GA-g-PAMPS/AA/ST凝胶的制备及对亚甲基蓝吸附性能

采用微波辐射技术,通过接枝共聚反应制备了阿拉伯胶（GA）-g-2-丙烯酰胺-2-甲基丙磺酸（AMPS）/丙烯酸（AA）/海泡石黏土（ST）（GA-g-PAMPS/AA/ST）复合水凝胶,利用FTIR、XRD、SEM对复合水凝胶进行了表征,研究了水凝胶对水溶液中亚甲基蓝（MB）染料的吸附性能.结果显示：GA、ST和AA与AMPS发生了接枝共聚反应,形成具有均匀三维网络结构的复合水凝胶.0.025g水凝胶可以使体积为50mL、pH值为6.4、浓度为600mg/L的MB溶液的吸附量和吸附率分别达1146mg/g和95.5%,水凝胶具有较好的重复利用性能.Freundlich等温模型和准二级动力学模型能更好地描述吸附过程.热力学研究表明水凝胶对亚甲基蓝吸附是自发、吸热和不可逆的过程.该水凝胶可用作阳离子染料和阳离子型污染物的潜在候选生物质吸附剂.     

Ni2+对好氧颗粒污泥系统性能的影响

以城镇污水处理厂A²/O工艺的回流污泥作为接种污泥,在序批式反应器（SBR）中培养好氧颗粒污泥（AGS）,探究Ni²⁺对AGS系统的影响.结果表明：在25℃的条件下,50d左右培养出成熟的AGS,其形态多呈球状或椭球状,外表分布着少量丝状菌,颗粒污泥粒径主要在2~4mm,MLSS达6000mg/L,SVI维持在40~50mL/g.将Ni²⁺作用于培养出的成熟AGS,Ni²⁺在0~2mg/L的浓度范围内会提高AGS的稳定性,使MLSS上升,SVI降低;同时会促进AGS分泌胞外多聚物（EPS）,EPS组成成分中的蛋白质（PN）明显多于多糖（PS）;Ni²⁺对好氧颗粒污泥去除总氮（TN）的抑制程度要大于COD,最终COD去除率可维持在95%以上,TN去除率可维持在70%以上.     

聚合物材料在快速原型制造技术中的应用

介绍聚合物材料作为成形原料在主要的快速原型制造(RPM)工艺中的应用情况。具体按照立体印刷成形(SLA)、层合实体制造(LOM)、选域激光烧结(SLS)及熔融沉积造型(FDM)这4种工艺的不同,阐述与各工艺对应的聚合物材料的种类、聚合物材料成形过程中可能出现的问题及解决方案。总结了聚合物材料原型的应用情况和聚合物材料在RPM技术应用中存在的问题。     

电解制备聚合铝过程中Alb形态生成条件研究

考察了电解法制备聚合铝过程中AIb的最佳形成条件。AIb的形成与电流密度、极板间距、电解液的温度、铝的浓度以及电解时间等因素有关。在制备AI浓度为2．0mol/L的聚合氯化铝时，最佳的电流密度和极板间距分别为1．1A／dm^2和10mm。由于电化学过程中产生的不均匀的界面pH差值较大而生成较多的AI（OH）4^-作为AIb结构的结晶核心，因此能形成更多的AIb聚合形态。     

混凝研究中的界面过程化学:IPF-颗粒物-水溶液的相互作用

仅以IPF 颗粒物 水溶液的相互作用为例 ,对混凝研究中二界面过程化学领域的进展加以介绍 .研究结果表明 ,经过预制的聚合铝在混凝过程中表现出较好的形态稳定性 ,而传统混凝剂则强烈地受溶液化学过程 ,尤其是溶液pH值的影响 .混凝剂水解聚合形态倾向于在颗粒物表面吸附沉积 ,而直接引发混凝作用 .单体形态则通过转化为聚合、沉淀形态起混凝作用     

