Comparison of four supports for adsorption of reactive dyes by immobilized beads

Four materials, sodium carboxymethylcellulose （Na-CMC）, sodium alginate （SA）, polyvinyl alcohol （PVA）, and chitosan （CTS）, were prepared as supports for entrapping fungus Aspergillusfumigatus. The adsorption of synthetic dyes, Reactive Brilliant Blue KN- R, and Reactive Brilliant Red K-2BP, by these immobilized gel beads and plain gel beads was evaluated. The adsorption efficiencies of Reactive Brilliant Red K-2BP and Reactive Brilliant Blue KN-R by CTS immobilized beads were 89.1% and 93.5% in 12 h, respectively. The adsorption efficiency by Na-CMC immobilized beads was slightly lower than that of mycelial pellets. But the dye culture mediums were almost completely decolorized in 48 h using the above-mentioned two immobilized beads （exceeding 95%）. The adsorption efficiency by SA immobilized beads exceeded 92% in 48 h. PVA-SA immobilized beads showed the lowest adsorption efficiency, which was 79.8% for Reactive Brilliant Red K-2BP and 92.5% for Reactive Brilliant Blue KN-R in 48 h. Comparing the adsorption efficiency by plain gel beads, Na-CMC plain gel beads ranked next to CTS ones. SA and PVA-SA plain gel beads hardly had the ability of adsorbing dyes. Subsequently, the growth of mycelia in Na-CMC and SA immobilized beads were evaluated. The biomass increased continuously in 72 h. The adsorption capacity of Reactive Brilliant Red K-2BP and Reactive Brilliant Blue KN-R by Na-CMC immobilized beads was 78.0 and 86.7 mg/g, respectively. The SEM micrographs show that the surface structure of Na-CMC immobilized bead is loose and finely porous, which facilitates diffusion of the dyes.     

物化-厌氧-好氧-溶气吸附工艺在毛条废水治理中的应用

介绍了应用物化 厌氧 好氧 溶气吸附工艺治理毛条废水（ＣＯＤＣｒ浓度１３８０００～１５６００ｍｇ／Ｌ）的工程实例。一年多的运行情况表明ＣＯＤＣｒ去除率达９９３％。     

IVP活性炭脱硫性能的研究

采用IVP活性炭吸附法治理污水场隔油池散发的多组分含H2 S废气。研究表明 ,复杂的废气组分并未影响到该活性炭对H2 S的吸附性能 ,且由于处理的废气湿度较高 ,使吸附性能有了较大的提高     

沉积物颗粒表面分形特征的研究

通过一阶分子连接性指数^1X与分子表面积TSA之间的相关性计算出吸附分子的尺度，采用分形吸附等温线法计算出妫河沉积物的Ds为2．379，官厅沉积物的Ds为2．836．基于沉积物对N2的吸附．脱附等温线数据，采用FHH(Frenkel-Halsey-Hill)方程计算出两种沉积物的表面分形维数Ds，发现官厅沉积物与妫河沉积物的Ds相差不大；温度影响Ds主要是由于升温改变了沉积物的组成与结构．在本实验中采用热力学模型(thenmodynamic model)计算出的Ds值大都超过3．此外，沉积物的Ds与其比表面积、矿物含量、CEC、有机质的相关性差．以萘、菲、芘作为码尺计算出的Ds并不完全是表面空间填充能力的客观表现，而是表面吸附过程的一个重要的综合性特征参数．     

染料中铅的测定

硝酸和双氧水进行消解 ,用石墨炉原子吸收光度法测定染料中的铅。     

玉米芯生物炭对含盐污水中氨氮的吸附特性

以玉米芯为原料制备生物炭,并采用"盐酸+超声波"改性,研究了其对含盐污水中氨氮的吸附特性。结果表明,改性玉米芯生物炭的比表面积和酸性含氧官能团含量较改性前分别提高了7.5、18.2倍,在氨氮初始质量浓度为40 mg/L、盐度为0.45%、p H值为5.0、投加量为2.5 g时,对氨氮的吸附率可达79.4%。改性玉米芯生物炭在含盐条件下对氨氮的吸附过程更符合准二级动力学模型和Langmuir模型,理论最大吸附量为2.538 2~2.842 6 mg/g,显著高于改性前。热力学分析表明,玉米芯生物炭对含盐污水中氨氮的吸附主要为物理吸附,且是自发、放热及熵增加的过程。以HCl为解吸剂,改性前后玉米芯生物炭的最佳吸附-解吸循环次数分别为3、7次,再生后对氨氮的平衡吸附量分别为解吸前的85.1%、93.8%。     

