混晶纳米TiO_2的制备及其光催化降解有毒有机污染物

以无定形TiO2沉淀为前驱体,在水热条件下得到了含板钛矿(121)相混晶纳米TiO2,考察了水热反应的温度和时间等因素对含板钛矿型TiO2光催化活性的影响.采用XRD、TEM对制备的TiO2进行初步表征,并结合光催化(λ≤387 nm)降解有机染料的光活性探针反应.结果表明,水热温度为150℃,时间为24 h时,可制得具有较高光催化活性的纳米TiO2,其纳米尺寸为14.20 nm,板钛矿相含量63.6%,锐钛矿含量为36.4%.光催化实验中跟踪研究了其对染料酸性桃红(sulforhodmineB,SRB)的褪色及2,4-DCP的降解情况,并对降解中间产物H2 O2、.OH进行跟踪测定,实验结果表明板钛矿相混晶TiO2的光催化主要涉及.OH氧化历程,光照射9 h对SRB和2,4-DCP的矿化氧化分别达到89%和78%,循环5次光催化降解SRB实验,催化剂表现出较好的稳定性,催化性能无明显变化.     

微囊藻毒素分离及鉴定

微囊藻毒素是一类由蓝藻产生的具有肝毒性的生物毒素。微囊藻毒素标准品是开展为微囊藻毒素相关研究的必需的实验材料,文章以滇池天然水华蓝藻为原料,建立了以5%乙酸和75%的甲醇溶液提取,通过优化提取、分离和制备条件,制备了一定量的微囊藻毒素高纯度样品,经HPLC鉴定分析,纯度可达90%以上。文章在相同的质谱条件下分别对MC-LR和[Dha7]MC-LR等毒素进行了质谱检测,一级质谱结果表明,MC-LR和[Dha7]MC-LR的一价电离离子峰分别为995和981,MC-RR的二价电离离子峰为520,并分析它们的二级质谱裂解特征,确定三种毒素化学结构MC-RR为环(Ala-Arg-MeAsp-Arg-Adda-Glu-Mdha)、MC-LR为环(Ala-Leu-MeAsp-Arg-Adda-Glu-Mdha)、[Dha7]MC-LR为环(Ala-Leu-MeAsp-Arg-Adda-Glu-Dha)。改良后的检测方法同样应用于检测受微囊藻毒素污染的武汉东湖水样。     

蔗渣吸附剂的制备及其对氨氮的吸附研究

从炭化蔗渣的炭化温度和用量,吸附动力学、吸附温度,溶液的酸度、组成,吸附等温线及氨氮的存在形式等方面探讨了实验制备的炭化蔗渣吸附去除溶液中氨氮的影响因素。结果表明,直接炭化法蔗渣吸附剂制备的最佳炭化温度为400℃;在初始氨氮浓度一定的条件下,随着吸附剂投加量的增大,炭化蔗渣对氨氮的吸附量减少;炭化蔗渣吸附氨氮的动力学曲线符合准二级动力学模型,吸附常数K2=3.59g(/mg/min);当pH=9.20时炭化蔗渣对氨氮的最大吸附量为10g/kg;在实验的pH范围内,pH=10时炭化蔗渣对氨氮的吸附去除最好;直接炭化法蔗渣吸附剂对氨氮吸附去除的最佳温度是40℃;pH为3.98～9.20时吸附等温线可用Langmuir与Freundlich吸附等温方程进行拟合。     

粉煤灰储能复合材料的实验研究

通过吸附、熔融浸滞将粉煤灰、月桂酸复合制备得到复合相变储能材料。通过DTA/TG、SEM测试分析,相变储能材料的相变峰值温度为46.01℃,且在44.0℃～55.0℃范围内有一个较大的吸热峰,可实现相变吸放热,且热稳定性好,粉煤灰基本不影响其热性能。微相结构显示粉煤灰能有效吸入大量的月桂酸,具有较好的吸附结合能力。     

