Study on the influence of various factors in the hydrometallurgical processing of waste printed circuit boards for copper and gold recovery

The present lab-scale experimental study presents the process of leaching waste printed circuit boards (WPCBs) in order to recover gold by thioureation. Preliminary tests have shown that copper adversely affects gold extraction; therefore an oxidative leaching pre-treatment was performed in order to remove base metals. The effects of sulfuric acid concentration, hydrogen peroxide volume and temperature on the metal extraction yield were studied by analysis of variance (ANOVA). The highest copper extraction yields were 76.12% for sample A and 18.29% for sample D, after leaching with 2 M H₂SO₄, 20 ml of 30% H₂O₂ at 30 °C for 3 h. In order to improve Cu removal, a second leaching was performed only on sample A, resulting in a Cu extraction yield of 90%. Other experiments have shown the negative effect of the stirring rate on copper dissolution. The conditions used for the process of gold extraction by thiourea were: 20 g/L thiourea, 6 g/L ferric ion, 10 g/L sulfuric acid, 600 rpm stirring rate. To study the influence of temperature and particle size, this process was tested on pins manually removed from computer central processing units (CPUs) and on waste CPU for 3½ h. A gold extraction yield of 69% was obtained after 75% of Cu was removed by a double oxidative leaching treatment of WPCBs with particle sizes smaller than 2 mm.     

Degradability Characterization of EPDM/IIR Blends by γ-irradiation

In this paper the modifications induced in butyl rubbers (pristine, chlorinated and brominated sorts) by γ-irradiation are investigated by swelling, chemiluminescence and FT-IR. The susceptibility of butyl rubbers for the generation of radicals orders their stabilities in the following sequence: IIR?>?IIR—Cl?>?IIR—Br. The incorporation of butyl rubbers into ethylene-propylene terpolymer matrix brings about increased densities of radicals initiating modifications in the oxidation state in respect with recombination, which are intensified as the processing dose increases. Based on the variation of carbonyl and hydroxyl indices the favorable route for the recycling EPDM based formulations would be suggested in this study. The chemiluminescence spectra proving the formation of peroxyl radicals at about 100?°C prove their availability as reclaiming solutions. IIR—Br is the recommendable butyl rubber for the recovery procedure by association with EPDM. The suitability of IIRs for recycling purposes is analyzed by the variation in their crosslink densities, free volumes and swelling degrees. The crosslinking behavior of stabilized EPDM/IIR blends that runs to the improvement of durability is depicted by Charlesby–Pinner representation, which involves the different simultaneous contribution of scission and crosslinking processes.     

Study concerning the recovery of zinc and manganese from spent batteries by hydrometallurgical processes

Used batteries contain numerous metals in high concentrations and if not disposed of with proper care, they can negatively affect our environment. These metals represent 83% of all spent batteries and therefore it is important to recover metals such as Zn and Mn, and reuse them for the production of new batteries. The recovery of Zn and Mn from used batteries, in particular from Zn–C and alkaline ones has been researched using hydrometallurgical methods. After comminution and classification of elemental components, the electrode paste resulting from these processes was treated by chemical leaching. Prior to the leaching process the electrode paste has been subjected to two washing steps, in order to remove the potassium, which is an inconvenient element in this type of processes. To simultaneously extract Zn and Mn from this paste, the leaching method in alkaline medium (NaOH solution) and acid medium (sulphuric acid solution) was used. Also, to determine the efficiency of extraction of Zn and Mn from used batteries, the following variables were studied: reagents concentration, S/L ratio, temperature, time. The best results for extraction yield of Zn and Mn were obtained under acid leaching conditions (2 M H₂SO₄, 1 h, 80 °C).