A new approach to Assess Atmospheric Nitrogen Deposition by Way of Standardized Exposition of mosses

A standardized method of moss exposition for assessing variations in nitrogen deposition was tested in the western part of Germany. Six pleurocarpous moss species were transplanted to two sites differing in their deposition rates but being comparable as to their climatic conditions. The mosses were exposed in standardized containers over a period of 12 months; the focus of interest was the effect of N deposition on nitrogen content and on ¹⁵N natural abundance (δ¹⁵N-values). Within the first nine months only trends could be observed. However, after one year all species tested showed significantly higher N concentrations at the highly polluted site. Besides, more negative δ¹⁵N-values possibly reflecting the higher ammonium input were detected at this site. Surprisingly, most of the plants though being kept in plastic containers without a favourable substratum did not show any conspicuous deficiency symptoms. The potential advantages of a standardized moss exposition for N monitoring purposes are discussed. It is concluded that the method presented here can yield significant results in particular if the number of testing sites is increased.     

Differences in the growth response of three bryophyte species to nitrogen

The effect of nitrogen on biomass production, shoot elongation and relative density of the mosses Pleurozium schreberi, Hylocomium splendens and Dicranum polysetum was studied in a chamber experiment. Monocultures were exposed to 10 N levels ranging from 0.02 to 7.35 g N m⁻² during a 90-day period. All the growth responses were unimodal, but the species showed differences in the shape parameters of the curves. Hylocomium and Pleurozium achieved optimum biomass production at a lower N level than Dicranum. Pleurozium had the highest biomass production per tissue N concentration. Tolerance to N was the widest in Dicranum, whereas Hylocomium had the narrowest tolerance. Dicranum retained N less efficiently from precipitation than the other two species, which explained its deviating response. All species translocated some N from parent to new shoots. The results emphasize that the individual responses of bryophytes to N should be known when species are used as bioindicators.     

Long term changes in atmospheric N and S throughfall deposition and effects on soil solution chemistry in a Scots pine forest in the Netherlands

In a Scots pine forest the throughfall deposition and the chemical composition of the soil solution was monitored since 1984. (Inter)national legislation measures led to a reduction of the deposition of nitrogen and sulphur. The deposition of sulphur has decreased by approximately 65%. The total mineral-nitrogen deposition has decreased by ca. 25%, which is mainly due to a reduction in ammonium-N deposition (−40%), since nitrate-N deposition has increased (+50%). The nitrogen concentration in the upper mineral soil solution at 10 cm depth has decreased, leading to an improved nutritional balance, which may result in improved tree vitality. In the drainage water at 90 cm depth the fluxes of NO₃⁻ and SO₄²⁻ have decreased, resulting in a reduced leeching of accompanying base cations, thus preserving nutrients in the ecosystem. It may take still several years, however, before this will meet the prerequisite of a sustainable ecosystem.     

Acid Deposition in the Tuscan Appennines During the Dry Period 1988-89

The typical parameters of acid precipitation are evaluated in the forest of Vallombrosa (Tuscan Appennines) during the dry period 1988-89. Individual rain events (dry and wet deposition) were sampled in a clearing of the forest and below the canopy of an evergreen tree as well as a deciduous broadleaf tree.

In atmospheric precipitation the pH values usually vary around 4.4, with neutralization in the hot season due to calcareous material from distant sources. Relatively large concentrations of Pb and Cd are found in rain, but only in a small amount in canopy leachate. Aluminium, manganese and iron are more significantly washed off than Pb and Cd.     

大气沉降向华中丘陵区稻田输入硫通量的观测

选取我国华中丘陵区的湖南省长沙县一个典型水稻种植区,对2015与2016年2年雨水样中的SO₄²-S和大气SO₂的沉降量进行监测,分析雨水中SO₄^2-、NO₃^-的关系,解析大气硫沉降的主要来源.结果表明,研究区大气中SO₂-S和雨水中SO₄^2--S的年均浓度分别为8.5 μg/m³和1.1mg/L,大气硫沉降年均总量为26.8kgS/（hm²·a）,其中年均降雨混合沉降量18.2kgS/（hm²·a）,年均干沉降量为8.6kgS/（hm²·a）.研究区域硫素干、混合沉降量存在明显的季节差异,硫素混合沉降春季高于夏、秋、冬季,而硫素干沉降冬季高于春、夏、秋季.雨水中NO₃^-/SO₄^2-的质量比大多小于1,表明研究区大气硫素主要来自固定污染源（燃煤）.华中丘陵区稻田具有较高的硫沉降,但硫沉降量已较21世纪初出现了较大幅度下降,农业生产中需要根据农田硫素收支状况酌情补充硫肥来保证作物高产稳产.     

