将含银废液中的Ag+转化为Ag Cl,再用铝片包裹Ag Cl固体,在Na2CO3溶液中采用置换法回收银。考察了各反应条件对Ag Cl还原为银的转化率的影响。实验结果表明,适宜的反应条件为:Na2CO3溶液质量分数20%,反应温度40℃,反应时间20 h,不搅拌静置反应。在此适宜的反应条件下,Ag Cl还原为银的转化率为95.32%。     

羟基乙叉二膦酸镀铜废液的处理及Cu~(2+)的高附加值资源化回收

采用Na BH4还原法将羟基乙叉二膦酸(HEDP)镀铜废液中的Cu~(2+)制备成纳米铜粉,并采用聚丙烯酰胺(PAM)对还原反应后的废液进行絮凝处理。研究了n(Cu~(2+))∶n(Na BH4)、还原反应温度、还原反应时间及PAM添加量对废液中剩余Cu~(2+)质量浓度的影响,并对回收的纳米铜粉进行了XRD和TEM表征。实验结果表明:当n(Cu~(2+))∶n(Na BH4)=4∶6、还原反应温度为50℃、还原反应时间为2 h时,废液中剩余Cu~(2+)质量浓度降低至1.1 mg/L,Cu~(2+)还原率达99.99%;可获得粒径为20~45 nm的近球型、高纯度、由多晶组成的纳米铜粉;当PAM添加量为10 mg/L时,废液中剩余Cu~(2+)质量浓度降至0.35 mg/L以下,达到GB 21900—2008《电镀污染物排放标准》(小于0.5 mg/L)的要求。     

赤泥制备含钛聚硅酸铝铁及亚甲基蓝溶液的混凝脱色

以拜耳法赤泥为原料、Na Cl为助溶剂,采用酸浸法溶出赤泥中的铁、铝元素,再与硅酸钠、硫酸氧钛反应制备出高效混凝剂含钛聚硅酸铝铁(T-PSAF),并将其用于模拟亚甲基蓝印染废水的脱色。实验结果表明:在硫酸浓度为8 mol/L、液固比(硫酸体积与干赤泥质量之比)为14 m L/g、酸浸温度为80℃、酸浸时间为80 min、Na Cl加入量为0.10 g/g(以干赤泥计)的优化酸浸条件下,铁、铝的浸出率分别为88.25%和73.21%;在n(Fe+Al)∶n(Ti)∶n(Si)=0.3∶0.3∶1、熟化p H为4~5、熟化时间为2 h、混凝剂加入量为25 m L/L的优化混凝条件下,初始亚甲基蓝质量浓度为10 mg/L的废水的脱色率可达87.1%,而当初始亚甲基蓝质量浓度增至150~200 mg/L时废水脱色率可达99%以上。     

用赤泥捕集二氧化碳

以拜耳法生产氧化铝产生的赤泥为捕集剂，对CO₂进行捕集，考察了液固比、反应温度、搅拌速率、CO₂流量对单位CO₂捕集量（以每克赤泥捕集的CO₂质量计）和赤泥脱碱率（以钠去除率计）的影响。实验结果表明：在液固比为7#x02236;1、反应温度为30℃、搅拌转速为500r/min、CO₂流量为200mL/min的最佳实验条件下，最大单位CO₂捕集量为0.0263g/g，赤泥的脱碱率可达到42.43%。赤泥具有较强的捕集CO₂的能力，因此，利用固体废弃物赤泥吸收工业废气中的CO₂可以达到以废治废的目的。     

液晶屏抛光废液的资源化利用

以液晶屏抛光废液为原料制备冰晶石，首先加入碳酸钠，反应生成氟硅酸钠沉淀，去除废液中的氟硅酸根;再向滤液中加入NaOH和NaAlO2混合溶液，反应生成冰晶石。最佳工艺条件为:碳酸钠加入量为理论加入量的2.2倍，冰晶石制备反应温度为80℃，反应原料中n(HF)∶n(NaAlO2)为5.4、n(Na)∶n(Al)为3.4、NaOH和NaAlO2质量分数为20%。在最佳条件下制得的冰晶石产品中n(Na)∶n(Al)为2.84，达到GB/T4291-2007《冰晶石》中牌号CH-1的质量标准。采用该工艺可实现液晶屏抛光废液的资源化综合利用。     

