六铝酸盐催化剂的催化还原脱硫脱硝性能

采用共沉淀法制备Cu和Fe掺杂的六铝酸盐催化剂(SrCuxFe1-xAl11O19-δ,x为0,0.2,0.4,0.5,0.6,0.8,1),通过XRD、TPR、BET等技术方法对催化剂的结构及性质进行了研究,并考察了以CO为还原剂的催化脱硝活性。结果表明,用碳酸铵作为沉淀剂在1 200℃焙烧4 h可以形成完整的六铝酸盐晶型,Cu和Fe能够取代Al3+,很好地促进六铝酸盐晶体结构的形成;SrCuxFe1-xAl11O19-δ催化剂有很好的脱硫脱硝催化活性,此类型的催化剂均使SO2、NO的转化率在空速为6 000 h-1下达到了80%和90%以上。向体系中加入氧气会对催化活性有较大影响。     

Ce-Sn-W-O_x催化剂的配伍优化及脱硝影响因素

采用共混热解法制备系列Ce-Sn-W-Ox复合氧化物,用于NH3选择性催化还原NO。通过正交实验优化CeSn-W-Ox配方,采用环境扫描电镜(ESEM)、X-射线衍射仪(XRD)等表征分析催化剂的微观形貌和固相结构,确立Ce-Sn-WOx最佳配比及结构形貌。结果表明,以粒度为5~8 mm的堇青石瓷片担载分散Ce-Sn-W-Ox,进行NH3-SCR脱除NO,当Ce/Sn/W元素摩尔比为1∶0.8∶0.6时,Ce Sn0.8W0.6Ox/堇青石NH3-SCR脱除NO效果最好。当空速为7 200 h-1,催化剂在252~426℃内脱除NO效率均大于94%。重点考察了反应空速(GHSV)、水蒸气(H2O)、SO2等对Ce Sn0.8W0.6Ox/堇青石NH3-SCR脱除NO活性的影响。研究表明,空速低于10 000 h-1时,催化剂脱硝活性受空速影响小;单独通入5%H2O对催化剂脱硝活性基本没有影响;单独通入429 mg/m3SO2导致催化剂活性略有降低;同时通入429 mg/m3SO2和5%H2O,催化剂脱硝活性下降至85.33%,除去SO2和H2O后,催化剂活性又能明显回升。     

钒硅催化脱硫脱硝的研究

考察了经10% H2-90% Ar(体积分数)还原的钒硅催化剂在固定床石英玻璃反应器中的脱硫脱硝活性,研究了反应温度、SO2/NO摩尔比及O2浓度对SO2和NO脱除率的影响.结果表明,还原后的钒硅催化剂的平均NO脱除率提高了15%左右;反应温度对脱硫脱硝影响较大,当温度为400℃以上时SO2和NO脱除率基本保持稳定;SO2/NO摩尔比为2和5时,钒硅催化剂的NO脱除率较高;模拟烟气中有O2条件下的脱硫脱硝活性明显高于无O2条件,O2体积分数为6.00%时SO2和NO脱除率达到最大.     

Fe2O3-Cr2O3/TiO2系列催化剂的结构和脱硝性能

研究以纳米TiO2为载体,浸渍负载过渡金属氧化物,以CO为还原剂的脱硝催化剂的脱硝性能。实验中以计算量的Ni（NO3）2和Fe（NO3）3混合溶液浸渍纳米TiO2粉末,室温下搅拌30 min至混合均匀,放入旋转蒸发器中,70℃下至水分蒸干为止;所得粉末在550℃下、空气气氛中焙烧4 h即得所需催化剂。用以上方法分别制备2%Fe2O3-10%Cr2O3/TiO2、4%Fe2O3-8%Cr2O3/TiO2、6%Fe2O3-6%Cr2O3/TiO2、8%Fe2O3-4%Cr2O3/TiO2与10%Fe2O3-2%Cr2O3/TiO2等5种催化剂样品。实验结果表明,制备的催化剂具有较好的结构,分散较为均匀。对于CO＋NO反应,Fe2O3-Cr2O3/TiO2系列催化剂具有较好的催化活性,NO的转化率都达到了100%。其中,10%Fe2O3-2%Cr2O3/TiO2样品具有最好的低温活性,H2-TPR结果表明,这是由于10%Fe2O3-2%Cr2O3/TiO2催化剂更易于被CO预还原。     

