Enhanced dehalogenation of halogenated methanes by bimetallic Cu/Al

A low-cost and high effective copper/aluminum (Cu/Al) bimetal has been developed for treatments of halogenated methanes, including dichloromethane, in near neutral and high pH aqueous systems. Bimetallic Cu/Al was prepared by a simple two-step synthetic method where Cu was deposited onto the Al surface. The presence of Cu on Al significantly enhanced rates of degradation of halogenated methanes and reduced toxic halogenated intermediates. The stability of Cu/Al was preliminarily studied by a multi-spiking batch experiment where complete degradation of carbon tetrachloride was achieved for seven times although the Cu/Al aging was found. Roles of Cu may involve protecting Al against an undesirable oxidation with water, enhancing reaction rates through the galvanic corrosion, and increasing the selectivity to a benign compound (i.e., methane). Kinetic analyses indicated that the activity of bimetallic Cu/Al was comparable to that of iron-based bimetals (e.g., palladized iron) and zero-valent metals. Bimetallic Cu/Al could be a promising reactive reagent for remediation of halogenated solvents-contaminated groundwater associated with high pH problems.     

钯/铝双金属体系对3-氯酚的脱氯降解

研究了钯/铝双金属体系对水相中3-氯酚的催化脱氯降解效果,通过置换沉积制备了钯/铝双金属颗粒,考察了该双金属颗粒的稳定性以及溶液pH和钯负载量对脱氯效果的影响。结果表明,pH在4.0以下的酸性条件,钯负载量在1.43%时,可实现水相中3-氯酚的有效脱氯,反应30 min后0.389 mmol/L的3-氯酚转化率可达99%以上,产物主要为苯酚,而钯/铝颗粒在重复测试中能保持较好的稳定性,这与铝基材表面自发形成的氧化膜有关。钯/铝材料表征的结果表明,钯颗粒高度分散在铝基材表面,并极大地提高了铝基材的表面积,从而有助于后续的脱氯反应。     

High-level arsenite removal from groundwater by zero-valent iron

The objectives of this study were to conduct batch and column studies to (i) assess the effectiveness of zero-valent iron for arsenic remediation in groundwater, (ii) determine removal mechanisms of arsenic, and (iii) evaluate implications of these processes with regard to the stability of arsenic and long-term remedial performance of the permeable reactive barrier (PRB) technology. A high concentration arsenic solution (50 mg l(-1)) was prepared by using sodium arsenite (arsenic (III)) to simulate groundwater at a heavily contaminated Superfund site in the USA. Batch studies indicate that the removal of arsenic is a two-step reaction with fast initial disappearance of arsenite followed by a slow subsequent removal process. Flow-through columns were conducted at a flow rate of 17 ml h(-1) under reducing conditions for 6.6 mo. Kinetic analysis suggested that arsenic removal behaves as a zero-order reaction at high arsenic concentrations. Arsenic removal rate constants decreased with time and arsenic breakthrough was observed in the column study. Arsenic removal capacity of zero-valent iron was determined to be approximately 7.5 mg As/g Fe. Carbonate green rust was identified from the analysis of surface precipitates; arsenite uptake by green rust may be a major mechanism responsible for arsenic remediation by zero-valent iron. Analysis of HCl-extractable arsenic from iron samples indicated that approximately 28% of arsenic was in the form of arsenate suggesting that a surface oxidation process was involved in the arsenic removal with zero-valent iron.     

Pathways and kinetics of carbon tetrachloride and chloroform reductions by nano-scale Fe and Fe/Ni particles: comparison with commercial micro-scale Fe and Zn

