优质页岩陶粒滤料的制备与基本性能研究

以天然页岩为原料,分别采用破碎法和成球法制成滤料生料,经焙烧,膨胀,制备了陶粒滤料.对这2种方法制备的陶粒滤料的孔隙率、孔径和酸碱可溶率等指标进行了分析比较.结果表明,2种方法均可制备出性能优异的陶粒滤料.陶粒滤料的制备方法对其性能影响不大,而焙烧程序对陶粒滤料的性能有较大影响.实际生产时,可根据页岩特性、生产成本等确定陶粒滤料的制备方法.     

物料下落过程中可吸入颗粒物产生特性及控制技术

利用实验室新设计开发的一套装置,研究物料自由下落过程影响可吸入颗粒物产生的因素.通过实验分别测定不同物料、质量流量、含水量、粒径组成和下垫面5个因素对可吸入颗粒物产生的影响.实验结果表明,不同物料可吸入颗粒物产生率不同;随着质量流量和物料含水量的增加,可吸入颗粒物产生率减小,加水是减少可吸入颗粒物排放的最有效方法之一;不同粒径组成和不同下垫面对可吸入颗粒物产生也有影响,但作用并不显著.     

应用POMS复合膜分离去除废气中挥发性有机污染物

依靠POMS平板单层膜或POMS卷式膜上选择性分离层的选择性溶解和渗透作用,常温负压分离回收废气中乙酸乙酯等挥发性有机污染物(VOC)组分.结果表明,膜两侧操作压差和原料气流量对乙酸乙酯分离效率影响较大;当原料气处理量为1.770 0～2.810 0 m3/(m2·h)、膜两侧操作压差为0.08 MPa,POMS卷式膜乙酸乙酯渗透速率可达7.86 × 10-7 mol/(s·m2·Pa);乙酸乙酯为1 500～4 500 mg/m3时,其去除率可达80%.测得几种VOC组分在POMS复合膜中的溶解吸附量都比较可观,由此预测该膜处理废气中VOC可取得很好的净化效果.甲苯在POMS复合膜中的溶解吸附量低于乙酸乙酯,其实验测得渗透速率也小于乙酸乙酯.甲苯去除率也能达到80%.     

粉煤灰/污泥烧结陶粒的研制与应用

以粉煤灰和工业污水处理站的剩余污泥为主要原材料,采用烧结法研制复合陶粒.分析了不同配方和不同烧结温度对陶粒性能的影响,以陶粒吸水率、容重为评价指标确定最佳配比和最佳烧结温度,并对陶粒用于铺设景观水底、治理城市水体进行了可行性分析.粉煤灰/污泥陶粒的容重为0.79～0.90 g/m3,吸水率为68.95%～80.01%.陶粒对水中氨氮和总磷吸附容量分别为0.03～0.05 mg/g和0.01～0.02 mg/g.     

柴油车尾气颗粒物净化用SiC过滤材料的研究与应用

近年来,SiC材料作为一种新型的柴油车尾气颗粒物过滤材料获得了迅速发展,正逐步取代目前广泛应用的堇青石多孔陶瓷材料.结合堇青石和SiC过滤材料的性能特点,重点概述了2种SiC改性过滤材料(重结晶SiC.RSiC和硅结合SiC,Si-SiC)的研究和应用进展,并介绍了SiC颗粒物过滤器的市场现状和发展前景.     

城市垃圾焚烧飞灰重金属药剂配伍稳定化实验研究

以飞灰中富含的Pb和Zn为目标重金属,对飞灰中重金属药剂配伍稳定化效果了实验研究.选用EDTA、Na2S、NaH2PO4等稳定化药剂和pH值控制,首先将试剂单独投加飞灰中测定重金属浸出浓度,分析各试剂的稳定化效果;然后通过系列试验观察现象,确定试剂最优投加顺序;最后,按照试剂性质制定4个配伍方案,按照最优投加顺序投加试剂,测定分析各个配伍方案的稳定化效果.结果表明:pH值保持在弱碱性(10左右),重金属稳定化效果较好.EDTA二钠、NaH2PO4和Na2S重金属稳定化效果明显,而有机试剂EDTA二钠稳定化效果明显优于NaH2PO4和Na2S;稳定化药剂投加顺序以Na2S、EDTA二钠、NaH2PO4顺序投加处理效果为最佳;配伍方案4处理效果明显优于其他方案,可以实现稳定化药剂配伍相合,提高飞灰中重金属稳定化效果,同时减少有机螯合剂的使用量,从而降低处理成本.     

