Ultrasound-assistant preparation of Cu-SAPO-34 nanocatalyst for selective catalytic reduction of NO by NH3

The influence of the various preparation methods of Cu-SAPO-34 nanocatalysts on the selective catalytic reduction of NO with NH₃ under excess oxygen was studied. Cu-SAPO-34 nanocatalysts were prepared by using four techniques: conventional impregnation (IM), ultrasound-enhanced impregnation (UIM), conventional deposition precipitation (DP) using NaOH and homogeneous deposition precipitation (HDP) using urea. These catalysts were characterized in detail by various techniques such as N₂-sorption, XRD, TEM, H₂-TPR, NH₃-TPD and XPS to understand the catalyst structure, the nature and the dispersed state of the copper species, and the acid sites for NH₃ adsorption. All of the nanocatalysts showed high activities for NO removal. However, the activities were different and followed the sequence of Cu-SAPO-34 (UIM) > Cu-SAPO-34 (HDP) > Cu-SAPO-34 (IM) > Cu-SAPO-34 (DP). Based on the obtained results, it was concluded that the NO conversion on Cu-SAPO-34 nanocatalysts was mainly related to the high reducibility of the isolated Cu^2 + ions and CuO species, the number of the acid sites and the dispersion of CuO species on SAPO-34.     

Structures and catalytic performances of Me/SAPO-34 (Me = Mn, Ni, Co) catalysts for low-tem perature SCR of NOx by ammonia

Me/SAPO-34 (Me = Mn, Ni, Co) series of catalysts were prepared by a wetness impregnation method and investigated for the selective catalytic reduction of nitrogen oxides with ammonia (NH₃-SCR). Among them, Mn/SAPO-34 catalyst was found as the most promising candidate based on its superior low-temperature activity. The catalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy images (TEM), nuclear magnetic resonance (NMR), X-ray photoelectron spectroscopy (XPS), temperature programmed reduction and desorption (TPR and TPD), and diffuse reflectance infrared Fourier transformed spectroscopy (DRIFTS) of NH₃/NO_x adsorption. Mn/SAPO-34 is obviously different from Ni/SAPO-34 and Co/SAPO-34 in the active species state and distribution. Surface MnO_x species which play an essential role in NO oxidation and NO₂ adsorption, act as better active sites than nickel and cobalt mostly in the form of the aluminates and silicates.     

The selective catalytic reduction of NO over Ce0.3TiOx-supported metal oxide catalysts

A Ce_(0.3)TiO_xoxide carrier was synthesized via a sol–gel process,and Ce_(0.3)TiO_xsupported metal(M=Cd,Mn,Fe,W,Mo)oxide catalysts were prepared by the method of incipient-wetness impregnation.The catalysts were characterized by means of X-ray diffraction(XRD),Brunauer–Emmett–Teller(BET)analysis,scanning electron microscopy(SEM),transmission electron microscopy(TEM),Fourier transform infrared(FT–IR)spectroscopy,UV–Visdiffusereflectancespectroscopy(UV–VisDRS),and Temperature-programmed reduction with H_2(H_2-TPR).The catalytic activities for de-NO_(x )were evaluated by the NH_3-SCR reaction.Among all the catalysts tested,the 2 wt.%Cd/Ce_(0.3)TiO_xcatalyst exhibited the best NH_3-SCR performance,with a wide temperature window of 250–450°C for NO conversion above 90%.Moreover,the catalyst showed N_2 selectivity greater than 99%from 200 to 450°C.     

