钒掺杂磁铁矿对亚甲基蓝的吸附性能研究

采用共沉淀硝酸盐氧化法合成了不同掺杂量的钒掺杂磁铁矿(Fe3-xVxO4, x<0.4),并运用化学分析、X射线衍射(XRD)、BET比表面积测试、傅立叶变换红外光谱(FTIR)以及N2和空气气氛下的热重-差示扫描量热分析(TG-DSC)等手段对合成的Fe3-xVxO4进行了结构表征. 结果显示,合成的Fe3-xVxO4为立方晶系尖晶石结构,钒离子主要类质同像替换八面体位上的Fe3+. 合成的Fe3-xVxO4是纳米级的磁性材料,晶粒尺寸为28～35 nm. 钒掺杂作用增加了磁铁矿的表面羟基量. 吸附实验结果表明,在中性pH下,Fe3-xVxO4对亚甲基蓝的饱和吸附量随钒掺杂量的增加明显增大,其吸附等温线符合Langmuir方程. Fe3-xVxO4对亚甲基蓝的吸附反应主要在前25 min内完成,动力学曲线符合准二级动力学方程. 此外,提高溶液的pH有利于Fe3-xVxO4对亚甲基蓝的吸附.     

Efficient dechlorination of chlorinated solvent pollutants under UV irradiation by using the synthesized TiO2 nano-sheets in aqueous phase

Titanium dioxide(TiO2), which is the widely used photo-catalyst, has been synthesized by simple hydrothermal solution containing tetrabutyl titanate and hydrofluoric acid. The synthesized product has been applied to photo-degradation in aqueous phase of chlorinated solvents, namely tetrachloroethene(PCE), trichloroethene(TCE) and 1,1,1-trichloroethane(TCA). The photo-degradation results revealed that the degradation of these harmful chemicals was better in UV/synthesized TiO2 system compared to UV/commercial P25 system and UV only system. The photo-catalytic efficiency of the synthesized TiO2 was 1.4, 1.8 and 3.0 folds higher compared to the commercial P25 for TCA, TCE and PCE degradation, respectively. Moreover, using nitrobenzene(NB) as a probe of hydroxyl radical(.OH), the degradation rate was better over UV/synthesized TiO2, suggesting the high concentration of.OH generated in UV/synthesized TiO2system. In addition,.OH concentration was confirmed by the strong peak displayed in EPR analysis over UV/synthesized TiO2system. The characterization result using XRD and TEM showed that the synthesized TiO2 was in anatase form and consisted of well-defined sheet-shaped structures having a rectangular outline with a thickness of 4 nm, side length of 50 nm and width of 33 nm and a surface 90.3 m2/g. XPS analysis revealed that ≡Ti-F bond was formed on the surface of the synthesized TiO2. The above results on both photocatalytic activity and the surface analysis demonstrated the good applicability of the synthesized TiO2 nano-sheets for the remediation of chlorinated solvent contaminated groundwater.     

Dyes adsorption using a synthetic carboxymethyl cellulose-acrylic acid adsorbent

Removal of noxious dyes is gaining public and technological attention. Herein grafting polymerization was employed to produce a novel adsorbent using acrylic acid and carboxymethyl cellulose for dye removal. Scanning electron microscopy and Fourier-transform infrared spectroscopy verified the adsorbent formed under optimized reaction conditions. The removal ratio of adsorbent to Methyl Orange, Disperse Blue 2BLN and malachite green chloride reached to 84.2%, 79.6% and 99.9%, respectively. The greater agreement between the calculated and experimental results suggested that pseudo second-order kinetic model better represents the kinetic adsorption data. Equilibrium adsorptions of dyes were better explained by the Temkin isotherm. The results implied that this new cellulose-based absorbent had the universaiity for removal of dyes through the chemical adsorption mechanism.     

石墨烯基磁性复合材料吸附水中亚甲基蓝的研究

建立了一种超声辅助共沉淀法制备磁性Fe3O4/氧化石墨烯(Fe3O4/GO)纳米粒子.透射电镜和磁滞回线研究表明,该复合物具有小的颗粒尺寸和超顺磁性.该磁性纳米材料可以吸附废水中的染料亚甲基蓝,实验研究了溶液pH值、吸附剂的用量、时间和温度对亚甲基蓝去除率的影响.结果表明,pH值在6~9范围内,Fe3O4/GO都能高效地吸附亚甲基蓝.反应过程在前25 min反应速率很快,到180 min内达到吸附平衡.该磁性纳米材料对亚甲基蓝的吸附符合Langmuir吸附等温模型和准二级动力学方程,吸附过程是一个自发和吸热过程.该吸附材料对亚甲基蓝吸附容量高,在313 K时Fe3O4/GO的饱和吸附量为196.5 mg·g-1.另外,可以方便地通过外部磁场分离回收吸附剂,利用过氧化氢可以再生重复使用,是一种优良的吸附染料废水的材料.     

