Potential utilization of burned wood in manufacture of medium density fiberboard

The potential utilization of burned wood in the manufacture of medium density fiberboard (MDF) was investigated. For this aim, the MDF panels were made of various mixtures of burned pine wood (Pinus sylvestris L.), unburned beech (Fagus orientalis L.) and oak (Ouercus robur L.) woods under commercial conditions in an MDF company. The mixture ratio of the unburned beech and oak woods to the burned pine wood were 50/50 wt%. The mixing ratios of burned wood chips with unburned wood chips were 0:100, 25:75, 50:50, 75:25 and 100:0, %, respectively. A commercial urea–formaldehyde resin was used as a binder. The physical properties measured in the investigation included density and thickness swelling, while the mechanical properties examined were bending strength, modulus elasticity, internal bond, screw holding ability perpendicular to the plane of panel, and janka hardness perpendicular to the plane of the panel. Surface roughness and color of the panels were also measured. The results indicated that all the panels met the mechanical properties of general-purpose MDF requirements of EN 622-5. The surface roughness of the MDF panels containing burned wood decreased with increasing burned wood content but remained higher than the control panels. The dimensional stability of the MDF panels decreased with the incorporation of burned wood fibers as compared with the control MDF panels.     

Properties of Biocomposite Films From PLA and Thermally Treated Wood Modified with Silver Nanoparticles Using Leaf Extracts of Oriental Sweetgum

Journal of Polymers and the Environment - The technological, thermal, and antimicrobial properties of biocomposite films produced from polylactic acid (PLA) and thermally treated wood flour with in...     

Utilization of Sunflower Stalk in Manufacture of Thermoplastic Composite

Dimensional stability and mechanical performance of polypropylene thermoplastic composites filled with sunflower stalk (SS) flour at 30, 40, 50, and 60 wt% contents of the SS flour were investigated. The thickness swelling and water absorption of the specimens increased with increasing SS flour content. The modulus in the flexural and tensile improved with increasing SS flour content while the tensile and flexural strengths of the specimens decreased. The use of maleic anhydride polypropylene (3 wt%) had a positive effect on the dimensional stability and mechanical properties of the polypropylene thermoplastic composites filled with SS flour. The melting temperature of polypropylene decreased with increasing content of the SS flour. The degree of crystallinity of filled polypropylene composites between fibre loading of 0–30 % by weight was higher than that of unfilled polypropylene composites. However, further increment in the filler content decreased the degree of crystallinity. The obtained results showed that SS flour could be potentially suitable raw material in the manufacture of polypropylene composites.     

Utilization of waste tire rubber in manufacture of oriented strandboard

Some physical and mechanical properties of oriented strandboards (OSBs) containing waste tire rubber at various addition levels based on the oven-dry strand weight, using the same method as that used in the manufacture of OSB. Two resin types, phenol–formaldehyde (PF) and polyisocyanate, were used in the experiments. The manufacturing parameters were: a specific gravity of 0.65 and waste tire rubber content (10/90, 20/80 and 30/70 by wt.% of waste tire rubber/wood strand). Average internal bond values of PF-bonded OSB panels with rubber chips were between 17.6% and 48.5% lower than the average of the control samples while polyisocyanate bonded OSBs were 16.5–50.6%. However, water resistance and mechanical properties of OSBs made using polyisocyanate resin were found to comply with general-purpose OSB minimum property requirements of EN 300 Type 1 (1997) values for use in dry conditions at the lowest tire rubber loading level (10%) based on the oven-dry panel weight. The tire rubber improved water resistance of the OSB panel due to its almost hydrophobic property. Based on the findings obtained from this study, we concluded that waste tire rubber could be used for general-purpose OSB manufacturing up to 10% ratio based on the oven-dry panel weight.