以纳米TiO2载体,利用浸渍法制备了HPA／ZnFe2O4-TiO2光催化剂。对制备的催化剂进行了XRD、BET、TEM和UV-vis DRS表征。结果表明,催化剂样品均为锐钛矿相且ZnFe2O4很好地分散在载体表面,HPA／ZnFe2O4-TiO2光催化荆的平均粒径为10nm且在380-670nm均有强的光响应;反应最佳的HPA浓度为O.08molfL,最佳的ZnFe2O4负载量为1％。考察了HPA溶液初始浓度、ZnFe2O4负载量、溶液初始pH值、H2O2用量、催化剂用量对催化剂活性的影响。在溶液初始pH=13,H2O2=6mmol／L,催化剂用量为2g/L的最优条件下,光照反应进行100min后,马拉硫磷的降解率可达87％;重复4次后马拉硫磷的降解率仍可以达到67％。     

掺杂型二氧化钛纳米管光催化降解甲基橙研究

利用本实验室制备的N-F原子掺杂二氧化钛纳米管作催化剂,在可见光区对甲基橙(MO)进行光催化降解实验。在催化剂用量固定为3cm2时考察了不同初始浓度、pH值、溶解氧(DO)等对降解率的影响。结果表明,在可见光区该催化剂具有较高的光催化活性;当溶液DO为19.2mg/L、pH值为3、初始浓度为10mg/L、反应时间300min时,降解率可达82.3%。     

阳离子艳红染料的光催化降解

本文研究了以沉淀法制备的TiO2为催化剂，紫外杀菌灯为光源，对阳离子艳红染料进行光催化降解的可行性，结果表明，在实验条件下，本系统对阳离子艳红染料有明显的降解效果，浓度为10mg/L的阳离子艳红染料经过30min的处理，其降解率＞88％，此外，还探讨了溶液初始pH值，催化剂的投加量，光照距离和液层高度等因素对光降解反应的影响。     

阳离子淀粉-双氰胺-甲醛絮凝剂的合成及其絮凝性能

以阳离子淀粉、双氰胺、甲醛为主要原料,以硫酸铝为催化剂,并引入添加剂合成了阳离子淀粉 双氰胺 甲醛脱色絮凝剂。探讨了阳离子淀粉用量、甲醛用量、催化剂用量、反应温度、反应时间及添加剂对阳离子淀粉 双氰胺 甲醛树脂混凝脱色性能的影响,并对印染废水进行了混凝脱色试验。实验结果发现,当双氰胺23 5g、阳离子淀粉5 6g、甲醛57 8g、硫酸铝4 8g、添加剂12 5g、反应温度(70±1)℃、反应时间为1 5小时。试验表明产品的混凝脱色性能良好,CODCr去除率≥91%,脱色率≥99%。并对制得的产品进行了絮凝性能试验,结果表明该产品具有良好的絮凝性能。     

负载型纳米TiO2光催化剂的制备及其降解水中微量间二甲苯的研究

采用浸涂-烧结法制备的纳米TiO2光催化剂负载量约为6mg／g载体，催化剂经5次重复使用其催化效果稳定，表明催化剂表面TiO2粉体负载牢固；以高压汞灯为光源，对水中微量间二甲苯的负载型纳米TiO2光催化氧化过程的研究表明：初始浓度在6．68～17．36mg／L的范围内，间二甲苯的光催化反应遵循表现一级反应动力学规律，反应的表现速率常数随溶液初始浓度的增大而减小，半衰期则随初始浓度的增大而增加。     

La掺杂TiO2/有机改性膨润土对TNT弹药废水的光催化降解性能研究

利用超声强化溶胶-凝胶法制备了La掺杂TiO2/有机改性膨润土复合光催化材料并进行了结构表征;以弹药废水中主要污染物质TNT作为目标物,考察了影响光催化降解性能的因素.结果表明：有机改性后复合材料的吸附性能和光催化性能均有所增加,对TNT的60min的吸附去除率和光催化降解率分别达到9.68％和94.53％;影响TNT光催化降解率的因素有光照时间、催化剂用量、TNT初始浓度、溶液pH值和光照强度.     

