砒砂岩对Pb(Ⅱ)的吸附特性研究

以红、白和灰3种不同颜色的砒砂岩作为吸附剂,通过研究不同吸附剂用量、pH和离子强度(IS)等外界条件对砒砂岩吸附Pb(Ⅱ)的影响,以及吸附动力学和等温吸附特征,应用动力学与热力学吸附模型,结合红外光谱(FTIR)分析,探讨砒砂岩吸附Pb(Ⅱ)的机理.结果表明,砒砂岩具有较强的吸附性,能够有效吸附Pb(Ⅱ),其吸附效果受铅浓度、吸附剂用量及pH、离子强度(IS)的影响强烈,即:随pH的增大,吸附量提高,但随离子强度的增大,吸附量却降低.3种颜色的砒砂岩对Pb(Ⅱ)的吸附均在30 min内达到平衡,吸附速率大小表现为灰色白色红色,其吸附过程符合准二级动力学模型.在试验浓度范围内,Freundlich和D-R模型能够较好地模拟砒砂岩对Pb(Ⅱ)的等温吸附特性,3种砒砂岩均是以非均匀孔隙或表面为主要吸附位.结合吸附模型和FTIR表征,吸附机理以静电吸附、离子交换为主,辅以部分化学吸附和一部分化学沉淀综合起作用.     

腐殖酸对生物炭去除水中Cr(Ⅵ)的影响机制研究

以污泥生物炭作吸附剂处理水中Cr(Ⅵ),研究了共存腐殖酸对生物炭吸附性能影响.结果表明,腐殖酸能显著促进生物炭对Cr(Ⅵ)的吸附,大幅提高吸附量以及缩短吸附平衡时间,生物炭吸附过程符合准二级动力学模型.在溶液初始pH4.0,生物炭浓度20 g·L-1,Cr(Ⅵ)初始浓度在50～800 mg·L-1范围下,Langmuir模型比Freundlich模型更好地描述等温吸附行为.加入腐殖酸(20 mg·L-1)后拟合得到的理论饱和吸附量达10.10 mg·g-1,较未加入腐殖酸的吸附量5.56 mg·g-1提高近1倍.在pH 2.0～8.0范围内,吸附量随溶液初始pH值升高而减小.腐殖酸浓度上升,生物炭吸附能力进一步提高.红外光谱显示,生物炭表面的羟基、羧基、酯基、芳香环上C—H和环状结构上的CC等化学活性官能团与Cr(Ⅵ)的吸附有关.结合XPS分析结果,推断腐殖酸共存促进生物炭吸附的机制是:腐殖酸提高了Cr(Ⅵ)在生物炭表面聚集浓度,有利于生物炭对Cr(Ⅵ)的直接吸附和还原,而腐殖酸本身具有的吸附能力增加了对溶液中Cr(Ⅵ)和Cr(Ⅲ)的去除.     

改性木屑对水中刚果红的吸附性能研究

对十六烷基三甲基溴化铵(CTAB)改性木屑用于水中刚果红(CR)的去除进行了研究.用扫描电子显微镜(SEM)和傅里叶红外光谱分析仪(FTIR)对木屑和改性木屑的性能进行表征.探讨了反应时间、pH、温度、剂量以及离子强度对改性木屑去除CR的影响.实验结果表明,CTAB改性后的木屑对刚果红的吸附量明显增大,改性前后木屑的最大吸附量分别为30.30和111.36 mg·g-1.反应过程在前20 min内反应速率很快,并约在120 min内达到吸附平衡.吸附动力学符合伪二级动力学模型.最佳反应温度为328 K,吸附剂最适投加量为0.09 g,吸附量的大小与溶液的初始pH值有关,且增加盐浓度,改性木屑的吸附能力增加.吸附等温线符合Langmuir方程,且吸附过程为吸热反应.     

