One-step preparation of a novel graphitic biochar/Cu0/Fe3O4 composite using CO2-ambiance pyrolysis to activate peroxydisulfate for dye degradation

Herein,a one-step co-pyrolysis protocol was adopted for the first time to prepare a novel pyrogenic carbon-Cu⁰/Fe₃O₄ heteroatoms (FCBC) in CO₂ ambiance to discern the roles of each component in PDS activation.During co-pyrolysis,CO₂ catalyzed formation of reducing gases by biomass which facilitated reductive transformation of Fe³⁺ and Cu²⁺ to Cu⁰ and Fe₃O₄,respectively.According to the a...     

Simultaneous removal of NO and dichloromethane（CH2Cl2） over Nb-loaded cerium nanotubes catalyst

Herein, a series of niobium oxide supported cerium nanotubes（Ce NTs） catalysts with different loading amount of Nb₂O₅（0–10 wt.%） were prepared and used for selective catalytic reduction of NOxwith NH₃（NH₃-SCR） in the presence of CH₂Cl₂. Commercial V₂O₅-WO₃-TiO₂ catalyst was also prepared for comparison. The physcial properties and chemical properties of the Nb₂O₅ lo...     

Construction of ternary CuO/CuFe2O4/g-C3N4 composite and its enhanced photocatalytic degradation of tetracycline hydrochloride with persulfate under simulated sunlight

In this study, a graphitic carbon nitride（g-C₃N₄） based ternary catalyst Cu O/Cu Fe₂O₄/gC₃N₄（CCCN） is successfully prepared thorough calcination method. After confirming the structure and composition of CCCN, the as-synthesized composites are utilized to activate persulfate（PS） for the degradation of organic contaminant. While using tetracycline hydrochloride（TC） as pollutant surrogate, the effects of initial p H, PS and catalyst ...     

Insights into the interface of NiCo2O4 spinel/LaCoO3 perovskite nano-composite for CO and soot oxidation

In the quest for the development of thermally stable, highly active and low-cost catalysts for use in catalyzed diesel particulate filter, nano-composites are new areas of research. Therefore, we reported the easy synthesis of spinel NiCo₂O₄/perovskite LaCoO₃ nano-composite,and its individual oxides NiCo₂O₄and LaCoO₃ for comparison. The detailed insights into the physio-chemical characteristics of formed NiCo₂O₄     

Effect of oxide interactions on chromium speciation transformation during simulated municipal solid waste incineration

Chromium released during municipal solid waste incineration (MSWI) is toxic and carcinogenic.The removal of chromium from simulated MSWI flue gas by four sorbents (CaO,bamboo charcoal (BC),powdered activated carbon (PAC),and Al₂O₃) and the effects of four oxides(SiO₂,Al₂O₃,Fe₂O₃,and CaO) on chromium speciation transformation were investigated.The results showed that the removal rates of total Cr by the four sorbents wer...     

Fe3O4/FeS2活化H2O2降解典型苯胂酸类污染物

利用水热法成功制备了Fe₃O₄/FeS₂催化剂,并将其用于构建非均相芬顿体系降解典型的苯胂酸类污染物（洛克沙胂,ROX）.XRD、SEM、XPS和磁学测量系统（VSM）等表征结果表明,Fe₃O₄/FeS₂呈明显的颗粒状且具有良好的磁性.降解实验结果显示,在最优条件下（初始pH值为4.5、ROX起始浓度为20mg/L、Fe₃O₄/FeS₂投加量为0.15g/L和H₂O₂浓度为0.034g/L,Fe₃O₄/FeS₂介导的非均相芬顿体系可以超快速降解ROX,1min后的降解效率达到96.74%,明显优于单独的Fe₃O₄或FeS₂体系.此外,Fe₃O₄/FeS₂可以通过磁铁进行快速回收利用,同时也具有良好的重复利用性能,使用3次后,ROX的降解效率仍超过80%.机理分析表明,Fe₃O₄/FeS₂能够快速地催化H₂O₂产生具有强氧化性的羟基自由基（·OH）.在·OH的作-用下,ROX分子结构中C-As、C-N和C-C等化学键发生断裂,发生脱砷、脱硝和开环等反应,进而生成一系列的有机产物（如酚类、醌类、小分子有机酸等）和无机产物（As （V）和NO₃^-）.之后,无机砷能够被吸附在催化剂表面,而有机产物则进一步被矿化.     

