Mn-Ce-Fe/TiO2低温催化还原NO的性能

采用浸渍法制备了Mn-Ce-Fe/TiO2.研究了其组分配比、焙烧温度等制备条件和NO进口浓度、空速、O2含量、NH3/NO摩尔比等操作条件对Mn-Ce-Fe/TiO2 NH3低温还原NO活性的影响,并探讨了H2O、SO2对Mn-Ce-Fe/Ti O2活性的影响.结果表明,Mn:Fe:Ce摩尔比为5:2:4、500℃下焙烧的Mn-Ce-Fe/TiO2在无H2O、SO2,NO体积分数为0.1%,空速为5000h～,反应温度为130℃、O2含量为6%、NH3/NO摩尔比为1.1的条件下,NO转化率接近98%,Fe的加入大大提高了催化剂的单独抗水和同时抗硫抗水性能,130℃下,体积分数10%的H2O对该催化剂的活性基本没有影响,转化率保持在96%以上;通硫、水后的400min内,活性仅下降3%.单独通人S02时,该催化剂中毒程度较深.该催化剂有望应用于基本不含SO2的燃气锅炉烟气和不含SO2的硝酸尾气等NO,工业废气的低温脱硝.     

制备条件对低温NH_3-SCR脱硝催化剂Mn-Ce/TiO_2结构与性能的影响

采用溶胶凝胶法制备了Mn-Ce/TiO2催化剂,以NH3为还原剂,通过程序升温反应考察其选择性催化还原NO的催化性能.同时,着重探讨了焙烧温度、焙烧时间、活性物质负载量及Mn、Ce负载比例对催化剂结构和性能的影响,并用BET、XRD等对催化剂进行了表征.结果表明,活性组分负载量由0增至20%时,NO转化率随着负载量的增加而提高,当(Mn+Ce)质量分数为20%,催化剂活性最高,此后随着活性组分负载量的增加,NO转化率明显下降;Mn与Ce的负载比例为0.85∶0.15时,催化剂比表面积最大,为112.31m2·g-1;焙烧温度500℃时催化剂晶相均为TiO2锐钛矿型结构,焙烧温度升高至600℃,催化剂晶相为TiO2锐钛矿型和金红石型混合结构,且催化剂比表面积急剧减小;焙烧时间对催化剂晶相结构影响不大,焙烧时间为5h时,Mn-Ce/TiO2的脱硝性能最好.     

废弃SCR脱硝催化剂的再生及其脱硝性能研究

对废弃脱硝催化剂处理后重新加工再生,研究了添加剂对其粉体成型和再生催化剂脱硝活性的影响,探讨了反应温度、空速、n(NH3)∶n(NO)摩尔比、氧含量、H2O和SO2对再生催化剂NH3选择性催化还原(SCR)NO的影响。结果表明:最佳再生条件是使用5%羧甲基纤维素和10%无机粘结剂辅助成型;废弃催化剂再生利用率高达90%;再生催化剂抗压强度为4.73 MPa,优于商用催化剂;空速5 000 h-1、氨氮摩尔比1、氧含量6%时,脱硝活性温度窗口为310⁴50℃,350℃时活性最高为94%;350℃时,单独通入1 000×10-6SO2或10%H2O对再生催化剂活性均有一定抑制作用,最低活性分别为70%和81%,停止通入SO2或H2O后其活性逐渐恢复;同时通入1 000×10-6SO2和10%H2O,再生催化剂活性下降至63%并于1 h内保持相对稳定,停止通入SO2和H2O 2 h后,活性逐渐恢复到73%。     

负载型Mn-Co/TiO2催化剂的制备及其低温NH3选择催化还原NO

采用浸渍法制备了一系列以成型TiO2为载体的Mn-Co/TiO2低温SCR催化剂,研究分析了活性组分担载量、Mn含量、焙烧温度、焙烧时间等制备参数和进口NO浓度、空速、O2体积分数、NH3/N2摩尔比等操作条件对催化剂脱硝反应活性的影响.结果表明:活性组分担载量为30%,Mn/(Mn+Co)摩尔比为80%,在500℃下焙烧6 h得到的Mn-Co/TiO2催化剂具有较高的NO转化率;在进口NO浓度为600×10-6、O2体积分数6%、空速10000 h-1、150℃条件下,NO脱除率接近100%.     

