氨氧化木质素作为硝化抑制剂的研究

通过室内培养实验对氨氧化木质素(AOL)的硝化抑制作用进行了探讨。在相同条件下,分别加AOL和DCD处理的铵态氮质量分数都要比未加硝化抑制剂处理的高;相应地,在开始阶段硝态氮质量分数也要比未加硝化抑制剂处理的低。研究结果表明,AOL作为硝化抑制剂是有效果的。     

Comparison between inhibitor and uncoupler for minimizing excess sludge production of an activated sludge process

In order to study the minimization of excess sludge production, the reduction in the excess sludge production in the presence of an inhibitor and uncoupler was studied in this work. The experimental results show that such an addition could effectively reduce the production of excess sludge. With the energy uncoupling model established in this work, energy uncoupling coefficient (E _u) was used to evaluate the reduction in excess sludge production. The energy uncoupling coefficients in the presence of dinitrophenol (dNP), Zn²⁺, and Cu²⁺ was 0.75, 0.46, and 0.18, respectively. The analysis demonstrated that energy spilling occurred in the presence of dNP, and that dNP was an effective uncoupler for reducing the production of excess activated sludge without affecting the microbial respiration activity.     

天然海水中碳钢缓蚀剂吸附和阳极脱附行为的研究

以锌盐、葡萄糖酸盐为主要缓蚀成分复配的适用于天然海水中碳钢的高效缓蚀剂,采用极化曲线、循环伏安曲线和交流阻抗谱图分析了该缓蚀剂的阳极脱附行为.结果表明,碳钢在海水中的零电荷电位约为-0.6 V;缓蚀剂的吸附电位区间为-0.5～-0.8 V,缓蚀剂在该区间内存在特性吸附.当阳极极化电位超过-0.45 V时,极化电流迅速增大,缓蚀剂因发生大量脱附而失去对阳极过程的控制.     

用氧吸收速率(OUR)表征活性污泥硝化活性的研究

研究了用氧吸收速率（ＯｘｙｇｅｎＵｐｔａｋｅＲａｔｅ，简称ＯＵＲ）表征活性污泥硝化活性的方法．利用生物抑制剂丙烯基硫脲（ａｌｙｌｔｈｉｏｕｒｅａ，简称ＡＴＵ）和氯酸钠（ＮａＣｌＯ３）可以选择性地抑制亚硝酸细菌和硝酸细菌的活性．通过测量不同时间的ＯＵＲ，可以分别计算出污泥的亚硝化活性和硝化活性．结果表明：该方法的测量结果与实际反应器中的硝化反应情况相当一致．该方法简单易行，快速方便，适用于硝化系统中硝化活性的测量．     

Trypsin inhibitor,antioxidant and antimicrobial activities as well as chemical composition of potato sprouts originating from yellow- and colored-fleshed varieties

Abstract

Potato sprouts could be a valuable resource of phytochemicals such as secondary plant metabolites, potential antioxidants and nutritive compounds. In this work, potato sprout extracts of five varieties were examined; they differed in major glycoalkaloid content, trypsin inhibitor activity, total polyphenol content and antioxidant activity, as well as in antimicrobial activity against Gram?+?and G???bacteria, and yeast. Sprouts of colored-fleshed tubers were characterized by higher trypsin inhibitor activity than sprouts of yellow potatoes. The strongest microorganism growth inhibition effect was observed for macerate with sprouts from the purple-fleshed Blaue Annelise variety against B. subtilis, whereas C. albicans yeasts were sensitive to macerates with sprouts from purple-fleshed Blue Congo and yellow-fleshed Vineta potato varieties.     

应用假单胞菌进行防蜡作用的研究

假单胞菌L－11菌体与其胞外产物可以作为一种很好的防蜡剂，对L－11的发酵条件进行了优化，确定了最适发酵培养基的配方，发酵培养基以葡萄糖、蛋白胨为其最适碳、氮源，防蜡剂生产的发酵条件为：前16h的发酵温度为35℃，后期将温度降至20℃，发酵液的pH=4．5为发酵终点，此时发酵液在内条件下的防蜡率为78％，将上述所得菌液在大庆油田做了防蜡实验，结果表明，注入L－11的油井洗井周期有所延长，实验证明了L－11的发酵液可以作为一种经济、有效的蜡剂。     

