粉煤灰合成NaA型沸石对重金属离子的吸附动力学

以粉煤灰为原料,采用两步法合成了单一沸石矿物种的NaA型沸石,对合成产物的结构和性能进行了表征.通过静态吸附实验,研究了NaA型沸石对水溶液中Cu(ΙΙ)、Cr(Ⅵ)和Zn(ΙΙ)离子的吸附特性,从动力学角度探讨了吸附机理.结果表明,在所研究的浓度和pH值条件下,NaA型沸石对3种重金属的吸附符合Langmuir等温吸附方程,静态饱和吸附量(Qm)分别为82.30,65.96,47.78mg/g;3种金属离子在水溶液中的存在方式和大小是影响它们吸附行为的主要因素,通过动边界模型推算表明:NaA型沸石对Cu(ΙΙ)和Zn(ΙΙ)离子的吸附过程的速度控制步骤为液膜扩散,对Cr(Ⅵ)离子的吸附过程的速度控制步骤为颗粒扩散,3种金属离子的吸附过程符合伪二级方程.     

Long-term evaluation of coal fly ash and mine tailings co-placement: A site-specific study

This study presents the results of a laboratory investigation conducted to evaluate the efficiency of coal fly ash to control the formation of acid mine drainage (AMD) from mine waste. Site-specific materials, coal fly ash from Atikokan Thermal Generating Station and mine tailings from Musselwhite mine, were mixed at different proportions for the investigation of the drainage chemistry and the optimal mix using static testing (acid–base accounting) and kinetic (column) testing. The acid–base accounting (ABA) results indicated that the fly ash possessed strong alkaline (neutralization) potential (NP) and could be used in the management of reactive mine tailings, thus ensuring prevention of AMD in the long-term. Column tests conducted in the laboratory to further investigate long-term performance of fly ash in the neutralization and prevention of acid mine drainage from tailings similarly showed that mixing fly ash with mine tailings reduces dissolution of many heavy metals from tailings by providing alkalinity to the system. It was found that a fly ash to tailings mass ratio equal to or greater than 15% can effectively prevent AMD generation from Musselwhite mine tailings in the co-placement approach.     

飞灰螯合剂中挥发性污染物的释放

采集了4个市售飞灰螯合剂样品，分析其在20，40℃下挥发性污染物的释放规律.结果表明，释放的挥发性污染物主要有甲醛、乙醛、苯、异戊醛/异丙醇、甲硫醇、乙硫醇等；其中3个螯合剂样品甲醛的释放浓度在20℃为748~1325 μg/L-螯合剂，占释放的易挥发污染物的68%~96%（质量比），在40℃为4282~6822 μg/L-螯合剂，占释放的易挥发污染物的87%~95%（质量比）.随着温度升高，释放的挥发性污染物种类变多，部分污染物浓度增加，40℃时，4个螯合剂样品释放的易挥发污染物浓度比20℃时增加了142%~444%.元素分析、拉曼光谱和热重分析结果表明，4个螯合剂的主要有效成分相似，为二硫代氨基甲酸盐类物质.因此，推测这种飞灰螯合剂在稀释和飞灰稳定化过程中，对工作人员的健康可能有潜在的危害风险，应收集释放的气体并进行处理；且在飞灰填埋过程中，可能会导致渗滤液中NH₄⁺-N等物质的浓度升高，增加渗滤液的处理难度.     

固化飞灰形状及填埋方式对重金属浸出的影响

为探究成型形状和填埋方式对生活垃圾焚烧飞灰固化体中重金属浸出的影响，设置固化体尺寸分别为10×10×10cm、10×10×2.5cm、DN=3cm（球），同时设置码放、散乱堆放2种填埋方式进行动态浸出试验.结果表明，在固化体开裂前，球状与长方体、整齐码放与散乱堆放的浸出液pH值存在显著差异；单位质量固化体重金属Pb、Zn、Cr累积浸出量随固液接触面积、堆填散乱度、液固比的增大而增加，固化稳定化飞灰中重金属的浸出符合缩芯模型且主要由扩散过程控制，试验前段Pb、Zn、Cr的2种速率常数与固化体成型比表面积、堆填散乱度、液固比正相关.因此，要减少生活垃圾焚烧厂原灰中重金属的浸出，提高生活垃圾填埋场共处置飞灰固化稳定化产物的安全性，固化体成型时应尽量缩小比表面积同时避免散乱填埋.     

碱熔融法合成NaA和NaX型粉煤灰沸石的品质表征

以粉煤灰为原料采用碱熔融法合成了2种单一沸石矿物种的NaA和NaX型沸石,并对产物的结构、性能和应用指标进行了详细表征.经x射线衍射和IR光谱分析,表明合成产物是无杂晶生成的NaA和NaX型沸石相;在扫描电镜观察下,产物分别具有NaA和NaX型沸石的立方体和八面体晶体骨架结构.DTA分析表明了合成产物中沸石水的存在,且产物热稳定性较好.通过对比,粉煤灰合成的NaA和NaX型沸石的比表面积达到了相应商品沸石的66.9%和83.6%;孔容为41.1%和70.2%;阳离子交换容量(CEC,cation exchange capacity)为82.93%和84.31%.通过比较化学组成表明,大规模应用合成产物不会对环境造成危害.     