钴-铁氧化物复合催化剂催化脱汞的试验研究

采用钴-铁氧化物制备复合催化剂,研究烟气中零价汞的催化氧化脱除性能。考察了催化剂制备的焙烧温度、不同活性组分及不同负载量、烟气温度、NH3/NO及SO2浓度对零价汞催化去除效率的影响规律。结果表明:以Co和Fe作为活性组分的复合催化剂脱汞效率明显高于单一金属催化剂,8%Co-2%Fe的催化剂活性最好,催化剂最佳活性温度为300℃,焙烧温度为400℃时活性最好,烟气中NH3/NO及SO2抑制催化剂的脱汞活性。温度为300℃时可获得86.7%的零价汞脱除效率。     

V_2O_5/TiO_2催化剂用于烟气同时脱硫脱硝的研究

研究了用V2O5/TiO2催化剂同时脱除烟气中的SO2和NO,考察了H2还原温度及其它反应条件对SO2和NO脱除率的影响。结果表明,经H2还原后所制得的V2O5/TiO2催化剂可以提高脱硫脱硝活性,最佳还原温度为700℃;在450～500℃的烟气温度范围内,该催化剂有较佳的脱硫脱硝活性;在相同反应温度下,空速越大,SO2和NO的脱除率越低;烟气中的氧气可大大提高V2O5/TiO2的脱硫脱硝活性,且氧气体积含量在5%～10%范围内变化时,对SO2和NO脱除率的影响较小。     

制备参数对Mn-Ce/TiO2催化剂脱硝性能的影响

以锐钛矿型TiO₂为载体,采用分步共混法制备了Mn-Ce/TiO₂催化剂,通过考察不同活性组分前驱体、焙烧温度以及活性组分负载量对催化剂样品脱硝性能的影响,以确定最佳制备参数;结合XRD（X射线衍射）、XPS（X射线光电子能谱分析）、BET比表积等表征手段研究制备参数对催化剂性能的影响.结果表明:无定型态MnO₂含量越多,越有利于提高催化剂的脱硝活性;催化剂样品表面原子浓度比Mn/Ti[或（Mn+Ce）/Ti]越高,催化剂表面有效活性组分越多,催化剂脱硝活性越好.以自制Mn盐（MX）为前驱体,在Mn-Ce活性组分负载量为16%时,经500℃焙烧的催化剂样品脱硝活性最高;反应空速为10000 h-1,反应温度为80℃时,其脱硝效率可达80%,150℃时脱硝效效率可达99%.      

热处理天然褐铁矿制备γ-Fe2O3及其NH3-SCR活性探究

以天然褐铁矿为前驱体,通过热处理制备γ-Fe_2O_3作为NH3-SCR催化剂.借助XRD、XRF、XPS、NH3-TPD、FR-IR等表征方法,考察反应温度、褐铁矿中的锰氧化物以及H_2O和SO_2对催化剂选择催化还原NO活性的影响并与α-Fe_2O_3作对比.结果表明,由于γ-Fe_2O_3表面比α-Fe_2O_3具有更强的酸性,使得γ-Fe_2O_3的脱硝温度窗口(200~350℃)宽于α-Fe_2O_3(200~300℃),且在活性温度窗口下,催化剂脱硝效率达到99%以上;γ-Fe_2O_3催化剂中少量MnO_2的存在,提高了催化剂低温段(100~200℃)脱硝活性,降低了高温段(400~450℃)脱硝活性;SO_2的存在会使γ-Fe_2O_3的脱硝温度窗口向高温区偏移100℃、体积分数为5%的H_2O对脱硝反应的抑制作用很小,但当SO_2和5%H_2O同时存在,尤其是SO_2的体积分数达到0.12%时,硫酸铵盐类的迅速生成会大大降低γ-Fe_2O_3的脱硝活性;此外,γ-Fe_2O_3经过NH3-SCR反应后,其磁化率略有降低,催化剂仍然具有磁回收循环利用的潜力.     

