Several natural and anthropogenic radionuclides (²¹⁰Pb, ²²⁶Ra and ¹³⁷Cs) in guano-phosphatic coral sediments and pure guano particles collected from Ganquan, Guangjin, Jinqing and Jinyin Islands of the Xisha archipelago, South China Sea, were analyzed. The Constant Initial Concentration (CIC) model and the Constant Rate of Supply (CRS) model were applied for age calculation. The average supply rate of ²¹⁰Pb was 126 Bq m⁻² a⁻¹, very close to the flux of northern hemisphere average (125 Bq m⁻² a⁻¹). The activities of anthropogenic radionuclides in the sediments were very low, indicating that human nuclear tests did not notably impact this region. The main source of radionuclides in the sediments was from atmospheric precipitation, and the organic matter derived from plant and produced by nutrient-rich guano could further enhance them.     

机载电子设备灌封材料在西沙环境下的耐老化性研究

目的考察机载电子设备常用灌封材料在西沙环境下的耐老化性能。方法开展西沙海洋环境下4种灌封材料的棚下暴露实验,暴晒实验时间为3年,分别通过测试表面电阻、体积电阻、介电常数、损耗角正切等手段研究其老化特点。结果 267有机硅、DC160有机硅两类样品外观未出现明显变化,且介电常数、损耗角正切、表面电阻、体积电阻均变化较小,112FR环氧树脂、8836聚氨酯两类样品出现变色、产生针孔起泡等现象,介电常数、损耗角正切、表面电阻和体积电阻均变化幅度较大。结论在机载电子设备选用绝缘灌封材料时,可优先选用267有机硅、DC160有机硅这两类灌封材料,112FR环氧树脂和8836聚氨酯谨慎选用。     

防腐涂层西沙户外试验与氙灯试验对比分析

以8种船用电子设备防腐涂层为研究对象,开展西沙户外暴露试验和氙灯光老化试验。从外观评级、光泽度、色差3个方面进行了评价与对比分析,探讨了涂层材料在2种试验条件下的老化现象及其差异性,研究了其在不同应力条件下的老化特征及老化原因。结果表明,参试涂层体系西沙户外2 a的老化程度高于氙灯光60 d的老化程度。     

海南西沙试验站大气霉菌群落初步调查

目的 筛选西沙试验站大气环境优势菌种,进行西沙试验站装备敏感菌研究。方法 采用撞击法进行大气霉菌采样,用统计学法计算出不同试验场地真菌数量,结合形态学法与ITS1-5.8S-TIS2或26SrDNA D1/D2区序列分析法鉴定菌种,并用SPSS初步探讨大气真菌与环境因素的关系,分析西沙试验站装备敏感菌。结果 西沙试验站优势种为Aspergillus aculeatus、Penicillium citrinum、Pithomyces sacchar、变红镰孢霉Fusarium incarnatum、Cladosporium oxysporum和Cladosporium oryzae,影响西沙试验站大气霉菌群落结构的重要环境因素是相对湿度和风速,贮存在西沙试验站的装备容易长霉,多种材料有不同的敏感菌,尤其是涂层样件和橡胶类材料。结论 西沙试验站大气环境中存在种类繁多的霉菌。     

铝合金/高强度钢连接件西沙暴露试验

选取某飞机铝合金/高强度钢连接件开展西沙暴露试验,掌握连接件腐蚀变化趋势。结果表明,连接件保护涂层耐老化性能良好,采用湿装配有效避免了电偶腐蚀和缝隙腐蚀,连接件背面螺栓、螺母和铆钉（30CrMnSiA,表面镀镉）为其腐蚀薄弱环节,需加强防护。     

