In this study, a three-dimension (3D) computational model was proposed to investigate the flow and heat transfer characteristics of the intake grilles of two different fuel cell vehicles. The models of the intake grilles were constructed according to the actual sizes of two vehicles, namely, Roewe 950 and Toyota Mirai, considering the heat dissipation unit to simplify the heat transfer model of the vehicle. The results showed that relative to Roewe 950, Mirai intake air flow rate was approximately 10% higher, the heat transfer capacity was approximately 7% higher, and the intake grille area was larger. The coolant outlet temperature of Mirai was lower than that of Roewe 950, which was beneficial for the long term and stable operation of a fuel cell. This comparative study provided guidance for the intake grille and radiator design of fuel cell vehicles. The only difference between fuel cell vehicles on the market and conventional vehicles was that in the former, the internal combustion engine was replaced with a fuel cell stack, which had insufficient heat transfer capacity because of the reducing temperature difference. Increasing the intake grille area and the heat exchange capacity of the radiator were the key issues for the development of fuel cell vehicles. In this study, an optimal window opening angle of the radiator fin of 23° provided a maximal heat transfer coefficient.     

内质网应激在氟暴露致小鼠睾丸损伤中的作用

探讨了内质网应激在亚慢性氟暴露致小鼠睾丸损伤中的作用及分子机制.选用健康初断乳ICR雄性小鼠30只,随机分为对照组（C）、低氟组（LF）和高氟组（HF）,分别饮用自来水、5、30 mg·L^-1氟化钠水溶液90 d.亚慢性氟暴露结束后,以睾丸脏器系数、睾丸组织氧化/抗氧化酶和形态结构、精子质量、睾丸细胞凋亡、葡萄糖调节蛋白78（GRP78）、CCAAT/增强子结合蛋白同源蛋白（CHOP）、半胱氨酸天冬氨酸蛋白酶12（CASPASE-12）、半胱氨酸天冬氨酸蛋白酶3（CASPASE-3）为观测点.结果表明,与对照组比,LF组和HF组LDH、SOD、T-AOC活性下降,MDA含量上升,HF组GSH-PX活性下降,差异有统计学意义（p<0.05或p<0.01）;LF组可见细胞层次减少、间隙变大,成熟精子数量减少,HF组细胞溶解、层次紊乱,空泡化严重,少见成熟精子;LF组和HF组小鼠的精子活力降低,HF组小鼠精子数量下降,畸形率上升,差异有统计学意义（p<0.05或p<0.01）;LF组和HF组睾丸细胞凋亡指数上升,差异有统计学意义（p<0.01）;LF组和HF组Grp78、Caspase-12、Caspase-3基因表达水平上升,差异有统计学意义（p<0.05或p<0.01）.结果提示,除氧化应激以外,Caspase-12和Caspase-3基因表达异常可能是氟暴露致小鼠睾丸细胞凋亡异常的分子机制之一.     

内饰材料发射率对密封舱室热防护效率的影响

目的探究密封舱室热防护效率与其内饰材料表面发射率的关系,分析内饰材料发射率对其表面温度、舱室内温度的影响规律。方法采用自行设计的小型密封舱室和加热测量装置,对内饰材料表面及舱室内温度进行测量。结果当内饰材料发射率为0.09时,内饰表面温度为141.2℃,舱室内平均温度仅为90.8℃;内饰材料发射率为0.91时,内饰表面温度为124.4℃,舱室内平均温度为109.1℃。结论试样表面温度随材料发射率的提高而降低,舱室内部空气平均温度随材料发射率的提高而升高;试样表面温度与舱室空气平均温度的温度差随材料发射率的提高而减小;同时,相同试样表面温度与舱室平均温度的温度差随加热温度的提高而增加。     

短期干旱胁迫对马尾松排放挥发性有机物的影响

为探究干旱环境对BVOCs排放的影响,应用动态封闭式采样系统和热脱附-气相色谱-飞行质谱仪,对短期干旱胁迫作用下马尾松的BVOCs排放进行了实验室测量,定量分析BVOCs排放速率和排放组成的变化.结果表明,干旱胁迫时异戊二烯的排放受到抑制,排放速率降低约50%;单萜烯和倍半萜烯的排放水平增强,排放速率分别为137.85和0.98μg/（m²·h）,是未受胁迫时的2.9和2.0倍.除反式-α-香柠檬烯外,干旱胁迫促进各单萜烯和倍半萜烯化合物的排放,是未受胁迫时的1.3~42.4倍,其中3-蒈烯排放的响应最敏感,α-葑烯、α-水芹烯和石竹烯的响应最弱.干旱胁迫时单萜烯和倍半萜烯的排放组成有所变化,但主导的化合物种类不变,单萜烯以α-蒎烯、香桧烯和β-蒎烯为主,占比分别为48%、17%和17%;倍半萜烯以石竹烯和长叶烯为主,占比分别为57%和34%.     

