利用自制光催化气体反应器体系,以活性炭纤维负载TiO2作催化剂,在紫外光照射下模拟降解室内污染气体甲醛,测试了活性炭纤维负载TiO2催化剂的催化活性,探讨了紫外光光强、催化剂的酸度、反应器内湿度及反应时间等控制反应的主要因素对甲醛降解率的影响。结果表明,活性炭纤维与TiO2的协同作用大大提高了对甲醛的降解效果;紫外光强增倍对甲醛降解率有一定提高,但提高幅度仅为11.71%;活性炭纤维用pH=5的TiO2溶胶浸泡做催化剂对甲醛的降解效果最好,60 min内降解率达到68.37%;反应器内的湿度为81%甲醛降解率最高,反应60 min后达82.2%;随着反应时间的延长,甲醛降解率的上升幅度不断减小,最高只能达到94.59%。     

活性炭纤维负载TiO2光催化降解甲醛的影响因素

利用自制光催化气体反应器体系，以活性炭纤维负载TiO₂作催化剂，在紫外光照射下模拟降解室内污染气体甲醛，测试了活性炭纤维负载TiO₂催化剂的催化活性，探讨了紫外光光强、催化剂的酸度、反应器内湿度及反应时间等控制反应的主要因素对甲醛降解率的影响。结果表明，活性炭纤维与TiO₂的协同作用大大提高了对甲醛的降解效果；紫外光强增倍对甲醛降解率有一定提高，但提高幅度仅为11.71%；活性炭纤维用pH=5的TiO₂溶胶浸泡做催化剂对甲醛的降解效果最好，60 min内降解率达到68.37％；反应器内的湿度为81%甲醛降解率最高，反应60 min后达82.2%；随着反应时间的延长，甲醛降解率的上升幅度不断减小,最高只能达到94.59%。     

泡沫镍负载改性TiO_2降解甲醛

为了消除甲醛气体对人类的危害,对甲醛气体的光催化降解行为进行了研究。采用沉淀-胶溶法制得了具可见光活性的纳米TiO2溶胶,然后将其负载于经过预处理的泡沫镍板上,置于自置的光催化反应器中,考察了在可见光照射下对密闭空间里面一定浓度的甲醛气体的降解情况。采用乙酰丙酮分光光度法,在最佳的检测条件下检测气相中甲醛气体经不同光照时间后的浓度。研究发现,负载了氮掺杂改性的TiO2的泡沫镍板在可见光照射下能够有效降解气相中的甲醛,反应240 min后对甲醛气体的降解率为93%;而同样条件下反应器中只有处理过的泡沫镍板时,甲醛气体浓度基本保持不变。     

纳米TiO2/活性炭复合光催化剂的制备及其对甲醛气体降解

研究了纳米TiO2/活性炭复合光催化剂对空气中典型污染气体甲醛的光催化降解特性。采用扫描电镜（SEM）表征复合催化剂的表面特征。结果显示,经改性后的纳米TiO2在复合催化剂表面分布均匀,呈球状。对甲醛气体的降解实验显示TiO2负载量为1%时对甲醛的去除效果最好,6 h去除率为61.7%。结果显示复合催化剂把甲醛气体分解成CO2,可以直接排空,无二次污染。     

纳米TiO2/活性炭复合光催化剂的制备及其对甲醛气体降解

研究了纳米TiO2/活性炭复合光催化剂对空气中典型污染气体甲醛的光催化降解特性。采用扫描电镜(SEM)表征复合催化剂的表面特征。结果显示,经改性后的纳米TiO2在复合催化剂表面分布均匀,呈球状。对甲醛气体的降解实验显示TiO2负载量为1%时对甲醛的去除效果最好,6 h去除率为61.7%。结果显示复合催化剂把甲醛气体分解成CO2,可以直接排空,无二次污染。     