氯酸钠氧化盐酸酸洗废液制备聚氯化铁

钢材在深加工过程中通常使用盐酸对其表面进行酸洗除锈,从而产生大量废液。为了实现盐酸酸洗废液的资源化处理,以氯酸钠作为氧化剂制备聚氯化铁,考察了氧化剂加入量、浓盐酸加入量、反应时间、反应温度等因素对Fe²⁺转化率的影响。实验得到的最佳工艺条件为：每处理100 mL废液需加入7.0 g氯酸钠、12 mL浓盐酸（12 mol/L）、0.3 g磷酸二氢钾,反应温度30 ℃,反应时间30 min,搅拌转速5 r/s。该条件下,Fe²⁺转化率可达98.51%,得到的聚氯化铁产品符合《水处理剂 聚氯化铁》（HG/T 4672—2014）标准。     

淀粉废水水解酸化处理中的酶比活变化特性

以淀粉废水水解酸化处理系统中的蛋白酶、淀粉酶、脱氢酶为研究对象,考察了在无机离子、营养元素、pH等条件作用下的酶比活变化规律.实验结果表明:Mg2+和Co2+对酶比活有显著影响,MgCl2·6H2O加入量为30 mg/L时蛋白酶、淀粉酶、脱氖酶的比活分别是空白的5.6倍、1.6倍、1.5倍,COD去除率提高17.6%;而CoCl2·6H2O加入量为10 mg/L时,蛋白酶和淀粉酶的比活较单独投加30 mg/L的MgCl2·6H2O时分别下降了80.6%和42.5%,脱氢酶比活却提高了13.2%;以NH4Cl与CO(NH2)2作为混合N源(m(NH4Cl):m(CO(NH2)2)=1:2)时蛋白酶、淀粉酶、脱氢酶的比活分别是单独以CO(NH2)2为N源时的3.0倍、1.4倍、1.8倍,COD去除率提高了11.8%;中性偏碱性条件较利于酶促反应的进行.     

化学还原法回收含银电镀废液中的银

以Na2S2O4为还原剂,采用化学还原法回收某电镀厂含银电镀废液中的银。实验结果表明,在n(Na2S2O4)∶n(Ag+)=2.5、反应温度35℃、废水pH7.5、搅拌速率300r/min的条件下,Ag+回收率达到99.92%。对回收的银粉进行X射线衍射和扫描电子显微镜分析,分析结果表明回收的银粉纯度较高,成球形。     

高铁酸盐对焦化废水的氧化-混凝深度处理

采用实验室自制的K2Fe O4对焦化废水进行氧化-混凝深度处理。考察了K2Fe O4加入量、初始废水p H、反应温度等因素对废水处理效果的影响。采用紫外光谱和GC-MS技术对处理前后的焦化废水进行表征。实验结果表明,在K2Fe O4加入量为8.8 mg/L、初始废水p H为4、反应温度为20℃、反应时间为30 min的条件下处理COD为252 mg/L、TOC为159.24 mg/L、浊度为24.90 NTU的焦化废水,处理后废水COD为78 mg/L、TOC为62.10 mg/L、浊度为9.46 NTU,去除率均可达60%以上。表征结果显示,高铁酸盐的氧化-混凝耦合作用对焦化废水中的有机物去除效果明显,处理后废水中的有机物种类和浓度大幅下降。     

钛白废酸制取高白度石膏

以石灰为中和剂、乙二胺四乙酸二钠(EDTA - 2Na)为络合剂、连二亚硫酸钠为还原剂,采用络合—还原法对钛白废酸进行处理,制取高白度石膏.实验结果表明,处理100 mL H2SO4质量浓度为213 g/L的钛白废酸,在中和反应液pH为0.75、EDTA - 2Na加入量为2.67g/L、络合反应时间为20 min、连...     

Review of the kinetics of alkaline degradation of cellulose in view of its relevance for safety assessment of radioactive waste repositories

The degradation of cellulose (a substantial component of low- and intermediate-level radioactive waste) under alkaline conditions occurs via two main processes: a peeling-off reaction and a basecatalyzed cleavage of glycosidic bonds (hydrolysis). Both processes show pseudo-first-order kinetics. At ambient temperature, the peeling-off process is the dominant degradation mechanism, resulting in the formation of mainly isosaccharinic acid. The degradation depends strongly on the degree of polymerization (DP) and on the number of reducing end groups present in cellulose. Beyond pH 12.5, the OH^- concentration has only a minor effect on the degradation rate. It was estimated that under repository conditions (alkaline environment, pH 13.3-12.5) about 10% of the cellulosic materials (average DP = 1000-2000) will degrade in the first stage (up to 10⁵ years) by the peeling-off reaction and will cause an ingrowth of isosaccharinic acid in the interstitial cement pore water. In the second stage (10⁵-10⁶ years), alkaline hydrolysis will control the further degradation of the cellulose. The potential role of microorganisms in the degradation of cellulose under alkaline conditions could not be evaluated. Proper assessment of the effect of cellulose degradation on the mobilization of radionuclides basically requires knowing the concentration of isosaccharinic acid in the pore water. This concentration, however, depends on several factors such as the stability of ISA under alkaline conditions, sorption of ISA on cement, formation of sparingly soluble ISA-salts, etc. A discussion of all the relevant processes involved, however, is far beyond the scope of the presented overview.     