巯基改性玉米秸秆吸附Hg(Ⅱ)的热力学特征研究

采用化学反应的合成方法向玉米秸秆中引入巯基官能团,并进行电镜扫描、红外光谱和X射线电子能谱分析.在此基础上,以巯基改性玉米秸秆为吸附剂,通过批处理试验讨论了吸附时间、体系pH和温度等因素对水体中Hg(Ⅱ)吸附的影响.结果表明,采用该合成方法可以成功地向玉米秸秆中引入0.98%的巯基官能团,巯基改性玉米秸秆对水体Hg(Ⅱ)的吸附最佳pH为6,吸附能在120min内达到平衡,在285K时对Hg(Ⅱ)的最大吸附量可达80.04mg·g-1.吸附过程是自发的放热过程,可用Langmuir模型描述,其吸附机理可能为络合反应控制的化学吸附.研究表明,巯基改性玉米秸秆是一种对水体Hg(Ⅱ)具有良好吸附能力的生物吸附剂.     

水中Cu~(2+)、Ni~(2+)与腐殖酸、膨润土的相互作用研究

研究了Cu2+、Ni2+与腐殖酸以及膨润土与腐殖酸的共存吸附剂的相互作用,考察了相互作用时间、初始pH、温度对相互作用的影响.结果表明,金属离子的去除率随时间增加而增大,吸附量随温度升高而增大.初始pH对Cu2+、Ni2+的去除率影响很大,pH在中性范围附近Cu2+、Ni2+的去除率可以达到最大.吸附动力学实验表明,Cu2+、Ni2+在腐殖酸及共存吸附剂上的吸附符合伪二级吸附速率模型,并得到Cu2+在腐殖酸及共存吸附剂上吸附的活化能Ea分别为17.01和38.49 kJ.mol-1,Ni2+在腐殖酸及共存吸附剂上吸附的活化能Ea分别为15.15和13.35 kJ.mol-1,表明吸附过程以物理吸附为主.Cu2+、Ni2+在腐殖酸及共存吸附剂上的吸附符合Langmuir等温线模型.得到的ΔH0、ΔS0和ΔG0表明金属离子在腐殖酸及共存吸附剂上的吸附是一个吸热、熵增、自发的过程.     

改性稻壳生物炭对水溶液中甲基橙的吸附效果与机制

本文以废弃稻壳为原料,通过不同改性方法将其制成生物炭吸附剂,并用于水体中甲基橙(MO)的吸附.通过氮吸附、X射线衍射(XRD)、傅立叶转换红外光谱(FT-IR)、扫描电镜分析(SEM)、热重分析(TG)、透射电镜(TEM)和X射线光电子能谱(XPS)等技术分析了改性剂种类、浸渍比和热解温度对生物炭的物理化学性质及对MO吸附量的影响,发现热解温度为400℃,以ZnCl_2为改性剂,浸渍比为2∶1时制备的生物炭Z2RT400对MO的去除效果最好.以Z2RT400为吸附剂,探究吸附剂添加量、吸附时间、初始污染物浓度、溶液pH等对甲基橙吸附效果的影响,结果表明,饱和吸附时间为420 min,吸附反应的最佳pH为4,当吸附剂用量为10 mg,初始甲基橙浓度为2 000 mg·L~(-1)时,Z2RT400对MO的最大吸附量可达1 967. 72 mg·g~(-1);当吸附剂添加量为80 mg时,去除率最高可达99. 52%.此外,对吸附机制进行分析,发现吸附等温线数据符合Freundlich模型,吸附动力学数据符合拟二级动力学模型,说明吸附以化学吸附为主,物理吸附为辅.因此,废弃稻壳为原料改性制备的生物炭可作为高效的有机染料吸附剂,并应用于水体中污染物的治理.     

球衣菌吸附重金属Hg2+的理化条件及其机理研究

采用球衣菌(Sphaerotglus natans)FQ32为生物吸附剂,研究了初始离子浓度、吸附剂用量、菌龄、pH值、温度和吸附时间等理化因素对其吸附重金属Hg2 的影响,并进一步研究了吸附机理.结果表明,球衣菌在Hg2 浓度为16 mg·L-1、吸附剂用量0.4g·L-1、菌龄16h、pH 7、温度30℃、吸附时间90 rmin时的优化条件下,对Hg2 的吸附量为72.86 mg·g-1;该吸附过程是一个快速的过程,在吸附5 min时,吸附量达总吸附量的74.10%,90 min达到吸附平衡;此过程符Langmuir等温方程.等温模型、透射电镜观察和红外光谱分析显示,菌体细胞表面的活性基团与Hg2 的络合反应是球衣菌吸附Hg2 的主要机理.     