Optimizing the crystallinity and acidity of H-SAPO-34 by fluoride for synthesizing Cu/SAPO-34 NH3-SCR catalyst

A series of H-SAPO-34 zeolites were synthesized by a hydrothermal method in fluoride media. The as-synthesized H-SAPO-34 zeolites were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), N₂ physisorption, temperature-programmed desorption of NH₃ (NH₃-TPD) and nuclear magnetic resonance (NMR) measurements. The results showed that a certain concentration of F⁻ anions promoted the nucleation and crystallization of H-SAPO-34. The H-SAPO-34 synthesized in the fluoride media showed high crystallinity, uniform particle size distribution, large specific surface area and pore volume, and enhanced acidity. Therefore, Cu/SAPO-34 based on the fluoride-assisted zeolite showed a broadened temperature window for the selective catalytic reduction of NO by NH₃ (NH₃-SCR) reaction due to the enhanced acidity of the zeolite and the improved dispersion of copper species.     

Deactivation of Cu-SAPO-34 by urea-related deposits at low temperatures and the regeneration

Selective catalytic reduction(SCR) with urea catalyzed by Cu-SAPO-34 is an effective method to eliminate NO_x from diesel exhaust. However, urea-related deposits may form during cold-start and urban driving due to low exhaust temperatures. The activity of CuSAPO-34 at 175°C is significantly degraded by urea exposure, and 300°C is required for regeneration. Through in-situ diffuse reflectance infrared Fourier transform spectroscopy(DRIFTS) and temperature-programmed hydrolysis studies, the dominant stable deposit at 175°C is identified as biuret, which can be eliminated at 300°C. The urea-derived deactivation and regeneration mechanisms of Cu-SAPO-34 were compared with those of anatase-supported catalysts.     

Photocatalytic decomposition of acrylonitrile with N–F codoped TiO2/SiO2 under simulant solar light irradiation

The solid acid catalyst, N–F codoped TiO₂/SiO₂ composite oxide was prepared by a sol–gel method using NH₄F as nitrogen and fluorine source. The prepared materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–Visible diffuse reflectance spectroscopy (UV–Vis), ammonia adsorption and temperature-programmed desorption (NH₃-TPD), in situ Fourier transform infrared spectroscopy (FT-IR) and N₂ physical adsorption isotherm. The photocatalytic activity of the catalyst for acrylonitrile degradation was investigated under simulant solar irradiation. The results showed that strong Lewis and Brønsted acid sites appear on the surface of the sample after N–F doping. Systematic investigation showed that the highest photocatalytic activity for acrylonitrile degradation was obtained for samples calcined at 450°C with molar ratio (NH₄F to Ti) of 0.8. The degradation ratio of 71.5% was achieved with the prepared catalyst after 6-min irradiation, demonstrating the effectiveness of photocatalytic degradation of acrylonitrile with N–F codoped TiO₂/SiO₂ composite oxide. The photocatalyst is promising for application under solar light irradiation. Moreover, the intermediates generated after irradiation were verified by gas chromatography–mass spectrometry (GC–MS) analysis and UV–Vis spectroscopy to be simple organic acids with lower toxicity, and the degradation pathway was also proposed for acrylonitrile degradation with the prepared catalyst.     

Effect of TiO2 calcination temperature on the photocatalytic oxidation of gaseous NH3

Carbon-modified titanium dioxide(TiO2) was prepared by a sol-gel method using tetrabutyl titanate as precursor, with calcination at various temperatures, and tested for the photocatalytic oxidation(PCO) of gaseous NH3 under visible and UV light. The test results showed that no samples had visible light activity, while the TiO2 calcined at 400℃ had the best UV light activity among the series of catalysts, and was even much better than the commercial catalyst P25. The catalysts were then characterized by X-ray diffractometry, Brunauer-Emmett-Teller adsorption analysis, Raman spectroscopy, thermogravimetry/differential scanning calorimetry coupled with mass spectrometry, ultraviolet-visible diffuse reflectance spectra, photoluminescence spectroscopy and in situ diffuse reflectance infrared Fourier transform spectroscopy. It was shown that the carbon species residuals on the catalyst surfaces induced the visible light adsorption of the samples calcined in the low temperature range( 300℃). However, the surface acid sites played a determining role in the PCO of NH3 under visible and UV light over the series of catalysts. Although the samples calcined at low temperatures had very high SSA, good crystallinity, strong visible light absorption and also low PL emission intensity, they showed very low PCO activity due to their very low number of acid sites for NH3 adsorption and activation. The TiO2 sample calcined at 400℃ contained the highest number of acid sites among the series of catalysts, therefore showing the highest performance for the PCO of NH3 under UV light.     