废旧锌锰电池生物淋滤-水热法制备纳米锰锌铁氧体

以氧化硫硫杆菌(A.thiooxidans)和氧化亚铁钩端螺旋菌(L.ferrooxidans)为混合淋滤菌株对废旧锌锰电池进行了生物浸提,并以获取的淋滤液为前驱体,采用水热法制备出系列锰锌铁氧体软磁材料(Mn_(1-x)Zn_xFe_2O_4,x=0.2~0.8);结合X射线衍射(XRD)、扫描电镜-能谱(SEMEDX)、振动样品磁强计(VSM)、透射电镜(TEM)、红外光谱(FT-IR)、热重-差热分析(TG-DTA)等表征手段对制备材料的结构、形貌、磁学性能和稳定性进行分析.结果表明,在5%固液比(质量体积比,5 g/100 mL,以下均表述为"5%固液比")下,经过5 d的外源酸调控生物浸提,分别获得了84.5%、63.2%的Zn、Mn浸出效率;当Zn∶Mn∶Fe=0.4∶0.6∶2.0(物质的量比,即x=0.4)时,制备的纳米级Mn_(0.6)Zn_(0.4)Fe_2O_4性能最优,属纯相的立方尖晶石结构,颗粒分布均匀,饱和磁化强度(M_s)、剩余磁化强度(M_r)和矫顽力(H_c)分别为68.9 emu·g~(-1)、4.7 emu·g~(-1)和53.6 Oe,具有热稳定性和耐酸碱性,有望成为一种新型的水处理磁性材料.     

Zr掺杂TiO_2介孔材料光催化降解头孢氨苄

采用固相合成法制备了Zr掺杂TiO_2(Zr-TiO_2),运用XRD技术对其进行了表征,并将其用于水中头孢氨苄的光催化降解,通过单因素实验及正交实验优化了光催化反应条件。结果表明:制备的Zr-TiO_2为锐钛矿型介孔材料,孔径约为8.12 nm;各因素对头孢氨苄去除率的影响由大到小依次为光照时间、Zr-TiO_2投加量、初始头孢氨苄质量浓度;在Zr-TiO_2投加量为1.5 g/L、初始头孢氨苄质量浓度为10 mg/L、溶液pH为7.0、光照(300 W UV)时间为1.5 h的优化条件下,头孢氨苄去除率高达99.46%;Zr-TiO_2光催化剂的重复使用性能良好。     

铝铁锡共聚物的合成及其特性研究

合成制备了铝铁锡共聚物，测定分析了其水解共聚合和熟化过程中的pH变化，并通过扫描电镜和混凝实验对共聚物的晶形貌像和絮凝作用进行了研究。结果表明：Sn^4 具有比Fe^3 ，Al^3 更强的水解活性，它有使共聚物的分子趋于均一的作用；铝铁锡共聚物的最佳配比为：NAl∶NFe∶NSn=5∶5∶3,最佳水解度B^*＝2．0,此共聚物具有比CPAFC更优良的絮凝性能。     

含锰废渣的氧化-活化再生回用工艺

为实现紫苏醛生产过程中二氧化锰（氧化剂）的循环利用,采用一种新型的氧化-活化工艺再生得到活性二氧化锰,即以紫苏醇合成紫苏醛过程中产生的含锰废渣为原料,首先采用氯酸钠氧化含锰废渣得到初级二氧化锰,然后使用高锰酸钾对初级二氧化锰进一步活化得到活性二氧化锰。实验表明,制取初级二氧化锰的最佳工艺条件为：反应时间为4h,反应温度为90～95℃,硫酸摩尔浓度为1.5 mol/L,氯酸钠加量为理论量的130%。制取活性二氧化锰的合适条件为：反应温度在60℃时,反应时间为1.5 h;反应温度在50℃时,反应时间为2.5 h。采用氧化-活化法再生的活性二氧化锰氧化紫苏醇,紫苏醛的产率可达52.8%,与使用电解二氧化锰氧化得到的紫苏醛的产率53.1%相当,而使用初级二氧化锰,紫苏醛的产率仅为14.9%。     

羧酸盐型双子表面活性剂的合成及性能研究

以月桂酰氯、乙二胺与丁二酸酐为原料合成了一种羧酸盐型双子(gemini)表面活性剂。采用IR、1 HNMR对中间产物和目标产物进行结构表征,并考察了合成所得羧酸盐型gemini表面活性剂的表面活性。结果表明:合成产物即为目标产物。合成产物的临界胶束浓度为0.027mmol/L,比普通单链表面活性剂低2～3个数量级,表面张力最低可降至29.5mN/m。     

溶剂热法合成SnWO_4及其可见光催化活性

采用溶剂热法合成了新型的可见光催化剂SnWO4,以甲基橙为目标污染物,考察了合成温度、合成时间和煅烧工艺对催化剂可见光催化活性的影响。实验结果表明:煅烧工艺会明显降低催化剂的光催化活性;在合成温度为180℃、合成时间为8h、未煅烧的条件下,合成的催化剂的光催化效果最好,光照90min后,对甲基橙的降解率可达99.93%。