固液界面NOM吸附中疏水效应的影响研究

文章以腐殖酸和纳米Fe2O3为对象,着重研究了腐殖酸分子在纳米Fe2O3表面的吸附过程中的疏水效应,借助红外光谱和热重等分析方法研究了腐殖酸吸附前后的疏水性随溶液环境变化的规律。结果表明,当离子强度为0、0.005、0.01和0.05 mol/kg,pH值从7变到12时,纳米Fe2O3吸附溶解性腐殖酸分子后形成的复合体的热失重量随着pH值的升高先减小后增大。当pH值从7升高到10时,亲水性降低,疏水性增强;当pH值从10升高到12时,亲水性增强,疏水性降低。当离子强度为0.001 mol/kg,pH值从7变到12时,复合体的热失重量随着pH值的升高而减小,亲水性降低,疏水性增强。当pH值为定值,离子强度变化时,纳米Fe2O3吸附溶解性腐殖酸分子后形成的复合体的热失重量随着离子强度的增加不断变化,曲线呈现出波动趋势,亲、疏水性在交替变化。红外光谱分析结果说明,对纳米Fe2O3吸附溶解性腐殖酸分子后形成的复合体的亲疏水性起主要影响的官能团可能是亲水性的羟基-OH、羰基C=O和疏水性的CH2烷烃。     

Cu2+存在下腐殖酸对磺胺嘧啶吸附解吸的影响

为探究重金属与抗生素共存时不同条件下土壤有机组分对抗生素吸附解吸的影响,通过批量静态吸附试验方法,研究了不同污染物浓度、初始pH、离子强度及阳离子类型下腐殖酸对磺胺嘧啶（sulfadiazine）和重金属Cu共存时吸附解吸行为及其交互作用,并做了显著性差异分析;采用Freundlich、Langmuir等温吸附模型和线性等温吸附模型对试验数据进行拟合,对吸附前后的样品进行红外光谱扫描分析.结果表明:①不同w（Cu2+）对腐殖酸吸附磺胺嘧啶的状况不同,当w（Cu2+）为1、10、100 mg/kg时,Cu2+的存在起促进吸附的作用;当w（Cu2+）为300 mg/kg时,Cu2+的存在起抑制吸附的作用;随着初始pH的增大,吸附量变化不明显,但略有减小;高离子强度促进吸附,低离子强度抑制吸附;高价态阳离子的存在抑制腐殖酸对磺胺嘧啶的吸附.②显著性差异分析显示,P均小于0.05,说明w（Cu2+）、pH、离子强度及阳离子类型对吸附量均有显著影响.③运用Freundlich、Langmuir等温吸附模型和线性等温吸附模型对不同条件下的吸附特征进行拟合,其拟合效果均较好,R2均大于0.952,其中线性等温吸附模型拟合效果最好;HI（滞后系数）在0.995~1.120之间,接近于1,表明腐殖酸对磺胺嘧啶的吸附解吸过程中不存在滞后现象.△G（吉布斯自由能变化量）在18.921~20.412 kJ/mol之间,均小于40 kJ/mol,属于物理吸附.④红外光谱分析表明,腐殖酸对磺胺嘧啶的吸附机制主要是形成氢键或发生络合反应.研究显示,不同条件下腐殖酸对磺胺嘧啶吸附解吸的影响不同,w（Cu2+）、初始pH、离子强度及阳离子类型的改变,均会导致腐殖酸对磺胺嘧啶的吸附情况有所差异.      