Remarkable promotion effect of trace sulfation on OMS-2 nanorod catalysts for the catalytic combustion of ethanol

OMS-2 nanorod catalysts were synthesized by a hydrothermal redox reaction method using MnSO₄ (OMS-2-SO₄) and Mn(CH₃COO)₂ (OMS-2-AC) as precursors. SO₄^2 −-doped OMS-2-AC catalysts with different SO₄^2 − concentrations were prepared next by adding (NH₄)₂SO₄ solution into OMS-2-AC samples to investigate the effect of the anion SO₄^2 − on the OMS-2-AC catalyst. All catalysts were then tested for the catalytic oxidation of ethanol. The OMS-2-SO₄ catalyst synthesized demonstrated much better activity than OMS-2-AC. The SO₄^2 − doping greatly influenced the activity of the OMS-2-AC catalyst, with a dramatic promotion of activity for suitable concentration of SO₄^2 − (SO₄/catalyst = 0.5% W/W). The samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma optical emission spectroscopy (ICP-OES), NH₃-TPD and H₂-TPR techniques. The results showed that the presence of a suitable amount of SO₄^2 − species in the OMS-2-AC catalyst could decrease the Mn–O bond strength and also enhance the lattice oxygen and acid site concentrations, which then effectively promoted the catalytic activity of OMS-2-AC toward ethanol oxidation. Thus it was confirmed that the better catalytic performance of OMS-2-SO₄ compared to OMS-2-AC is due to the presence of some residual SO₄^2 − species in OMS-2-SO₄ samples.     

Preparation and evaluation of aminopropyl-functionalized manganese-loaded SBA-15 for copper removal from aqueous solution

A novel material, aminopropyl-functionalized manganese-loaded SBA-15 (NH₂-Mn-SBA-15), was synthesized by bonding 3-aminopropyl trimethoxysilane (APTMS) onto manganese-loaded SBA-15 (Mn-SBA-15) and used as a Cu^2 + adsorbent in aqueous solution. Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction spectra (XRD), N₂ adsorption/desorption isotherms, high resolution field emission scanning electron microscopy (FESEM) and X-ray photoelectron spectroscopy (XPS) were used to characterize the NH₂-Mn-SBA-15. The ordered mesoporous structure of SBA-15 was remained after modification. The manganese oxides were mainly loaded on the internal surface of the pore channels while the aminopropyl groups were mainly anchored on the external surface of SBA-15. The adsorption of Cu^2 + on NH₂-Mn-SBA-15 was fitted well by the Langmuir equation and the maximum adsorption capacity of NH₂-Mn-SBA-15 for Cu^2 + was over two times higher than that of Mn-SBA-15 under the same conditions. The Elovich equation gave a good fit for the adsorption process of Cu^2 + by NH₂-Mn-SBA-15 and Mn-SBA-15. Both the loaded manganese oxides and the anchored aminopropyl groups were found to contribute to the uptake of Cu^2 +. The NH₂-Mn-SBA-15 showed high selectivity for copper ions. Consecutive adsorption–desorption experiments showed that the NH₂-Mn-SBA-15 could be regenerated by acid treatment without altering its properties.     

