钙钛矿型La_(0.8)Ce_(0.2)Fe_(1-x)Co_xO_3催化剂的制备及其三效催化活性

采用自燃烧法制备了一组钙钛矿型复合氧化物La_(0.8)Ce_(0.2)Fe_(1-x)Co_xO_3(x=0.9,0.7,0.5,0.3,0.1),并考察了其对CO、C_3H_6和NO的三效催化活性。XRD和SEM表征结果显示,La_(0.8)Ce_(0.2)Fe_(1-x)Co_xO_3具有良好的钙钛矿型晶体结构,晶粒大小为纳米级并自组装成片状结构。催化剂的比表面积为14.73~22.43 m~2/g,含有微孔和介孔结构。催化活性评价结果表明:La_(0.8)Ce_(0.2)Fe_(0.1)Co_(0.9)O_3具有很好的三效催化活性,在理论空燃比的条件下,CO、C_3H_6和NO的起燃温度分别为195℃、264℃和290℃,完全转化温度分别为239℃、418℃和415℃,低温三效催化活性良好;Fe和Co的掺杂量同时影响着La_(0.8)Ce_(0.2)Fe_(1-x)Co_xO_3的催化效果。     

CaH2对Cu-Ce-La-ZSM-5催化分解NO性能的影响

实验采用一步离子交换法制备Cu-Ce-La-ZSM-5催化剂,然后采用共混法制得Cu-Ce-La-ZSM-5/CaH2催化剂。采用扫描电镜（SEM）,电感耦合等离子体发射光谱（ICP-AES）,X射线衍射（XRD）,红外（FTIR）以及NO吸脱附（NO-TPD）对催化剂进行表征。结果显示CaH2的加入使得催化剂中铜离子存在形式发生变化,催化剂表面变光滑洁净,并且吸附NO能力增强。NO催化分解实验的结果表明CaH2提高了催化剂活性和抗氧性。CaH2助催性是由于其受热分解过程中产生的H2能将Cu^2＋还原为具有催化活性的Cu^＋,同时使催化剂表面洁净光滑更容易吸附NO。     

酸雨与镧对大豆幼苗生长的复合伤害效应研究

为探索酸雨与稀土镧对大豆幼苗生长的复合影响及其内在机制,以重要油粮作物大豆(Glycine max)为材料,研究在模拟酸雨pH分别为3.0、3.5、4.5与稀土镧La(Ⅲ)浓度分别为60、100和300mg·L-1处理下大豆幼苗生长及光合作用的变化.结果表明,相对单一酸雨与镧处理,酸雨与La(Ⅲ)复合处理组中大豆幼苗的生长受抑制程度增大,两者呈协同效应,且pH越低,La(Ⅲ)浓度越高,抑制效应越明显.光合参数的变化规律与生长指标近同,相同处理组各光合参数的降幅不一致,其中最大荧光(Fv/Fm)和叶绿素含量(Chl)的降幅范围分别为9.53%～22.75%和9.14%～24.53%,较净光合速率Pn(22.78%～84.7%)、希尔(Hill)反应速率(15.52%～73.38%)和Mg2+-ATPase活性(14.51%～71.54%)小,表明各光合参数对2个胁迫因子的敏感程度存在差异.进一步相关性分析发现,Pn变化主要受Hill反应速率与Mg2+-ATPase活性的影响,而Chl、Fv/Fm次之.表明酸雨与La(Ⅲ)对植物光合过程各环节的作用机制不同,光合作用受阻是影响植物生长的重要因素之一.     

氧化铝负载镧去除水中F-的研究

通过固相反应合成了氧化铝负载的氧化镧吸附剂并研究了其对水中F-的吸附.结果表明.合成的材料对F-有很好的去除效果,最大吸附量达到53.4 mg·g-1;适当提高吸附温度和氧化镧负载量都能在一定范围内提高吸附量;较低的固相反应焙烧温度有利于提高去除率,随着焙烧温度的升高,吸附量从170℃焙烧的42.2 mg·g-1下降到了350℃焙烧的32.9 mg·g-1.同时,吸附剂表现出了很好的适应性,在较宽的pH范围内都能保持较高的吸附量.     

镧对UV-B胁迫下大豆幼苗类黄酮含量与抗氧化能力影响

为进一步认识La(Ⅲ)提高类黄酮含量及减轻UV-B辐射伤害植物机制,以大豆幼苗为材料,采用水培实验的方法研究了La(Ⅲ)对UV-B辐射胁迫下大豆幼苗类黄酮抗氧化能力的动态影响.结果表明, UV-B辐射(T1:0.15W·m-2和T2:0.45W·m-2)胁迫下,大豆幼苗类黄酮含量在胁迫期和恢复期均先升后降,质膜透性、MDA含量先升(1～5d)后降(6～11d),类黄酮对O·-2和·OH的清除率与其含量变化趋势近同.各处理组类黄酮含量La(Ⅲ) UV-B>UV-B>La(Ⅲ)>CK, La(Ⅲ) T1>La(Ⅲ) T2;质膜透性、MDA含量UV-B>La(Ⅲ) UV-B>CK>La(Ⅲ), La(Ⅲ) T2>La(Ⅲ) T1;类黄酮对O-2和·OH清除率La(Ⅲ) UV-B>UV-B>La(Ⅲ)>CK, La(Ⅲ) T1, La(Ⅲ) T2,表明La(Ⅲ)对类黄酮的调控作用,提高了清除活性氧自由基的运行效率,降低了MDA浓度,维持了质膜正常透性,且对低剂量(T1)的防护效果优于高剂量(T2),进而在防御系统层面实现了La(Ⅲ)对UV-B辐射伤害大豆幼苗的防护效应.     