Effect of unburned carbon on lead, zinc, and copper recovery from molten fly ash by chloride-induced volatilization

The present work focuses on investigation of the effective recovery of heavy metals from molten fly ash by applying chloride-induced volatilization. In particular, the effect of unburned carbon on the chloride-induced volatilization of lead, zinc, and copper from model and real molten fly ashes was investigated in the temperature range 873–1173 K under a N₂ atmosphere. As a result, almost 100% of lead and a significant proportion of zinc were volatilized from the real molten fly ash samples at 1173 K. In contrast, for the model fly ash, volatilization ratios of lead and zinc at 1173 K were only 85% and 25%, respectively. Further, the results of X-ray diffraction analysis suggested that PbO in molten fly ash was converted either to Pb₂OCl₂ or Pb by respective chlorination and reduction reactions. Meanwhile ZnO and CuO in the molten fly ash were reduced to Zn and Cu by reaction with unburned carbon. Subsequently, Pb, Zn, and Pb₂OCl₂ were volatilized, but Cu remained in the solid residue. Finally, the volatilization ratio of zinc increased with the addition of carbon, and more than 98% of zinc was volatilized at 1173 K from a fly ash with a carbon content of 20%.     

垃圾焚烧飞灰处置与资源化利用研究进展

随着生活垃圾焚烧处理方式的不断推广，焚烧飞灰的产生量也不断增加。按照我国固体废物分类方法，焚烧飞灰属于危险废物，必须进一步处置才能进入填埋场或资源化利用。本文分析了飞灰物理化学特性，论述了常规处置技术（水泥固化、化学药剂稳定化、酸溶剂提取和熔融固化等）存在的问题。将原始飞灰直接应用于水泥、混凝土或路基材料，飞灰中高含量的重金属和盐类会产生新的环境问题。飞灰水洗可以高效去除其中的可溶性盐类，水洗飞灰在焙烧后重金属的浸出浓度远低于原始飞灰烧结后的相应浓度，飞灰水洗-焙烧技术具有很好的应用前景。     

Characterization of MSWI fly ash through mineralogy and water extraction

This paper investigates the mineralogical characteristics of fresh, aged and hot water extracted MSWI fly ash for providing the baseline information of minerals stability which controls the released heavy metals into the environment. Quantitative determination of bulk phase abundance in the fresh fly ash by the XRD Rietveld refinement method provided composition levels for amorphous and crystalline phases such as potassium tetrachlorozincate (K₂ZnCl₄), gehlenite, halite, quartz, anhydrite, and feldspar. The minerals association in the fly ash is clearly unstable and subject to mineralogical reactions. The phases of K₂ZnCl₄, halite and anhydrite in the fresh fly ash were involved in hydration and dissolution/precipitation processes to form new minerals such as the Zn-bearing mineral gordaite, syngenite, gypsum and hydrocalumite. The solubility-controlling phases and extractability of heavy metals were examined in a Soxhlet hot water-extractor. Here the soluble salts were simply removed from fly ash while Ca-, Al-, Si- and SO₄²⁻-bearing hydrate minerals were precipitated from the extraction solution. Furthermore, a low release of heavy metals Zn, Pb and Cd in hot water was noticed, indicating a strong retention of the trace metals in the mineral phases remaining in the insoluble fly ash residues.     

基于二次铝灰的地聚反应稳固化垃圾飞灰

基于工业生产铝过程中回收的二次铝灰（SAD）的地质聚合反应,提出了一种稳固化城市生活垃圾焚烧飞灰（MSWIFA）的新方法,分析硅铝物质的量之比对飞灰中重金属浸出浓度及地聚物固化体力学性能的影响规律.结果表明,当硅铝物质的量之比小于2.5时,二次铝灰-SiO₂基固化体与偏高岭土-SiO₂基固化体中的重金属浸出浓度均随着硅铝物质的量之比的增加而逐渐降低,2种固化体的抗压强度随着硅铝物质的量之比的增加而增加;硅铝物质的量之比达到2.5时,重金属的浸出浓度与固化体的抗压强度均趋于稳定.XRD分析结果显示,偏高岭土-SiO₂基固化体中聚合物的种类与数量均略高于二次铝灰-SiO₂基固化体.但从重金属的浸出浓度与固化体的抗压强度来看,2类固化体对飞灰中重金属的稳固化效果的差别很小,二次铝灰加上部分硅基材料可以作为偏高岭土的替代品,用于稳固化飞灰重金属的地质聚合反应中.二次铝灰-SiO₂基固化体的抗压强度达到13.65MPa,具备一定的力学性能,可用于部分特定的建筑材料.     

不同粒度飞灰中16种微量元素的含量分布

研究了不同粒级的燃煤飞灰中的Ｂａ、Ｂｅ、Ｃｄ、Ｃｒ、Ｃｕ、Ｈｇ、Ｌｉ、Ｍｎ、Ｎｉ、Ｐｂ、Ｓｒ、Ｔｉ、Ｖ、Ｚｎ、Ｚｒ元素的含量分布,煤中元素的含量比及富集因子。