近场地震作用下库区深水钢筋混凝土高墩地震易损性分析∗

为研究近场地震作用下库区深水钢筋混凝土高墩的概率损伤特性,以90 m高的矩形空心薄壁钢筋混凝土深水高墩为研究对象,综合考虑桥墩设计参数和近场地震动的随机性,基于OpenSees软件建立深水高墩有限元模型,开展不同水深的7种工况(水深:0、15、30、45、60、75、90 m)下,顺桥向和横桥向近场地震激励的增量动力非线性分析。以截面临界曲率值为损伤指标,研究深水高墩的易损性。结果表明:各工况下,轻微损伤、中等损伤和严重损伤阶段的损伤概率均随地震波峰值加速度的增加而增大,并且当峰值加速度达到1.0g时损伤概率达到最大,而完全损伤阶段的损伤概率则在峰值加速度为0.5g时出现峰值点;近场地震顺桥向激励时,墩身中上部和墩底区域均较容易损伤,而横桥向激励时仅墩底区域较容易损伤;当水深超过45 m后,高墩最大损伤概率变化不大且截面曲率概率需求基本一致,45 m水深为深水高墩显著水深。因此,应重点分析水深达到高墩高度一半时深水高墩的损伤情况。     

改性植被混凝土基材力学与植生试验研究

为探明羧甲基纤维素钠(CMC)与麦秸秆纤维对植被混凝土基材力学与植生性能的影响,通过直剪试验、植生试验研究了改性后植被混凝土基材(简称改性基材)的抗剪性能与黑麦草生长性能.结果 表明:①改性基材的剪切强度随CMC掺量的增加呈先增后减的变化趋势,0.5％CMC掺量时基材的剪切强度出现峰值,而随纤维掺量的增加改性基材剪切强...     

温拌阻燃沥青混合料阻燃效果评价

通过氧指数、质量损失率及路用性能试验,研究EC130温拌剂、FRMAX型阻燃剂对沥青混合料阻燃效果的影响。试验结果显示,相比普通沥青混合料,阻燃沥青混合料、温拌阻燃沥青混合料氧指数分别增加23.3%、25.6%,质量损失率减小28.0%、32.0%,残留动稳定度增加14.0%、16.1%,残留最大弯拉应变增加14.1%、17.1%,冻融劈裂强度比增加5.3%、9.0%。相比普通沥青路面,阻燃沥青路面、温拌阻燃沥青路面发生火灾时能够减少34.0%、41.1%的毒害气体生成,并减少路面修补所需的混合料质量。其次得出普通沥青路面、阻燃沥青路面及温拌阻燃沥青路面的质量损失率、残留动稳定度、残留最大弯拉应变、残留冻融劈裂强度比与燃烧时间的关系模型。结果表明:阻燃剂对沥青混合料的阻燃效果显著;温拌剂有助于阻燃剂更好地发挥阻燃作用,降低火灾对道路的破坏,降低隧道火灾发生时有害气体的生成,提升隧道安全性。     

Arsenic and chromate removal from water by iron chips-Effects of anions

The purpose of this study is to estimate the removal efficiency of As and Cr (VI) by one kind of industrial waste — iron chips, as well as to estimate the effects of typical inorganic anions (sulfate, phosphate, and nitrate), and typical organic anions (citrate, oxalate, and humate) on As or Cr (VI) removal. The results showed that 98% of As (V) and 92% of As (III) could be removed from aqueous phase by the iron chips within 60 min. Compared with As species, Cr (VI) was removed much more rapidly and efficiently with 97% of Cr (VI) being removed within 25 min. The removal efficiency for arsenic was in the order: As (III) (sulfate), As (III) (nitrate) or As (III), As (III) (humate), As (III) (oxalate), As (III) (citrate), As (III) (phosphate), and for chromate was in the order: Cr (VI) (sulfate), Cr (VI) (phosphate) or Cr (VI) (nitrate) or Cr (VI) (oxalate), Cr (VI), Cr (VI) (citrate), Cr (VI) (humate). In all the treatments, pH level increased with time except for As (III), the removal of which was either without anions or in the presence of humate or nitrate.     

Mechanical performance and capillary water absorption of sewage sludge ash concrete (SSAC)

Disposal of sewage sludge from waste water treatment plants is a serious environmental problem of increasing magnitude. Waste water treatment generates as much as 70 g of dry solids per capita per day. Although one of the disposal solutions for this waste is through incineration, still almost 30% of sludge solids remain as ash. This paper presents results related to reuse of sewage sludge ash in concrete. The sludge was characterised for chemical composition (X-ray flourescence analysis), crystalline phases (X-ray diffraction analysis) and pozzolanic activity. The effects of incineration on crystal phases of the dry sludge were investigated. Two water/cement (W/C) ratios (0.55 and 0.45) and three sludge ash percentages (5%, 10% and 20%) per cement mass were used as filler. The mechanical performance of sewage sludge ash concrete (SSAC) at different curing ages (3, 7, 28 and 90 days) was assessed by means of mechanical tests and capillary water absorption. Results show that sewage sludge ash leads to a reduction in density and mechanical strength and to an increase in capillary water absorption. Results also show that SSAC with 20% of sewage sludge ash and W/C = 0.45 has a 28 day compressive strength of almost 30 MPa. SSAC with a sludge ash contents of 5% and 10% has the same capillary water absorption coefficient as the control concrete; as for the concrete mixtures with 20% sludge ash content, the capillary water absorption is higher but in line with C20/25 strength class concretes performance.     