几种典型金属材料西沙海洋飞溅区腐蚀行为规律研究

目的研究几种典型金属材料在西沙海洋飞溅区的腐蚀行为规律。方法通过外场暴露试验,分析3种钢、1种铜和3种铝合金材料暴露0.5,1,2 a后的腐蚀形貌与动力学规律。结果 3种钢的腐蚀质量损失与点蚀均较为严重,T2整个表面均匀减薄的同时,会产生大量微小的腐蚀坑,3种铝合金发生以点蚀为主的局部腐蚀,伴随有晶间腐蚀、选择性腐蚀等。结论试验条件下,3种钢中Q235耐蚀性最差,T2整体耐蚀性较好,3种铝合金中5083耐点蚀性能最差,5052略优于6063。     

万宁滨海与西沙群岛大气腐蚀性对比研究

统计分析了西沙群岛和万宁试验站近海场的润湿时间、空气中二氧化硫和氯离子沉积速率,根据环境因素法和标准金属法评定了两地的大气腐蚀性,两地的大气腐蚀等级同为C5级,但西沙群岛的腐蚀性稍弱于万宁试验站近海场。Q235钢、镀镍钢、镀铬钢、不锈钢钝化件在两地的试验结果证实了上述结论,试验结果表明,万宁试验站近海场积累的大量试验数据可应用于西沙群岛。     

几种典型金属材料西沙海洋全浸区腐蚀行为规律研究

目的研究几种典型金属材料在西沙海洋全浸区的腐蚀行为规律。方法通过外场暴露试验,分析EH36和CM690船用钢、316L不锈钢以及5083铝合金材料暴露0.5、1、2a后的腐蚀形貌与动力学规律。结果CM690腐蚀速率要大于EH36,而点蚀深度规律相反。316L不锈钢发生较为严重缝隙腐蚀,5083铝合金则以局部腐蚀为主。结论试验条件下,EH36与CM690钢腐蚀质量损失与点蚀最为严重,316L不锈钢与5083铝合金生物污损严重,伴有局部腐蚀。     

机载电子设备印制电路板环境适应性研究

目的考察机载电子设备印制电路板在西沙环境下的环境适应性。方法开展西沙海洋环境下2种印制电路板的棚下暴露实验,暴晒实验时间为3年,分别通过外观、绝缘电阻、耐压性、品质因数研究其老化特点。结果两类印制电路板样品的绝缘电阻和品质因数呈总体下降趋势,PCB2的绝缘电阻下降相对较小,PCB1样本耐电压测试出现击穿并有明显的腐蚀情况。结论 PCB2工艺体系的环境适应性能好于PCB1,在机载电子设备印制电路板选用过程中推荐优先。     

西沙海洋大气环境中典型材料腐蚀形貌识别

目的获得西沙海洋大气环境中典型材料的表面腐蚀形貌参数,分析其腐蚀规律。方法采用室外大气暴露试验,研究5052铝合金、304不锈钢和EH36低合金钢在西沙海洋大气环境中的腐蚀形貌及腐蚀规律,并采用图像数字处理方法识别试样表面腐蚀特征。结果 EH36钢的大气腐蚀形貌以均匀腐蚀和腐蚀坑为主,而5052铝合金以及304不锈钢以点蚀为主,EH36低合金钢的腐蚀速率明显高于5052铝合金和304不锈钢。三种典型材料腐蚀面积百分比与腐蚀坑面积百分比的变化趋势相同,5052铝合金和EH36低合金钢的腐蚀面积百分比和腐蚀坑面积百分比与二者腐蚀速率变化规律一致,而304不锈钢的腐蚀面积百分比和腐蚀坑面积百分比与其腐蚀速率变化规律相反。5052铝合金和EH36低合金钢1年周期试样的腐蚀坑数目均大于2年周期试样,而对于304不锈钢,1年周期试样的腐蚀坑数目与2年周期试样差别不大。结论西沙大气环境中,三种典型材料的腐蚀速率、腐蚀面积百分比、腐蚀坑面积百分比均有明显不同,对同一种材料,其正面的腐蚀面积百分比、腐蚀坑面积百分比、腐蚀坑数与背面也有较大差别。