Ce改性钒磷氧催化剂的制备及其脱硝性能研究

采用Ce调控负载型钒磷氧（VPO/TiO₂）催化剂的表面酸性并与之形成密切相关的微观结构,研究催化剂VPO-Ce/TiO₂的脱硝性能.结果表明,当P/V为1/3、Ce/V为1/4、活性组分负载量10%、催化剂焙烧温度为400℃时,催化剂的脱硝活性最好,反应温度250~350℃范围内的脱硝率高于96.0%.BET测试结果表明,催化剂0.1VP（0.33）O-Ce（0.25）/TiO₂的比表面积为10.74m²/g,较0.1VP（0.33）O/TiO₂提高了约58.6%.0.1VP（0.33）O/TiO₂表面化学吸附氧（O_α）和晶格氧（O_β）的比例O_α/O_β为72%,掺杂Ce后O_α/O_β升高至85%,Ce掺杂还能促进相邻V⁵⁺和V⁴⁺的形成,提高催化剂的氧化还原性能.Ce掺杂对催化剂的表面酸性影响较大,当Ce/V为1/4时催化剂表面Brønsted酸最强,这与活性测试相吻合.控制烟气中SO₂和水蒸气的体积浓度分别为200×10^-6和4vol.%,催化剂的脱硝活性在150~300℃温度范围内最高下降约15.8%,当温度高于300℃时催化剂的脱硝活性几乎不下降,且反应后的催化剂表面无硫酸根生成,催化剂呈现出较强的抗SO₂和水蒸汽的性能.     

单斜相纳米氧化锆基低温SCR催化剂脱硝机制研究

以纳米m-ZrO2为载体,用浸渍法制备出MnOx-CeO2/m-ZrO2催化剂,考察反应温度、活性组分负载量对催化剂NH3-SCR脱硝活性影响,探讨催化剂表面织构特征,分析催化剂脱硝活性机制.结果表明,在低温脱硝温度范围,提高反应温度、增加活性组分负载量,有利于催化剂脱硝效率的增加.110℃时,2.5%MnOx-CeO2/m-ZrO2脱硝效率为55.5%,15%MnOxCeO2/m-ZrO2脱硝效率达93.5%.XRD、BET、XPS、H2-TPR表征结果表明,催化剂表面具有良好的氧化还原能力,表面织构对脱硝反应有利.NH3-TPD测试显示,MnOx-CeO2/m-ZrO2催化剂的脱硝反应机制为:NH3吸附在催化剂表面的Lewis酸性位和Brnsted酸性位上,通过反应生成相应中间产物NH2NO或NH4NO2,中间产物进一步分解最终转变为N2和H2O;催化剂总脱硝反应效率中,在Lewis酸性位上的脱硝反应占比较大.     

NH3-SCR performance and the resistance to SO2 for Nb doped vanadium based catalyst at low temperatures

Niobium oxide as the promoter was doped in the V/WTi catalyst for the selective catalytic reduction(SCR)of NO.The results showed that the addition of Nb_2O_5could improve the SCR activity at low temperatures and the 6 wt.%additive was an appropriate dosage.The enhanced reaction activity of adsorbed ammonia species and the improved dispersion of vanadium oxide might be the reasons for the elevation of SCR activity at low temperatures.The resistances to SO_2of 3V6Nb/WTi catalyst at different temperatures were investigated.FTIR spectrum and TG-FTIR result indicated that the deposition of ammonium sulfate species was the main deactivation reason at low temperatures,which still exhibited the reactivity with NO above 200°C on the catalyst surface.There was a synergistic effect among NH_3,H_2O and SO_2that NH_3and H_2O both accelerated the catalyst deactivation in the presence of SO_2at 175°C.The thermal treatment at 400°C could regenerate the deactivated catalyst and get SCR activity recovered.The particle and monolith catalysts both kept stable NO_xconversion at 225°C with high concentration of H_2O and SO_2during the long time tests.     