Fe2O3-Cr2O3/TiO2系列催化剂的结构和脱硝性能

研究以纳米TiO2为载体,浸渍负载过渡金属氧化物,以CO为还原剂的脱硝催化剂的脱硝性能。实验中以计算量的Ni(NO3)2和Fe(NO3)3混合溶液浸渍纳米TiO2粉末,室温下搅拌30 min至混合均匀,放入旋转蒸发器中,70℃下至水分蒸干为止;所得粉末在550℃下、空气气氛中焙烧4 h即得所需催化剂。用以上方法分别制备2%Fe2O3-10%Cr2O3/TiO2、4%Fe2O3-8%Cr2O3/TiO2、6%Fe2O3-6%Cr2O3/TiO2、8%Fe2O3-4%Cr2O3/TiO2与10%Fe2O3-2%Cr2O3/TiO2等5种催化剂样品。实验结果表明,制备的催化剂具有较好的结构,分散较为均匀。对于CO+NO反应,Fe2O3-Cr2O3/TiO2系列催化剂具有较好的催化活性,NO的转化率都达到了100%。其中,10%Fe2O3-2%Cr2O3/TiO2样品具有最好的低温活性,H2-TPR结果表明,这是由于10%Fe2O3-2%Cr2O3/TiO2催化剂更易于被CO预还原。     

过渡金属离子复合掺杂的六铝酸盐催化剂的脱硝性能

采用CO为还原气催化还原NO,考察了Mn与Fe复合掺杂六铝酸盐对催化剂结构和NO+CO反应活性的影响,采用X射线衍射(XRD)、比表面积、H2-程序升温还原(H2-TPR)等对形成的SrMnFex Al11-x O19-δ系列催化剂(x为铁的掺杂量,x为1、2、4、6、8；δ为校正系数,在多数情况下小于0.5)进行表征...     

锰铜铈氧化物催化剂氧化NO性能及动力学研究

实验以TiO2为载体采用浸渍法制备CuOx/TiO2、CeOx/TiO2、CuCeOx/TiO2和MnCuCeOx/TiO2催化剂,考察这些催化剂氧化NO活性,探究Cu、Ce摩尔比和添加Mn元素对CuCeOx/TiO2催化剂氧化NO活性的影响,使用扫描电镜观察催化剂表面结构。研究发现,Cu、Ce元素配合后的CuCeOx/TiO2催化剂氧化活性明显好于单独含Cu、Ce的催化剂,当Cu、Ce摩尔比为Cu:Ce=1∶2时,CuCeOx/TiO2催化剂氧化活性最好,在NO浓度500×10-6,O210%,空速为24 000 h-1,350℃时,NO氧化度为0.62;添加Mn元素可以提高CuCeOx/TiO2催化剂低温氧化活性,250℃时,MnCuCe/Ti-3和MnCuCe/Ti-5催化剂氧化度为0.53和0.69,300℃时,MnCuCe/Ti-3和MnCuCe/Ti-5催化剂氧化度均为0.76;此外,实验还研究了NO在MnCuCe/Ti-3催化剂上反应的动力学方程。     

Ce掺杂改性对MnFe2O4低温选择性催化还原脱硝性能的影响研究

采用水热合成法制备了Ce掺杂MnFe2O4催化剂,用于低温选择性催化还原(SCR)脱硝.对催化剂晶型、脱硝性能和表面结构等进行分析,结果表明,Ce/(Fe+Mn)为0.5％(摩尔分数,下同)时催化剂表现出最优的SCR活性,80℃NO去除率可达100％;Ce/(Fe+Mn)分别为5.0％ 和10.0％ 时,催化剂80℃N...     

不同方法制备LaCu0.8Zn0.2Al11O19-δ催化剂及其催化分解N2O活性研究

采用共沉淀法、溶胶-凝胶法和反相微乳液法制备了六铝酸盐催化剂LaCu0.8Zn0.2Al11O19-δ,进行了X射线衍射(XRD)和BET表征.并考察了它们对N2O催化分解反应的活性,研究了制备方法对催化剂LaCu0.8Zn0.2Al11O19-δ的结构、粒径、比表面积和催化分解N2O活性的影响.结果表明,3种方法制备的催化剂经1200℃焙烧4 h后.都能形成六铝酸盐晶相,其中反相微乳液法制备的催化剂具有较小的粒径和较大的比表面积,其催化分解N2O的活性表现最佳,起始反应温度(T10%)为494℃,完全反应温度(T99%)为678℃.     