海水中阴极极化对X80钢应力腐蚀及氢脆敏感性的影响

目的研究不同p H值海水中阴极极化对X80管线钢应力腐蚀及氢脆的抑制作用。方法采用慢应变速率拉伸试验、电化学测试、微观组织观察等分析方法。结果 X80钢在天然海水中的析氢电位约为-940m V(vs.SCE,下同),海水p H为3.5时析氢电位发生正移。其应力腐蚀敏感性与极化电位有很大关系,随着极化电位负移,X80钢的氢脆敏感性增加。天然海水中当极化电位负于-950 m V时,断口出现准解理断裂特征形貌。在-1050 m V极化电位下,钢材进入氢脆断裂区发生脆性断裂。海水p H为3.5时,-900 m V钢材有发生氢脆的危险。结论与天然海水相比,X80钢在p H为3.5的酸性海水中具有较高的应力腐蚀敏感性,两种海水介质中X80钢的应力腐蚀敏感性均随极化电位负移而增加。     

玻璃纤维-铝合金层合板氙灯老化性能研究

目的研究氙灯环境对玻璃纤维-铝合金层合板性能的影响。方法通过研究玻璃纤维-铝合金层合板在氙灯老化后的力学性能、基体红外光谱、铝合金表面形貌及元素变化,分析层合板的氙灯老化机理。结果随氙灯老化时间的延长,树脂基体老化降解程度越高,树脂与纤维、铝合金的界面强度下降,使材料拉伸及弯曲性能降低,拉伸强度受老化影响最为显著的是正交结构层合板,老化84 d后强度降低13.7%,正交结构0°方向层合板的弯曲强度受氙灯老化影响降低4.6%,其他试样的弯曲强度降幅均低于5%,氙灯老化后的铝合金层表面的微凹坑数量及尺寸无明显变化,但凹坑氧元素随老化周期延长略微增加。结论氙灯环境主要影响玻璃纤维-铝合金层合板中的复合材料层及各界面,树脂基体的降解导致力学性能的衰退,而对于铝合金的影响并不明显。     

铍青铜弹簧片应力腐蚀断裂研究

目的研究传感器微动开关弹簧片应力腐蚀的机理,找到断裂原因。方法对弹簧片进行断口形貌观察、能谱成分分析,并进行产品模拟腐蚀实验。结果传感器内部意外进入雨水,在工作温度下形成湿热环境,开关盒中的游离氨在此环境下释放出来,在开关盒内部形成潮湿氨气氛,铍青铜弹簧片工作时凹面一侧承受静拉应力作用,从而在潮湿氨和拉应力共同作用下发生应力腐蚀开裂。结论通过采用无氨酚醛塑料制备开关盒,弹簧片的应力腐蚀得到了有效预防。     

Air Pollution and Heat Exposure Study in the Workplace in a Glass Manufacturing Unit in India

Air pollution in the workplace environment due to industrial operation have been found to cause serious occupational health hazard. Similarly, heat stress is still most neglected occupational hazard in the tropical and subtropical countries like India. The hot climate augments the heat exposure close to sources like furnaces. In this study an attempt is made to assess air pollution and heat exposure levels to workers in the workplace environment in glass manufacturing unit located in the State of Gujarat, India. Samples for workplace air quality were collected for SPM, SO₂, NO₂ and CO₂ at eight locations. Results of workplace air quality showed 8-hourly average concentrations of SPM: 165–9118 μg/m³, SO₂: 6–9 μg/m³ and NO₂: 5–42 μg/m³, which were below the threshold limit values of workplace environment. The level of CO₂ in workplace air of the plant was found to be in the range 827–2886 μg/m³, which was below TLV but much higher than the normal concentration for CO₂ in the air (585 mg/m³). Indoor heat exposure was studied near the furnace and at various locations in an industrial complex for glass manufacturing. The heat exposure parameters including the air temperature, the wet bulb temperature, and the globe parameters were measured. The Wet Bulb Globe Temperature (WBGT), an indicator of heat, exceeded ACGIH TLVs limits most of the time at all the locations in workplace areas. The recommended duration of work and rest have also been estimated.     

吉林延吉八道金矿构造控矿模式

八道金矿为延吉中生代火山岩型金矿中较为典型的矿床之一。其矿床成因，除与火山作用有关之外直接受构造的控制，而火山作用本身又与区域深大断裂有关。本文着重讨论了矿区火山岩与朝阳河断裂的关系及构造控矿模式。     

曲面零件在拉深过程中内皱时刻及影响因素

进一步推导了曲面零件悬空区上的应力分布及临界失稳公式。然后通过计算机编程 ,求解了临界失稳方程 ,得到了拉深系数、相对锥顶半径、相对圆角半径、材料相对厚度与临界失稳时刻间的关系曲线 ,并对曲线变化的规律进行了分析。