镍、铬对活性污泥真实产率的影响

采用两个直流完全混合式反应器,研究了Ni(Ⅱ) 、Cr(Ⅵ) 对好氧活性污泥真实产率系数(YH)、COD去除率、MLSS和污泥呼吸作用的影响.结果表明,当Ni(Ⅱ) 、Cr(Ⅵ) 为3 mg/L时,YH(MMLSS/MCOD)从无重金属的0.388分别升高到Ni(Ⅱ) 的0.427和Cr(Ⅵ) 的0.408;COD的去除率不受影响,MLSS增加了7.5%;污泥呼吸作用增强了5%.随着Ni(Ⅱ) 、Cr(Ⅵ) 浓度的进一步增加,YH、COD去除率、MLSS和呼吸作用都迅速下降.当Ni(Ⅱ) 、Cr(Ⅵ) 为15 mg/L时,YH(MMLSS/MCOD)分别为0.289和0.218;而Ni(Ⅱ) 、Cr(Ⅵ) 为25 mg/L时,对污泥呼吸的抑制作用分别达43%和60%.总体来看,Cr(Ⅵ) 比Ni(Ⅱ) 对系统的毒性更大.     

铀和铅对枯草杆菌毒性的研究

采用3种方法研究了铀和铅对枯草杆菌的毒性:(1)试纸法测抑菌圈的直径;(2)血球计数板测细菌菌数;(3)高倍显微镜下观察细菌形态和密度的变化.实验考察铀和铅的质量浓度为1～2 000 mg/L.结果表明:铀和铅对枯草杆菌的生长繁殖有显著影响;铀和铅对枯草杆菌的最大无作用剂量均小于1 mg/L;铀对枯草杆菌的致死质量浓度为500 mg/L,铅对枯草杆菌的致死质量浓度为 1 000 mg/L.同时,对以上3种方法进行了比较,确定了其各自的应用范围,为重金属对微生物毒性研究方法的选择提供了参考.     

上海市排水系统雨天出流及地表径流沉降特性初探

实际SS沉降特性是雨水池、沉淀池设计及优化运行的重要参数.采用累积曲线法测定了上海市典型排水系统雨天出流和地表径流的SS沉降特性.结果表明:地表径流中SS的2 h沉降去除率为58%～88%,且SS沉降去除率随SS初始质量浓度增加呈递增趋势;各类排水系统雨天出流中SS沉降速率和沉降去除率在合流制中相对较大,分流制相对较小,混接的分流制介于前两者之间,SS沉降去除率均在50%以上;合流制中COD的2 h沉降去除率为50%～80%.     

不确定性水质模型及其研究进展

水环境是一个充满不确定性因素的复杂巨系统,研究这些不确定性的变化有利于提高人们对水环境分析的认识和做出更切合实际的决策.详细、清晰地评述了不确定性水质模型研究的必要性、研究的方法和国内外研究进展等,并针对此类模型研究与应用过程中普遍存在的一些问题、主要表现和成因进行了分析与论述,最后结合目前的研究热点指出了今后不确定性水质模型发展的3个重要方向.     

Investigation of the characteristics of the reflectivity of clouds

This paper investigates some of the reflectivity characteristics that clouds (when modelled as solid bodies) must exhibit to be compatible with observations that the reflecting surface of a cloud (i) appears almost equally bright across its face, (ii) is brightest when the cloud is opposite to the Sun but decreases in brightness as the cloud moves to other positions and (iii) increases in brightness with increasing optical thickness of the cloud in the observer's line of sight. These observations, respectively, are shown to imply that the peak value of the bidirectional total reflectivity from a cloud surface (i) increases in inverse proportion to the cosine of the angle between the Sun and the normal to the cloud surface, as the incident angle increases, (ii) appears to be directed back in the direction of the incident radiation, and (iii) increases as optical thickness of the cloud in the observer's line of sight increases. The results could have application in many fields (e.g. modelling diffuse radiance distributions for cloudy skies).     

