水泥对垃圾焚烧飞灰的固化处理试验研究

对垃圾焚烧飞灰的化学成分、重金属物质的含量及浸出浓度进行测试分析.结果表明,飞灰中Pb和Cr等重金属物质浸出量超过浸出毒性标准,因而被认为是危险废物,必须进行固化处理.还考察了水泥对焚烧飞灰中重金属物质固化的效果,研究表明当飞灰掺量适当时,重金属物质的固化效果良好.重金属物质通过物理固封、替代,沉淀反应和吸附等形式可固化进水泥水化产物结构中.     

地聚合材料固化处理垃圾焚烧飞灰

以垃圾焚烧飞灰和高岭土为主要原料,氢氧化钾为碱激活剂制备了地聚合材料,当焚烧飞灰的掺加量在70%时,其28 d抗压强度可达19.36 MPa。重金属浸出实验表明,地聚合物材料对垃圾焚烧飞灰中的重金属有明显的固化效果,在28 d时基本无溶出。SEM结果表明,地聚合材料的断面结构与力学性能和固化效果相关,XRD和FTIR的分析结果表明,焚烧飞灰和高岭土在碱的激发下生成新的硅铝酸盐聚合物,所得地聚合材料为无定形态。     

垃圾焚烧飞灰浸出特性及固化试验的研究

垃圾焚烧飞灰残留有重金属元素和二恶英等物质而被认为是危险废物,必须对之进行稳定化处理.通过试验研究分析了国内首家自主开发成功的广东省东莞市某回转窑垃圾焚烧发电厂垃圾焚烧飞灰的化学成分及矿物组成,研究了飞灰的浸出毒性,考察了水泥固化焚烧飞灰的效果,并与熔融/玻璃固化进行了比较.研究表明,该焚烧飞灰中重金属Cd的浸出毒性严重超标,并且随pH值的减小而增大,水泥固化效果随龄期的增大而更加显著.熔融/玻璃固化的效果优于水泥固化,但其经济性有待提高.     

城市生活垃圾焚烧飞灰的熔融分离处理

焚烧法处理城市生活垃圾已在世界先进发达国家广泛采用。垃圾焚烧飞灰含有大量的重金属，必须进行合理安全处置。在分析城市生活垃圾焚烧飞灰的物理化学性质基础上，研究了垃圾焚烧飞灰固化成型、熔融分离的无害化处理新工艺。实验结果表明：飞灰固化成球的适宜粘结剂为5%～7%消石灰，养护时间为10～12 d，固化球强度达0.24 kg/cm²以上，可以满足运输和熔化分离要求；固化后的飞灰在1 300℃左右熔融分离后，重金属的分离效果好，达到97%以上，可达到无害化处理标准；对1 300℃和1 400℃熔融分离后熔渣的重金属浸出毒性测试显示，重金属浸出毒性问题可以完全解除。研究结果表明，采用飞灰固化-熔融分离工艺处理城市生活垃圾焚烧飞灰是可行的。     

垃圾焚烧飞灰有毒重金属固化稳定技术研究综述

采用焚烧法处理生活垃圾正呈快速增长的趋势,焚烧过程产生的飞灰中所含有的大量有毒重金属对自然环境和人类生存都造成极大影响。阐述了目前常用的几种固化稳定垃圾焚烧飞灰有毒重金属的方法,综合分析了其固化特点和优缺点,并初步探索了一种低能耗环境下实现高温熔融处置技术的有效途径,从而为垃圾焚烧飞灰高温固化稳定有毒重金属的实施提供一定的理论基础和技术支持。     

水泥对垃圾焚烧飞灰中重金属的固化研究

采用水泥固化法处理垃圾焚烧飞灰,研究了飞灰与水泥质量比、养护时间、添加剂和化学预处理对垃圾焚烧飞灰固化块中重金属Zn、Pb、Cu、Cd、Cr浸出的影响.结果表明,当飞灰与水泥质量比为3:4,养护时间为11d的条件下,以砂浆塑化剂为添加剂,固化块Pb、Cu、Cd和Cr的浸出浓度分别降低了72.4％、70.6％、60.0％...     

