基于EIS的航空涂层老化研究

选用当量加速试验0~9周期的聚氨酯涂层试样进行电化学阻抗(EIS)测试。通过聚氨酯涂层的电化学信息,判断涂层表面、内部和金属基体的腐蚀状况,研究聚氨酯涂层的老化失效机制。     

典型大气环境玻璃钢天线罩聚氨酯涂层工艺老化行为研究

通过南海海洋大气环境、海南万宁湿热乡村大气环境、西藏拉萨高原大气环境户外大气暴露对玻璃钢基灭线罩聚氨酯涂层工艺进行了老化试验,运用光泽、颜色、粉化率、SEM等手段测试了涂层在户外大气暴露的性能变化和表面形貌,并进行对比分析。结果表明,在相同大气环境中,工艺玻璃钢板／雷达罩底漆／浅灰航天聚氨酯涂层耐候性能优于工艺玻璃钢板／环氧聚酰胺／弹性聚氨酯磁漆涂层的耐侯性能;对于同种工艺,西沙海洋大气环境对其耐侯性的影响最大,其次是万宁湿热乡村环境,拉萨高原环境影响较小;光照、温度、湿度是涂层老化的主要原因。     

土壤中石油烃微生物降解动力学

以长安大学渭水校区未被污染的粉质壤土为研究对象,通过土壤灭菌、添加由石油污染土壤红三叶草(Trifolium Repens Linn)根际修复区分离筛选得到的4株以原油作为惟一碳源和能源的高效石油烃降解菌(动性杆菌、藤黄微球菌、蜡状芽孢杆菌和短小芽孢杆菌),调控反应温度与石油烃初始浓度,研究在土壤中添加优势石油烃降解菌后石油烃降解动力学及其影响因子。结果表明:优势石油烃降解菌对土壤中石油烃降解起主导作用,在40d内,在2 000mg/kg石油烃浓度下添加石油烃降解菌其石油烃降解率是灭菌条件下的2倍左右,土壤中石油烃降解菌降解量为36~271mg/kg,非灭菌处理半衰期时间短于灭菌处理;在设定的实验温度范围内,石油烃降解速率随着温度增加逐渐加快,在(38±1)℃时残留量最小为1 662mg/kg,半衰期最短;土壤中的石油烃在浓度为2 000mg/kg时降解最快,随着初始浓度的增加,石油烃降解速率呈递减趋势,半衰期逐渐增长。     

UV-H_2O_2联用工艺去除水中阿特拉津的研究

采用间歇式反应器考察了UV-H2O2高级氧化技术去除水中阿特拉津的效果及其影响因素,并进行了相关的反应动力学研究。结果表明,在pH值6.9,阿特拉津初始浓度500μg/L,紫外辐照强度172μW/cm2时,H2O2投加量50mg/L,反应10min后,阿特拉津的去除率90%。UV-H2O2联用工艺对阿特拉津的降解符合一级反应动力学。H2O2在该联用工艺降解阿特拉津中具有双重作用,一方面,当H2O2投加量较小时,一级反应速率常数随H2O2投加量的增加基本呈现线性增加的趋势;另一方面,当H2O2浓度增加到一定程度(90mg/L)后,阿特拉津的降解速率随H2O2浓度的变化已不明显,而H2O2浓度为102mg/L时,则出现了抑制作用。     

304L不锈钢钝化膜的半导体性能研究

本利用电容测量方法结合Mott-Schottky分析,研究了不锈钢在硫酸溶液中所形成钝化膜的半导体性质,同时对成膜电位、成膜时间以及溶液pH值对膜半导体性能的影响也做了分析。结果表明:不锈钢钝化膜具有p型-n型-p型半导体特性,膜内的杂质浓度随成膜电位的增加而增加,随极化时间的延长而减小,这主要是由于极化电位和极化时间的变化引起了膜组成的变化所引起的。溶液PH值的改变可以显著影响0.16V~0.74V电位扫描区间内膜的平带电位EFB。溶液PH值与平带电位呈线性关系,斜率为58.58mV/pH。     

原油在土壤中的渗透及降解规律

为了了解原油在江苏地区土壤中的迁移转化规律,真武油田分别在多雨及少雨季节进行了原油在土壤中的渗透及降解实验。实验结果表明：随着时间的增加,原油在土壤中的渗透作用逐渐加强;而其降解的可能性较小。     

