Experimental investigation of gamma-ray attenuation in Jordanian building materials using HPGe-spectrometer

The capabilities of some building materials used in Jordan to attenuate gamma radiation were tested. Measurements of the attenuation coefficients of limestone, bricks and concrete have been carried out using a HPGe-spectrometer. Narrow beam technique was used, with a multiple gamma radiation source of different energy lines. Results indicate that variations in the attenuation coefficient for all limestone samples, at the same energy line, are within the experimental uncertainties. On the basis of the results achieved, an empirical formula mu(m)=AE(-0.44) was proposed to calculate attenuation at various incident energies. Limestone of average thickness 7cm was found to stop 75% of a gamma beam of energy 662keV. Meanwhile a brick of effective thickness 7cm was found to stop 60% of the same beam. The total attenuation coefficient of concrete calculated at 1333keV was 11.2m(-1), which is less than that of limestone and bricks.     

ZrxMg1-xO supported cobalt catalysts for methane decomposition into COx-free hydrogen and carbon nanotubes

Zirconia-magnesia supported cobalt catalysts with various Zr/Mg atomic ratios were prepared and evaluated for non-oxidative catalytic decomposition of methane to produce CO_x-free hydrogen and carbon nanotube. The catalytic performance of the catalysts was performed in a continuous fixed bed flow reactor at 700°C under atmospheric pressure. The fresh and spent catalysts were characterized by XRD, TPR, BET, TEM, and Raman spectroscopy. The results showed that the change in Zr/Mg ratio of the mixed oxide support has a significant effect on the catalytic performance of the active Co metal. The catalyst 30%Co/Zr_0.8Mg_0.2 showed the highest activity and stability within the used series of catalysts with hydrogen yield reached up to 79%. Both Co/Mg_1.0 and Co/Zr_1.0 showed poor stability due to strong Co-Mg interaction and aggregation of Co species on Zr support, respectively. All catalysts produced mainly MWCNTs with different diameters depending on the Zr/Mg ratio. The outer diameter increased with increasing Zr content in the catalyst due to the enlargement of the particle size of cobalt as a result of aggregation.     

Synthesis of high-quality graphene sheets via decomposition of non-condensable gases from pyrolysis of polypropylene waste using unsupported Fe,Co, and Fe–Co catalysts

Producing high-quality graphene sheets from plastic waste is regarded as a significant economic and environmental challenge. In the present study, unsupported Fe, Co, and Fe–Co oxide catalysts were prepared by the combustion method and examined for the production of graphene via a dual-stage process using polypropylene (PP) waste as a source of carbon. The prepared catalysts and the as-produced graphene sheets were fully characterized by several techniques, including XRD, H₂-TPR, FT-IR, FESEM, TEM, and Raman spectroscopy. XRD, TPR, and FT-IR analyses revealed the formation of high purity and crystallinity of Fe₂O₃ and Co₃O₄ nanoparticles as well as cobalt ferrite (CoFe₂O₄) species after calcining Fe, Co, and Fe–Co catalysts, respectively. The Fe–Co catalyst was completely changed into Fe–Co alloy after pre-reduction at 800 °C for 1 h. TEM and XRD results revealed the formation of multi-layered graphene sheets on the surface of all catalysts. Raman spectra of the as-deposited carbon showed the appearance of D, G, and 2D bands at 1350, 1580, and 2700 cm⁻¹, respectively, confirming the formation of graphene sheets. Fe, Co, and Fe–Co catalysts produced quasi-identical graphene yields of 2.8, 3.04, and 2.17 g_C/g_cat, respectively. The graphene yield in terms of mass PP was found to be 9.3, 10.1, and 7.2 g_C/100g_PP with the same order of catalysts. Monometallic Fe and Co catalysts produced a mix of small and large-area graphene nanosheets, whereas the bimetallic Fe–Co catalyst yielded exclusively large-area graphene sheets with remarkable quality. The higher stability of Fe–Co alloy and its carbide phase during the growth reaction compared to the Fe and Co catalysts was the primary reason for the generation of extra-large graphene sheets with relatively low yield. In contrast, the segregation of some metallic Fe or Co particles through the growth time was responsible for the growth small-area graphene sheets.