Groundwater and wastewater contaminated with chlorinated organic compounds (COCs) can be treated with zero-valent metals. The practicality of this treatment method depends on the reduction rates of the target compounds and their byproducts. In this study, nano-scale Fe and Fe/Ni particles were synthesized so that they could be used to rapidly degrade carbon tetrachloride (CT) and chloroform (CF). Their BET surface areas were around two orders higher than those of commercial micro-scale Fe and Zn particles. Batch reduction experiments carried out with a metal loading of 2.5 gl(-1) showed that complete reduction of CT by the nano-scale Fe/Ni and Fe particles could be achieved within 20 min and 60 min, respectively. With the commercial micro-scale Fe and Zn particles applied at 125 gl(-1), complete CT reduction could only be achieved after 4h and 1.5h, respectively. Reductions of CT and CF with the nano-scale particles followed pseudo-first-order kinetics, and the specific reaction rate constants with the nano-scale Fe/Ni particles were 2-8 times higher than those of the nano-scale Fe particles. CT was degraded through hydrogenolysis to CF, and subsequently via both complete reduction pathway to methane and hydrogenolysis pathway to dichloromethane (DCM). Significantly more methane was generated with the use of the nano-scale Fe/Ni particles than with the nano-scale Fe particles. While the commercial Zn particles were more reactive than the commercial Fe particles, they failed to transform CT directly into methane, causing accumulation of DCM in the aqueous phase.     

The effect of silica on the degradation of organohalides in granular iron columns

Dissolved silica species are naturally occurring, ubiquitous groundwater constituents with corrosion-inhibiting properties. Their influence on the performance and longevity of iron-based permeable reactive barriers for treatment of organohalides was investigated through long-term column studies using Connelly iron as the reactive medium. Addition of dissolved silica (0.5 mM) to the column feed solution led to a reduction in iron reactivity of 65% for trichloroethylene (TCE), 74% for 1,1,2-trichloroethane (1,1,2-TCA), and 93% for 1,1,1-trichloroethane (1,1,1-TCA), compared to columns operated under silica-free conditions. Even though silica adsorption was a gradual process, the inhibitory effect was evident within the first week, with subsequent decreases in reactivity over 288 days being relatively minor. Lower concentrations of dissolved silica species (0.2 mM) led to a lesser decrease (70%) in iron reactivity toward 1,1,1-TCA. The presence of dissolved silica species produced a shift in TCE product distribution toward the more highly chlorinated product cis-dichloroethylene (cis-DCE), although it did not appear to alter products originating from the trichloroethanes. The major corrosion products identified were magnetite (Fe3O4) or maghemite (gamma-Fe2O3) and carbonate green rust ([Fe4(2+)Fe(2)3+(OH)12][CO(3).2H2O]). Iron carbonate hydroxide (Fe(II)1.8Fe(III)0.2(OH)2.2CO3) was only found in the silica-free column, indicating that silica may hinder its formation. A comparison with columns operated under the same conditions, but using Master Builder iron as the reactive matrix, showed that Connelly iron is initially less reactive, but performs better than Master Builder iron over 288 days.     

Catalytic amination and dechlorination of para-nitrochlorobenzene (p-NCB) in water over palladium-iron bimetallic catalyst

Chemical treatment of para-nitrochlorobenzene (p-NCB) by palladium/iron (Pd/Fe) bimetallic particles represents one of the latest innovative technologies for the remediation of contaminated soil and groundwater. The amination and dechlorination reaction is believed to take place predominantly on the surface site of the Pd/Fe catalysts. The p-NCB was first transformed to p-chloroaniline (p-CAN) then quickly reduced to aniline. 100% of p-NCB was removed in 30 min when bimetallic Pd/Fe particles with 0.03% Pd at the Pd/Fe mass concentration of 3g 75 ml(-1) were used. The p-NCB removal efficiency and the subsequent dechlorination rate increased with the increase of bulk loading of palladium and Pd/Fe. As expected, p-NCB removal efficiency increased with temperature as well. In particular, the removal efficiency of p-NCB was measured to be 67%, 79%, 80%, 90% and 100% for reaction temperature 20, 25, 30, 35 and 40 degrees C, respectively. Our results show that no other intermediates were generated besides Cl(-), p-CAN and aniline during the catalytic amination and dechlorination of p-NCB.     