不同SAPO分子筛负载MnOx催化剂的低温NH3-SCR性能研究

以磷酸硅铝分子筛SAPO-5、SAPO~(-1)1和SAPO-34为载体,采用乙醇分散法制备了用于低温氨选择性还原(NH_3-SCR)NO_x的分子筛负载MnO_x催化剂.活性测试结果显示,3种分子筛催化剂均展现出优良的NH_3-SCR活性,但三者在低温区间的SCR活性存在较明显差异,其SCR活性顺序如下:MnO_x/SAPO-34MnO_x/SAPO-5MnO_x/SAPO~(-1)1.借助XRD、N2吸附-脱附、XPS、H2-TPR、NH_3-TPD、NH_3FT-IR等技术对催化剂的表面活性物种及表面酸性等进行表征分析,结果表明,MnO_x主要以无定型状态分散于载体上,负载后载体的比表面积和孔体积均有所下降.XPS和H2-TPR分析证实,不同分子筛载体上MnO_x的表面浓度与氧化态明显不同.NH_3-TPD和NH_3FT-IR分析揭示了催化剂表面均存在Bronsted酸位和Lewis酸位,其中,Lewis酸性位对低温SCR反应起着关键作用.研究表明,催化剂的催化性能会因载体不同而存在差异,高Mn4+表面浓度和丰富的Lewis酸性位对催化剂在低温区间实现优良的催化活性尤为重要.     

Selective catalytic reduction of nitrogen oxides over a modified silicoaluminophosphate commercial zeolite

Nitrogen oxides(NO_x:NO,NO_2)are a concern due to their adverse health effects.Diesel engine transport sector is the major emitter of NO_x.The regulations have been strengthened and to comply with them,one of the two methods commonly used is the selective catalytic reduction of NO_xby NH_3(NH_3-SCR),NH_3being supplied by the in-situ hydrolysis of urea.Efficiency and durability of the catalyst for this process are highly required.Durability is evaluated by hydrothermal treatment of the catalysts at temperature above 800°C.In this study,very active catalysts for the NH_3-SCR of NO_xwere prepared by using a silicoaluminophosphate commercial zeolite as copper host structure.Characterizations by X-ray diffraction(XRD),scanning electron microscopy(SEM)and temperature programmed desorption of ammonia(NH_3-TPD)showed that this commercial zeolite was hydrothermally stable up to 850°C and,was able to retain some structural properties up to950°C.After hydrothermal treatment at 850°C,the NO_xreduction efficiency into NH_3-SCR depends on the copper content.The catalyst with a copper content of 1.25 wt.%was the most active.The difference in activity was much more important when using NO than the fast NO/NO_2reaction mixture.     

Effects of WOx modification on the activity, adsorption and redox properties of CeO2 catalyst for NOx reduction with ammonia

A series of WO₃/CeO₂ (WOx/CeO₂) catalysts were synthesized by wet impregnation of ammonium metatungstate on a CeO₂ support. The resulting solid acid catalysts were characterized by X-ray diffraction (XRD), UV-Vis spectroscopy (UV-Vis), Raman spectroscopy (Raman), in-situ Fourier transform infrared spectroscopy (in-situ FT-IR) of ammonia adsorption, NH₃-TPD, H₂ temperature-programmed reduction (H₂-TPR), NH₃/NO oxidation and activity measurements for NOx reduction by NH₃ (NH₃-SCR). The results show that polytungstate (WOx) species are the main species of tungsten oxide on the surface of ceria. The addition of tungsten oxide enhances the Brönsted acidity of ceria catalysts remarkably and decreases the amount of surface oxygen on ceria, with strong interaction between CeO₂ and WOx. As a result, the N₂ selectivity of NH₃ oxidation and NH₃-SCR at high temperatures (> 300℃) is enhanced. Therefore, a wide working temperature window in which NOx conversion exceeds 80% (NOx conversion > 80%) from 200 to 450℃, is achieved over 10 wt.% WOx/CeO₂ catalyst. A tentative model of the NH₃-SCR reaction route on WOx/CeO₂ catalysts is presented.     

