通过对24个飞灰样品的重金属全量消解和高精度X射线荧光光谱法（HDXRF）快速检测结果进行线性回归分析,发现HDXRF法可较准确测定飞灰中Cu、Pb、Zn、Ni和Cd含量（线性回归决定系数R²³0.90）.采用HDXRF法对某焚烧厂飞灰重金属含量6个月快速检测及浸出毒性测定数据统计分析发现：飞灰重金属月均含量较稳定（变异系数CV<0.14）但日均含量波动较大（CV>2.54）;飞灰中Pb、Cu和Zn含量呈正相关（相关系数r>0.78）;金属浸出浓度受浸出液终点pH值影响显著,超标频率依次为Pb（68.9%）、Cd（66.1%）、Ni（24.0%）、Cu（14.2%）和Zn（1.6%）.短期飞灰金属含量和浸出毒性数据受焚烧工况,烟气处理工况和垃圾组分等多种因素共同影响,不具有代表性.为评估垃圾分类源头削减重金属效果,建议采用快速检测方法对焚烧飞灰重金属含量进行长期监测.     

新型防腐涂层对直升机典型结构材料防护性能研究

目的研究新型防腐涂层对直升机典型结构用铝合金及复合材料在热带海洋性气候环境下的防护性能,并与原防护涂层进行对比。方法通过测试涂层腐蚀后的形貌、光泽度、色差、电化学阻抗等,对比新/原涂层对直升机典型结构用铝合金和复合材料的防护性能。结果经过2年腐蚀后,新涂层表面无明显变化,而原涂层表面有轻微腐蚀,光泽度和色差下降较大。电化学阻抗测试表明,暴露前后涂层结构无明显变化,涂层阻抗值呈现持续下降的趋势,但是原涂层阻抗下降更快。结论新涂层对直升机典型铝合金和复合材料有更好的防护性,更加适于海洋性环境的使用。     

7B04铝合金和30CrMnSiA钢短期腐蚀的电化学行为研究

目的研究7B04铝合金和30CrMnSiA合金钢试样的电化学性能。方法采用电化学实验、扫描电子显微镜(SEM)、腐蚀坑深度测试分别对7B04铝合金和30CrMnSiA合金钢试样在是否经过天然海水浸泡的情况下进行测试分析,得到微观腐蚀形貌和腐蚀坑深度以及试样表面不带锈和带锈时的电化学性能。结果随着Na Cl浓度增大,7B04铝合金和30CrMnSiA钢的自腐蚀电流变大,两者之间存在明显的电位差,接触后会发生电偶腐蚀。电偶电流与阴阳极面积比和Na Cl浓度有关,阴阳极面积比增大或Na Cl浓度升高均会导致电偶效应增强。经过海水短期浸泡后,7B04铝合金表面的锈层不仅没有起到抑制腐蚀的作用,反而使自腐蚀加重,但电偶效应确实有所减弱。结论沿海设备在使用过程中应竭力避免铝合金在锈层下工作。     

飞机用铝合金腐蚀行为和腐蚀预测研究现状及问题分析

针对不同的航空铝合金结构及部位,从腐蚀机理、腐蚀行为和腐蚀预测技术三方面较为系统地分析了研究现状及进展。在此基础上,明确了航空铝合金腐蚀预测技术需要进一步研究的问题,分别为飞机结构表面腐蚀环境的确定问题,材料在海洋大气环境下腐蚀电化学性能的准确测量问题,腐蚀预测模型的选取问题。     

铝合金的实验室盐雾试验腐蚀行为图像特征提取

目的提取铝合金材料在盐雾箱试验中可以表征腐蚀程度的表面形貌图像特征量。方法首先,对采集于表面化学清洗过的试样原始图像进行图像增强等预处理,突出腐蚀部位;其次,基于数字图像处理的分形和小波分解方法提取出分形维数和小波能量特征值。结果与以质量损失量为基础的腐蚀深度特征值进行相关性对比,基于图像分析的特征提取法的准确度和精度比较高。结论该方法可以应用于对试样的腐蚀程度进行定性和定量分析,判断并预测试样的腐蚀速度。     