Catalytic dechlorination kinetics of p-dichlorobenzene over Pd/Fe catalysts

p-Dichlorobenzene (p-DCB) was dechlorinated using Pd/Fe bimetallic catalytic reductants synthesized by chemical deposition. Batch experiments demonstrated that the Pd/Fe bimetallic particles could effectively dechlorinate p-DCB, p-DCB and its intermediate chlorobenzene were removed completely at a Pd loading of 0.02% (weight ratio of Pd to Fe) and Pd/Fe power to solution ratio about 4g 75 ml-1 in 90 min. Dechlorination was affected by various factors such as the reaction temperature, pH, Pd loading percentage over Fe and the introduction of Pd/Fe catalysts et al. Chlorobenzene represents partially stable dechlorinated intermediates in the generation of benzene and part of p-DCB was dechlorinated to benzene indirectly on the surface of Pd/Fe. The dechlorination of p-DCB took place on the surface of the Pd/Fe bimetallic particles in a pseudo-first-order reaction, the activation energy of the dechlorination reaction was determined to be 80.0 kJ mol-1 at the temperature range of 287-313 K.     

Use of waste iron metal for removal of Cr(VI) from water

Cr(VI) removal from water was evaluated using waste iron particles in batch experimental mode. The reaction rates were inversely proportional to the initial Cr(VI) concentrations, and the reaction rates of Cr(VI) removal with the waste iron metal were faster than those with Peerless iron, a commercial zero-valent iron. The loss in iron reactivity due to the oxidation, from Fe(0) to Fe(II), ultimately to Fe(III), could be recovered by adding iron-reducing consortium (IRC) to the oxidized iron. Bacterial reduction of Cr(VI) also helped to decrease the aqueous concentration of Cr(VI), but the reduction of oxidized iron by IRC and the consequent reduction of Cr(VI) to Cr(III) by the reduced iron was more significant. Thus, reusing waste iron metal for Cr(VI) removal can reduce the cost of reactive media. Furthermore, the addition of IRC to the waste iron metal can accelerate the removal rate of Cr(VI), and can recover the reactivity of irons which were oxidized by Cr(VI).     

Isotopic fractionation during reductive dechlorination of trichloroethene by zero-valent iron: influence of surface treatment

During reductive dechlorination of trichloroethene (TCE) by zero-valent iron, stable carbon isotopic values of residual TCE fractionate significantly and can be described by a Rayleigh model. This study investigated the effect of observed reaction rate, surface oxidation and iron type on isotopic fractionation of TCE during reductive dechlorination. Variation of observed reaction rate did not produce significant differences in isotopic fractionation in degradation experiments. However, a small influence on isotopic fractionation was observed for experiments using acid-cleaned electrolytic iron versus experiments using autoclaved electrolytic iron, acid-cleaned Peerless cast iron or autoclaved Peerless cast iron. A consistent isotopic enrichment factor of epsilon = -16.7/1000 was determined for all experiments using cast iron, and for the experiments with autoclaved electrolytic iron. Column experiments using 100% cast iron and a 28% cast iron/72% aquifer matrix mixture also resulted in an enrichment factor of -16.9/1000. The consistency in enrichment factors between batch and column systems suggests that isotopic trends observed in batch systems may be extrapolated to flowing systems such as field sites. The fact that significant isotopic fractionation was observed in all experiments implies that isotopic analysis can provide a direct qualitative indication of whether or not reductive dechlorination of TCE by Fe0 is occurring. This evidence may be useful in answering questions which arise at field sites, such as determining whether TCE observed down-gradient of an iron wall remediation scheme is the result of incomplete degradation within the wall, or of the dissolved TCE plume by passing the wall.     

Microbial reduction of nitrate in the presence of nanoscale zero-valent iron

Microbial reduction of nitrate in the presence of nanoscale zero-valent iron (NZVI) was evaluated to assess the feasibility of employing NZVI in the biological nitrate treatment. Nitrate was completely reduced within 3 d in a nanoscale Fe(0)-cell reactor, while only 50% of the nitrate was abiotically reduced over 7 d at 25 °C. The removal rate of nitrate in the integrated NZVI-cell system was unaffected by the presence of high amounts of sulfate. Efficient removal of nitrate by Fe(II)-supported anaerobic culture in 14 d indicated that Fe(II), which is produced during anaerobic iron corrosion in the Fe(0)-cell system, might act as an electron donor for nitrate. Unlike abiotic reduction, microbial reduction of nitrate was not significantly affected by low temperature conditions. This study demonstrated the potential applicability of employing NZVI iron as a source of electrons for biological nitrate reduction. Use of NZVI for microbial nitrate reduction can obviate the disadvantages associated with traditional biological denitrification, that relies on the use of organic substrates or explosive hydrogen gas, and maintain the advantages offered by nano-particle technology such as higher surface reactivity and functionality in suspensions.     