活性炭负载Co3O4活化过一硫酸盐降解金橙G

通过浸渍煅烧法制备活性炭负载Co的活化剂(Co/AC),采用X射线衍射仪(XRD)、扫描电镜(SEM)及X射线能谱仪(EDS)技术对活化剂进行表征,发现Co主要以Co_3O_4的形式负载于活性炭表面,并利用Co/AC活化过一硫酸盐(PMS)产生硫酸根自由基(SO_4~-·)降解偶氮染料金橙G(OG),研究了活化反应机制及不同因素对OG降解的影响.结果表明,SO_4~-·在OG降解过程中起主要作用,并且随Co/AC用量、PMS浓度、温度的提高,OG降解效率明显增加.反应初始pH对降解OG有较大影响,当p H在4~8范围内,SO_4~-·均能有效降解OG,但在强酸碱条件下,则不利于OG降解.Cl~-对活化降解OG具有双重作用,低浓度时抑制降解,而在高浓度时促进降解.Co/AC在重复使用6次时仍具有较好活化性能.通过紫外可见光谱及气相色谱-质谱(GC/MS)对OG降解过程及中间产物进行了分析.     

Effects of synthesis methods on catalytic activities of CoOx–TiO2 for low-temperature NH3-SCR of NO

A series of cobalt doped TiO_2(Co-TiO_2) and Co Oxloaded TiO_2(Co/TiO_2) catalysts prepared by sol–gel and impregnation methods respectively were investigated on selective catalytic reduction with NH_3(NH_3-SCR) of NO. It was found that Co-TiO_2 catalyst showed more preferable catalytic activity at low temperature range. From characterization results of XRD,TEM, Raman and FT-IR, Co species were proved to be doped into TiO_2 lattice by replaced Ti atoms. After being characterized and analyzed by NH_3-TPD, PL, XPS, EPR and DRIFTS, it was found that the better NH_3-SCR activities of Co-TiO_2 catalysts, compared with Co/TiO_2 catalyst, were ascribed to the formation of more oxygen vacancies which further promoted the production of more superoxide ions(O-2). The superoxide ions were crucial for the formation of low temperature SCR reaction intermediates(NO-3) by reacting with adsorbed NO molecule. Therefore, these aspects were responsible for the higher low temperature NH_3-SCR activity of Co-TiO_2 catalysts.     

Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

Integrated removal of NO and mercury from coal combustion flue gas using manganese oxides supported on TiO2

A catalyst composed of manganese oxides supported on titania(MnO_x/TiO_2) synthesized by a sol–gel method was selected to remove nitric oxide and mercury jointly at a relatively low temperature in simulated flue gas from coal-fired power plants. The physico-chemical characteristics of catalysts were investigated by X-ray fluorescence(XRF), X-ray diffraction(XRD), and X-ray photoelectron spectroscopy(XPS) analyses, etc. The effects of Mn loading,reaction temperature and individual flue gas components on denitration and Hg~0 removal were examined. The results indicated that the optimal Mn/Ti molar ratio was 0.8 and the best working temperature was 240°C for NO conversion. O_2 and a proper ratio of [NH_3]/[NO]are essential for the denitration reaction. Both NO conversion and Hg~0 removal efficiency could reach more than 80% when NO and Hg~0 were removed simultaneously using Mn0.8 Tiat 240°C.Hg~0 removal efficiency slightly declined as the Mn content increased in the catalysts. The reaction temperature had no significant effect on Hg~0 removal efficiency. O_2 and HCl had a promotional effect on Hg~0 removal. SO2 and NH_3were observed to weaken Hg~0 removal because of competitive adsorption. NO first facilitated Hg~0 removal and then had an inhibiting effect as NO concentration increased without O_2, and it exhibited weak inhibition of Hg~0 removal efficiency in the presence of O_2. The oxidation of Hg~0 on Mn O x/TiO_2 follows the Mars–Maessen and Langmuir–Hinshelwood mechanisms.     