Fe3O4/BC复合材料的制备及其吸附除磷性能

为解决磁性吸附剂Fe₃O₄不稳定、易在水中团聚以及吸附效率较低的问题,以BC（生物炭）为载体,采用化学共沉淀法制备了Fe₃O₄/BC（生物炭负载的纳米四氧化三铁）复合材料,并将其应用于水体中PO₄3--P的吸附去除;探究了Fe₃O₄/BC对水中PO₄3--P的吸附-解析性能,考察了纳米Fe₃O₄负载比例、吸附体系pH和初始ρ（PO₄3--P）等因素对Fe₃O₄/BC吸附PO₄3--P效率的影响,并考察了吸附机制.结果表明:所制备的Fe₃O₄纳米颗粒呈球形,均匀散布在生物炭表面;Fe₃O₄/BC复合材料能高效吸附水中的PO₄3--P,在pH=3、温度为25℃、ρ（PO₄3--P）为50 mg/L、Fe₃O₄/BC投加量为400 mg（二者质量比为1:1）,吸附3 h达到平衡后,Fe₃O₄/BC吸附PO₄3--P效率达到92.14%. Fe₃O₄/BC复合材料吸附PO₄3--P的机制包括配位体交换和静电吸引,吸附过程较好地符合准二级动力学模型和Langmuir等温吸附方程. Fe₃O₄/BC具有良好的解析性能,用c（NaOH）为2.0 mol/L的溶液对吸附PO₄3--P饱和后的Fe₃O₄/BC进行解析,解析效率达到80%.研究显示,Fe₃O₄/BC重复利用性好,在第4次利用后还能保持75%以上的吸附效率.      

Fe2O3/TiO2负载膨胀珍珠岩光催化降解罗丹明B

为获得高效催化活性的光催化材料,研究不同煅烧氛围对材料在可见光下催化性能的影响,以膨胀珍珠岩（EP）为载体,采用溶胶-凝胶法,在不同煅烧氛围（O₂和/或NH₃）下制备Fe₂O₃/TiO₂负载EP的光催化复合材料〔Fe₂O₃-TEP（O₂）、Fe₂O₃-TEP（NH₃）、Fe₂O₃-TEP（O₂,NH₃）、Fe₂O₃-TEP（NH₃,O₂）〕,采用EDS（X-射线色散能谱）、BET（比表面积及孔径分析）、XRD（X射线衍射）、SEM（扫描电子显微镜）、XPS（X射线光电子能谱）等对复合材料进行表征,并研究了其在可见光下对罗丹明B的光催化降解效果.结果表明:①复合材料成功负载了Ti、Fe元素,负载的TiO₂以锐钛矿型存在,Fe₂O₃的掺杂增强了TiO₂对可见光的响应能力;②不同的煅烧氛围明显影响复合材料的晶粒尺寸、比表面积和光催化性能,其中,Fe₂O₃-TEP（O₂,NH₃）的光催化性能最好,4 h后罗丹明B降解率达到87.59%,Fe₂O₃-TEP（NH₃,O₂）、Fe₂O₃-TEP（O₂）和Fe₂O₃-TEP（NH₃）4 h后对罗丹明B的降解率则分别为65.02%、62.48%和47.48%;③在试验条件下,复合材料的光催化反应符合一阶反应动力学方程,Fe₂O₃-TEP（O₂,NH₃）、Fe₂O₃-TEP（NH₃,O₂）、Fe₂O₃-TEP（O₂）和Fe₂O₃-TEP（NH₃）相应的降解速率常数分别为0.008 3、0.004 3、0.004 3和0.002 7 min-1.研究显示,通过溶胶-凝胶法所制备的复合材料（Fe₂O₃-TEP）经煅烧后所得矿相均一;Fe₂O₃掺杂TiO₂可形成Ti—O—Fe键,减小TiO₂固有的禁带宽度;复合材料光催化性能也受到煅烧氛围的影响,先O₂后NH₃煅烧条件下所得材料的光催化性能最佳.      

Study on the mechanism and reaction characteristics of metal-supported phosphogypsum as oxygen carrier in a chemical looping gasification application

This study aimed to explore the chemical looping gasification (CLG) reaction characteristics of the metal-supported composite phosphogypsum (PG) oxygen carriers (OCs) and the thermodynamic mechanism.The FactSage 7.1 thermodynamic simulation was used to explore the oxygen release and H₂S removal mechanisms.The experimental results showed that the syngas yield of CLG with PG-CuFe₂O₄was more than that with PG–Fe₂O₃20/CuO40or PG–Fe₂O<...     