TiO2光催化处理络合铜废水的实验研究

研究了以悬浮态TiO2为催化剂,在紫外光的作用下对络合铜废水进行光催化反应,分别考察了常温下TiO2投加量、反应时间、废水初始pH值、反应气氛等因素对处理效果的影响,并探讨了反应机理。结果表明：TiO2投加量为2 g/L,废水pH=4,300 W高压汞灯照射下,载入60 mL/min的空气反应40 min,120 mg/L EDTA络合铜废水的Cu（II）与COD的去除率达到最高,分别为96.56%和57.67%。     

TiO2光催化处理络合铜废水的实验研究

研究了以悬浮态TiO2为催化剂,在紫外光的作用下对络合铜废水进行光催化反应,分别考察了常温下TiO2投加量、反应时间、废水初始pH值、反应气氛等因素对处理效果的影响,并探讨了反应机理。结果表明:TiO2投加量为2 g/L,废水pH=4,300 W高压汞灯照射下,载入60 mL/min的空气反应40 min,120 mg/L EDTA络合铜废水的Cu(II)与COD的去除率达到最高,分别为96.56%和57.67%。     

负载TiO2/Fe^3＋的玻璃纤维反应器光催化苯酚

以玻璃纤维为载体,将TiO2负载到其表面形成了空间玻璃纤维反应器,引入Fe3＋作为掺杂改性离子,形成了负载TiO2/Fe^3＋的空间玻璃纤维光催化反应器,并以高压汞灯为光源进行了光催化降解水中苯酚的实验研究,考察了影响苯酚光催化降解的因素,确定了在UV365-250 W光源照射下,pH为3-5,O2通入量1.0 L/（min.L）,反应器内上升流速为0.7 m/min等实验条件下,初始浓度为30 mg/L的苯酚废水经120 min光催化反应后,降解率可达到85%,矿化率可达80%。     

负载TiO2/Fe3+的玻璃纤维反应器光催化苯酚

以玻璃纤维为载体,将TiO2负载到其表面形成了空间玻璃纤维反应器,引入Fe3+作为掺杂改性离子,形成了负载TiO2/Fe3+的空间玻璃纤维光催化反应器,并以高压汞灯为光源进行了光催化降解水中苯酚的实验研究,考察了影响苯酚光催化降解的因素,确定了在UV365～250 W光源照射下,pH为3～5,O2通入量1.0 L/(min.L),反应器内上升流速为0.7 m/min等实验条件下,初始浓度为30 mg/L的苯酚废水经120 min光催化反应后,降解率可达到85%,矿化率可达80%。     

活性炭负载Fe~(3+)催化H_2O_2氧化邻苯二甲酸二甲酯

将Fe3+负载在活性炭上制得载铁催化剂Fe/AC,并研究了该催化剂对邻苯二甲酸二甲酯(DMP)的催化降解性能。通过正交实验和单因素实验,探讨了催化剂投加量、H2O2投加量、溶液pH值和反应温度对水中DMP降解率的影响,同时对DMP矿化度进行了分析。实验结果表明,制得的载铁催化剂具有较高的催化活性;降解效果的影响顺序是反应温度催化剂投加量H2O2投加量溶液pH值;在反应温度为80℃、催化剂投加量为4 g/L、H2O2投加量为20 mL/L和溶液pH值为3的条件下反应120 min后,质量浓度为10 mg/L的DMP降解率最高可达97.73%;在优化的实验条件下反应150 min,DMP矿化度可达62.73%;催化剂反复使用5次仍具有较好的催化活性,DMP降解率仍可达到77%以上;反应过程中溶液Fe3+浓度的变化维持在1.07 mg/L左右,且可推测催化降解DMP主要是由非均相和均相催化氧化反应共同作用的。     

Performance of photocatalytic reactors using immobilized TiO2 film for the degradation of phenol and methylene blue dye present in water stream

