铈锆固溶体负载LaCoO_3催化碳烟的性能和表征

用柠檬酸法制备了铈锆固溶体负载不同量LaCoO3的催化剂。用热重法测试了催化剂样品对碳烟的催化活性。采用程序升温还原法(H2-TPR)、BET、X-射线衍射仪(XRD)和X-射线光电子能谱仪(XPS)对催化剂进行了测试。结果表明,铈锆固溶体表面形成了稳定的LaCoO3钙钛矿相结构;负载量为30%LaCoO3的催化剂具有最高的催化活性,起燃温度降到530℃;催化剂的催化活性与催化剂还原峰强度以及催化剂表面氧物种OII的含量紧密相关。     

Catalytic evaluation of promoted CeO2-ZrO2 by transition, alkali, and alkaline-earth metal oxides for diesel soot oxidation

Series of mixed metal oxides were synthesized by gel-combustion method and their catalytic activities for soot oxidation were investigated. The catalysts were M-Ce-Zr （M = Mn, Cu, Fe, K, Ba, Sr）, and χK-20Mn-Ce-Zr （χ= 0, 5, 10, 20）, they were characterized by XRD, SEM, TPR and BET surface area techniques. The results of soot temperature programmed oxidation （TPO） in an O2 oxidizing atmosphere indicate that K-Ce-Zr has the highest catalytic activity for soot oxidation under loose contact condition, due to enhancement of the soot and catalyst contacts. On the other hand, under a tight contact condition, Mn-Ce-Zr and Cu-Ce-Zr nano-composites have high activities for soot oxidation and lower the soot TPO peak temperatures by about 280 and 270℃, respectively, as compared to non-catalytic soot oxidation. Furthermore, the addition of up to 10 wt.% potassium oxides into Mn-Ce-Zr increases its catalytic activity and further reduces the soot TPO peak temperature by about 40℃ under loose contact condition.     

铈锆固溶体负载LaCoO3催化碳烟的性能和表征

用柠檬酸法制备了铈锆固溶体负载不同量LaCoO3的催化剂。用热重法测试了催化剂样品对碳烟的催化活性。采用程序升温还原法（H2-TPR）、BET、X-射线衍射仪（XRD）和X-射线光电子能谱仪（XPS）对催化剂进行了测试。结果表明,铈锆固溶体表面形成了稳定的LaCoO3钙钛矿相结构;负载量为30%LaCoO3的催化剂具有最高的催化活性,起燃温度降到530℃;催化剂的催化活性与催化剂还原峰强度以及催化剂表面氧物种OII的含量紧密相关。