纳米级铁粉脱氯降解四氯化碳

四氯化碳的生产和使用,给人类带来了较大危害.为此,采用纳米铁粉这一新方法对其进行脱氯处理.试验以纳米级铁粉对四氯化碳的脱氯率为考察指标,选用L25(56)正交试验方案,考察了降解介质的初始pH值、纳米铁粉的质量、降解温度、摇床转速和脱氯时间5个影响因素.结果表明,pH值这一因素有极显著影响;在得出的纳米铁粉对四氯化碳脱氯的最佳工艺条件下,获得了99.5%的脱氯率,为有机氯化物脱氯开辟了一条新途径.     

Performance evaluation of granular iron for removing hexavalent chromium under different geochemical conditions

Long-term column experiments were conducted under different geochemical conditions to estimate the longevity of Fe 0 permeable reactive barriers (PRBs) treating hexavalent chromium (Cr(VI)). Secondary carbonate minerals were precipitated, and their effects on the performance, such as differences in the mechanism for Cr removal and the changes in system hydraulics, were assessed. Sequestration of Cr(VI) occurred primarily by precipitation of Fe(III)-Cr(III) (oxy)hydroxides. Trace amounts of Cr were observed in iron hydroxy carbonate presumably due to substitution of Cr3+ for Fe3+. The formation of Fe(III)-Cr(III) (oxy)hydroxide greatly decreased the reactivity of the Fe 0 and thus resulted in migration of the Cr removal front. Carbonate minerals did not appear to contribute to further passivation with regard to reactivity toward Cr removal; rather, the column receiving high contents of dissolved calcium carbonate showed slightly enhanced Cr removal by means of a higher corrosion rate of Fe 0 and because of sequestration by an iron hydroxy carbonate. Precipitation of carbonates, however, governed other geochemical parameters. The porosity and hydraulic conductivity in the column receiving high contents of dissolved calcium carbonate did not indicate a great loss in system permeability because the accumulation of carbonates declined as the Fe 0 was passivated over time. However, the accumulated carbonates and associated Fe(III)-Cr(III) (oxy)hydroxide could cause problems because the presence of these solids resulted in a decline in flow rate after about 1400 pore volumes of operation.     

Impact of carbon,oxygen and sulfur content of microscale zerovalent iron particles on its reactivity towards chlorinated aliphatic hydrocarbons

Zerovalent iron (ZVI) abiotically degrades several chlorinated aliphatic hydrocarbons (CAHs) via reductive dechlorination, which offers perspectives for in situ groundwater remediation applications. The difference in reactivity between ZVI particles is often linked with their specific surface area. However, other parameters may influence the reactivity as well. Earlier, we reported for a set of microscale zerovalent iron (mZVI) particles the disappearance kinetic of different CAHs which were collected under consistent experimental conditions. In the present study, these kinetic data were correlated with the carbon, oxygen and sulfur content of mZVI particles. It was confirmed that not only the specific surface area affects the disappearance kinetic of CAHs, but also the chemical composition of the mZVI particles. The chemical composition, in addition, influences CAHs removal mechanism inducing sorption onto mZVI particles instead of dechlorination. Generally, high disappearance kinetic of CAHs was observed for particles containing less oxygen. A high carbon content, on the other hand, induced nonreactive sorption of the contaminants on the mZVI particles. To obtain efficient remediation of CAHs by mZVI particles, this study suggested that the carbon and oxygen content should not exceed 0.5% and 1% respectively. Finally, the efficiency of the mZVI particles may be improved to some extent by enriching them with sulfur. However, the impact of sulfur content on the reactivity of mZVI particles is less pronounced than that of the carbon and oxygen content.     