腐殖酸负载羟基磷灰石对废水中Cd2+吸附性能的影响

以硝酸钙、磷酸氢二铵和腐殖酸为原料,制备了腐殖酸负载羟基磷灰石(HA/HAP)复合吸附剂.同时,利用SEM、BET、FT-IR、XRD对复合吸附剂结构和形貌进行表征,研究了HA/HAP对废水中Cd~(2+)的吸附工艺.结果表明,腐殖酸使羟基磷灰石孔容和孔径增大、比表面积减小,从而提高了羟基磷灰石的吸附性能.在pH=6、吸附剂投加量为800 mg、接触时间为180 min时吸附率最佳,为98.3%.HA/HAP对废水中Cd~(2+)的吸附是自发的、吸热的、可持续的化学吸附,反应前120 min适合采用准一级动力学伴随着内扩散模型描述,后120 min适合采用准二级动力学伴随着内扩散模型描述,Dubinin-Radushkevich(D-R)等温线模型拟合的吸附数据在不同温度下效果最好(R~20.98),吸附量分别为259.15、266.05和264.66 mg·g~(-1).研究表明,静电吸附到腐殖酸活性位点后Cd~(2+)主要以络合反应被吸附到羟基磷灰石的表面和两个羟基中间.     

钢渣-蒙脱石复合吸附剂对水中Cd~(2+)的吸附去除

研究了钢渣-蒙脱石复合吸附剂对废水中Cd2+的吸附性能,并探讨了影响吸附的因素和吸附机理.结果表明,钢渣蒙脱石质量比为1∶1的复合吸附剂对Cd2+的吸附效果优于钢渣及蒙脱石对Cd2+的单一吸附.当温度为25℃,废水pH=6~7时,1.2 g钢渣-蒙脱石复合吸附剂对100 mL Cd2+溶液(100 mg·L-1)吸附60 min后,Cd2+的去除率可达到96.99%.钢渣-蒙脱石复合吸附剂对镉离子的吸附反应符合二级动力学方程,可决系数为0.9991;符合Langmuir方程,可决系数为0.9725.对Cd2+的理论饱和吸附量为12.45 mg·g-1.溶液中Pb2+、Cu2+的存在会降低复合吸附剂对Cd2+的吸附量,且Cd2+受Cu2+的影响较大.吸附饱和的钢渣-蒙脱石颗粒材料用1 mol·L-1的氯化钠溶液再生效果好.     

氯化十六烷基吡啶改性活性炭对水中硝酸盐的吸附作用

采用阳离子表面活性剂氯化十六烷基吡啶(CPC)对活性炭进行了改性,并通过实验考察了CPC改性活性炭对水中硝酸盐的吸附作用.结果表明,CPC改性活性炭对水中的硝酸盐具备较好的吸附能力.CPC改性活性炭对水中硝酸盐的吸附能力明显高于未改性的活性炭.CPC改性活性炭对水中硝酸盐的吸附能力随着CPC负载量的增加而增加.CPC改性活性炭对水中硝酸盐的吸附动力学满足准二级动力学模型.CPC改性活性炭对水中硝酸盐的吸附平衡数据可以较好地采用Langmuir等温吸附模型加以描述.根据Langmuir等温吸附方程,CPC负载量(以活性炭计)为444 mmol·kg-1的改性活性炭对水中硝酸盐的最大单位吸附量为16.1 mg·g-1.CPC改性活性炭对水中硝酸盐的吸附能力随着pH的增加而降低.水中共存的氯离子、硫酸根离子和碳酸氢根离子会抑制CPC改性活性炭对水中硝酸盐的吸附.升高反应温度略微降低了CPC改性活性炭对水中硝酸盐的吸附能力.采用1 mol·L-1的NaCl溶液可以使95%左右吸附到CPC改性活性炭上的硝酸盐解吸下来.CPC改性活性炭吸附水中硝酸盐的主要机制是阴离子交换和静电吸引作用.上述实验结果说明,CPC改性活性炭适合作为一种吸附剂用于去除水中的硝酸盐.     