20年来安徽省人口时空分布特征分析

在GIS技术支持下,建立安徽省人口地理数据库,使用密度分析法、重心分析法和空间自相关分析法对安徽省1990—2012年人口时空分布特征进行了分析。结果显示,全省人口密度总体上呈由北向南递减分布格局,皖北地区人口密度呈增加趋势,皖南人口密度相对稳定,人口重心位于几何重心的西北方向,20年来人口重心从长丰县沿西北方向移动到寿县境内。全省各县(市)人口密度存在空间正相关性,且随时间推移逐渐减弱。     

会议信息

首届"中美光伏组件材料耐久性测试技术研讨会"召开3月27日,由中国电器科学研究院有限公司(CEI)与美国Atlas材料测试技术有限公司(ATLAS)共同主办,工业产品环境适应性国家重点实验室和广州威凯技术检测技术有限公司协办的首届"中美光伏组件材料耐久性测试技术研讨会"在上海隆重召开。     

微生物对石油污染物的降解作用

针对油井附近落地油污染地表土壤的问题,利用热蒸发色谱技术,对油污土壤中加入微生物对原油的降解特征进行了实验研究。实验结果表明,在油污土壤中加入微生物,对落地油有明显的降解作用,可以减轻石油生产过程中油污对土壤的破坏和对环境的污染。随着微生物降解作用的不断进行,土壤中污油的相对降解速度逐渐加快,相对降解率逐渐增加。生物处理法的过程较简单,处理费用低,处理效果好,一般不会产生二次污染。     

拟除虫菊酯农药的微波辅助无极汞灯下的降解机理研究

在水溶液中,以微波辅助无极汞灯(Microwave-Assisted Eletrodeless Discharge Mercury Lamp,MW-EDML)降解氯氰菊酯、甲氰菊酯和功夫菊酯等3种拟除虫菊酯农药(Synthetic pyrethroids,SPs),采用固相萃取(Solid Phase Extraction,SPE)富集后,用GC-MS鉴定降解产物,并根据降解产物重点探讨了SPs的降解机理。3种SPs的主要降解产物有6种,其降解途径有:酯键水解、氰基水解、脱羧、醚键断裂、氧化、苯环的羟基化以及与溶剂反应等。实验结果还表明:MW-EDML是个高效、简便的降解SPs类农药手段,可应用于其他有机污染物的降解过程。     

溶剂型聚氨酯涂料废物热解特性及动力学研究

采用TG研究溶剂型聚氨酯涂料废物在不同升温速率、N2气氛影响下的热解特性规律。升温速率取5,10,20,30℃/min;气氛取N2气氛(50 m L/min);实验温度范围为20~800℃。研究表明,随着升温速率的增大,涂料废物热解反应各阶段起始温度、终止温度、最大失重速率温度均向高温方向移动。在500℃时,涂料废物的热分解已基本完成。运用Kissinger法和Flynn-Wall-Ozawa法进行热解动力学分析,得到溶剂型聚氨酯涂料废物热解阶段的表观活化能为196.053 3 kJ/mol。     

航空聚氨酯涂层老化分析

随着飞机服役时间的增长,其结构表面的有机涂层逐渐老化失效,最终导致机体金属结构的腐蚀。基于某沿海机场的严酷环境条件,依据编制的适用于有机涂层的加速试验谱,开展涂层加速老化试验,分析涂层老化规律。     

循环盐雾标准方法

循环盐雾试验是近年来应用逐渐广泛的一种试验方法,较之传统盐雾试验,其与真实环境有着更好的相关性。介绍了循环盐雾试验的常用标准方法,包括涂层材料用标准方法,金属和合金用标准方法,电工电子产品用标准方法和汽车材料用标准方法等。并分析了每种方法的特点,同时指出了标准方法使用中的关注点。     

铝合金/高强度钢连接件西沙暴露试验

选取某飞机铝合金/高强度钢连接件开展西沙暴露试验,掌握连接件腐蚀变化趋势。结果表明,连接件保护涂层耐老化性能良好,采用湿装配有效避免了电偶腐蚀和缝隙腐蚀,连接件背面螺栓、螺母和铆钉（30CrMnSiA,表面镀镉）为其腐蚀薄弱环节,需加强防护。     