Enhanced removal of high-As(Ⅲ) from Cl(-Ⅰ)-diluted SO4(-Ⅱ)-rich wastewater at pH 2.3 via mixed tooeleite and(Cl(-Ⅰ)-free) ferric arsenite hydroxychloride formation

An advanced cost-saving method of removal of high-As(Ⅲ) from SO₄(-Ⅱ)-rich metallurgi cal wastewater has been developed by diluting the SO₄(-Ⅱ) content with As(Ⅲ)-Cl(-Ⅰ)-rich metallurgical wastewater and then by the direct precipitation of As(Ⅲ) with Fe(Ⅲ) at pH2.3.As(Ⅲ) removal at various SO₄(-Ⅱ)/Cl(-Ⅰ) molar ratios and temperatures was investigated The results showed that 65.2–98.2%of As(III) immobilization into solids occurred at the SO₄(Ⅱ)/Cl(-Ⅰ) mo...     

双金属和多金属系统对零价铁利用效率的改进

为解决Fe0-PRB(零价铁-渗透反应格栅)中Fe0利用效率低、易板结堵塞的问题,分别采用粒径为0.074 mm的试剂铁粉和0.150～0.270 mm的工业铁粉为反应介质,在铁粉表面负载不同比例的Cu或Ni制备Cu/Fe、Ni/Fe双金属和Cu/Ni/Fe多金属颗粒,研究Fe0、双金属和多金属系统去除Cr(Ⅵ)的性能、机制.结果表明:双金属和多金属系统的Cr(Ⅵ)去除率明显高于Fe0,试剂铁粉的Cr(Ⅵ)去除率明显高于工业铁粉.反应8 h达到平衡后,试剂铁粉和工业铁粉的Cr(Ⅵ)去除率仅为45%和20%,Cu/Fe双金属、Cu/Ni/Fe多金属的Cr(Ⅵ)去除率均能达到90%以上,以试剂铁粉和工业铁粉制备的Ni/Fe双金属的Cr(Ⅵ)去除率最高分别为76.6%和44.0%.不同负载率的双金属和多金属系统反应过程中可溶的ρ〔Cr(Ⅲ)〕较低.反应后溶液的pH从反应前的5.0升至10.0左右.反应初期ρ(TFe)(TFe为总铁)超过了0.30 mg/L,其余时间均达标.反应过程中ρ(Cu2+)均在0.40 mg/L以下,均未检测出Ni2+.研究显示,双金属和多金属系统显著提高了Fe0利用效率.      

零价铁PRB修复硝酸盐和铬复合污染地下水

通过连续流动试验研究了Fe0(零价铁)-PRB(渗透反应格栅)修复受NO₃--N、Cr(Ⅵ)以及NO₃--N和Cr(Ⅵ)复合污染模拟地下水的反应特性,分析了Fe0对NO₃--N和Cr(Ⅵ)的氧化还原产物,并且对NO₃--N和Cr(Ⅵ)的相互影响进行了研究. 采用粒径为0.15～0.42 mm的Fe0和粒径为0.15 mm的活性炭作为PRB反应介质,二者的质量比为1∶1. 结果表明,Fe0单独与NO₃--N反应情况下,当进水中ρ(NO₃--N)为20 mg/L时,去除率达95%,NO₂-为还原过渡状态,NH₄+是主要产物,出水pH从原水的7.1升至9.0左右,出水中ρ(TFe)<0.60 mg/L. Fe0处理Cr(Ⅵ)情况下,对Cr(Ⅵ)有较高的去除效果,进水中ρ〔Cr(Ⅵ)〕为10 mg/L时,去除率达96%,反应产物Fe3+和Cr(Ⅲ)可以形成沉淀附着在反应介质上,不会迁移到“下游”水体中,出水pH从原水的7.0升至8.0左右,出水中ρ(TFe)<0.30 mg/L. Fe0去除NO₃--N和Cr(Ⅵ)复合污染时,共存的NO₃--N对Cr(Ⅵ)的去除效果没有影响,Cr(Ⅵ)的存在降低了NO₃--N的去除效果.      