新型饮用水除氟材料Bio-F的除氟特性和比较研究

对3种传统除氟剂活性氧化铝、骨炭和改性沸石与自制的新型生物除氟剂Bio-F的除氟性能及影响因素（材料粒径、pH值、吸附时间、水样含氟浓度、其它离子、再生能力等）进行了比较,并模拟动态实验评估了这4种除氟材料对实际高氟地下水处理的效果.结果表明,Bio-F生物除氟剂对F^-的吸附过程符合Lagergren一级吸附动力学特征（R²=0.958 0）,吸附速率较快,且该过程属于吸热反应; Bio-F吸附F^-符合Langmuir吸附等温模型（R²=0.999 2）,吸附容量高,静态吸附容量可达4.088 3 mg·g^-1,分别约是活性氧化铝和改性沸石的1.8和 5.8倍.4种除氟材料吸附容量与氟浓度正相关,与吸附剂粒径负相关.高浓度的CO^2-₃、HCO^-₃明显抑制Bio-F的除氟（p<0.05）,但高浓度的Ca²⁺、NO^-₃、HPO^2-₄有利于Bio-F的除氟（p<0.001）.Bio-F除氟最佳停留时间3～4 min,远远低于沸石20 min和活性氧化铝11 min.在pH 4.0～9.0范围内Bio-F可保持90％以上吸附F^-的能力.再生性能稳定,10次再生后吸附容量变化不超过15%.Bio-F综合性能优于其它3种传统除氟剂,在我国广大农村地区推广有显著优越性.     

Heavy metal removal from aqueous solution using carbonaceous K2S-impregnated adsorbent

A novel carbonaceous adsorbent for heavy metal removal was prepared from raw coal by one-step simple sulfur impregnation using K2S. Raw coal was mixed with K2S powder and then heated at 800°C for 30 min in nitrogen to produce K2S char. The sulfur content and form in K2S char were determined, and the ability of K2S char to adsorb Zn2+, Cd2+ and Pb2+ was examined. The K2S impregnation was e ective at impregnating sulfur into coal, especially in the form of elemental, thiophenic and sulfatic sulfur. The sulfur content of K2S char was higher than those of raw coal and pyrolysis char. The Zn2+ removal in 2.4 mmol/L of Zn2+ solution by K2S char was higher than raw coal with the removal rate of 100%. K2S char adsorbed Pb2+ and Cd2+ in 24 mmol/L of Pb2+ and Cd2+ solution with the removal rate of 97% and 35%, respectively. The elution extents of adsorbed Pb2+ and Cd2+ were zero in distilled water and 27% in 0.1 mol/L HCl solution. These results indicated that an e ective adsorbent for heavy metal ions was prepared from coal using K2S sulfur impregnation, and that the adsorbed metals were strongly retained in K2S char.     

催化剂及其制备对催化湿式氧化反应的影响

催化湿式氧化法是一种有效的处理有毒、有害、高浓度有机废水的水处理技术,文章专门针对催化剂本身的制备对催化湿式氧化的影响,以及催化剂的失活、再生、重复利用等研究做出总结,以期对有关研究者提供一定的参考。     

Application of magnetic particles modified with amino groups to adsorb copper ions in aqueous solution

A magnetic adsorbent can be easily recovered from treated water by magnetic force,without requiring further downstream treatment.In this research,amine-functionalized silica magnetite has been synthesized using N-[3-(trimethoxysilyl)propyl]-ethylenediamine(TPED) as a surface modification agent.The synthesized magnetic amine adsorbents were used to adsorb copper ions in an aqueous solution in a batch system,and the maximum adsorption was found to occur at pH 5.5 ± 0.1.The adsorption equilibrium data fitted t...     

利用泰乐菌素菌渣生产复合酶制剂及效果研究

发酵法生产抗生素过程中会产生大量废弃菌渣,这些菌渣因有机质含量高,堆放极易发生霉变,给当地环境造成危害.文章采用固体发酵法,以微生物降解处理后的泰乐菌素菌渣为主要原料,生产复合酶制剂,并对其在肉鸡上的使用效果进行研究.结果表明:在水含量50％～60％、干物质中麸皮含量不低于40％的泰乐菌素菌渣培养基中,接入5％～10％...     

烟气脱硫剂制浆系统一体化设计及应用

石灰石粉制浆系统是石灰石-石膏湿法烟气脱硫工艺中脱硫剂浆液干式制备系统的一个主要部分。针对石灰石粉制浆系统传统设计的不足,提出了石灰石浆液罐与粉仓一体化设计的优化方案,具有节省投资、占地小、设计简单紧凑、系统可靠和寿命长的优点,尤其适合我国老小燃煤机组烟气脱硫改造工程。目前已成功应用于多个烟气脱硫工程。