Investigation of three system shut-down strategies alongside optimization suggestion for proton exchange membrane fuel cells via in-situ measurements

ABSTRACT

Carbon corrosion caused by H₂/O₂ interface during the shut-down process is one of the factors that exacerbate the overall degradation of proton exchange membrane fuel cells (PEMFC) in automotive applications. Numerous studies have shown that system strategies are beneficial for reducing the duration of H₂/O₂ interface and alleviating performance degradation. In this paper, three different shut-down strategies are investigated and compared based on the internal behaviors acquired by in-situ measurements. For the three shut-down strategies, reverse current and high potential are mainly observed in a lower constant current and constant power strategy. Comparatively speaking, the internal uniformity of the cell under constant current and power load is better than that with constant voltage strategy when the shut-down time is about the same. The results suggest that adopting a higher constant power load followed by a larger voltage load during the shut-down process can effectively shorten the shut-down time and relieve carbon corrosion. These results add significant new insights into the shut-down process and will be of practical importance in directing design of combined shut-down strategy that can withstand carbon corrosion.     

Advanced superhydrophobic electroactive fluorinated polyimide and its application in anticorrosion coating

A novel superhydrophobicelectroactive fluorinated polyimide (HEFPI) was first synthesized from aniline trimer and 4,4′-(Hexafluoroisopropylidene) diphthalic anhydride. The HEFPI could be fabricated as superhydrophobicfilm by replicated the surface of the Xanthosomasagittifolium leaves. The water contact angle of HEFPI film reaches as high as 157 ° and the superhydrophobic property of HEFPI could coat on cold-rolled steel (CRS) to prevent the metal corrosion. Electroactivity of EFPI was evaluated by performing electrochemical cyclic voltammetry study. Besides, redox catalytic capabilities of aniline trimer units existed in HEFPI main chain may induce the formation of passive metal oxide layers on the CRS electrode. The synergistic effects (hydrophobic property and passive metal oxide layers) make the HEFPI coating has great potential for advanced anticorrosion material.     

Controlled-release system for the insect growth regulator cyromazine

An encapsulation system designed to give long-lasting effectiveness of the insect growth regulator (IGR) cyromazine (Neporex) against Culex pipiens (Culicidae) mosquito larvae was developed. The main thrust of the research was to develop a simple method for preparing controlled-release formulations by means of an extrusion technique in combination with a supplementary coating and to study the release characteristics and effectiveness of the formulations. A series of formulations were prepared with low-density polyethylene (LDPE 600) for the matrix and with polyurea or one of four types of polyurethane for the coating. The rate of release of the active material from the controlled-release formulations was determined in an in vitro dissolution system. The biological activity of the controlled-release formulations was tested in vivo against C. pipiens larvae.     

An investigation into the likely impact of oxy-coal retrofit on fire-side corrosion behavior in utility boilers

Real-time electrochemical measurements of corrosion rate were performed to evaluate the respective corrosion rates of one boiler waterwall material (SA210) and three boiler superheater materials (T22, P91 and 347H) while firing Utah Western bituminous, Illinois high-sulfur bituminous and Powder River Basin (PRB) sub-bituminous coals in a 1.5 MW pulverized coal-fired furnace. The raw average measured corrosion rates were very low, between 0.0003 and 0.016 mm/year (0.012 and 0.63 mils/year) for most materials under air- and oxy-fired conditions. For some high-sulfur conditions measured corrosion rates were as high as 0.72 mm/year (28 mils/year). Waterwall corrosion rates decreased consistently when converting from air- to oxy-firing while superheater corrosion rates generally increased, although they were less than twice the air-fired rate under most conditions. Corrosion rates for the lower alloyed materials (SA210 and T22) increased significantly during transients from reducing to oxidizing conditions. Measured increases in the corrosion rate of 347H material under high sulfur and low temperature conditions, and associated decrease in corrosion rate at higher temperatures on this alloy, were consistent with the formation of trisulphates in the superheater deposits. The increase of corrosion rate with increased metal temperatures was demonstrated, as was the consistently repeatable nature of the observed results.