ClO_2对活性艳红K—2G和分散蓝2BLN染料的脱色研究

本论文主要利用自制高纯二氧化氯对两种常用且结构具有代表性的活性艳红K— 2G和分散蓝 2BLN料染 ,进行氧化脱色研究 ,作了温度 ,pH值 ,二氧化氯用量等条件试验 ,并用实际印染废水进行了实验 ,取得了良好的效果。在室温时 ,t =5min～ 7min ,pH值偏碱性条件下 ,单一染料溶液及混合染料溶液的脱色率均达到 90 %以上 ,实际印染废水的脱色也在 90 %左右。pH值、温度和ClO2 用量等多种因素对脱色率均有一定的影响 :pH值越高 ,染料脱色率越高。ClO2 用量存在一最佳值 ,与活性艳红K— 2G及分散蓝 2BLN染料的最佳摩尔比分别为 4 0及 2 0左右。ClO2 耗量随染料起始浓度的增大而增加 (脱色率相同时 )     

茄子秸杆活性炭对染料废水的吸附性能研究

以茄子秸秆为原料,ZnCl2为活化剂制备粉末状活性炭,主要研究了活性炭对染料废水的吸附性能;以活性红X-3B和酸性蓝RL为模型染料,考察了染料初始浓度、pH值、活性炭投加量和吸附时间等对染料脱色率的影响。结果表明,染料初始浓度和活性炭投加量对染料脱色率影响较大。初始浓度为300mg／L时,活性炭的最佳投加量分别为1g／L和1．4g／L;在最佳工艺条件下,脱色率分别在93％和98％以上,COD去除率分别为94．5％和86．4％,出水水质达到国家一级《纺织染整工业水污染物排放标准》（GB 4287—1992）。     

ClO2对活性艳红K—2G和分散蓝2BLN染料的脱色研究

本论文主要利用自制高纯二氧化氯对两种常用且结构具有代表性的活性艳红K－2G和分散蓝2BLN料染,进行氧化脱色研究,作了温度,pHWFHG,二氧化氯用量等条件试验,并用实际印染废水进行了实验,取得了良好的效果。在室温时,t=5min-7min,pH值偏碱性条件下,单一染料溶液及混痊染料溶液的脱色率均达到90％以上,实际印染废水的脱色也在90％左右。pH值、温度和ClO2用量等多种因素对脱色率均有一定的影响：pH值越高,染料脱色率越高。ClO2用量存在一最 佳值,与活性艳红K－2G及分散蓝2BLN染料的最佳摩尔比分别为4.0及2.0左右。ClO2耗量随染料起始浓度的增大而增加（脱色 率相同时）。     

介孔氧化铁催化降解诺氟沙星实验条件的优化研究

选取诺氟沙星为目标污染物,以介孔氧化铁为催化剂,催化过氧化氢降解水中微量有机污染物,设计正交实验并利用SPSS软件进行数据分析,分别讨论了pH、H_2O_2初始浓度、诺氟沙星初始浓度以及催化剂投加量对降解率的影响,并得到选定因素水平范围内的最优化反应条件:初始p H为7,初始H_2O_2浓度100 m M,初始诺氟沙星浓度2 mg/L,催化剂投加量0.7 g/L。最优化反应条件下,120 min诺氟沙星的降解率达到99%。通过SPPS方差分析可得,各因素影响大小的排序为诺氟沙星初始浓度催化剂投加量初始pH初始H_2O_2浓度。     

光催化氧化处理低浓度含醇废水实验

室内实验了TiO2紫外光催化氧化处理废水中的低浓度甲醇。通过对TiO2催化剂活性及添加方式、溶液pH、紫外光强与催化剂加量等参数优化,在TiO2加入浓度为300mg/L和120 W紫外灯照射条件下,对6.8L甲醇浓度为2.77%的低浓度含醇废水持续处理70min后,废水中的甲醇去除率可达98.31%。该实验为进一步处理低浓度含醇废水提供了方法依据。     

UV-H_2O_2联用工艺去除水中阿特拉津的研究

采用间歇式反应器考察了UV-H2O2高级氧化技术去除水中阿特拉津的效果及其影响因素,并进行了相关的反应动力学研究。结果表明,在pH值6.9,阿特拉津初始浓度500μg/L,紫外辐照强度172μW/cm2时,H2O2投加量50mg/L,反应10min后,阿特拉津的去除率90%。UV-H2O2联用工艺对阿特拉津的降解符合一级反应动力学。H2O2在该联用工艺降解阿特拉津中具有双重作用,一方面,当H2O2投加量较小时,一级反应速率常数随H2O2投加量的增加基本呈现线性增加的趋势;另一方面,当H2O2浓度增加到一定程度(90mg/L)后,阿特拉津的降解速率随H2O2浓度的变化已不明显,而H2O2浓度为102mg/L时,则出现了抑制作用。     

Removal of Fe(II) from the wastewater of a galvanized pipe manufacturing industry by adsorption onto bentonite clay