Effects of rare earth elements La and Yb on the morphological and functional development of zebrafish embryos

In recent years, with the wide applications and mineral exploitation of rare earth elements, their potential environmental and health effects have caused increasing public concern. Effect of rare earth elements La and Yb on the morphological and functional development of zebrafish embryos were studied. The embryos were exposed to La³⁺ or Yb³⁺ at 0, 0.01, 0.1, 0.3, 0.5 and 1.0 mmol/L, respectively. Early life stage parameters such as egg and embryo mortality, gastrula development, tail detachment, eyes, somite formation, circulatory system, pigmentation, malformations, hatching rate, length of larvae and mortality were investigated. The results showed La³⁺ and Yb³⁺ delayed zebrafish embryo and larval development, decreased survival and hatching rates, and caused tail malformation in a concentration-dependent way. Moreover, heavy rare-earth ytterbium led to more severe acute toxicity of zebrafish embryo than light rare-earth lanthanum.     

镧及其配合物对鱼体肝脏中酶活性的影响

以鲫鱼（Ｃａｒａｓｓｉｕｓ ａｕｒａｔｕｓ）为实验对象，研究了镧（Ｌａ）及其配合物（Ｌａ－ＥＤＴＡ）对鱼体肝脏中过氧化氢酶和超氧歧化酶的早期作用过程。结果表明：在实验浓度下Ｌａ＾３＋与Ｌａ－ＥＤＴＡ对鱼肝中过氧化氢酶有激活作用，但最终表现为强烈抑制：而对超氧歧化酶最初显著抑制，最后表现为激活作用。     

CaH_2对Cu-Ce-La-ZSM-5催化分解NO性能的影响

实验采用一步离子交换法制备Cu-Ce-La-ZSM-5催化剂,然后采用共混法制得Cu-Ce-La-ZSM-5/CaH2催化剂。采用扫描电镜(SEM),电感耦合等离子体发射光谱(ICP-AES),X射线衍射(XRD),红外(FTIR)以及NO吸脱附(NO-TPD)对催化剂进行表征。结果显示CaH2的加入使得催化剂中铜离子存在形式发生变化,催化剂表面变光滑洁净,并且吸附NO能力增强。NO催化分解实验的结果表明CaH2提高了催化剂活性和抗氧性。CaH2助催性是由于其受热分解过程中产生的H2能将Cu2+还原为具有催化活性的Cu+,同时使催化剂表面洁净光滑更容易吸附NO。     

Mg-La-Fe/沸石复合材料的制备及其处理低浓度含磷废水的性能

以沸石为载体,选用镁、镧和铁为改性剂,采用水热法制备了一种新型高效且易于磁性分离回用的载镧磁性沸石吸附剂（MLFZ）.等温吸附和动力学研究结果表明,其吸附行为符合Langmuir等温模型和准二级动力学模型,MLFZ饱和吸附量为13.46 mg·g^-1; MLFZ在pH为3～9范围内均表现出良好的吸附性能,共存离子条件下对磷酸根具有特异吸附能力,通过磁性吸附重复使用5次后,MLFZ对磷酸盐去除率维持在90%左右,突显了其易于回收再利用的优点;FTIR、 XPS和Zeta电位表征显示,表面沉积、静电吸附作用和镧与磷酸盐通过配体交换形成内层络合物在吸附过程中为主要作用.将MLFZ用于处理自然池塘污水,结果显示磷酸盐浓度由0.86 mg·L^-1降低到0.013 mg·L^-1,表明该吸附剂具有良好的实际应用前景.     

镧掺杂氧化锌光催化降解染料废水研究

以醋酸锌和硝酸镧为原料,丙烯酰胺为单体,N,N’-亚甲基双丙烯酰胺为网络剂,过硫酸铵为引发剂,采用高分子网络凝胶法制备得到掺镧的Zn O纳米粉体。用制备的粉体对甲基橙进行光催化降解实验,考察了掺镧量对其光催化性能的影响。用X射线衍射仪、高分辨率透射电镜、X射线能谱仪、比表面积与孔隙率分析仪等对其进行表征。结果表明,镧的掺入提高了Zn O的光催化活性,镧锌摩尔质量比为0.2%时光催化性能最好,高压汞灯下反应1 h,甲基橙的脱色率为96.5%,相比于未掺杂的Zn O提高了11.5%。