Adsorption of humic acid from aqueous solution on bilayer hexadecyltrimethyl ammonium bromide-modified zeolite

Surfactant-modified natural zeolites (SMNZ) with different coverage types were prepared by loading hexadecyltrimethyl ammonium bromide (HTAB) onto the surface of a natural zeolite. The adsorption behavior of humic acid (HA) on SMNZ was investigated. Results indicate that the adsorbent SMNZ exhibited a higher affinity toward HA than the natural zeolite. HA removal efficiency by SMNZ increased with HTAB loading. Coexisting Ca²⁺ in solution favored HA adsorption onto SMNZ. Adsorption capacity decreased with an increasing solution pH. For typical SMNZ with bilayer HTAB coverage, HA adsorption process is well described by a pseudo-second-order kinetic model. The experimental isotherm data fitted well with the Langmuir model. Calculated maximum HA adsorption capacities for SMNZ with bilayer HTAB coverage at pH 5.5 and 7.5 were 63 and 41 mg·g⁻¹, respectively. E2/E3 (absorbance at 250 nm to that at 365 nm) and E4/E6 (absorbance at 465 nm to that at 665 nm) ratios of the residual HA in solution were lower than that of the original HA solution. This indicates that the HA fractions with high polar functional groups, low molecular weight (MW), and aromaticity had a stronger tendency for adsorption onto SMNZ with bilayer HTAB coverage. Results show that HTAB-modified natural zeolite is a promising adsorbent for removal of HA from aqueous solution.     

金属有机骨架MIL-68(Al)对水中典型荧光增白剂VBL的吸附去除

以金属有机骨架材料MIL-68(Al)为吸附剂,探究其对水中典型荧光增白剂VBL分子的吸附行为.采用粉末X射线衍射仪(XRD)、傅里叶变换红外光谱(FTIR)、场发射扫描电镜(SEM)及N_2吸附脱附对MIL-68(Al)的结构性质进行表征.探讨了p H值、离子强度、污染物初始浓度、反应温度及吸附时间对MIL-68(Al)吸附去除水中VBL的影响,并对吸附等温线、动力学、热力学及吸附机制进行了分析.实验结果表明,MIL-68(Al)对VBL的吸附能适应较宽的p H范围,吸附等温线符合Langmuir模型,最大吸附容量达到400.02 mg·g~(-1);吸附速率在前20 min很快,并且能在180 min达到吸附平衡,吸附动力学符合准二级动力学模型;吸附过程是吸热反应,吸附自发进行并且主要由熵驱动;静电作用和氢键作用对吸附均有贡献,静电作用是吸附发生的主要机制.由以上结果可知,MIL-68(Al)是一种潜在的高效吸附剂,在去除水中的VBL分子方面极具潜力.     

锆-十六烷基三甲基氯化铵改性活性炭对水中硝酸盐和磷酸盐的吸附特性

采用锆(Zr)和阳离子表面活性剂十六烷基三甲基氯化铵(CTAC)对活性炭进行联合改性,考察了所制备的Zr-CTAC改性活性炭对水中硝酸盐和磷酸盐的吸附去除作用,并探讨了相关的吸附去除机制.结果表明,Zr-CTAC改性活性炭对水中硝酸盐和磷酸盐均具备较好的吸附去除能力.Zr-CTAC改性活性炭对硝酸盐和磷酸盐吸附动力学过程满足准二级动力学模型.Langmuir、Freundlich和Dubinin-Radushkevich(D-R)等温吸附模型可以较好地描述Zr-CTAC改性活性炭对水中硝酸盐的等温吸附过程,Langmuir和D-R等温吸附模型可以较好地描述Zr-CTAC改性活性炭对水中磷酸盐等温吸附过程,通过Langmuir模型计算得到吸附剂对硝酸盐和磷酸盐的最大单位吸附量分别为7.58 mg·g-1和10.9 mg·g-1.高的p H会抑制Zr-CTAC改性活性炭对水中硝酸盐和磷酸盐的吸附.水中共存的Cl-、HCO-3和SO2-4等阴离子均会抑制Zr-CTAC改性活性炭对硝酸盐和磷酸盐的吸附,且对吸附硝酸盐的抑制作用较强而对吸附磷酸盐的抑制作用较弱.水中共存的磷酸盐对Zr-CTAC改性活性炭吸附硝酸盐的抑制作用较强,而水中共存的硝酸盐对Zr-CTAC改性活性炭吸附磷酸盐的抑制作用较弱.1 mol·L-1Na Cl溶液可以使90%左右被吸附到Zr-CTAC改性活性炭表面上的硝酸盐解吸下来.1 mol·L-1的Na OH溶液可以使78%左右被吸附到Zr-CTAC改性活性炭表面上的磷酸盐解吸下来.Zr-CTAC改性活性炭对硝酸盐的吸附机制主要包括阴离子交换作用和静电吸引作用,对磷酸盐的吸附机制主要包括配位体交换作用、阴离子交换作用和静电吸引作用.上述结果说明Zr-CTAC改性活性炭适合作为一种吸附剂去除废水中的硝酸盐和磷酸盐.     