Dechlorination of chlorinated hydrocarbons by bimetallic Ni/Fe immobilized on polyethylene glycol-grafted microfiltration membranes under anoxic conditions

In this study, the dechlorination of chlorinated hydrocarbons including trichloroethylene (TCE), tetrachloroethylene (PCE) and carbon tetrachloride (CT) by bimetallic Ni/Fe nanoparticles immobilized on four different membranes was investigated under anoxic conditions. Effects of several parameters including the nature of membrane, initial concentration, pH value, and reaction temperature on the dechlorination efficiency were examined. The scanning electron microscopic images showed that the Ni/Fe nanoparticles were successfully immobilized inside the four membranes using polyethylene glycol as the cross-linker. The agglomeration of Ni/Fe were observed in poly(vinylidene fluoride), Millex GS and mixed cellulose ester membranes, while a relatively uniform distribution of Ni/Fe was found in nylon-66 membrane because of its hydrophilic nature. The immobilized Ni/Fe nanoparticles exhibited good reactivity towards the dechlorination of chlorinated hydrocarbons, and the pseudo-first-order rate constant for TCE dechlorination by Ni/Fe in nylon-66 were 3.7-11.7 times higher than those in other membranes. In addition, the dechlorination efficiency of chlorinated hydrocarbons followed the order TCE > PCE > CT. Ethane was the only end product for TCE and PCE dechlorination, while dichloromethane and methane were found to be the major products for CT dechlorination, clearly indicating the involvement of reactive hydrogen species in dechlorination. In addition, the initial rate constant for TCE dechlorination increased upon increasing initial TCE concentrations and the activation energy for TCE dechlorination by immobilized Ni/Fe was 34.9 kJ mol⁻¹, showing that the dechlorination of TCE by membrane-supported Ni/Fe nanoparticles is a surface-mediated reaction.     

Catalytic degradation of chlorothalonil in water using bimetallic iron-based systems

Modified zero valent iron (MZVI) was used to study the transformation of a chlorothalonil (CLT) solution and the variation of the observed degradation rate of the reduction reactions. This was carried out when transition metals e.g. Pd, Cu and Co plated on the surface of micrometric iron particles (< 150 microm) were used as reducing catalytic agents for pesticide removal. Reactions were undertaken under both oxic and anoxic conditions in the presence and the absence of a phosphate buffer solution (PBS). Results of batch studies in nitrogen sparged solutions revealed that incomplete slow dechlorination merely occurred with zero valent iron (ZVI), however, complete rapid dechlorination reactions took place with MZVI especially Fe/Pd. Dechlorination was depicted by studying UV absorbance and MS spectra of CLT and all corresponding by-products. Typical blue shifts (deltalambda = 4-6 nm/chlorine atom) were observed at the same time as chlorine cluster isotopes disappeared. After the plating process, metal loading was controlled by analyzing the remaining metal in the solution by atomic absorption spectroscopy. Experiments showed that CLT degradation mechanism is faster in nitrogen sparged solutions in the absence of PBS. Time needed for complete removal of 2.08 +/- 0.19 microM CLT solution was about 2 h when experiments were conducted with ZVI (t1/2 = 15.0 min) and about 10 min when the reaction was carried out under the same conditions with Fe/Pd 1% (t1/2 = 1.0 min). Degradation rates for all bimetallic systems were determined showing that Pd is the more exciting catalytic transition metal followed by Cu and Co. Furthermore, MZVI method showed obvious advantage to traditional CLT treatment methods.     

Reductive dechlorination of chlorinated methanes in cement slurries containing Fe(II)

Degradative solidification/stabilization (DS/S) is a novel remediation technology that combines chemical degradation with conventional solidification/stabilization. The applicability of the Fe(II)-based DS/S to treating chlorinated alkanes was tested by characterizing degradation reactions of carbon tetrachloride (CT) and its daughter products in cement slurries containing Fe(II). Degradation kinetics of CT and chloroform (CF) were generally very rapid with reaction rates comparable to rates that can be obtained with zero-valent iron. Dechlorination reactions of CT proceeded primarily via a hydrogenolysis pathway, which yielded CF and methylene chloride (MC) as major products and chloromethane and methane as minor products. However, reaction pathways other than hydrogenolysis also appeared to be important at very high pH conditions. MC apparently was resistant to dechlorination reactions over a period of about two months. Kinetics of CT and CF transformation were strongly dependent on pH with an optimal value around 13, which was higher than found previously for PCE. When the initial CF concentration varied between 0.01 and 1 mM, and the Fe(II) dose was 104 mM, pseudo-first-order kinetics generally described the degradation reactions of CF. However, there was also some indication of substrate saturation kinetics in these experiments. This suggests that a saturation model would better describe the kinetics in systems with higher concentration of substrates or lower concentration of the reactive surfaces.     