CeO_2/Al_(0.2)Ti_(0.6)Zr_(0.2)O_(1.9)/ATS复合脱硝催化剂的制备及其抗硫抗水性能研究

将预先经酸处理的铝钛硅(ATS)多相陶瓷片先后负载Al0.2Ti0.6Zr0.2O1.9复合氧化物与CeO2活性组分,制得新型CeO2/Al0.2Ti0.6Zr0.2O1.9/ATS复合脱硝催化剂。运用X射线衍射(XRD)、扫描电镜(SEM)手段对该催化剂进行表征,研究催化剂的晶相、微观形貌。评价了催化剂的脱硝活性,研究了H2O和SO2对其脱硝活性的影响。实验结果表明,CeO2/Al0.2Ti0.6Zr0.2O1.9/ATS具有良好的脱硝活性,高活性温度窗口在100～350℃,当反应温度为250℃时,NO的转化率达98.49%。SO2和H2O在一定程度抑制该催化剂的低温脱硝活性,但随着温度的升高,其脱硝活性逐渐恢复。催化剂中活性组分CeO2具有储硫作用,当有SO2存在时,活性温度窗口向高温区偏移了100℃,在250～400℃时,H2O的存在反而提高了催化剂的脱硝活性。     

A review of the catalysts used in the reduction of NO by CO for gas purification

The reduction of NO by the CO produced by incomplete combustion in the flue gas can remove CO and NO simultaneously and economically. However, there are some problems and challenges in the industrial application which limit the application of this process. In this work, noble metal catalysts and transition metal catalysts used in the reduction of NO by CO in recent years are systematically reviewed, emphasizing the research progress on Ir-based catalysts and Cu-based catalysts with prospective applications. The effects of catalyst support, additives, pretreatment methods, and physicochemical properties of catalysts on catalytic activity are summarized. In addition, the effects of atmosphere conditions on the catalytic activity are discussed. Several kinds of reaction mechanisms are proposed for noble metal catalysts and transition metal catalysts. Ir-based catalysts have an excellent activity for NO reduction by CO in the presence of O₂. Cu-based bimetallic catalysts show better catalytic performance in the absence of O₂, in that the adsorption and dissociation of NO can occur on both oxygen vacancies and metal sites. Finally, the potential problems existing in the application of the reduction of NO by CO in industrial flue gas are analyzed and some promising solutions are put forward through this review.

     

Co3O4/介孔分子筛催化剂对苯催化完全氧化的研究

分别以介孔分子筛MCM-41、MCM-48、SBA-15为载体，采用等体积浸渍法制备了氧化钴/介孔分子筛催化剂，利用N₂吸附、X射线衍射、程序升温还原等技术对催化剂进行了表征，考察了Co₃O₄的负载量及载体的孔结构对催化剂完全催化氧化苯的性能的影响。结果表明，Co₃O₄的负载量为20%时，催化剂的催化活性最好；载体的孔径和催化剂的可还原性能是影响催化活性的主要因素，催化剂活性顺序为Co₃O₄ /SBA-15> Co₃O₄ /MCM41> Co₃O₄ /MCM-48。     

燃煤烟气低温SCR脱硝中试研究

低温选择性催化还原(SCR)脱硝是国内外脱硝技术研发的热点,但目前主要集中在实验室小试范围,无法完全反映催化剂在实际烟气中的运行状况。在30 t/h循环流化床燃煤锅炉脱硫除尘装置后建设了2 000~5 000 m3/h的SCR脱硝中试装置,经系统研究发现,中试使用的蜂窝式催化剂对SO2和NO具有很强的吸附能力,且反应温度、喷氨速率和气体空速均会影响催化脱硝效率。为期5 d的连续运行实验结果表明,催化剂的脱硝效率一直稳定在30%~50%,并未发现明显的失活,这证明设计除雾除尘器、较大的混合器、混合器与反应器间较长的管路均有利于缓解催化剂因SO2、H2O和飞灰中的碱性金属导致的失活。     