高强预腐蚀铝合金单轴拉-拉疲劳断口定量分析

目的通过断口定量分析获得7A09铝合金的疲劳裂纹扩展规律,为7A09铝合金结构的寿命评估提供依据。方法使用EXCO溶液对试验件进行预腐蚀,利用疲劳拉伸机进行疲劳加载直至断裂,使用扫描电镜对疲劳断口进行定量化分析。结果疲劳裂纹在试件的腐蚀坑处萌生,从自由界面附近向纵深发展导致试件的断裂。通过断口分析和Paris公式确定了裂纹的萌生寿命和扩展寿命。结论腐蚀之后的试件裂纹萌生寿命占总寿命的比例下降,当裂纹扩展程度较大之后,受腐蚀影响减轻,得出裂纹扩展速率和应力强度因子的关系。     

A ten year summary of concurrent ambient water column and sediment toxicity tests in the Chesapeake Bay watershed: 1990-1999

The goal of this study was to identify the relative toxicity ofambient areas in the Chesapeake Bay watershed by using a suiteof concurrent water column and sediment toxicity tests at seventy-five ambient stations in 20 Chesapeake Bay rivers from1990 through 1999. Spatial and temporal variability was examinedat selected locations throughout the 10 yr study. Inorganicand organic contaminants were evaluated in ambient water andsediment concurrently with water column and sediment tests toassess possible causes of toxicity although absolute causalitycan not be established. Multivariate statistical analysis wasused to develop a multiple endpoint toxicity index (TOX-INDEX) at each station for both water column and sediment toxicity data. Water column tests from the 10 yr testing period showed that49% of the time, some degree of toxicity was reported. The mosttoxic sites based on water column results were located inurbanized areas such as the Anacostia River, Elizabeth River andthe Middle River. Water quality criteria for copper, lead,mercury, nickel and zinc were exceeded at one or more of thesesites. Water column toxicity was also reported in localizedareas of the South and Chester Rivers. Both spatial and temporalvariability was reported from the suite of water column toxicitytests. Some degree of sediment toxicity was reported from 62% of the tests conducted during the ten year period. The ElizabethRiver and Baltimore Harbor stations were reported as the most toxic areas based on sediment results.Sediment toxicity guidelines were exceeded for one or more of thefollowing metals at these two locations: arsenic, cadmium,chromium, copper, lead, nickel and zinc. At the Elizabeth Riverstations nine of sixteen semi-volatile organics and two of sevenpesticides measured exceeded the ER-M values in 1990. Ambientsediment toxicity tests in the Elizabeth River in 1996 showedreduced toxicity. Various semi-volatile organics exceeded the ER-M values at a number of Baltimore Harbor sites; pyrene anddibenzo(a,h)anthracene were particularly high at one of thestations (Northwest Harbor). Localized sediment toxicity was alsoreported in the Chester, James, Magothy, Rappahannock, andPotomac Rivers but the link with contaminants was not determined.Both spatial and temporal variability was less for sedimenttoxicity data when compared with water column toxicity data. Acomparison of water column and sediment toxicity data for thevarious stations over the 10 yr study showed that approximatelyhalf the time agreement occurred (either both suite of testsshowed toxicity or neither suite of tests showed toxicity).     

Response of the Ascorbate-Peroxidase of Selenastrum capricornutum to Copper and Lead in Stormwaters

The green alga Selenastrum capricornutum expresses a uniqueascorbate peroxidase, that responds to copper and lead. Attemptswere made to test if this peroxidase could be used to monitor thelevels of copper and lead in natural waters. When S.capricornutum was exposed to a stormwater sample, the specificactivity of the peroxidase in the cell extract was commensuratewith the combined copper and lead contents in the sample. Theperoxidase responses were also correlated with the 96 hr biomasstoxicity assay of S. capricornutum. However, unlike thebiomass toxicity assay, the peroxidase activity was not affectedby the anions in the samples. The use of this peroxidase can beused as a marker for testing heavy metal toxicity in the water.     

发光细菌法评价工业废水的毒性

用发光细菌测定法估算了两城市污水对河道水体污染的分担率，评价了工厂排放废水的毒性，并据此确定了污染源监督管理中应优先治理的工厂（车间）废水。