木质垃圾与废铁泥制备Fe0-BC材料及其对水中Cr(Ⅵ)的去除行为

含铬废水的直接排放会对自然环境造成严重危害.为探究零价铁-生物炭材料(Fe⁰-BC)与Cr(Ⅵ)的反应效能,以木质垃圾与印染行业废铁泥两种亟需处理的固体废物作为原料,在不同温度下通过碳热还原制备Fe⁰-BC,并将其应用于水中Cr(Ⅵ)的去除.材料表征结果表明,1 200℃下制备的Fe⁰-BC材料(Fe⁰-BC-1200)性能最佳,其比表面积为105.6 m³/g,孔径为6.23 nm,物相主要由Fe⁰、Cu0、C以及少量杂质构成,其中Fe⁰以球状的颗粒形式分散附着在碳的孔结构中,且大小均匀,粒度基本达到纳米级.通过静态试验考察了Fe⁰-BC材料对Cr(Ⅵ)的去除过程,发现Fe⁰-BC-1200对Cr(Ⅵ)的去除效果最好,在初始浓度为20 mg/L、初始pH为3.5、投加量为2.5 g/L的条件下,Cr(Ⅵ)的去除率达到95.2%. Cr(Ⅵ)的去除过程符合准二级反应动力学过程和Langmui...     

中试尺度下连续式可渗透反应墙修复Cr(Ⅵ)污染地下水效果评估

以Cr(Ⅵ)污染地下水场地为例,基于室内模拟实验确定的PRB墙体尺寸及反应介质,建设了国内首座连续式PRB装置,自墙体建成后运行10个月内,对墙体内外监测井水位、水环境指标进行了 4次监测.结果表明:PRB墙体内地下水流速＞周边含水层中地下水流速,地下水流向虽局部有所改变,但总体上仍垂直穿过PRB墙体,未出现绕流现象;...     

生物炭负载纳米零价铁对污染土壤中铜钴镍铬的协同去除

合成了一种低成本、高效生物炭负载纳米零价铁的复合材料(ZVI-SM)并应用于铜、钴、镍、铬污染土壤的修复。采用X射线衍射(XRD)、X射线光电子能谱(XPS)和金属吸附实验等方法,考察了不同碳化温度下制备的生物炭前驱体和生物炭复合材料对复合重金属污染修复的影响及去除作用机制。其中,吸附-还原后形成的FeCr₂O₄极大地降低了铬的毒性,同时提高了铜、钴、镍的去除率。Fe0的引入既提高了生物炭对重金属的吸附量,又解决了Cr(Ⅵ)毒性的问题;XPS的结果进一步阐明了生物炭可以作为电子传递介质,通过表面官能团得失电子与Fe0间形成强相互作用,增强了复合材料对多重金属离子的去除效果。除ZVI-SM500外,ZVI-SM100、300、400、700 4种材料对于铜、钴、镍、铬的去除率要远高于商用纳米Fe0和单纯的生物炭材料,表现为对铬和铜有较强的亲和力和反应性,均能在5 min内完全去除铜和铬,钴和镍也能在180 min内达到80%以上的去除率。在反应过程中存在显著的离子竞争效应:铬≥铜>钴>镍,这与金属离子的标准还原电位大小的趋势一致。土壤修复实验表明:ZNI-SM300用于污染土壤的修复,15 d后,Cr(Ⅵ)含量从480 mg/kg降至0.52 mg/kg,水溶态Cr总量从500 mg/kg降至1.2 mg/kg,两者的固定化效率均达到99%以上,并能达到完全去除水溶态的铜、钴、镍、Cr(Ⅵ)的效果。因此,以SM300为载体的纳米零价铁可作为复合重金属污染土壤修复的理想材料。     

硫酸根离子强化零价铁去除Cr(Ⅵ)的试验研究

普通零价铁去除Cr（VI）的反应活性较低且Cr（VI）会导致零价铁较快钝化.通过连续流实验,研究了硫酸根离子提高零价铁去除水中Cr（Ⅵ）的可行性与反应机理.实验结果表明,在未加入硫酸根离子时,运行5.5h后柱子出水总铬及Cr（VI）已开始超出饮用水标准.而在加入1~3mmol/L SO₄^2-后,出水总铬及Cr（VI）持续降低,并最终降至饮用水水质标准以下且稳定运行长达240h以上.XPS分析结果表明,还原作用是零价铁除Cr（Ⅵ）的主要机理,硫酸根离子加速了零价铁的腐蚀进而促进了Cr（VI）的去除.     