Superior Pillared Clay Catalysts for Selective Catalytic Reduction of Nitrogen Oxides for Power Plant Emission Control

ABSTRACT

Fe³+-, Cr³+-, Cu²+-, Mn²+-, Co²+-, and Ni²+-exchanged Al₂O₃-pillared interlayer clay (PILC) or TiO₂-PILC catalysts are investigated for the selective catalytic reduction (SCR) of nitric oxide by ammonia in the presence of excess oxygen. Fe³+-exchanged pillared clay is found to be the most active. The catalytic activity of Fe-TiO₂-PILC could be further improved by the addition of a small amount of cerium ions or cerium oxide. H₂O and SO₂ increase both the activity and the product selectivity to N₂. The maximum activity on the Ce-Fe-TiO₂-PILC is more than 3 times as active as that on a vanadium catalyst. Moreover, compared to the V₂O₅-WO₃/TiO₂ catalyst, the Fe-TiO₂-PILC catalysts show higher N₂/N₂O product selectivities and substantially lower activities (by ~85%) for SO₂ oxidation to SO₃ under the same reaction conditions. A 100-hr run in the presence of H₂O and SO₂ for the CeO₂/Fe-TiO₂-PILC catalyst showed no decrease in activity.     

Selective Reduction of Nitrogen Oxides In Combustion Flue Gases

The body of Information presented in this paper is directed to those Individuals concerned with the removal of NO_x in combustion flue gases. A catalytic process for the selective reduction of nitrogen oxides by ammonia has been investigated. Efforts were made toward the development of catalysts resistant to SO_x poisoning. Nitrogen oxides were reduced over various metal oxide catalysts in the presence or absence of SO_x(SO₂ and SO₃). Catalysts consisting of oxides of base metals (for example, Fe₂O₃) were easily poisoned by SO₃, forming sulfates of the base metals. A series of catalysts which are not susceptible to the SO_x poisoning has been developed. The catalysts possess a high activity and selectivity over a wide range of temperatures, 250—450°C. The catalysts were tested in a pilot plant which treated a flue gas containing 110-150 ppm NO_x, 660-750 ppm SO₂, and 40-90 ppm SO₃. The pilot plant was operated at 350°C and at a space velocity of 10,000 h^-1. The removal of nitrogen oxides was more than 90% for several months.

A mechanism of the NO-NH₃ reaction has also been investigated. It is found that NO reacts with NH₃ at a 1:1 mole ratio in the presence of oxygen and the reaction is completely inhibited by the absence of oxygen. The experimental data show that the NO-NH₃ reaction in the presence of oxygen is represented byNO + NH₃ + 1/4 O₂ = N₂ + 3/2 H₂O.     

Manganese-cerium oxide (MnOx-CeO2) catalysts supported by titanium-bearing blast furnace slag for selective catalytic reduction of nitric oxide with ammonia at low temperature

A series of manganese-cerium oxide (MnO_x-CeO₂) catalysts supported by Ti-bearing blast furnace slag were prepared by wet impregnation and used for low-temperature selective catalytic reduction (SCR) of NO with NH₃. The slag-based catalyst exhibited high nitrogen oxide removal (deNO_x) activity and wide effective temperature range. Under the condition of NO = 500 ppm, NH₃ = 500 ppm, O₂ = 7–8 vol%, and total flow rate = 1600 mL/min, the Mn-Ce/Slag catalyst exhibited a NO conversion higher than 95% in the range of 180–260 °C. The activity of Mn/Slag catalysts was greatly enhanced with the addition of CeO₂. The results indicated that Ti-bearing blast furnace slag had suitable phase composition as good support of SCR catalyst.

Implications: Ti-bearing blast furnace slag is a kind of industrial waste in China. Much slag was underused and piling up, which could cause many environmental issues, such as enormous waste of titanium and groundwater and soil contamination by heavy metals in leachates. The utilization of slag as the support of SCR catalyst will not only make use of solid waste but also cut down the NO_x emitted from power plant.     