绵农小麦种子巯基蛋白酶抑制剂的纯化及性质研究

绵农11号小麦种子磨粉后的胚和麸皮，经溶液浸取和硫酸铵分级沉淀获得巯基蛋白酶抑制剂（CPI）粗品，再经木瓜蛋白酶－Sepharose4B亲和层析，DEAE－Sepharose离子交换层析和SephadexG－100分子筛层析，可获得两种CPI．通过SDS－PAGE或凝胶过滤法测得其Mr分别为18800［简称CPI（H）］和10500［简称CPI（L）］．它们在PAGE，SDS－PAGE和HPLC上均为单一蛋白带．CPI（L）和CPI（H）对木瓜白酶的抑制活性（ID50）分别为7．8×10－6mol／L和3．40×10－6mol／L．对无花果蛋白酶的抑制活性分别为9．5×10－5mol／L和5．8×10－6mol／L；CPI（H）对菠萝蛋白酶有弱抑制作用，但CPI（L）则无抑制作用；无论是CPI（L）或CPI（H）对胰蛋白酶、胰凝乳蛋白酶和胃蛋白酶均无抑制作用．CPI（H）的N－末端为Ile．CPI（H）和CPI（L）在pH2．0～11．0范围内和90℃处理5min，两种CPI的抑制活性均无变化；CPI（H）和CPI（L）对木爪蛋白酶的抑制曲线经Dixon作图法，得出CPI（H）为反竞争性抑制类型，而CPI（L）为竞争性抑制类型，其Ki值为8．32×10－6mol／L．     

鼓泡法对聚天冬氨酸阻垢性能的评价

用鼓泡法对六种聚天冬氨酸 (Polyasparticacid ,PASP)的阻碳酸钙垢性能进行了评价 ,考察了pH值、阻垢剂用量、温度、恒温时间等对阻垢性能的影响。研究发现 ,阻垢率随着聚天冬用量的增加而增大 ,其用量在 1 0mg/L时 ,已能获得较好的阻垢效果。另外 ,与聚丙烯酸 (PAA)和聚马来酸 (HPMA)的比较发现 ,聚天冬在高温水系统中作长时间停留 ,仍对碳酸钙垢有较强的抑制作用     

杂散电流下新型阻锈剂对混凝土中氯离子扩散的影响

目的探寻混凝土在杂散电流和氯离子耦合作用下的腐蚀规律,研究新型阻锈剂的阻锈性能。方法运用电通量法和RCM法,对20 V杂散电流作用下,混凝土的抗氯离子渗透性能进行表征,设置空白组对照实验,对添加阻锈剂后,混凝土的抗氯离子渗透性能进行效果评价。结果在杂散电流和氯离子的共同作用下,混凝土结构腐蚀的倾向将变大,并且会加速腐蚀反应的进行。混凝土结构在通电48 h后,其电通量高达5778.67 C。与空白组相比,添加阻锈剂混凝土试块的氯离子扩散系数下降45.62%。结论添加4%阻锈剂的混凝土试块有着较好的抵抗氯离子渗透的能力。     

曲堤油田结垢机理研究与防治

目的解决曲堤油田的结垢问题。方法采用离子色谱仪,对水样理化性质进行测试分析,采用X射线衍射仪对现场垢样进行成分分析,通过室内静态结垢实验结合滴定法,研究油井采出液及联合站注入水混合的配伍性,并对阻垢剂进行筛选及评价。结果曲堤油田水样水型均为CaCl_2型,含有较多的结垢性阳离子Mg~(2+),Sr~(2+)和Ba~(2+)的含量相对较少。对于结垢性阴离子,主要为HCO_3~-,CO_3~(2-)和SO_4~(2-)含量较少。曲堤油田结垢主要是由于Ca~(2+)、Mg~(2+)与HCO3-反应,生成白云石晶体造成的。各油井采出液在低温下混输,配伍性较好;随着温度的升高,会出现一定程度的结垢,但结垢率均小于5%。除Q10-X16油井采出液以外,其余各油井采出液与联合站注入水均不配伍,混合后结垢率达10%以上。选择7#阻垢剂,加注浓度50 mg/L作为曲堤油田的阻垢剂类型及加药制度。结论现场调研的7#缓蚀剂对于曲堤油田的环境具有适用性,阻垢率高,能够有效减缓曲堤油田的结垢问题。