新型铁铜铝三元复合氧化物除磷性能与机制研究

采用共沉淀法制备了一种新型铁铜铝三元复合氧化物吸附剂,系统研究了其对磷的吸附行为,并对吸附磷前后的吸附剂进行了表征.吸附实验结果表明,铁铜铝三元复合氧化物对磷具有优异的吸附去除效能,Freundlich吸附等温线模型能更好地拟合其对磷的吸附,最大吸附量为62.6 mg·g-1(pH=7.0),显著高于多数文献报道的磷吸附剂;吸附速率较快,吸附动力学更符合Elovich模型;溶液pH对磷吸附有一定影响,随着pH的升高,磷吸附量降低,离子强度则影响不大;共存阴离子对磷吸附具有抑制作用,影响的大小顺序为SiO_3~(2-)SO_4~(2-)CO_3~(2-)Cl~-,而共存阳离子Ca2+和Mg2+则对磷吸附略有促进作用.Zeta电位、红外谱图(FTIR)和X射线光电子能谱(XPS)表征分析表明,磷在铁铜铝三元复合氧化物表面发生了特性吸附,磷酸根主要通过取代复合氧化物表面的羟基形成内表面络合物而被吸附去除.溶出实验结果表明,当pH在5.0~8.5范围内,Fe~(3+)、Cu~(2+)、Al~(3+)的溶出量均较低.由此可知,铁铜铝三元复合氧化物是一种具有良好应用前景的除磷吸附剂.     

包埋固定化海洋硅藻吸附材料的制备及其对水中铅离子的吸附特性研究

采用海藻酸钠(SA)凝胶包埋法对海洋硅藻藻粉进行固定化,考察了藻粉用量、海藻酸钠浓度、Ca Cl2质量分数、交联时间及小球粒径对固定化小球吸附铅离子性能的影响,并研究了这种吸附材料对Pb~(2+)的吸附特性.结果表明,固定化海洋硅藻生物吸附剂的最佳制备条件为:藻粉用量5.0 g/100 m L SA、海藻酸钠浓度20 g·L~(-1)、Ca Cl2质量分数0.5%、交联时间1 h、小球粒径2.8 mm左右.Langmuir等温吸附模型能够较好地描述固定化小球吸附对Pb~(2+)的等温吸附特征,R2为0.9983,最大理论吸附量为833.33 mg·g~(-1).准二级动力学模型能够较好地拟合固定化小球吸附Pb~(2+)的动力学过程,理论平衡吸附量为714.29 mg·g~(-1),与实验所得平衡吸附量706.55 mg·g~(-1)较为接近.固定化小球吸附Pb~(2+)的适宜初始p H值为4~5.Na Cl、Ca(NO3)2、Mg(NO3)2对固定化小球的吸附性能有一定的促进作用.本研究所制固定化海洋硅藻球形吸附材料对Pb~(2+)的吸附容量明显优于大部分研究所报道的固定化生物吸附剂,是一种很有潜力的生物吸附材料.     

改性石墨烯对水中亚甲基蓝的吸附性能研究

对十六烷基三甲基溴化铵(CTAB)改性石墨烯用于水中亚甲基蓝(MB)的去除进行了研究.用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射分析仪(XRD)、傅里叶红外光谱分析仪(FTIR)和热重分析仪(TGA)对石墨烯和改性石墨烯性能进行表征.探讨了反应时间、pH、温度、剂量对石墨烯和改性石墨烯去除MB的影响.结果表明,在石墨烯制备过程中添加CTAB可以明显增大比表面积,提高MB的去除率.反应过程在前15 min内反应速率很快,并约在120 min内达到吸附平衡.吸附动力学符合伪二级动力学模型.最佳反应温度为293 K,吸附剂投加量的最适浓度为2 g·L-1,且吸附量的大小与溶液的初始pH值无关.通过Langmuir等温吸附方程得到改性石墨烯的最大吸附量86.43 mg·g-1,且为放热反应.     

