This paper studied the biofilm properties and corrosion behavior of sulfate reducing bacteria (SRB) on stainless steel 316L (SS316L) surface in circulating cooling water system with and without additives including hydroxy ethyl fork phosphonic acid (HEDP), dodecyl dimethyl benzyl ammonium chlotide (1227) and NaClO. Biochemical technique, electrochemical technology, X-ray photoelectron spectroscopy (XPS) and scanning electron microscope (SEM) were used. The results show that the extracellular polymeric substance (EPS) in biofilm attached on the SS316L surface mainly contain proteins and polysaccharides, the contents are 98 ug·cm-2 and 635ug·cm-2, respectively. The polysaccharides were cut by 1227 about 80%, while 55% by NaClO. The proteins were reduced by NaClO about 53%, while only 30% by 1227. The potentiodynamic polarization shows that the corrosion potential of SS316L was enhanced from -0.495 V to -0.390 V by the chemical additives, delaying the occurrence of the corrosion. And the corrosion rate was also reduced from 5.19 × 10-3 mm·a-1 to 2.42 × 10-3 mm·a-1. But NaClO still caused pitting corrosion after sterilizing the bacteria, while 1227 can form a protective film on the surface of SS316L. Though HEDP contribute to the bacteria activity, it can enhance the breakdown potential. XPS results confirmed that 1227 can change the value of C:O in the biofilm attached on metal surface, and NaClO can eliminate the existence of amidogen. This study would provide some recommendations for the selection of chemical additives in the thermal power plant.
Environmental Science and Pollution Research - Phytoremediation is considered to be the most environmentally friendly green restoration technology for dealing with mine waste. Adding amendments can... 相似文献
• Fe(III) accepted the most electrons from organics, followed by NO3‒, SO42‒, and O2.• The electrons accepted by SO42‒ could be stored in the solid AVS, FeS2-S, and S0.• The autotrophic denitrification driven by solid S had two-phase characteristics.• A conceptual model involving electron acceptance, storage, and donation was built.• S cycle transferred electrons between organics and NO3‒ with an efficiency of 15%. A constructed wetland microcosm was employed to investigate the sulfur cycle-mediated electron transfer between carbon and nitrate. Sulfate accepted electrons from organics at the average rate of 0.84 mol/(m3·d) through sulfate reduction, which accounted for 20.0% of the electron input rate. The remainder of the electrons derived from organics were accepted by dissolved oxygen (2.6%), nitrate (26.8%), and iron(III) (39.9%). The sulfide produced from sulfate reduction was transformed into acid-volatile sulfide, pyrite, and elemental sulfur, which were deposited in the substratum, storing electrons in the microcosm at the average rate of 0.52 mol/(m3·d). In the presence of nitrate, the acid-volatile and elemental sulfur were oxidized to sulfate, donating electrons at the average rate of 0.14 mol/(m3·d) and driving autotrophic denitrification at the average rate of 0.30 g N/(m3·d). The overall electron transfer efficiency of the sulfur cycle for autotrophic denitrification was 15.3%. A mass balance assessment indicated that approximately 50% of the input sulfur was discharged from the microcosm, and the remainder was removed through deposition (49%) and plant uptake (1%). Dominant sulfate-reducing (i.e., Desulfovirga, Desulforhopalus, Desulfatitalea, and Desulfatirhabdium) and sulfur-oxidizing bacteria (i.e., Thiohalobacter, Thiobacillus, Sulfuritalea, and Sulfurisoma), which jointly fulfilled a sustainable sulfur cycle, were identified. These results improved understanding of electron transfers among carbon, nitrogen, and sulfur cycles in constructed wetlands, and are of engineering significance. 相似文献