Study on the denitrification performance of FexLayOz/activated coke for NH3-SCR and the effect of CO escaped from activated coke at mid-high temperature on catalytic activity

Currently, activated coke is widely used in the removal of multiple pollutants from industrial flue gas. In this paper, a series of novel Fe_xLa_yO_z/AC catalysts was prepared by the incipient wetness impregnation for NH₃-SCR denitrification reaction. The introduction of Fe-La bimetal oxides significantly improved the denitrification performance of activated coke at mid-high temperature, and 4% Fe_0.3La_0.7O_1.5/AC exhibited a superior NO_x conversion efficiency of 90.1% at 400 °C. The catalysts were further characterized by BET, SEM, XRD, Raman, EPR, XPS, FTIR, NH₃-TPD, H₂-TPR, et al., whose results showed that the perovskite-type oxide of LaFeO₃ and oxygen vacancies were produced on the catalysts’ surfaces during roasting. Fe-La doping enhanced the amount of acid sites (mainly Lewis and other stronger acid sites) and the content of multifarious oxygen species, which were beneficial for NO_x removal at mid-high temperature. Moreover, it was investigated that the effect of released CO from activated coke at mid-high temperature on the NO_x removal through the lifetime test, in which it was found that a large amount of CO produced by pyrolysis of activated coke could promote the NO_x removal, and long-term escaping of CO on the activated coke carrier did not have a significant negative impact on catalytic performance. The results of the TG-IR test showed that volatile matter is released from the activated coke while TG results showed that the weight loss rate of 4% Fe_0.3La_0.7O_1.5/AC only was 0.0015~0.007%/min at 300–400 °C. Hence, 4% Fe_0.3La_0.7O_1.5/AC had excellent thermal stability and denitrification performance to be continuously used at mid-high temperature. Finally, the mechanisms were proposed on the basis of experiments and characterization results.

     

改进钒基SCR脱硝催化剂的抗碱金属中毒性能

以锐钛矿型二氧化钛和钛钨粉(5%WO3-TiO2)为载体,制备了系列钒和钨负载量不同的钒钛催化剂,考察碱金属和碱土金属(钾、钠和钙)对催化剂在氨选择性催化还原(NH3-SCR)氮氧化物反应中催化活性的影响。钾、钠和钙对钒钛催化剂的中毒影响大小顺序为钾钠钙。提高钒钛催化剂中钒的含量可显著提高催化剂的SCR活性和抗碱金属中毒性能,但高钒负载量(4.5%V2O5)造成催化剂氮气选择性明显下降,氧化亚氮生成显著增加。钨的添加有利于提高钒钛催化剂的低温活性和抗碱金属中毒性能,对氮气选择性无明显影响。     

Catalytic destruction of pentachlorobenzene in simulated flue gas by a V2O5-WO3/TiO2 catalyst

Pentachlorobenzene (PeCB) in simulated flue gas was destructed by a commercial V₂O₅-WO₃/TiO₂ catalyst in this study. The effects of reaction temperature, oxygen concentration, space velocity and some co-existing pollutants on PeCB conversion were investigated. Furthermore, a possible mechanism for the oxidation of PeCB over the vanadium oxide on the catalysts was proposed. Results show that the increase of gas hourly space velocity (GHSV) and the decrease of operating temperature both resulted in the decrease of PeCB removal over the catalyst, while the effect of the oxygen content in the range of 5-20% (v/v) on PeCB conversion was negligible. PeCB decomposition could be obviously affected by the denitration reactions under the conditions because of the positive effect of NO but negative effect of NH₃. The introduction of SO₂ caused the catalyst poisoning, probably due to the sulfur-containing species formed and deposited on the catalyst surface. The PeCB molecules were first adsorbed on the catalyst surface, and then oxidized into the non-aromatic acyclic intermediates, low chlorinated aromatics and maleic anhydride.     

Fenton氧化法同时脱硫脱硝的实验研究

应用Fenton液相氧化吸收法进行同时脱硫脱硝实验。首先,利用单因素实验,分别考察了H2O2浓度、Fe2+投加量、初始pH值、UV照射和温度对脱硫脱硝的影响。结果表明,SO2和NO去除率随着H2O2浓度和Fe2+投加量的增大而提高;初始pH对SO2和NO的去除有较大影响;UV能促进SO2和NO的净化;温度对脱硫效率影响不大,但对NO的去除有显著作用,适当升温可以提高脱硝效率。随后,考察了SO2对NO去除率的影响。通过单独脱硝和同时脱硫脱硝的对比实验发现,SO2的加入对NO的去除有一定的促进作用,Fenton法可同时获得起始约80%的脱硝效率和98%以上的脱硫效率。