Sustainability assessment of EPS-geofoam in road construction: a case study

ABSTRACT

In the present study, construction procedure and performance assessment of expanded polystyrene EPS-geofoam layer, which is utilized in the repair and rehabilitation of road work, is demonstrated. EPS geo-foam application was suggested after observing excessive settlement and distress of approach roads near Cross drainage (C-D) works constructed on bypass road of an important National Highway Project in India. EPS-geofoam was used as an alternative to earth backfill in approaches of newly constructed culvert on the same bypass road on one side of the C-D work and, for comparison purpose; the other side of the C-D work was retained with existing earth backfill. EPS-Geofoam was convenient to handle, easy to place and executed effeciently in terms of machineries and man power. Also, after 6 months of observation, it was noted that Pavement Quality Concrete (PQC) constructed over earthfill material have shown sign of distress and longitudinal cracks were observed due to excessive settlement; on the other hand PQC constructed over EPS-geofoam was intact with no sign of distress. Outcome of the study suggest the use of EPS-geofoam in similar situations as per the proposed guidelines for construction as well as cross-sectional details and design recommended.     

透水砖铺装的设施构造对运行效果的影响

为考察缝隙透水砖铺装的基层构造与材料对设施运行效果的影响,在上海市区建造了2个缝隙透水砖铺装(permeable interlocking concrete pavement,PICP)与1个不透水混凝土铺装(concrete pavement,CP)停车场,其中2个缝隙透水砖铺装分别采用水泥稳定碎石(PICP1)和普通碎石(PICP2)作为基层结构.在2018年实际降雨条件下对2个设施的水文效果及底部出流水质进行了长期监测.结果表明PICP1与PICP2的年径流总量控制率相近,分别为37. 0%和38. 7%,PICP1的峰值削减率及峰现延迟时间略优于PICP2.水质控制效果方面,PICP1比PICP2有更好地NH_4~+-N转化效果,两种设施底部出流均存在NO_3~--N淋出的现象; PICP1底部出流的TSS、TP、颗粒态磷和溶解态磷浓度均低于PICP2.采用水泥稳定碎石作为基层有助于提高设施的水质净化效果,并改善设施的水文控制效果.     

过硫酸钠缓释胶囊反应带修复苯胺污染地下水

针对有机污染地下水原位化学氧化修复中普遍存在的氧化剂过量使用、污染物反弹和二次污染问题,以苯胺（AN）为特征污染物,以活化过硫酸盐为氧化剂,采用硬脂酸为胶结剂,制备过硫酸钠（PS）和硫酸亚铁（FeSO₄）缓释胶囊,构建基于PS和FeSO₄缓释胶囊的可渗透反应屏障（PS-FeSO₄-PRB）,考查了缓释胶囊组分、地下水流速对PRB中活性物质释放和AN去除的影响.结果表明,当缓释胶囊中活性物质/硬脂酸为1/2,地下水流速为0.1mL/min时,48h后PRB中PS和Fe²⁺累计释放率分别为43.18%和14.98%.当PRB中FeSO₄/PS为1/9时,AN累计去除率达到95.37%,TOC累计去除率为57.07%.采用砂柱模拟AN污染地下水,比较了直接注射PS和FeSO₄与PS-FeSO₄-PRB两种处理方式的修复性能,4d内两者的AN累计去除率分别为35.22%和69.74%,TOC累计去除率分别为15.83%与14.88%.PS-FeSO₄-PRB修复效果明显高于直接注射处理.GC/MS分析表明,处理后产生了对苯醌、偶氮苯以及长链烷烃等产物,导致AN矿化率不高.pH值和Eh连续记录结果表明,PS-FeSO₄-PRB处理能够保持反应体系氧化还原电位和酸碱性的相对稳定.相比直接注射氧化剂,基于PS和FeSO₄-缓释胶囊的PRB处理中地下水的急性毒性更低,二次污染风险更小.     

钢筋混凝土结构盐冻破坏分析及寿命预测

为评估北方季冻区除冰盐对钢筋混凝土结构耐久性的影响,开展了混凝土试件的盐冻试验,根据试验测得的混凝土相对动弹性模量与质量损失率,分析了钢筋混凝土结构在冻融环境下的损伤情况,得到了盐冻环境下钢筋混凝土盐冻损伤度随冻融循环周期变化的关系式。同时将钢筋混凝土盐冻损伤度引入到氯离子扩散模型(DuraCete模型)中,修正了公式中氯离子扩散系数,使得该公式更适用于冻融环境,最终得到了钢筋混凝土结构的寿命预测公式。修正后的钢筋混凝土结构的寿命预测公式既考虑了冻融和氯离子侵蚀双重作用,又不需要对氯离子扩散系数进行经验取值,使得本预测模型更方便、实用。     

火灾下钢筋混凝土梁热力学性能数值模拟分析*

为了研究火灾下钢筋混凝土（RC）简支梁的热力学性能,建立火灾高温下RC梁的数值分析模型,与火灾试验对比验证模型的有效性;分别对4根完全相同的RC梁进行不同受火试验,研究受火时间、混凝土高温爆裂及钢筋-混凝土黏结高温退化对RC梁截面温度场分布、钢筋应力与滑移量分布、残余抗弯承载力的影响规律。研究结果表明:截面温度梯度随受火时间增长而扩大,底部角筋比其他纵筋升温均快;混凝土爆裂对直接受火面10 mm厚度范围内温度影响较为显著,角筋升温速率随受火时间增长而增大;底部纵筋应力随受火时间增长而下降,中筋的应力高于角筋;钢混界面滑移量随受火时间增长而增大,底部中筋的滑移量小于角筋;残余抗弯承载力随受火时间增长而线性减小;爆裂深度对残余抗弯承载力的影响程度要高于爆裂面积,跨中1/5跨长位置爆裂对残余抗弯承载力影响最大。