Fe-MnOx-CeO2/ZrO2低温催化还原NO性能研究

以纳米ZrO2为载体,用浸渍法制备出Fe-MnOx-CeO2/ZrO2催化剂,考察了活性组分配比和助剂负载量对催化剂低温NH3选择性催化还原NO活性的影响,并对催化剂进行了XRD、SEM、EDS和BET表征;探讨了温度、H2O和SO2对Fe-MnOx-CeO2/ZrO2催化剂低温下NH3选择性催化还原NO的影响,结果表明,无SO2和H2O条件下,8%Fe-10%MnOx-CeO2/ZrO2催化剂具有良好的催化活性和稳定性.120℃时,催化剂的脱硝效率为85.23%,当温度升至180℃时,脱硝效率可达到92.0%.SO2和H2O共存条件下,催化剂易失活,采用傅立叶变换红外光谱对各反应阶段的催化剂进行了表征,对其失活机制进行深入研究,结果表明,催化剂失活的主要原因是催化剂表面硫酸铵盐的沉积和催化剂本身活性成分的硫酸盐化.     

Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3

The catalysts of iron-doped Mn-Ce/TiO 2(Fe-Mn-Ce/TiO 2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction(SCR) of NO with NH 3.It was found that the NO conversion over Fe-Mn-Ce/TiO 2 was obviously improved after iron doping compared with that over Mn-Ce/TiO 2.Fe-Mn-Ce/TiO 2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity.The results showed that 96.8% NO conversion was obtained over Fe(0.1)-Mn-Ce/TiO 2 at 180°C at a space velocity of 50,000 hr 1.Fe-Mn-Ce/TiO 2 exhibited much higher resistance to H 2 O and SO 2 than that of Mn-Ce/TiO 2.The properties of the catalysts were characterized using X-ray diffraction(XRD),N 2 adsorption,temperature programmed desorption(NH 3-TPD and NOx-TPD),and Xray photoelectron spectroscopy(XPS) techniques.BET,NH3-TPD and NOx-TPD results showed that the specific surface area and NH3 and NOx adsorption capacity of the catalysts increased with iron doping.It was known from XPS analysis that iron valence state on the surface of the catalysts were in Fe3+ state.The doping of iron enhanced the dispersion and oxidation state of Mn and Ce on the surface of the catalysts.The oxygen concentrations on the surface of the catalysts were found to increase after iron doping.Fe-Mn-Ce/TiO2 represented a promising catalyst for low temperature SCR of NO with NH3 in the presence of H2 O and SO2.     

低温条件下Nano-MnOx上NH3选择性催化还原NO

采用流变相法制备了无载体Nano-MnO_x催化剂,在低温条件下(50～150℃)以NH₃为还原剂系统考察了氮氧化物的选择催化还原特性.结果表明,流变相法制备的Nano-MnO_x催化剂具有良好的低温催化活性.实验条件下,80℃即可获得98.25%的NO转化率,100～150℃内NO几乎完全转化;SO₂和H₂Ｏ会与NO和NH₃在催化剂表面产生竞争吸附,导致催化活性下降,但该影响是可逆的.经分析,较大的比表面积和较低的晶化度是Nano-MnO_x具有良好低温活性的2个主要原因.     

Effect of MoO3 on vanadium based catalysts for the selective catalytic reduction of NOx with NH3 at low temperature

The selective catalytic reduction(SCR) activities of the MoO_3 doped V/WTi catalysts prepared by the incipient wetness impregnation method at low temperature were investigated.The results showed that the addition of MoO_3 could enhance the NO_ xconversion at low temperature and the best SCR activity was obtained when the dosage of MoO_3 reached5 wt.%. The NH3-TPD and DRIFTS experiments indicated that the addition of MoO_3 changed the type and number of acid sites on the surface of catalysts and reaction activities of acid sites were altered at the same time. The redox capacity and amount of active oxygen species got improved for V3Mo5/WTi catalyst, which could be confirmed by the H_2-TPR and transient response experiments. Water vapor inhibited the NO_xconversion at low temperature. Deposition of ammonium sulfate or bisulfate might be main reason for the loss of catalytic activity in the presence of SO_2 at low temperature. Choosing the suitable NH_3/NO ratio and elevation of reaction temperature both could weaken the influence of SO_2 on the SCR activity of the V3Mo5/WTi catalyst. Thermal treatment of the deactivated catalyst at350°C could get the low temperature activity recovered. The decrease of GHSV improved the de NO_x efficiency at low temperature and we speculated that the rational technological process and operation parameters could contribute to the application of this kind of catalysts in real industrial environment.     