SGA对垃圾焚烧飞灰中重金属的固化性能研究

根据EPA1311、HJ／T299—2007、HJ／T300—2007和HJ557—2009等国内外不同标准，研究了深圳某垃圾焚烧发电厂垃圾焚烧飞灰的浸出毒性，探讨了六硫代胍基甲酸（sixthioguanidineacid，SGA）、二甲基二硫代氨基甲酸盐（sodiumdimethyldithiocarbamate，SDD）和Ca（OH）2浓度对垃圾焚烧飞灰中重金属的固定性能的影响。研究结果表明，随着浸提液pH的降低，该厂焚烧飞灰中大部分金属元素的浸出量增大，焚烧飞灰浸出液中的cd、Ni、Ph和zn浓度分别超过国家危险废物鉴别标准（GB5085．3—2007）规定值的4．75倍、1．47倍、6．72倍和2．20倍，属于危险废弃物，必须进行稳定化处理。当固化剂SGA加入量为0．1mol／kg时，稳定化后的重金属浸出浓度已经低于危险废物鉴别标准，且对Cd、Cr、Cu和Pb的固化性能优于SDD和Ca（OH）2；当固化剂SGA、SDD和Ca（OH）2加入量为0．5mol／kg时，稳定化后的焚烧飞灰重金属浸出浓度均低于国家危险废物鉴别标准（GB5085．3-2007）中的规定值。与SDD和Ca（OH）：相比，SGA对垃圾焚烧飞灰中重金属的固化处理更具有优势。     

垃圾焚烧飞灰综合利用研究进展

焚烧处理是解决日益增长生活垃圾的有效方法。垃圾焚烧产生的飞灰因含有大量的重金属等污染物而属危险废物，目前常采用的处理方法是填埋。本文就垃圾飞灰的综合利用研究现状进行了论述。从环境和技术的角度看，垃圾飞灰的预处理、水泥固化和玻璃化是目前飞灰综合利用的主要研究方向。     

垃圾焚烧飞灰中重金属固化稳定机理及系统评价方法的研究进展

垃圾焚烧飞灰中的重金属是必须处理的环境污染物.目前,对于垃圾焚烧飞灰的固化稳定化处理已经有了大量的实验研究.但是,不同地区垃圾焚烧厂产生的飞灰中,重金属含量和形态大不相同,故相应的飞灰仍然难以实现大规模、普适性的处理.在查阅文献及实际调研的基础上,系统总结了垃圾焚烧飞灰中重金属的存在形态与浸出特性;通过对重金属固化稳定机理的分析,指出了垃圾焚烧飞灰固化材料和稳定剂选择的方向.此外,还计算了不同的固化剂与稳定剂对不同重金属的固化率,发现材料复配的方式对多种重金属的稳定效果较好.最后,比较了不同评价方法在垃圾焚烧飞灰固化系统选择中的应用效果,指出综合评价方法是目前相对较完善、系统的方法,在工程实际中具有广阔的应用前景.     

垃圾焚烧飞灰综合利用研究进展

焚烧处理是解决日益增长生活垃圾的有效方法。垃圾焚烧产生的飞灰因含有大量的重金属等污染物而属危险废物 ,目前常采用的处理方法是填埋。本文就垃圾飞灰的综合利用研究现状进行了论述。从环境和技术的角度看 ,垃圾飞灰的预处理、水泥固化和玻璃化是目前飞灰综合利用的主要研究方向     