阳离子型聚合物对低温低浊水的絮凝效果与形态学特性

采用微絮凝-深床直接过滤工艺,以西安市曲江水厂低温低浊水质为原水(水温低于10 ℃,初始浊度低于10NTU),投加阳离子型聚合物(简称CP)作主混凝剂或助凝剂,借助分形数学理论与图像分析技术,对滤料粒径、原水浊度、原水温度、药剂种类、聚合物分子量及投加量、混合强度等因素对处理效果的影响进行了研究,分析探讨了不同药剂处理低温低浊水的作用机理、絮凝形态学特征以及絮体结构的分形特性.结果表明,①当温度低于4 ℃、初始浊度小于4NTU时,不宜单独采用Al2(SO4)3或PAC作为絮凝剂;当温度为4～10 ℃、初始浊度小于10NTU时,如果只投加Al2(SO4)3或PAC作为絮凝剂,宜用细砂滤料过滤;低温低浊条件下,无机混凝剂形成的絮体粒径小、结构松散脆弱、有效质量密度低、沉速慢,但表征絮体分形特性的分维值较高.②CP作絮凝剂能显著改善低温低浊水的絮凝效果与过滤性能,但混合强度需增大,宜用粗砂滤料过滤;③单独用CP作絮凝剂时,宜投加分子量较低的弱阳性聚合物或投加低剂量较高分子量的强阳性聚合物;CP用作助凝剂时,能显著减少主混凝剂用量,但宜投加强阳性聚合物或增加弱阳性聚合物的剂量.④CP兼备电性中和与吸附架桥絮凝作用,能形成粒径较大、吸附性能与过滤性能良好的网状絮体构型,其有效质量密度高,产生的污泥量少,污泥沉降速度快,脱水效果好,但分维值低.⑤各种水处理药剂的处理效果为:Al2(SO4)3(或PAC) CP＞CP＞PAC＞Al2(SO4)3,这种差别由絮体的形态学特性与构型特征各异引起.     

聚合氯化铝与有机高分子复合絮凝剂的形态分布研究——AlFerron和~(27)AlNMR相结合

主要研究了Ａｌ－Ｆｅｒｒｏｎ逐时络合比色法和＾２７Ａｌ－ＮＭＲ法应用于聚合铝与有机高分子复合絮凝剂形态分布的测定，结果表明，两种方法分别测定的Ａｌｂ和Ａｌ１３的结果具有一定的相关性；聚合铝与有机高分子复合后其形态分布发生了一定的变化，Ａｌｂ（或Ａｌ１３）的含量有所降低，但仍是优势形态，Ａｌａ（或Ａｌ单）的含量基本保持不变。     

无机高分子絮凝剂的开发与应用进展

主要介绍了各种离子型和复合型无机高分子絮凝剂的种类、原料来源、合成工艺应用情况及其絮凝机理，对无机高分子絮凝剂的发展提出了几点建议。     

Turnover mechanisms of organic conformation on turbidity in drinking water

The turbidity variation in artificial water and samples from a water plant was investigated in the presence of organics with different relative molecular mass. The results show that recessive turbidity existed when water chemical conditions were changing. The formation of turbidity depended on organic relative molecular mass and their conformations on particles. At higher pH and lower ionic strength, the organic chains with a more extended conformation resulted in rising turbidity of the suspension. At lower pH, the reconformation of organics took place due to charge neutralization by the proton, resulting in a decline in turbidity. The addition of NaCl and MgCl₂ at pH 7.00 also resulted in a decrease of turbidity in the suspension. It is believed that the occurrence of recessive turbidity has a significant influence on the stability of water supply quality.     

Synthesis and biodegradation of poly(γ-butyrolactone-co-l-lactide)

Biodegradable polyesters were synthesized by ring-opening copolymerization of -butyrolactone (BL) and its derivatives withl-lactide (LLA). Although tetraphenyl tin was the main catalyst used, other organometallic catalysts were used as well.¹H and¹³C NMR spectra showed that poly(BL-co-LLA)s were statistical and that their number-average molecular weights were as high as 7×10⁴. The maximum BL content obtained from copolymerization BL/LLA was around 17%. TheT _m andT _g values of the copolymers showed a gradual depression with an increase in BL content. NoT _m was obtained for the copolymers containing more than 13 mol% BL. The biodegradability of the copolyesters was evaluated by enzymatic hydrolysis and nonenzymatic hydrolysis tests. The enzymatic hydrolysis was carried out at 37°C for 24 h using lipases fromRhizopus arrhizus andR. delemar. Hydrolyses by both lipases showed that an increase in BL content of the copolymer resulted in enhanced biodegradability. Nonenzymatic accelerated hydrolysis of copolymers at 70°C was found to increase proportionally to their exposure time. The hydrolysis rate of these copolymers was considerably faster than that of PLLA. The higher hydrolyzability was recorded for the BL-rich copolymers. The copolymerization of -methyl--butyrolactone (MBL) or -ethyl--butyrolactone (EBL) with LLA resulted in relatively LA-rich copolymers.