Catalytic reduction of nitric oxide with carbon monoxide on copper-cobalt oxides supported on nano-titanium dioxide

A series of copper-cobalt oxides supported on nano-titanium dioxide were prepared for the reduction of nitric oxide with carbon monoxide and characterized using techniques such as XRD, BET and TPR. Catalyst CuCoOx/TiO2 with Cu/Co molar ratio of 1/2, Cu- Co total loading of 30% at the calcination temperature of 350°C formed CuCo2O4 spinel and had the highest activity. NO conversion reached 98.9% at 200°C. Mechanism of the reduction was also investigated, N2O was mainly yielded below 100°C, while N2 was produced instead at higher temperature. O2 was supposed to accelerate the reaction between NOx and CO for its oxidation of NO to give more easily reduced NO2, but the oxidation of CO by O2 to CO2 decreased the speed of the reaction greatly. Either SO2 or H2O had no adverse impact on the activity of NO reduction; however, in the presence of both SO2 and H2O, the catalyst deactivated quickly.     

纳米TiO_2-Al_2O_3负载CuMnO_x对甲苯的催化燃烧

研究采用改进的溶胶-凝胶法制备了TiO2-Al2O3复合载体,并用浸渍法制备CuMnOX/TiO2-Al2O3催化剂,通过对甲苯废气催化燃烧的实验,分别考察了Cu-Mn负载量、Cu/Mn摩尔比、焙烧温度及载体对催化剂制备过程及催化剂活性的影响。实验结果表明:活性组分负载量25%,铜锰活性组分的配比Cu:Mn=1:2,焙烧温度500℃是浸渍法制备CuMnOX/TiO2-Al2O3催化剂较佳的工艺条件;XRD衍射图谱表明,500℃下铜锰尖晶石的存在是催化剂催化活性优良的主要原因;由复合载体制备的CuMnOX/TiO2-Al2O3催化剂比单一载体制备的CuMnOX/Al2O3催化剂具有更高的甲苯转化率,其T99比单一载体要低20℃以上。     

Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3

The catalysts of iron-doped Mn-Ce/TiO 2(Fe-Mn-Ce/TiO 2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction(SCR) of NO with NH 3.It was found that the NO conversion over Fe-Mn-Ce/TiO 2 was obviously improved after iron doping compared with that over Mn-Ce/TiO 2.Fe-Mn-Ce/TiO 2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity.The results showed that 96.8% NO conversion was obtained over Fe(0.1)-Mn-Ce/TiO 2 at 180°C at a space velocity of 50,000 hr 1.Fe-Mn-Ce/TiO 2 exhibited much higher resistance to H 2 O and SO 2 than that of Mn-Ce/TiO 2.The properties of the catalysts were characterized using X-ray diffraction(XRD),N 2 adsorption,temperature programmed desorption(NH 3-TPD and NOx-TPD),and Xray photoelectron spectroscopy(XPS) techniques.BET,NH3-TPD and NOx-TPD results showed that the specific surface area and NH3 and NOx adsorption capacity of the catalysts increased with iron doping.It was known from XPS analysis that iron valence state on the surface of the catalysts were in Fe3+ state.The doping of iron enhanced the dispersion and oxidation state of Mn and Ce on the surface of the catalysts.The oxygen concentrations on the surface of the catalysts were found to increase after iron doping.Fe-Mn-Ce/TiO2 represented a promising catalyst for low temperature SCR of NO with NH3 in the presence of H2 O and SO2.     