Optimization of Height of Release of Air Pollutants

A number of key projects in the Environmental Protection Agency (EPA) particulate R&;D program having applicability to industry are presented. For electrostatic precipitators (ESP) there is presented the result of work on large diameter discharge electrodes which provide a decrease in penetration of up to a factor of 4 when compared to conventional small diameter electrodes. Also discussed is the multistage ESP which provides a collection efficiency that would require a collecting plate area 4 or 5 times larger with conventional ESP technology. The E-SOX technology makes use of the multistage concept to free up space in the ESP for SO₂ removals of up to 90%. Electrostatically augmented fabric filtration provides a reduction in pressure drop of about 5 0% as compared to conventional fabric filtration. Wind tunnel modeling of windbreaks for material storage piles indicates a potential for providing engineering design data that would allow significant emission reduction caused by wind erosion     

Estimation of uncertainty of sampling for analysis of pesticide residues

Abstract

A computer model was used to take random samples from primary sample populations obtained from field trials to simulate the uncertainty of sampling for residue analysis of plant commodities and soil. The results indicate about 40%, 30% and 20% relative uncertainty when random samples of size 5, 10 and 25 are taken respectively, from a single lot. Therefore the sample size should be the same for establishing and enforcing legal limits.     

扬中生态环境建设的思考与实践

结合扬中生态环境的基本情况和存在的不足，进行了具体分析，对扬中未来生态建设的发展方向提出了建议及实施措施。     

实验室质量管理体系内部审核的实施

在实施ISO／IEC17025：1999标准《检测和校准实验室能力的通用要求》过程中，通过实验室质量管理体系内部审核的实践与系统分析，识别出内部审核实施阶段的关键环节，提出召开首次会议、收集审核证据、确定审核发现和召开末次会议的技术方法，对提高内部审核的质量和有效性、获得可靠的审核结论具有重要意义。     

次氯酸钠发生器的研制

介绍了电解法生产次氯酸钠的原理 ,并在原有生产工艺的基础上进行了重新设计和对设备的重新选择、改造 ,得出了各个工艺参数的最佳值 ,生产出高品质的次氯酸钠     

Spectrophotometric Determination of Atmospheric Acidity by means of the Displacement of the Equilibrium of Acid-Base Indicators

A method is described for determining acidity by means of the spectrophotometric determination of the displacement of the equilibrium of açid-base indicators. The method is simple, sensitive and free of known interferences. There is no dependence on costly or sophisticated equipment and the results obtained are reliable and reproducible.     

不同泥源对厌氧氨氧化反应器启动的影响

采用2套上流式生物膜反应器,分别接种少量厌氧氨氧化污泥和大量硝化污泥,考察其对厌氧氨氧化反应器启动的影响。污泥接种入反应器后,测得接种厌氧氨氧化污泥的反应器(R1)内MLSS为0.22 g/L,另一个反应器(R2)MLSS为2.7 g/L。与直接接种厌氧氨氧化污泥相比,R1经过72 d的运行才显现出厌氧氨氧化特性。经过114 d的培养,前者氮去除速率由0.23 kg/(m3.d)提升到5.29 kg/(m3.d),总氮去除率大于89%;R2的氮去除速率由0.01 kg/(m3.d)提升到1.1 kg/(m3.d),总氮去除率大于84.6%。说明普通污泥启动需要一个较长的筛选过程,直接接种少量的厌氧氨氧化污泥比接种普通的污泥能够更快启动厌氧氨氧化反应器。     

阳宗海沉积物中重金属生物有效性评估

通过测定和分析阳宗海表层沉积物中酸可挥发性硫化物(AVS)和同步提取重金属(SEM)的含量和分布特征,采用SEM/AVS方法对阳宗海表层沉积物中重金属的生物有效性进行评估;同时,采用生物有效阈值法评估了单一重金属的生物有效性。研究得出以下结论:阳宗海表层沉积物中AVS含量为15.09~149.74μmol/g,平均值为49.42μmol/g,从南向北呈递减趋势;AVS在南部和中部均与湖泊水深呈现正相关关系;∑SEM(包括Cu、Cr、Pb、Zn、Mn、As、Cd)含量分布波动较小,其范围为4.84~16.10μmol/g,平均值为10.28μmol/g,其分布规律为北部大于南部;阳宗海各采样点SEM/AVS1,说明阳宗海表层沉积物中重金属不会对生物产生不良影响;从单一重金属来看,Pb可能经常产生生物毒性,Cu有可能产生生物毒性,其他金属除部分点可能产生生物毒性外,整体上几乎不会产生生物毒性。