3种吸附剂对污水磷污染去除性能与机制比较

为探索高效利用膨润土、红壤和炉渣去除农业污水磷污染的可行性,对比分析了3种吸附剂对人工合成含磷污水的吸附去除特性,结合SEM、XDS和BET等测试结果以及等温吸附、吸附动力学及Ca2+释放量探讨了3种材料对磷的吸附机制.结果表明,炉渣对磷的吸附能力高于膨润土和红壤,吸附过程均适合Langmuir等温吸附方程(R2 0. 96),对磷的理论饱和吸附量为:炉渣(16. 87 mg·g~(-1))红壤(1. 21 mg·g~(-1))膨润土(0. 92 mg·g~(-1)).炉渣对磷的吸附动力学特征符合Elovich方程(R2=0. 966),而膨润土和红壤对磷的吸附特征则更适合准二级动力学方程(R2为0. 982和0. 959).炉渣的Ca2+释放量(10. 46 mg·g~(-1))显著大于膨润土(0. 31 mg·g~(-1))和红壤(0. 03 mg·g~(-1))(P 0. 05).红壤对磷的吸附量随着p H的升高而降低;膨润土在初始p H为7. 0时,吸附量最低;但初始p H值对炉渣去除磷的影响不大.相比红壤和炉渣,膨润土解吸较快,易于进行重复利用.综上所述,吸附材料的磷吸附能力主要与其结构、化学组成、Ca2+释放能力及溶液初始p H值等有关,炉渣较膨润土和红壤对磷酸盐有着更强的去除能力,适合处理农村污水磷污染.     

EDTA-nSiO2纳米颗粒对Cd2+的吸附

nSiO_2纳米颗粒是一种广泛应用的工程纳米材料,为增加其对水溶液中Cd~(2+)的吸附性能,采用接枝改性的方法制备出乙二胺四乙酸(EDTA)改性nSiO_2纳米颗粒(EDTA-nSiO_2),并用透射电镜、氮气吸附-解吸、红外光谱和差热分析等手段对其进行了结构表征,同时以其为吸附剂,通过批处理实验法探讨了体系pH、吸附时间、温度、离子强度等因素对Cd~(2+)吸附的影响,并结合X射线能谱(XPS)分析对其吸附机制进行了分析.结果表明,以EDTA为改性剂,可以成功制备出稳定性良好的EDTA-nSiO_2纳米颗粒,其对Cd~(2+)的吸附受体系p H控制;nSiO_2对Cd~(2+)的吸附量较小,EDTA改性可增加nSiO_2对Cd~(2+)的吸附作用,随着p H的升高,Cd~(2+)的吸附效果逐渐增强,在p H大于4.0后逐渐趋于稳定.EDTA-nSiO_2对Cd~(2+)的吸附速率较快,可在1 h内达到吸附平衡.EDTA-nSiO_2对Cd~(2+)的吸附为吸热的自发过程,吸附等温线可用Langmuir模型描述.NaCl浓度增加会导致Cd~(2+)的吸附量下降,当体系Na Cl浓度从0增加到100 mmol·L~(-1),Cd~(2+)的最大吸附量从0.433 mmol·g-1降低至0.294mmol·g-1.0.1 mol·L~(-1)HCl是较为合适的吸附剂再生液,Cd~(2+)洗脱率约94.36%.结合pH、温度、离子强度、再生和XPS分析结果,可以推测出EDTA-nSiO_2对Cd~(2+)的吸附是包含有简单的物理吸附和离子交换过程,并以化学络合为主的吸附过程.EDTA-nSiO_2是一种对水体Cd~(2+)具有较好吸附能力的工程纳米材料吸附剂.