有机蒙脱石负载纳米铁去除溶液中四溴双酚A的研究

研究了改性蒙脱石负载纳米铁材料(NZVI-CMT)在甲醇-水体系中对四溴双酚A(TBBPA)的去除作用,并确定了反应温度、TBBPA初始浓度以及材料投加量等因素对去除效果的影响.结果表明,在25℃条件下,0.02 g NZVI-CMT对初始浓度为10 mg·L-1TBBPA溶液的去除率可达97.5%,而且NZVI-CMT对TBBPA的去除率明显高于两种单一材料即纳米零价铁(NZVI)及有机蒙脱石(CMT)的去除率(18.3%、67.3%),同时也大于两者之和(85.6%).利用NZVI-CMT对TBBPA进行重复去除实验时,前3次的去除率均可达到90%以上.通过检测降解产物并分析材料对TBBPA去除过程的特性,发现NZVI-CMT对TBBPA的去除以吸附为主,并伴有少量还原脱溴反应发生,而且较高的反应温度对降解反应有利.     

Photocatalytic activity of TiO2 containing anatase nanoparticles and rutile nanoflower structure consisting of nanorods

A series of TiO2 with different crystal phases and morphologies was synthesized via a facile hydrothermal process using titanium nbutoxide and concentrated hydrochloric acid as raw materials. The photocatalytic activity of the samples was evaluated by degradation of Methyl Orange in aqueous solution under UV-Visible light irradiation. On the basis of detailed analysis of the characterizing results of high-resolution transmission electron microscopy, X-ray powder diffraction measurements, X-ray photoelectron spectroscopy and Brunauer-Emmett-Teller measurement, it was concluded that the photo-activity of the catalyst is related directly to the 3D morphology and the crystal phase composition. An excellent catalyst should have both a futile 3D flower-like structure and anatase granulous particles. The 3D flower-like structure could enhance light harvesting, as well as the transfer of reactant molecules from bulk solution to the reactive sites on TiO2. In addition, the optimum anatase/rutile phase ratio was found to be 80：20, which is beneficial to the effective separation of the photogenerated electron-hole pairs.     

Enhanced photocatalytic activity of quantum-dot-sensitized one-dimensionally-ordered ZnO nanorod photocatalyst

An efficient photocatalyst was fabricated by assembling quantum dots （QDs） onto one-dimensionally-ordered ZnO nanorods, and the photocatalytic properties for Methyl Orange degradation were investigated by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-Vis-NIR absorption spectroscopy and photoluminescence. The results indicate that the catalyst with assembled QDs is more favorable for the degradation than the pristine ZnO nanorods. The QDs with core-shell structure lower the photocatalytic ability due to the higher carder transport barrier of the ZnS shell layer. Besides its degradation efficiency, the photocatalyst has several advantages given that the one-dimensionally-ordered ZnO nanorods have been grown directly on indium tin oxide substrates. The article provides a new method to design an effective and easily recyclable photocatalyst.     

磁性纳米Fe_3O_4对毒死蜱的增效和催化降解研究

应用溶剂热法制备了磁性纳米Fe3O4(NMFO),并用聚乙二醇-6000对其进行改性,使纳米Fe3O4表面由亲水性转变为亲脂性,从而实现与亲脂性毒死蜱的复合。纳米Fe3O4的加入使毒死蜱的生物活性明显提高。室内毒力试验结果表明:含0.2%纳米Fe3O4的Fe3O4/毒死蜱制剂的毒力在室内和紫外光照下分别是同浓度纯毒死蜱的3.84倍和4.17倍;其降解率也显著提高,纳米Fe3O4/毒死蜱制剂在太阳光照下放置10 d,其降解率可达93.2%,相同条件下纯毒死蜱的降解率是10.14%,而将添加或未添加纳米Fe3O4的毒死蜱于暗处放置相同的时间,其降解率分别为1.21%和0.23%。     