疏水型H-ZSM-5分子筛上NO氧化反应的研究

针对NO低温氧化催化剂的抗水汽性差的问题,以疏水型高硅H-ZSM-5分子筛为NO氧化催化剂,在温度为10~90℃、NO进口浓度为0.05%~0.08%,及相对湿度为0~100%条件下,考察了NO的氧化反应.结果表明,H-ZSM-5分子筛的硅铝比由50提高至300时,湿气条件(水汽含量1.18%)下,NO氧化率由20%升高至56%;干气下,低温有利于NO氧化;湿气下(水汽含量1.18%),NO氧化率随着温度的升高先增加后减少,最佳反应温度为20℃,与NOx工业废气的排放温度相近.200h的稳定性试验结果显示,在30℃、NO进口浓度0.08%、空时0.5s、保持相对湿度为50%或100%时,NO氧化率可维持在60%和50%,催化剂具有良好的稳定性.     

Fe-MnOx-CeO2/ZrO2低温催化还原NO性能研究

以纳米ZrO2为载体,用浸渍法制备出Fe-MnOx-CeO2/ZrO2催化剂,考察了活性组分配比和助剂负载量对催化剂低温NH3选择性催化还原NO活性的影响,并对催化剂进行了XRD、SEM、EDS和BET表征;探讨了温度、H2O和SO2对Fe-MnOx-CeO2/ZrO2催化剂低温下NH3选择性催化还原NO的影响,结果表明,无SO2和H2O条件下,8%Fe-10%MnOx-CeO2/ZrO2催化剂具有良好的催化活性和稳定性.120℃时,催化剂的脱硝效率为85.23%,当温度升至180℃时,脱硝效率可达到92.0%.SO2和H2O共存条件下,催化剂易失活,采用傅立叶变换红外光谱对各反应阶段的催化剂进行了表征,对其失活机制进行深入研究,结果表明,催化剂失活的主要原因是催化剂表面硫酸铵盐的沉积和催化剂本身活性成分的硫酸盐化.     

尖晶石型MnCo_2O_4催化剂的制备及SCR性能研究

用柠檬酸配位燃烧法制备了尖晶石复合金属氧化物MnCo2O4,使用X射线衍射仪、傅立叶红外分析仪对其进行了表征,并进一步在固定床反应器中考查了该催化剂的催化氧化、还原NO的性能以及SO2的影响。结果表明,所制备的MnCo2O4催化剂呈现典型的尖晶石结构,在300℃,空速20000h-1时,NO氧化率可以达到30%,而NH3催化还原NO的效率可达99.5%,但SO2对其还原性能有明显影响。     

钒钛基SCR催化剂中毒及再生研究进展

在烟气脱硝系统中,选择性催化还原催化剂的中毒和再生是广泛关注的问题。文章介绍了钒钛基催化剂的碱金属中毒、碱土金属中毒、砷中毒和二氧化硫中毒,探讨其成因,并对中毒机理进行了分析,同时研究了避免催化剂中毒的措施以及中毒催化剂的再生技术。对碱金属中毒和碱土金属中毒催化剂的水洗再生和硫酸酸洗再生方法进行了实验评价。文章对溶胶凝胶法制备的以陶瓷颗粒为骨架的纳米负载型催化剂V2O5-WO3/TiO2(C)进行研究。实验结果表明,硫酸酸洗再生对碱金属和碱土金属中毒催化剂具有较好的再生效果。在380～410℃温度范围内可使中毒催化剂的NO去除率恢复至90%以上。水洗再生对碱金属中毒催化剂无明显效果,而在380～410℃温度范围内可使碱土金属中毒催化剂的NO去除率达到80%以上。对V2O5-WO3/TiO2(C)抗SO2性能研究表明,以锐钛TiO2为载体的V2O5-WO3/TiO2(C)催化剂具有较好的抗SO2效果。