Study of Aging Characteristics of Ternary Blends of Polyethylenes—II

Six film samples of low-density polypropylene (LDPE)/linear LDPE (LLDPE)/high-density polypropylene (HDPE) with varying ratios of LDPE (20–45 ... wt%) and LLDPE (25–50 wt%) having a fixed amount of HDPE at 30 wt% were prepared by blown film extrusion technique. The samples were aged at four different temperatures, 55°, 70°, 85°, and 100°C, for four different time periods in the interval of between 150 hours and up to 600 hours. The change in the structure of various constituents and the formation of various oxygenated (peroxy and hydroperoxy) and unsaturated groups during thermo-oxidative degradation was discussed by infrared spectroscopy. The visiosity-average molecular weight was found to have decreased slowly in the initial aging hours and temperatures, whereas it decreased by 10% with its previous value tensile strength that is, 100°C when aged for 600 hours. The tensile strength of the sample first increased by 67% at 55°C and 89% at 70°C up to 450 hours, whereas the values increased by 52.5% at 85°C and 33.9% at 100°C when aged for 150 hours and then decreased. The percentage elongation at break increased by 2.7% at 55°C and 10.7% at 70°C for 150 and 300 hours of aging, respectively, whereas the percentage decreased when aged at 85°C and 100°C for up to 600 hours of aging. The values of gel content (percent) increased and initial degradation temperature decreased with aging time and temperature.     

Determination of the Burning Characteristics of a Slick of Oil on Water

The burning rate of a slick of oil on a water bed is characterized by three distinct processes, ignition, flame spread and burning rate. Although all three processes are important, ignition and burning rate are critical. The former, because it defines the potential to burn and the latter because of the inherent possibility of boilover. Burning rate is calculated by a simple expression derived from a one-dimensional heat conduction equation. Heat feedback from the flame to the surface is assumed to be a constant fraction of the total energy released by the combustion reaction. The constant fraction (χ) is named the burning efficiency and represents an important tool in assessing the potential of in situ burning as a counter-measure to an oil spill. By matching the characteristic thermal penetration length scale for the fuel/water system and an equivalent single layer system, a combined thermal diffusivity can be calculated and used to obtain an analytical solution for the burning rate. Theoretical expressions were correlated with crude oil and heating oil, for a number of pool diameters and initial fuel layer thickness. Experiments were also conducted with emulsified and weathered crude oil. The simple analytical expression describes well the effects of pool diameter and initial fuel layer thickness permitting a better observation of the effects of weathering, emulsification and net heat feedback to the fuel surface. Experiments showed that only a small fraction of the heat released by the flame is retained by the fuel layer and water bed (of the order of 1%). Ignition has been studied to provide a tool that will serve to assess a fuels ease to ignite under conditions that are representative of oil spills. Two different techniques are used, piloted ignition when the fuel is exposed to a radiant heat flux and flash point as measured by the ASTM D56 Tag Closed Cup Test. Two different crude oils were used for these experiments, ANS and Cook Inlet. Crude oils were tested in their natural state and at different levels of weathering, showing that piloted ignition and flash point are strong functions of weathering level.     