Rapid and complete dechlorination of PCP in aqueous solution using Ni-Fe nanoparticles under assistance of ultrasound

The Ni-Fe bimetallic particles have been laboratory prepared using sodium borohydride (NaBH4) as the reductant to reduce Ni2+ and Fe2+ in aqueous solution simultaneously, and characterized by TEM, XRD, BET and XPS. The particles were proved to be nanoscale amorphous alloy with an average diameter of about 30 nm and a BET surface area of 20.9 m2 g(-1). Experiments for dechlorination of pentachlorophenol (PCP) by the Ni-Fe bimetallic nanoscale particles in aqueous solutions were carried out under the enhancement of ultrasound. Major factors that influence the dechlorination efficiency, such as initial pH value, Ni content in the Ni-Fe particles, and output power of ultrasonic irradiation, were investigated. The results indicated that Ni-Fe nanoscale bimetallic particles were very effective for the dechlorination of PCP. Dechlorination efficiency was 46% in 30 min under the optimal condition without assistance of ultrasound, whereas it increased to 96% when ultrasonic irradiation was present. Initial pH value showed apparent effect on the dechlorination. As the pH varied from acidic condition to neutral condition, the dechlorination efficiency decreased dramatically. In addition, the dechlorination efficiency was improved with increased Ni/Fe ratio and ultrasonic output power. Less chlorinated phenols including tetrachlorophenol, trichlorophenol, dichlorophenol, monochlorophenol were formed during the initial reaction, and phenol was determined by GC-MS as sole product in the end of reaction.     

Reduction of nitrobenzene in groundwater by iron nanoparticles immobilized in PEG/nylon membrane

The highly reactive iron nanoparticles (NPs) immobilized in nylon membrane were synthesized and characterized, and the reduction of nitrobenzene (NB) in groundwater by the NPs was investigated. Environmental scanning electron microscopy (ESEM) images showed that the NPs distributed homogeneously on the membrane surface without agglomeration. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) analyses revealed that the NPs immobilized in membrane were mainly composed of Fe-oxides rather than zero-valent iron. Thermogravimetric (TG) analysis suggested that the weight percentage of the immobilized NPs and the oxygen introduced to the reacted sample after 80min reaction were about 18.5% and 13%, respectively. Moreover, Fourier transform infrared (FTIR) analysis further demonstrated the changes on the membrane surface after thermal grafting, NPs immobilizing and reacting for 80min. Using the reactive NPs immobilized in nylon membrane, NB in groundwater was rapidly and quantitatively decreased by 68.9% just in the first 20min, the Fe(2+) associated with the iron NPs immobilized in PEG/nylon66 membrane was mainly responsible for this reduction. The reaction appeared to follow pseudo-first-order kinetics and the rate constants increased upon decreasing the pH value. The samples we prepared exhibited good corrosion resistance for humic acid (HA) but had a short-term performance for NB degradation. More so, the groundwater chemistry had a negative influence on the reactivity of membrane immobilized NPs.     

Removal of chromium from synthetic plating waste by zero-valent iron and sulfate-reducing bacteria.

Experiments were conducted to evaluate the potential of zero-valent iron and sulfate-reducing bacteria (SRB) for reduction and removal of chromium from synthetic electroplating waste. The zero-valent iron shows promising results as a reductant of hexavalent chromium (Cr+6) to trivalent chromium (Cr+3), capable of 100% reduction. The required iron concentration was a function of chromium concentration in the waste stream. Removal of Cr+3 by adsorption or precipitation on iron leads to complete removal of chromium from the waste and was a slower process than the reduction of Cr+6. Presence SRB in a completely mixed batch reactor inhibited the reduction of Cr+6. In a fixed-bed column reactor, SRB enhanced chromium removal and showed promising results for the treatment of wastes with low chromium concentrations. It is proposed that, for waste with high chromium concentration, zero-valent iron is an efficient reductant and can be used for reduction of Cr+6. For low chromium concentrations, a SRB augmented zero-valent iron and sand column is capable of removing chromium completely.