Dehalogenation potential of municipal waste incineration fly ash

BACKGROUND, AIMS AND SCOPE: It is well known that the fly ash from filters of municipal waste incinerators (MWI-FA) shows dehalogenation properties after heating it to 240-450 degrees C. However, this property is not general, and fly ash samples do not possess dehalogenation ability at all in many cases. Fly ash has a very variable composition, and the state of the fly ash matter therefore plays the decisive role. In the present paper, the function of important components responsible for the dehalogenation activity of MWI-FA is analysed and compared with the model fly ash. METHODS: With the aim of accounting for the dehalogenation activity of MWI-FA, the following studies of hexachlorobenzene (HCB) dechlorination were performed: The role of copper in dehalogenation experiments was evaluated for five types of metallic copper. The gasification of carbon in MWI-FA was studied in the 250-350 degrees C temperature range. Five different kinds of carbon were used, combined with conventional Cu(o) and activated nanosize copper powder. The dechlorination experiments were also carried out with Cu(II) compounds such as CuO, Cu(OH)2, CuCl2 and CuSO4. The results were discussed from the standpoint of thermodynamics of potential reactions. Based on these results, the model of fly ash was proposed, containing silica gel, metallic copper and carbon. The dechlorination ability of MWI-FA and the model fly ash are compared under oxygen-deficient atmosphere. CONCLUSIONS: The results show that, under given experimental conditions, copper acts in the dechlorination as a stoichiometric agent rather than as a catalyst. The increased surface activity of copper enhances its dechlorination activity. It was found further that the presence of copper leads to a decrease in the temperature of carbon gasification. The cyclic valence change from Cu(o) to Cu+ or Cu2+ is a prerequisite for the dehalogenation to take place. RECOMMENDATION AND OUTLOOK: Thermodynamic analysis of the dechlorination effect, as well as the comparison of dechlorination pathways on MWI-FA and model fly ash, can provide a deeper understanding of the studied reaction.     

粉煤灰资源化的现状

本文检索了国内外综合利用粉煤灰的有关文献 ,由粉煤灰特性入手 ,介绍了它在农业、建筑、环保等行业的资源化现状。指出粉煤灰作为二次资源的重要意义 ,并对粉煤灰资源化提出了一些设想     

粉煤灰资源化的一种有效途径

本文对影响粉煤灰泡沫玻璃质量的主要因素:玻璃软化温度与发泡剂的选择、发泡温度与发泡时间、发泡剂生成气体的温度、坯体成型压力等关键问题进行了探索,这些问题的探索对提高粉煤灰泡沫玻璃质量,获得性能优良的粉煤灰泡沫玻璃具有十分重要的意义。     

对火电厂粉煤灰平衡湿含量的试验和分析

对粉煤灰的平衡湿含量在各影响因素下进行了试验研究 ,并且利用半经验公式对实验数据进行了回归 ,得到了较好的拟合效果 ;为相关的理论及试验研究提供了计算公式及实验数据     

回收粉煤灰磁珠在污水处理中的应用

从粉煤灰综合利用角度,探时利用回收粉煤灰中磁珠作磁种,用高梯度磁分离技术进行污水处理的可行性,进一步研究了粉煤灰磁珠粒度组成对污水处理效果的影响。     

不同释钾菌对粉煤灰的生态效应

粉煤灰治理难度大，但它含有植物生长必需的营养元素钾，将其就地资源化生物利用是一条较好的途径。释钾菌是一种能把矿物中的难溶性钾转化为有效钾的细菌，从土壤中筛选出2种释钾菌，经过在粉煤灰基质中的驯化培养，通过盆栽试验种植紫花苜蓿，比较不同菌株对粉煤灰的改良作用及其对植物生长的影响。结果表明，筛选出的菌株C6对粉煤灰中速效钾的释放效果明显，降低了基质pH，显著地促进了植物的生长，对粉煤灰生态修复具有重要意义。     

生活垃圾焚烧飞灰重金属的受热特性

研究了飞灰重金属在不同煅烧温度下的挥发情况及其存在形态.结果表明:重金属挥发能力由强到弱依次为Hg＞Pb＞As、Cd＞Zn＞Cr、Ni、Cu;其中Hg、Pb、As和Cd属易挥发重金属,在1 150 ℃时几乎全部挥发;Zn属较易挥发重金属,1 150 ℃时的挥发率在40%～50%;Cr、Ni和Cu属难挥发重金属,在1 150 ℃的挥发率不超过10%;在400～1 150 ℃,随温度的升高,部分Zn、Hg、Cu、Pb、Cd、Ni和As由可溶态向残渣态、铁锰氧化态转化;在400～900 ℃,随温度的升高Cr可溶态比例减少,而在900～1 150 ℃,随温度的升高其可溶态比例增加.     