锰铈脱硝催化剂的制备及其再生性能研究

采用等体积浸渍法制备了一系列Mn-Ce-Ox复合氧化物脱硝催化剂用于NH3选择性催化还原(NH3-SCR)NO。考察了Mn/Ce摩尔比、焙烧温度、H2O和SO2对Mn-Ce-Ox复合氧化物脱硝催化剂活性的影响及催化剂中毒再生性能。结果表明:当NH3:NO=1:1,空速为5 000 h-1,550℃焙烧制得的Mn/Ce摩尔比为5∶1的Mn-Ce-Ox复合脱硝催化剂活性最佳,活性温度窗口为100~260℃,在此温度区间内催化剂活性大于90%。200℃时,Mn-Ce-Ox复合催化剂活性最高为97.84%;在10%(V/V)H2O蒸汽和300×10-6SO2共存条件下,200℃时,催化剂活性在开始反应2.5 h内迅速下降至53%左右,并在之后的6 h内没有明显变化;中毒催化剂经常温水洗再生处理、质量分数为3%的硝酸溶液再生处理和550℃焙烧2 h再生处理后200℃活性均能恢复到90%以上,其中中毒催化剂经质量分数为3%硝酸处理后活性恢复率最高。     

Kinetics of selective catalytic reduction of NO by NH3 on Fe-Mo/ZSM-5 catalyst

The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction (SCR) of nitric oxide (NO) with NH3. The kinetics of the SCR reaction in the presence of O2 was studied in this work. The results show that the observed reaction orders were 0.74-0.99, 0.01-0.13, and 0 for NO, O2 and NH3, respectively, at 350-450℃. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst. The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N2 and H2O. Gaseous O2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process. It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH3.     

Mn-CeOx/Ti-PILCs for selective catalytic reduction of NO with NH3 at low temperature

Titanium-pillared clays (Ti-PILCs) were obtained by different ways from TiCl₄, Ti(OC₃H₇)₄ and TiOSO₄, respectively. Mn-CeO_x/Ti-PILCs were then prepared and their activities of selective catalytic reduction (SCR) of NO with NH₃ at low-temperature were evaluated. Mn-CeO_x/Ti-PILCs were characterized by X-ray diffraction, N₂ adsorption, Fourier transform infrared spectroscopy, thermal analysis, temperature-programmed desorption of ammonia and H₂-temperature-programmed reduction. It was found that Ti-pillar tend to be helpful for the enlargement of surface area, pore volume, acidity and the enhancement of thermal stability for Mn-CeO_x/Ti-PILCs. Mn-CeO_x/Ti-PILCs catalysts were active for the SCR of NO. Among three resultant Mn-CeO_x/Ti-PILCs, the catalyst from TiOSO₄ showed the highest activity with 98% NO conversion at 220℃, it also exhibited good resistance to H₂O and SO₂ in flue gas. The catalyst from TiCl₄ exhibited the lowest activity due to the unsuccessful pillaring process.     

钒和钨负载量对V2O5-WO3/TiO2表面形态及催化性能的影响

采用浸渍法制备了一系列不同钒和钨负载量的V₂O₅-WO₃/TiO₂催化剂样品,对样品NH₃选择性催化还原NO性能进行了评价,并用BET、XRD、XPS等手段对催化剂样品的表面形态进行了表征.研究发现,钒的负载量对催化剂的比表面积和催化活性有显著影响,当钒负载量从1％升高到8％时,催化剂比表面积下降了16 m²/g,最高活性温度降低了约100℃.钨起到稳定剂和助剂的双重作用,当钒负载量为1％时,钨负载量从0升高到6％,催化剂比表面积仅下降了3 m²/g,而活性温度窗口向高温和低温各拓宽了约50℃.研究表明钒和钨负载量都能影响催化剂表面的VO_x物种,但对催化剂的表面晶型没有明显影响.     