Calculation of carbon balances for evaluation of the biodegradability of polymers

Establishing carbon balances has been proven to be an applicable and powerful tool in testing biodegradability of polymers. In controlled degradation tests at a 4-L scale with the model polymer poly(-hydroxybutyrate) (PHB), it was shown that the degree of degradation could not be determined with satisfactory accuracy from CO₂ release alone. Instead, the course of degradation was characterized by means of establishing carbon balances for the degradation of PHB withAcidovorax facilis and a mixed culture derived from compost. Different analytical methods for determining the different carbon fractions were adapted to the particular test conditions and compared. Quantitative determination of biomass and residual polymer were the main problems in establishing carbon balances. Amounts of biomass derived from protein measurements depend strongly on assumptions of the protein content of the biomass. Selective oxidation of biomass with hypochlorite was used as alternative, but here problems arose from insoluble metabolic products. Determination of soluble components with the method of chemical oxygen demand (COD) also includes empirical assumptions but seems acceptable if the dissolved carbon fraction is in the range of some 10% total carbon. Results confirm both analytical assays and theoretical approaches, in ending up at values very close to 100%, within an acceptable standard deviation range under test conditions comparable to standard test practice.Paper presented at the Bio/Environmentally Degradable Polymer Society—Third National Meeting, June 6–8, 1994, Boston, Massachusetts.     

Model of technological alternatives of production of sodium chromate (VI) with the use of chromic wastes

This article presents a mathematical model which describes the sodium chromate (VI) production process with the use of chromic waste as a substitution of natural raw materials. This model is a function of selected process parameters common for all of the examined alternatives and based on equations of material balance. Optimization of the elaborated technological alternatives of the production process with use of recycling of chromic waste has been evaluated by determining the extreme value of the quality indicator WJ. This indicator defines the quantity of waste created in the process. Optimization results enabled the selection of the optimal technological solution from all of the alternatives possible for use in industrial practice. Negative values of the indicator prove that there is the possibility of introducing to the process a larger quantity of waste than the one obtained in the process and transported to the storage heaps.     

化学品生物降解性的评价与预测

介绍了有机化学物质生物降解性的测定方法及其预测方法研究概况，并讨论了生物降解性评价的发展前景。     

鼓泡式反应器高径比对氨法烟气脱碳性能的影响

以N2和CO2混合气模拟燃烧烟气，研究了鼓泡反应器的高径比以及反应条件对氨法烟气脱碳性能的影响。实验结果表明:在相同高径比的条件下，CO2吸收率随氨水质量分数的增加、反应温度的升高而逐渐增大，随进气CO2体积分数和模拟烟气流量的增加而逐渐减小;CO2吸收率随高径比的增加而增大，在高径比为3.98、氨水质量分数为28%、进气CO2体积分数为10%、模拟烟气流量为1.0L/min、反应温度为40℃的条件下，CO2吸收率最高可达100%。     

Mechanism of Microbial Degradation of Slow-Release Fertilizers

Methyleneureas are condensation products of urea and formaldehyde of different molecular mass and solubility; they are used in large amounts both as resins, binders, and insulating materials for industrial applications, as well as a slow-release nitrogen fertilizer for greens, lawns, or in bioremediation processes. In the present study, the microbial breakdown of these products was investigated. The nitrogen was released as ammonia and urea, and the formaldehyde released immediately oxidized via formiate to carbon dioxide. The enzymatic mechanism of metabolization of methyleneureas was studied in microorganisms isolated from soil, which were able to use these compounds as the sole source of nitrogen for growth. A strain of the Gram-negative bacterium Ralstonia paucula (formerly Alcaligenes sp. CDC group IVc-2) completely degraded methylenediurea and dimethylenetriurea to urea, ammonia, formaldehyde, and carbon dioxide. The enzyme initiating this degradation (methylenediurease) was purified and turned out to be different from the previously described enzyme from Ochrobactrum anthropi with regard to its regulation of expression and physicobiochemical properties. Fungal degradation of methyleneureas may occur via the formation of organic acids, thus leading to a nonenzymatic degradation of methyleneureas, which are unstable under acidic conditions.     

Effect of Degree of Substitution of Octenyl Succinate Starch on Enzymatic Degradation

Octenyl succinate starch of degree of substitution (ds) 0.03, 0.07, and 0.11 was synthesized in an aqueous medium. These compounds were then tested for the susceptibility to enzymatic degradation. The multiple-enzyme regime of -amylase, amyloglucosidase, and pullulanase was chosen for the evaluation. This combination of enzymes had been proven to degrade 99.5% of unmodified starch to glucose and hence was chosen for this study. It was found that even small amounts of subsituent caused a considerable decrease in the extent of degradation. The net extent of degradation decreased with increasing ds. Surprisingly, the amount of glucose from all three substituted substrates was quite similar, suggesting the effect small amounts of subtituent had on the enzymatic activity.     

GGH换热元件堵塞原因分析及解决措施探讨

分析了湿法脱硫系统中GGH换热元件堵塞的原因及对系统运行的影响,并结合目前GGH使用状况给出了解决措施,为脱硫系统安全运行提供参考。