粉煤灰砖块对磷酸盐的吸附特性

以建筑废料粉煤灰砖块为吸附剂材料,通过静态吸附实验研究其对磷酸盐的吸附特征,以及磷酸盐初始浓度、吸附剂投加量、pH等因素对吸附反应的影响。Langmuir、Freundlich和Temkin等温模型的分析发现,Langmuir等温式方程最适合描述吸附过程,对磷酸盐的理论饱和吸附容量为44.62 mg/g。利用伪一级动力学模型、伪二级动力学模型和颗粒内扩散模型考察了吸附过程特征,其中伪二级动力学模型为最适于描述粉煤灰砖块对磷酸盐的吸附过程的动力学模型。通过颗粒内扩散模型、Bangham方程及Boyd模型对吸附动力学机理进行的探讨表明,颗粒内扩散速率不是粉煤灰砖块吸附磷酸盐反应的惟一速率控制步,膜扩散速率和颗粒内扩散速率共同影响着吸附反应速率。磷酸盐浓度较低时主要是膜扩散限制吸附反应速率,而磷酸盐浓度较高时则颗粒内扩散成为速率控制步。研究证明,粉煤灰砖块粉末作为湿地基质具有对磷酸盐很强的吸附能力,在减少了固体废弃物的数量的同时又可以实现水污染控制的目的。     

飞灰热处理过程中基本特性研究

对不同粒径飞灰中重金属的分布情况进行了研究，并采用高温熔融管式电炉试验装置，对垃圾焚烧飞灰进行了高温热处理研究，探讨了热处理过程中飞灰减重率和重金属挥发率的变化规律，并对飞灰热处理后的收集物进行XRD实验。结果表明，Cd和Pb在小粒径飞灰中含量较高，Zn和Cu的分布与飞灰的粒径分布相似，Cr富集于相对较大粒径的飞灰中。热处理过程中，1 150 ℃和1 350 ℃时飞灰减重率增长快，而在650～1 050 ℃之间减重率增长缓慢，仅从8%增加至17%。飞灰中重金属经热处理后，挥发率依次为Pb＞Cd＞Cu＞Zn。XRD实验结果表明，Pb主要以双金属氯化物（KPb₂Cl₅）形式挥发。     

粉煤灰深度处理低浓度的磷

为了探讨低浓度磷吸附的方法,比较了粉煤灰、煤质活性炭和粉煤灰碎砖块颗粒这3种价廉易得的吸附材料的除磷效果。经对比确定以粉煤灰为吸附剂,研究了反应时间、粉煤灰投加量以及溶液p H对深度除磷效果的影响。同时为了解粉煤灰高效除磷原理,利用SEM和XRD对其表面形状、所含元素及其内部结构进行了表征。结果表明,粉煤灰比煤质活性碳和粉煤灰砖砖块颗粒的除磷效果更好,去除率高达98.9%;SEM和XRD表征结果显示,由于粉煤灰表面积较大、表面能高、含有Si—O—Si和Si—O—Al—O偶极键及铝、铁和钙的氧化物,使得粉煤灰对低浓度的磷有着高效的去除率;吸附磷后的粉煤灰表面形成了一层絮状物,经EDS分析显示其组成以钙磷沉淀为主;1 g粉煤灰对1 mg/L的磷酸盐溶液在p H=10、反应时间60 min时表现出最佳吸附性能。