Bentonite clay has been used for the adsorption of Fe(II) from aqueous solutions over a concentration range of 80-200 mg/l, shaking time of 1-60 min, adsorbent dosage from 0.02 to 2 g and pH of 3. The process of uptake follows both the Langmuir and Freundlich isotherm models and also the first-order kinetics. The maximum removal (>98%) was observed at pH of 3 with initial concentration of 100 mg/l and 0.5 g of bentonite. The efficiency of Fe(II) removal was also tested using wastewater from a galvanized pipe manufacturing industry. More than 90% of Fe(II) can be effectively removed from the wastewater by using 2.0 g of the bentonite. The effect of cations (i.e. zinc, manganese, lead, cadmium, nickel, cobalt, chromium and copper) on the removal of Fe(II) was studied in the concentration range of 10-500 mg/l. All the added cations reduced the adsorption of Fe(II) at high concentrations except Zn. Column studies have also been carried out using a certain concentration of wastewater. More than 99% recovery has been achieved by using 5 g of the bentonite with 3M nitric acid solution.     

Fenton氧化处理微电解后制浆中段废水的研究

对微电解后废水初始pH、外加Fe2+、H2O2浓度、处理时间对色度及CODCr去除率的影响进行研究。实验结果表明随着pH的增加,色度和CODCr的去除率均呈现先增加后降低的趋势,在pH值等于4时,处理效果最好。外加Fe2+,H2O2和反应时间对废水CODCr和色度去除率的影响类似于pH的影响,获得的H2O2最佳投加量4 mL/L,FeSO4.7H2O为1.5g/L,最佳处理时间60min。在优化实验条件下,CODCr和色度的去除率稳定在80%和84%附近。     

Response surface optimization of acid red 119 dye from simulated wastewater using Al based waterworks sludge and polyaluminium chloride as coagulant

In this research, the performance of Polyaluminium Chloride (PAC) and Polyaluminium Chloride sludge (PACS) as coagulants for acid red 119 (AR119) dye removal from aqueous solutions were compared. The sample of PACS was collected from "Baba Sheikh Ali" water treatment plant (Isfahan, Iran) where PAC is used as a coagulant in the coagulation/flocculation process. A response surface methodology was applied to evaluate the simple and combined effects of the operating variables including initial pH, coagulant dosage and initial dye concentration and to optimize the operating conditions of the treatment process. Results reveal that the optimal conditions for dye removal were initial pH 3.42, coagulant dosage of 4.55 g dried PACS/L and initial dye concentration of 140 mg/L for PACS, while the optimal initial pH, coagulant dosage and initial dye concentration for PAC were 3.8, 57 mg/L and 140 mg/L, respectively. Under these optimal values of process parameters, the dye removal efficiency of 94.1% and 95.25% was observed for PACS and PAC, respectively. Although lower amount of PAC in comparison with PACS was needed for specific dye removal, the reuse of PACS as a low-cost material can offer some advantages such as high efficiency for AR119 dye removal and economic savings on overall water and wastewater treatment plant operation costs.     

零价铁活化过硫酸盐降解污水中萘普生的研究

为了提高零价铁(ZVI)活化过硫酸盐(PS)的ZVI/PS体系对有机污染物萘普生(NAP)处理的技术水平,即实现对污水中NAP的有效降解.采用对比试验,通过设置不同投加量的PS与ZVI的方式,观察在不同酸碱度条件下NAP的降解量.研究结果表明,酸性条件下,当PS投加量为0.5mM或ZVI投加量为1.50mM时,NAP的...     

超声-双氧水和亚铁离子体系处理含酚废水研究

在实验装置上对超声-双氧水和亚铁离子体系联合处理含酚废水进行了实验研究。主要考察了废水初始pH值、初始双氧水浓度、超声功率、反应时间等因素对酚去除率的影响。实验结果表明：超声辐射可以在双氧水和亚铁离子体系氧化过程中起加速反应的作用，而且随着超声功率的增大，加速反应的能力增强；实验条件下废水初始pH值为4～6．8，初始双氧水浓度为140mg／L时酚去除效果最佳；超声-双氧水和亚铁离子体系处理含酚废水过程中苯酚的降解规律符合表现一级反应。     

三维电极电解硝基苯废水处理实验研究

以涂膜活性炭-活性炭为填充粒子,对三维电极电解硝基苯废水进行了研究。通过实验探讨了投盐量、槽电压、主电极间距、反应时间及初始浓度对电解硝基苯废水的影响。结果表明,三维电极在电极间距为9mm、槽电压为20V、硫酸钠投加量为1.5g/L、pH值为6、电解时间为90min的条件下,硝基苯去除率可达90%以上。在三维电极电解作用下,硝基苯转化为可生化和低毒的苯胺,苯胺在三维电极电解作用下还可以得到进一步的降解。