Reduced graphene oxide-nano zero value iron(rGO-nZVI) micro-electrolysis accelerating Cr(Ⅵ) removal in aquifer

Nanoscale zero-valent iron(nZVI) assembled on graphene oxide(GO)(rGO-nZVI) composites were synthesized by reduction of GO and ferrous ions with potassium borohydride,for use in Cr(VI) removal from aqueous solution.The results showed that the two-dimensional structure of GO could provide a skeleton support for Fe~0,thus overcoming the bottleneck of aggregation for nZVI.Also,rGO-nZVI would form a ferric-carbon micro-electrolysis system in Cr(VI)-contaminated aquifers,enhancing and accelerating electron transfer,exhibiting high rate and capacity for Cr(VI) removal.The optimum dosage of the applied r GO-nZVI was linearly correlated with the initial Cr(VI) concentration.Characterization of rGO-nZVI before and after reaction with Cr(VI) revealed the process of Cr(VI) removal:r GO-nZVI firstly transferred electrons from Fe~0 cores via their Fe(II)/Fe(III) shells to the GO sheet;there,negatively charged Cr(VI) received electrons and changed into positively charged Cr(III),which was adsorbed by the negatively charged GO sheet,avoiding the capping and passivating of nZVI.rGO-nZVI formed a good electrically conductive network,and thus had long-term electron releasing properties,which was important for groundwater remediation.     

光助纳米铁还原Cr(VI)的研究

采用液相还原法制备了纳米铁,并用X射线衍射仪(XRD)、扫描电镜(SEM)对其晶体结构、形貌特征进行了表征.以Cr(Ⅵ)为模拟污染物,中压汞灯作为光源,考察了不同投加量、不同pH值等条件下光照对纳米铁还原Cr(Ⅵ)的影响.结果表明:制备的纳米铁具有很高的反应活性,粒径约为7.6nm,呈球形,可在空气中自燃.在25℃、Cr(Ⅵ)浓度为20mg/L、pH=7±0.5,加入0.1g的纳米铁,光照60min后Cr(Ⅵ)的还原率达到62.3%,而无光照时Cr(Ⅵ)的还原率仅为27.6%,说明光照对Cr(Ⅵ)的还原具有明显的促进作用.当纳米铁投加量较大时,纳米铁对Cr(Ⅵ)的还原速率大于光照对其产生的影响.反应液pH值对Cr(Ⅵ)还原速率的影响较光照对其产生的影响显著.在紫外光的照射下,纳米铁中电荷可能在诱导下作受迫振荡,与吸附分子发生电荷传递是光照促进纳米铁还原Cr(Ⅵ)的主要原因.     

海藻酸钠固定化Fe-Cu双金属去除Cr(Ⅵ)的作用机制

通过运用海藻酸钠(SA)固定化Fe-Cu双金属(SAB)来克服Fe0-PRB利用率低、易板结、堵塞的缺陷.结果表明,SA和Fe-Cu双金属的运用能极大地提高Fe0的利用率,SA的运用可以使Fe-Cu双金属以较低的镀铜量获得较高的Cr(Ⅵ)去除率,SAB镀铜0.9%(SAB0.9)为最佳的填料.FEI电镜扫描结果表明,SA跟2价金属阳离子Ca2+交联形成孔隙结构,为双金属的附着提供了大量的吸附点位,增大了金属颗粒的比表面积;场发射扫描电子显微镜(FESEM)及X-射线光电子能谱(XPS)结果表明,Cu负载于Fe0表面,呈疏松层状结构,在Fe0与Cr(Ⅵ)反应中起催化剂作用,通过自身化合态变化传递Fe0失去的电子,从而提高了Fe0的利用率.渗透系数实验结果表明,SAB0.9能控制Fe0与Cr(Ⅵ)反应产物的释放,缓解Fe0-PRB易板结、堵塞的缺陷.     

改性沸石和铁粉的复合材料处理水中六价铬的研究

利用海藻酸盐的凝胶化将零价铁粉固定于改性沸石表面,制得复合材料,以期在保留改性沸石的吸附性的同时增加铁粉的还原性.复合材料的扫描电镜图片可以看出铁粉分散嵌于海藻酸钙薄层,同时海藻酸钙不会阻碍Cr(VI)与改性沸石的接触.实验考察材料去除水中Cr(VI)性能,结果表明:复合材料,改性沸石,铁粉的除Cr(VI)效率分别为:74.1%,38.4%,9.1%,这得益于改性沸石和铁粉相互的协同作用. 对反应后复合材料进行XPS检测,其表面含有Cr3+,Cr6+表明了材料吸附能力同时还具有还原性.并且对Cr(VI)去除的现象能用伪二级吸附动力学方程描述.平衡吸附量qe和反应速率常数k呈相反的变化趋势.铁粉含量为5.4%的材料性能较好:qe为0.96mg/g, k为0.011g/(mg×h);在Cr(VI)浓度为70mg/L时,上述铁含量的复合材料仍具有较高的处理性能,其qe和k分别为 1.29mg/g, 0.0094g/(mg×h).