人造沸石负载纳米氧化镁同步脱氮除磷的研究

氮、磷是引发水体富营养化的限制性因素,控制水体中的氮、磷总量可以有效抑制水体富营养化的产生。以人造沸石为研究对象,探究不同改性方法对人造沸石同步去除水中氮、磷的影响。主要工艺为高温碱(NaOH)浸改善沸石结构,高温盐浸(MgCl)负载纳米态氧化镁。结果表明改性的最佳条件为:两阶段的烘干温度45℃;NaOH溶2+3-液浓度0.5 mol/L;MgCl溶液的浓度1 mol/L。对NH-N和PO的去除效率分别可达到83.76%和74.24%。对人造沸石2 4 4的热稳定性进行了实验,其烧失量达40.6%。最后,对吸附饱和的人造沸石进行脱附实验,脱附剂的选择为NaCl、KCl以及+3-两者的混合液。NaCl对NH4+-N和PO43-都有较为明显的脱附效果,脱附率分别可达84.54%和59.35%。     

纳米氢氧化钛及焙烧产物对磷酸根的吸附特性研究

以纳米氢氧化钛(NTH)作为吸附水溶液中磷酸根的吸附剂,考察了NTH不同焙烧温度下的分子式及其对PO4吸附效果的影响。选择PO4初始浓度为50mg/L,通过正交试验确定在pH=2、吸附剂用量为0.1g、吸附时间3-3-为40min、温度25℃时,NTH吸附效果达到最佳,吸附量为55.5mg/g,经200、300、400及500℃焙烧后的NTH对磷酸根的吸附量逐渐减小;吸附量分别为49.4、40.6、25.5及16.8mg/g;NTH经800℃焙烧后,焙烧产物TiO2不具有吸附性。TG、XRD分析表明随着焙烧温度的升高,NTH的表面活性基团(-OH)数量逐渐减少。结果表明,吸附剂的吸附性与吸附剂表面羟基的数量有直接关系。     

采掘业井工开采项目地下水环境影响评价相关问题探讨-以凯达煤矿项目为例

本文针对采掘业并工开采项目地下水环境影响评价的特点,根据在环境影响评价工作中的实践经验,以位于内蒙古自治区鄂尔多斯市准格尔旗境内的凯达煤矿为例,就地下水导水裂隙带、地下水影响范围、含水层、居民水井等问题具体分析、并结合产生的影响提出具体的防治措施.     

江西浮梁葫芦尖锡矿地质特征及外围找矿前景分析

本文介绍了葫芦尖锡矿区区域地质背景、锡矿体的地质特征,系统阐述了地层、构造和岩浆岩地质特征。通过重点分析该矿区及外围地区的找矿前景,发现葫芦尖矿区构造蚀变岩带是重要的找矿标志,认为莲花山(潘村)——鄣公山地区成矿地质条件优越,锡多金属矿找矿潜力巨大,进一步在该地区进行锡多金属矿找矿、勘查工作都将对找矿突破产生积极的促进和指导作用。     

三峡库区消落带生态环境问题探讨

三峡工程的竣工,在库区两岸形成了垂直高差达30m的涨落地带,称之为消落带,对水库的实际运行影响深远。通过对这片区域特点和现状的研究,总结了当前三峡库区消落带出现的各种环境问题,如生态破坏、环境污染、景观影响、疾病问题、地质灾害等。针对各类环境问题的出现,提出了生态恢复、污染预防与治理、合理规划管理、出台相应政策等解决方法和控制措施,以期实现库区消落带的保护和充分利用,为库区社会、经济、环境的可持续发展提供参考。     

活性炭/纳米零价铁复合吸附剂的制备及对砷的去除应用

纳米零价铁在重金属去除领域应用前景广阔。为了大批量、低成本地制备纳米零价铁,本文采用电化学还原法在粒状活性炭表面电沉积纳米零价铁,通过X射线衍射分析对产物的结构进行了表征,并初步探讨了制备的纳米零价铁/活性炭复合吸附剂对模拟地下水中As(III)的去除效果。结果表明,通过自行设计的电沉积装置,成功地在颗粒活性炭上沉积了纳米零价铁颗粒。制备的活性炭/纳米零价铁复合吸附剂对模拟地下水中As(III)的去除效果良好。电化学沉积法制备纳米零价铁,技术可行,成本低廉,在重金属去除领域具有较大的应用潜力。