钒钛基SCR催化剂中毒及再生研究进展

在烟气脱硝系统中,选择性催化还原催化剂的中毒和再生是广泛关注的问题。文章介绍了钒钛基催化剂的碱金属中毒、碱土金属中毒、砷中毒和二氧化硫中毒,探讨其成因,并对中毒机理进行了分析,同时研究了避免催化剂中毒的措施以及中毒催化剂的再生技术。对碱金属中毒和碱土金属中毒催化剂的水洗再生和硫酸酸洗再生方法进行了实验评价。文章对溶胶凝胶法制备的以陶瓷颗粒为骨架的纳米负载型催化剂V2O5-WO3/TiO2(C)进行研究。实验结果表明,硫酸酸洗再生对碱金属和碱土金属中毒催化剂具有较好的再生效果。在380～410℃温度范围内可使中毒催化剂的NO去除率恢复至90%以上。水洗再生对碱金属中毒催化剂无明显效果,而在380～410℃温度范围内可使碱土金属中毒催化剂的NO去除率达到80%以上。对V2O5-WO3/TiO2(C)抗SO2性能研究表明,以锐钛TiO2为载体的V2O5-WO3/TiO2(C)催化剂具有较好的抗SO2效果。     

Catalytic reduction of nitric oxide with carbon monoxide on copper-cobalt oxides supported on nano-titanium dioxide

A series of copper-cobalt oxides supported on nano-titanium dioxide were prepared for the reduction of nitric oxide with carbon monoxide and characterized using techniques such as XRD, BET and TPR. Catalyst CuCoOx/TiO2 with Cu/Co molar ratio of 1/2, Cu- Co total loading of 30% at the calcination temperature of 350°C formed CuCo2O4 spinel and had the highest activity. NO conversion reached 98.9% at 200°C. Mechanism of the reduction was also investigated, N2O was mainly yielded below 100°C, while N2 was produced instead at higher temperature. O2 was supposed to accelerate the reaction between NOx and CO for its oxidation of NO to give more easily reduced NO2, but the oxidation of CO by O2 to CO2 decreased the speed of the reaction greatly. Either SO2 or H2O had no adverse impact on the activity of NO reduction; however, in the presence of both SO2 and H2O, the catalyst deactivated quickly.     

尖晶石型MnCo_2O_4催化剂的制备及SCR性能研究

用柠檬酸配位燃烧法制备了尖晶石复合金属氧化物MnCo2O4,使用X射线衍射仪、傅立叶红外分析仪对其进行了表征,并进一步在固定床反应器中考查了该催化剂的催化氧化、还原NO的性能以及SO2的影响。结果表明,所制备的MnCo2O4催化剂呈现典型的尖晶石结构,在300℃,空速20000h-1时,NO氧化率可以达到30%,而NH3催化还原NO的效率可达99.5%,但SO2对其还原性能有明显影响。     

Performance and mechanism study for low-temperature SCR of NO with propylene in excess oxygen over Pt/TiO2 catalyst

A 0.5 wt.% Pt/TiO2 catalyst was prepared and used for the low-temperature selective catalytic reduction(SCR) of NO with C3 H6 in the presence of excess oxygen.The effects of Pt loading and O2 concentration on Pt/TiO2 catalytic performance for low-temperature SCR were investigated.It was found that optimal Pt loading was 0.5 wt.% and excess O2 favored low-temperature SCR of NOx.The mechanism of low-temperature SCR of NO with C3 H6 was investigated with respect to the behavior of adsorbed species over Pt/TiO2 at 150°C using in situ DRIFTS.The results indicated that surface nitrosyl species(Pt δ+-NO and Ti 3+-NO) and Pt 2+-CO are main reaction intermediates during the interactions of NO,C3 H6 and O2.A simplified NO decomposition mechanism for the low-temperature SCR of NO with C3 H6 was proposed.     

Kinetics of selective catalytic reduction of NO by NH_3 on Fe-Mo/ZSM-5 catalyst

The catalyst of Fe-Mo/ZSM-5 has been found to be more active than Fe-ZSM-5 and Mo/ZSM-5 separately for selective catalytic reduction (SCR) of nitric oxide (NO) with NH_3.The kinetics of the SCR reaction in the presence of O_2 was studied in this work.The results showed that the observed reaction orders were 0.74-0.99,0.01-0.13,and 0 for NO,O_2 and NH_3 at 350-450℃,respectively. And the apparent activation energy of the SCR was 65 kJ/mol on the Fe-Mo/ZSM-5 catalyst.The SCR mechanism was also deduced. Adsorbed NO species can react directly with adsorbed ammonia species on the active sites to form N_2 and H_2O.Gaseous O_2 might serve as a reoxidizing agent for the active sites that have undergone reduction in the SCR process.It is also important to note that a certain amount of NO was decomposed directly over the Fe-Mo/ZSM-5 catalyst in the absence of NH_3.     