热改性活性炭吸附甲萘威的性能

在N2保护下采用不同高温对活性炭进行热改性,得到了4种改性活性炭(AC-1至AC-4)。采用气体吸附仪、Boehm滴定、傅里叶变换红外光谱仪(FTIR)对活性炭表面的物化性质进行了表征。通过等温吸附试验考察了改性前后活性炭对甲萘威的吸附性能,确定了最佳改性温度为600℃,探讨了活性炭的吸附能力与其表面物化性质之间的关系。结果表明:热改性使活性炭表面的物化性质发生了改变,活性炭对甲萘威的吸附量与其比表面积、孔容、表面酸性官能团和O元素含量具有显著相关性;活性炭对甲萘威的吸附行为符合准二级吸附动力学方程和Langmuir等温吸附方程,颗粒内扩散模型表明内扩散不是控制活性炭吸附速率的唯一阶段。     

湘江衡阳段沉积物对硝态氮的吸附特性研究

为探究沉积物对水体中硝态氮的吸附特性,以湘江衡阳段上游沉积物为研究对象,通过室内模拟吸附试验,探讨沉积物吸附硝态氮的影响因素、动力学规律及吸附等温线特征,并且利用SEM、FTIR等表征手段揭示吸附机理。结果表明,环境因素的改变会对硝态氮的吸附产生一定影响,泥水比的增大使沉积物的固体浓度效应明显,吸附量减小;硝态氮初始质量浓度越高,吸附量越大;温度越低越有利于沉积物对硝态氮的吸附;扰动速率偏高和偏低都会使吸附量减小。吸附过程在60 min后逐渐达到稳定,其吸附过程符合准二级动力学模型方程和Langmuir等温吸附方程,以化学吸附和单分子层吸附为主。SEM表征分析表明,沉积物呈粗糙多孔的片层结构,具有较多的吸附位点;FTIR表征分析表明,沉积物对硝态氮有一定的吸附作用,沉积物中含有羟基、酰基等多种基团,与硝态氮反应的机理主要表现为置换和吸附作用。     

水葫芦/污泥共热解法制备生物炭粒及其对Cr3+的吸附特性

为了促进水葫芦和污泥的资源化利用,探究水葫芦/污泥生物炭粒的基本理化性质及其对水中Cr3+的吸附机制,以水葫芦、污泥为原料,在300~500℃热解温度下制得生物炭粒,通过产率分析、灰分分析、比表面积和孔径分析及SEM（扫描电镜）分析,同时利用吸附动力学模型和等温吸附模型对生物炭粒吸附水中Cr3+的内在机制进行研究,最后采用TCLP（毒性浸出法）测定了不同生物炭粒中重金属的浸出毒性.结果表明:随着热解温度从300℃升至500℃,生物炭粒的产率从14.93%降至11.75%,生物炭粒的灰分含量逐渐升高,比表面积增大.SEM结果显示,水葫芦与污泥质量比为1:10时,生物炭粒比表面积较大,孔隙结构明显.当水葫芦与污泥质量比为1:10、热解温度为500℃时生物炭粒对Cr3+的吸附量最大,为44.96 mg/g.热力学分析显示,生物炭粒对溶液中Cr3+的吸附以化学吸附为主,且为单层吸附.TCLP试验表明,水葫芦/污泥生物炭粒中各重金属（Cd、Zn、Cu、Pb、Ni、Cr）的浸出浓度均低于GB 5085.3-2007《危险废物鉴别标准浸出毒性鉴别》的限值.研究显示,添加水葫芦能改善生物炭粒的理化性质,使得生物炭粒对Cr3+的吸附量增大,以化学吸附为主,且为单层吸附,水葫芦/污泥生物炭粒浸出毒性较低,可为生物炭类环境功能材料的研制提供选材依据.      

Fe2O3@SCe多相芬顿催化剂的制备及其降解放热性能

为研究多相Fenton体系降解有机污水过程的放热规律,为污水处理的能源化利用提供技术支撑,本文以半焦（SCe）为载体,制备了Fe₂O₃@SCe新型复合材料,并对复合材料进行了BET、FTIR、XRD、SEM表征,研究了Fe₂O₃@SCe/H₂O₂多相Fenton体系处理邻苯二胺（OPD）模拟废水的降解性能和放热规律.结果表明,Fe₂O₃均匀负载于SCe颗粒表面,Fe₂O₃@SCe复合材料保留了改性SCe的多孔形态和强吸附性,在3.1~8.9的pH值范围内均表现出较高的催化活性;Fe₂O₃@SCe/H₂O₂多相Fenton体系在去离子水中自身分解和在邻苯二胺模拟废水的降解反应都释放了大量的热量,在[OPD]= 0.04mol/L;pH=7.8;T₀=30℃;[H₂O₂]=0.25mol/L;[Fe₂O₃@Sce]=533g/L;t=180min反应条件下的溶液温度升高数值为7.1℃,降解率为88.2%; H₂O₂的投加浓度是影响反应放热量的主要因素.