新型防腐涂层对直升机典型结构材料防护性能研究

目的研究新型防腐涂层对直升机典型结构用铝合金及复合材料在热带海洋性气候环境下的防护性能,并与原防护涂层进行对比。方法通过测试涂层腐蚀后的形貌、光泽度、色差、电化学阻抗等,对比新/原涂层对直升机典型结构用铝合金和复合材料的防护性能。结果经过2年腐蚀后,新涂层表面无明显变化,而原涂层表面有轻微腐蚀,光泽度和色差下降较大。电化学阻抗测试表明,暴露前后涂层结构无明显变化,涂层阻抗值呈现持续下降的趋势,但是原涂层阻抗下降更快。结论新涂层对直升机典型铝合金和复合材料有更好的防护性,更加适于海洋性环境的使用。     

7B04铝合金和30CrMnSiA钢短期腐蚀的电化学行为研究

目的研究7B04铝合金和30CrMnSiA合金钢试样的电化学性能。方法采用电化学实验、扫描电子显微镜(SEM)、腐蚀坑深度测试分别对7B04铝合金和30CrMnSiA合金钢试样在是否经过天然海水浸泡的情况下进行测试分析,得到微观腐蚀形貌和腐蚀坑深度以及试样表面不带锈和带锈时的电化学性能。结果随着Na Cl浓度增大,7B04铝合金和30CrMnSiA钢的自腐蚀电流变大,两者之间存在明显的电位差,接触后会发生电偶腐蚀。电偶电流与阴阳极面积比和Na Cl浓度有关,阴阳极面积比增大或Na Cl浓度升高均会导致电偶效应增强。经过海水短期浸泡后,7B04铝合金表面的锈层不仅没有起到抑制腐蚀的作用,反而使自腐蚀加重,但电偶效应确实有所减弱。结论沿海设备在使用过程中应竭力避免铝合金在锈层下工作。     

飞机用铝合金腐蚀行为和腐蚀预测研究现状及问题分析

针对不同的航空铝合金结构及部位,从腐蚀机理、腐蚀行为和腐蚀预测技术三方面较为系统地分析了研究现状及进展。在此基础上,明确了航空铝合金腐蚀预测技术需要进一步研究的问题,分别为飞机结构表面腐蚀环境的确定问题,材料在海洋大气环境下腐蚀电化学性能的准确测量问题,腐蚀预测模型的选取问题。     

铝合金的实验室盐雾试验腐蚀行为图像特征提取

目的提取铝合金材料在盐雾箱试验中可以表征腐蚀程度的表面形貌图像特征量。方法首先,对采集于表面化学清洗过的试样原始图像进行图像增强等预处理,突出腐蚀部位;其次,基于数字图像处理的分形和小波分解方法提取出分形维数和小波能量特征值。结果与以质量损失量为基础的腐蚀深度特征值进行相关性对比,基于图像分析的特征提取法的准确度和精度比较高。结论该方法可以应用于对试样的腐蚀程度进行定性和定量分析,判断并预测试样的腐蚀速度。     

高强预腐蚀铝合金单轴拉-拉疲劳断口定量分析

目的通过断口定量分析获得7A09铝合金的疲劳裂纹扩展规律,为7A09铝合金结构的寿命评估提供依据。方法使用EXCO溶液对试验件进行预腐蚀,利用疲劳拉伸机进行疲劳加载直至断裂,使用扫描电镜对疲劳断口进行定量化分析。结果疲劳裂纹在试件的腐蚀坑处萌生,从自由界面附近向纵深发展导致试件的断裂。通过断口分析和Paris公式确定了裂纹的萌生寿命和扩展寿命。结论腐蚀之后的试件裂纹萌生寿命占总寿命的比例下降,当裂纹扩展程度较大之后,受腐蚀影响减轻,得出裂纹扩展速率和应力强度因子的关系。