V2O5/TiO2催化剂脱除NO的研究

采用了等体积浸渍法制备二氧化钛负载钒氧化物催化剂（V2O5/TiO2）,研究了V2O5负载量、反应温度、烟气流量、氨氮比以及运行时间各因素对NH3选择性催化还原NO反应（SCR）效率的影响.研究结果表明：经过500℃温度下煅烧,烟气流量为200ml/min,负载量为7wt％的V2O5/TiO2催化剂,在400℃温度下反应,NO脱除率可达70.5％.     

Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

Simultaneous removal of NO and dichloromethane（CH2Cl2） over Nb-loaded cerium nanotubes catalyst

Herein, a series of niobium oxide supported cerium nanotubes（Ce NTs） catalysts with different loading amount of Nb₂O₅（0–10 wt.%） were prepared and used for selective catalytic reduction of NOxwith NH₃（NH₃-SCR） in the presence of CH₂Cl₂. Commercial V₂O₅-WO₃-TiO₂ catalyst was also prepared for comparison. The physcial properties and chemical properties of the Nb₂O₅ lo...     

V_2O_5/TiO_2催化剂用于烟气同时脱硫脱硝的研究

研究了用V2O5/TiO2催化剂同时脱除烟气中的SO2和NO,考察了H2还原温度及其它反应条件对SO2和NO脱除率的影响。结果表明,经H2还原后所制得的V2O5/TiO2催化剂可以提高脱硫脱硝活性,最佳还原温度为700℃;在450～500℃的烟气温度范围内,该催化剂有较佳的脱硫脱硝活性;在相同反应温度下,空速越大,SO2和NO的脱除率越低;烟气中的氧气可大大提高V2O5/TiO2的脱硫脱硝活性,且氧气体积含量在5%～10%范围内变化时,对SO2和NO脱除率的影响较小。     

Ag/Al2O3催化剂用于碳氢化合物选择性还原NO

比较了富氧条件下CH4、C3H8、C3H6和C2H5OH分别用作还原剂时,NO在Ag/Al2O3催化剂上的还原活性.结果表明, CH4和C3H8还原NO的活性很低,而C3H6和C2H5OH能有效地还原NO.在此基础上,研究了H2O和SO2对C3H6和C2H5OH在Ag/Al2O3催化剂上还原NO活性的影响.结果表明,H2O的存在会降低低温区的NO还原活性,而且这种影响是可逆的.将H2O 和SO2同时加入反应混合气,引起NO还原活性较大幅度降低,结合程序升温脱附实验结果,认为可能是由于存在SO2时,Ag/Al2O3催化剂吸附NO的能力降低.     

以MnOx/TiO2作为催化剂的低温SCR反应过程中还原剂NH3的作用

研究了在以MnOx/TiO2作为催化剂的低温SCR反应过程中,还原剂NH3所起的作用.当系统中NH3浓度较低时,增加气相中NH3的浓度可以大幅度提高NO的去除率.但当系统中NH3浓度较高时,NO去除率基本不随NH3浓度变化而变化.并且瞬态研究中,NH3对NO去除率的影响较为复杂.为了探明NH3在SCR反应中的作用,用原位傅立叶红外检测了各个反应历程中NH3在催化剂表面形成的基团变化及其活性特征.结果表明,在SCR反应过程中,在催化剂表面形成的配位态的NH3是参与反应的主要物质.并且在催化剂表面,此种NH3会与NO生成的硝酸盐形成竞争吸附,当催化剂活性点首先被硝酸盐占领时,将会影响配位态NH3的生成,从而在一定程度上降低了NO的转化率.     

Mn/TiO2和Mn-Ce/TiO2低温脱硝催化剂的抗硫性研究

在低温选择性催化还原(SCR)反应条件下考察了烟气残余SO2对Mn/TiO2和Mn-Ce/TiO2催化剂选择性催化还原活性的影响,同时对SO2的影响机理进行了探讨.结果发现,Mn/TiO2催化剂在SO2反应气氛中失活很快,硫铵盐的沉积和活性组分的硫酸化是催化剂失活的重要原因;Ce的加入可以有效地抑制催化剂活性组分的硫酸化,同时还能降低硫酸盐在催化剂表面的稳定性,从而可以提高催化剂的抗硫性.