碱土金属钙沉积对Mn-Ce/TiO2低温SCR催化剂脱硝性能的影响

本研究采用浸渍法分别制备CaCl2、CaCO3和CaSO4这3种钙盐前驱体沉积的Mn-Ce/TiO2催化剂,通过分析催化剂活性与催化剂理化特性之间的关系,考察碱土金属钙沉积对Mn-Ce/TiO2低温SCR催化剂脱硝性能的影响.结果表明,钙的加入会导致催化剂中毒,且不同钙前驱体掺杂对催化剂中毒效应不同.CaCO3的沉积对Mn-Ce/TiO2催化剂脱硝效率的影响最小,而CaCl2沉积对催化剂活性抑制作用最为强烈.通过比表面积测试(BET)、X射线光电子能谱(XPS)、X射线晶体衍射(XRD)、程序升温脱附(TPD)等方法对不同催化剂进行表征发现,催化剂的晶型变化、孔道结构破坏、表面活性元素及酸性点位的减少是催化剂中毒的主要原因.     

Preparation and evaluation of aminopropyl-functionalized manganese-loaded SBA-15 for copper removal from aqueous solution

A novel material, aminopropyl-functionalized manganese-loaded SBA-15 (NH₂-Mn-SBA- 15), was synthesized by bonding 3-aminopropyl trimethoxysilane (APTMS) onto manganeseloaded SBA-15 (Mn-SBA-15) and used as a Cu²⁺ adsorbent in aqueous solution. Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction spectra (XRD), N₂ adsorption/ desorption isotherms, high resolution field emission scanning electron microscopy (FESEM) and X-ray photoelectron spectroscopy (XPS) were used to characterize the NH₂-Mn-SBA-15. The orderedmesoporous structure of SBA-15 was remained aftermodification. The manganese oxides were mainly loaded on the internal surface of the pore channels while the aminopropyl groups were mainly anchored on the external surface of SBA-15. The adsorption of Cu²⁺ on NH₂-Mn-SBA-15 was fitted well by the Langmuir equation and the maximum adsorption capacity of NH₂-Mn-SBA-15 for Cu²⁺ was over two times higher than that of Mn-SBA-15 under the same conditions. The Elovich equation gave a good fit for the adsorption process of Cu²⁺ by NH₂-Mn-SBA-15 and Mn-SBA-15. Both the loaded manganese oxides and the anchored aminopropyl groups were found to contribute to the uptake of Cu²⁺. The NH₂-Mn-SBA-15 showed high selectivity for copper ions. Consecutive adsorption-desorption experiments showed that the NH₂-Mn-SBA-15 could be regenerated by acid treatment without altering its properties.     

Preparation of birnessite-supported Pt nanoparticles and their application in catalytic oxidation of formaldehyde

Flaky and nanospherical birnessite and birnessite-supported Pt catalysts were successfully prepared and characterized by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and N₂ adsorption-desorption. Effects of the birnessite morphology and Pt reduction method on the catalytic activity for the complete oxidation of formaldehyde (HCHO) were investigated. It was found that flaky birnessite exhibited higher catalytic activity than nanospherical birnessite. The promoting effect of Pt on the birnessite catalyst indicated that the reduction method of the Pt precursor greatly influenced the catalytic performance. Flaky birnessite-supported Pt nanoparticles reduced by KBH₄ showed the highest catalytic activity and could completely oxidize HCHO into CO₂ and H₂O at 50℃, whereas the sample reduced using H₂-plasma showed lower activity for HCHO oxidation. The differences in catalytic activity of these materials were jointly attributed to the effects of pore structure, surface active sites exposed to HCHO and the dispersion of Pt nanoparticles.     

Visible light responsive N-F-codoped TiO2 photocatalysts for the degradation of 4-chlorophenol

Visible light responsive N-F-codoped TiO₂ photocatalysts exhibit a higher catalytic activity than N-doped TiO₂ for the degradation of 4-chlorophenol due to the synergistic effect of nonmetal elements.