl titanate as precursor. The characteristics of the TiO2 films were investigated by XPS, XRD, FE-SEM, TEM and UV-Vis absorption spectra. The photocatalytic activities of TiO2 films were investigated by photocatalytic degradation reactions of gaseous acetaldehyde, an indoor pollutant, under ultraviolet light irradiation. It was found that Ni^2＋ doping into TiO2 films due to the foam nickel substrates resulted in the extension of absorption edges of TiO2 films from UV region to visible light region. The pre-heating for foam nickel substrates resulted in the formation of NiO layer, which prevented effectively the injection of photogenerated electrons from TiO2 films to metal nickel. The TiO2 films displayed high photocatalytic activity for the degradation of acetaldehyde, and were enhanced by calcining the substrates and coating TiO2 films repeatedly. The high activity was mainly attributed to the improvement of the characteristics of substrate surface and the increase of active sites on photocatalyst.     

印染废水的光催化氧化研究

以活性炭负载TiO2薄膜为催化剂,采用光催化氧化法分别处理靛蓝类染料、三苯甲烷类染料和偶氮类染料模拟废水以及某印染厂的出水。研究了光化时间、废水pH值及COD对处理效果的影响。结果表明：光催化氧化处理印染废水的最适光化时间为240min,最适pH值为4,且在这几种染料中,靛蓝类染料最易降解,而偶氮类染料最难降解。     

活性炭负载TiO2催化剂对直接耐酸大红4BS溶液的光催化降解研究

采用溶胶-凝胶法制备了活性炭负载型TiO2催化剂,采用了XRD、BET和SEM对催化剂进行表征。研究了催化剂对直接耐酸大红4BS的紫外光催化降解,比较了活性炭、P25和TiO2／AC对4BS溶液的降解能力,探讨了催化剂煅烧温度和投加量以及染料溶液的初始浓度对光催化降解率的影响,并对催化剂进行了回收再生实验。结果表明,500℃下煅烧的TiO2／AC催化剂比表面积为1147．88m^2／g、TiO2粒径为21．9nm、晶相组成以锐钛矿为主,具有良好的光催化活性和稳定性;90min后2g／L催化剂对150mg／L的4BS溶液紫外光催化降解率达到99．8％。     

不同基质负载的TiO2薄膜光催化性能的比较

采用溶胶凝胶法制备出纳米TiO2粉末、ITO导电玻璃和普通玻璃负载的纳米TiO2薄膜光催化刺。通过对乙酸的降解实验表明：镀膜4次的TiO2／ITO薄膜的催化活性大约是TiO2／giass薄膜的2倍,与等负载量的TiO2粉末相比也具有较高的光催化活性。使用10次后,TiO2／ITO薄膜和TiO2／glass薄膜的光催化活性分别降低了25％和12％。但经再生后,催化活性可恢复至90％左右。     

不同煅烧温度制备的Mn、N掺杂TiO2光催化性能研究

以MnSO4·H2O为锰源,尿素为氮源,采用溶胶-凝胶法制备不同锻烧温度的纯TiO2、Mn-TiO2及Mn-N-TiO2光催化剂,利用X射线衍射、紫外-可见光漫反射光谱及电子自旋共振等技术对样品形貌和结构进行表征,并以罗丹明B的光催化降解为模型反应,考察不同锻烧温度对其光催化活性的影响.结果表明,Mn、N成功掺入TiO2后,有利于提高光催化剂的热稳定性,抑制锐钛矿相向金红石相转化,且光吸收拓展到可见光区域.Mn、N共掺杂样品比单Mn掺杂样品具有更高的光催化活性,400℃下锻烧的Mn-N-TiO2在可见光下对罗丹明B的降解具有最高的光催化活性,光照2h降解率达到100%.高温锻烧Mn-N-TiO2和Mn-TiO2样品在紫外光照射30min后对罗丹明B的降解率在90%以上.     

金属离子掺杂TiO_2薄膜光催化去除气相中甲醛

采用溶胶-凝胶法在普通玻璃表面制备TiO2,Fe3+/TiO2,La3+/TiO2三种光催化剂,研究了煅烧温度、煅烧时间、涂膜层数、Fe3+和La3+加入量等因素对光催化剂降解气相甲醛的影响。结果表明,La3+/TiO2光催化性能略好于TiO2,Fe3+/TiO2光催化性能最佳。当掺Fe3+的TiO2催化剂煅烧温度为450℃,煅烧时间为2h,Fe:T(imol)=0.3%,涂覆层数为4层,光催化反应3h,实验封闭体系中甲醛的降解率可达49.24%。     

TiO2纤维光催化降解X-3B影响因素研究

采用溶胶-凝胶法及水蒸汽活化热处理工艺制备了15%(质量分数)SiO2掺杂的TiO2纤维,并利用SEM、XRD和HRTEM对其结构进行了表征.同时,以活性艳红X-3B染料水溶液为降解对象,研究了热处理温度、溶液pH值、紫外光源、溶液浓度等因素对TiO2纤维光催化活性的影响.结果表明,所制得的TiO2纤维为锐钛矿相,直径约为5～10μm;其最佳热处理温度为700℃,且在强酸(pH=2)或强碱(pH=14)条件下均表现出良好的光催化活性,并对不同浓度的X-3B溶液都有良好的降解效果,同时TiO2纤维也具有良好的可重复使用性.     

紫外波长与粒径对纳米TiO_2光催化效果的影响

以甲基橙为光催化降解对象,研究了不同波长紫外灯与不同粒径TiO2组合(365 nm紫外灯+10 nm TiO2,365 nm紫外灯+50 nm TiO2,254 nm紫外灯+10 nm TiO2,254 nm紫外灯+50 nm TiO2)光催化降解甲基橙的效果。结果表明,不同波长紫外灯与不同粒径TiO2组合影响光催化降解甲基橙的效果。其中,254 nm紫外灯+10 nm TiO2组合降解效果最好,其次为254 nm紫外灯+50 nm TiO2组合,再其次为365 nm紫外灯+10 nm TiO2组合,降解效果最差的为365 nm紫外灯+50 nm TiO2组合。由此可见,254 nm紫外灯+10 nm TiO2组合的光催化降解甲基橙的效果最好。