TiO2 thin film photocatalyst was successfully synthesized and immobilized on glass reactor tube using sol-gel method. The synthesized TiO2 coating was transparent, which enabled the penetration of ultra-violet (UV) light to the catalyst surface. Two photocatalytic reactors with different operating modes were tested: (a) tubular photocatalytic reactor with re-circulation mode and (b) batch photocatalytic reactor. A new proposed TiO2 synthesized film formulation of 1 titanium isopropoxide: 8 isopropanol: 3 acetyl acetone: 1.1 H2O: 0.05 acetic acid (in molar ratio) gave excellent photocatalytic activity for degradation of phenol and methylene blue dye present in the water. The half-life time, t1/2 of photocatalytic degradation of phenol was 56 min at the initial phenol concentration of 1000 microM in the batch reactor. In the tubular photocatalytic reactor, 5 re-circulation passes with residence time of 2.2 min (single pass) degraded 50% of 40-microM methylene blue dye. Initial phenol concentration, presence of hydrogen peroxide, presence of air bubbling and stirring speed as the process variables were studied in the batch reactor. Initial methylene blue concentration, pH value, light intensity and reaction temperature were studied as the process variables in the tubular reactor. The synthesized TiO2 thin film was characterized using SEM, XRD and EDX analysis. A comparative performance between the synthesized TiO2 thin film and commercial TiO2 particles (99% anatase) was evaluated under the same experimental conditions. The TiO2 film was equally active as the TiO2 powder catalyst.     

外负载Ce-TiO2/活性炭复合体对亚甲基蓝光催化

用超临界流体沉积法处理过的活性炭(AC)为载体,钛酸丁酯为前驱物,硝酸铈为掺杂剂,乙醇为溶剂,制备了外负载TiO2-Ce/Csurf复合材料。在紫外灯照射下,以亚甲基蓝溶液为标准模拟降解物,研究了复合体不同热处理温度、不同浓度、不同亚甲基蓝浓度、不同铈掺杂量以及不同反应温度对光催化性能的影响。结果表明:外负载催化剂的催化性能要高于纯TiO2和体负载催化剂。铈离子掺杂能抑制TiO2晶粒生长,阻碍了TiO2由锐钛矿型向金红石型的转变。当铈离子掺杂量为1.5%,热处理温度为600℃,亚甲基蓝溶液初始浓度为5.5 mg/L,样品浓度为1.5 g/L时,光催化性能最好。     

Kinetics and mechanism of TNT degradation in TiO2 photocatalysis

The photocatalytic degradation of TNT in a circular photocatalytic reactor, using a UV lamp as a light source and TiO(2) as a photocatalyst, was investigated. The effects of various parameters such as the initial TNT concentration, and the initial pH on the TNT degradation rate of TiO(2) photocatalysis were examined. In the presence of both UV light illumination and TiO(2) catalyst, TNT was more effectively degraded than with either UV or TiO(2) alone. The reaction rate was found to obey pseudo first-order kinetics represented by the Langmuir-Hinshelwood model. In the mineralization study, TNT (30 mg/l) photocatalytic degradation resulted in an approximately 80% TOC decrease after 150 min, and 10% of acetate and 57% of formate were produced as the organic intermediates, and were further degraded. NO(-)(3) NO(-)(2), and NH(+)(4) were detected as the nitrogen byproducts from photocatalysis and photolysis, and more than 50% of the total nitrogen was converted mainly to NO(-)(3)in the photocatalysis. However, NO(-)(3) did not adsorbed on the TiO(2) surface. TNT showed higher photocatalytic degradation efficiency at neutral and basic pH.     

Effect of adsorbents coated with titanium dioxide on the photocatalytic degradation of propoxur

Photocatalytic oxidation of pesticides in aqueous media irradiated by UV light is a rapidly growing field of research. Therefore, the treatment technology for degradation of propoxur (an insecticide) using titanium dioxide coated on the supports such as activated carbon, zeolite, brick, quartz and glass beads, was performed in this research. Results show that GAC/TiO2 is the best complexing agent for oxidizing propoxur because of its adsorption properities. The others follow the sequence: plain TiO2 > glass beads > zeolite > brick > quartz. The degradation rate of propoxur with plain TiO2 is higher than that with TiO2/GAC complexing agent. But the mineralization rate of propoxur with plain TiO2 is lower than that with TiO2/GAC complexing agent. However, it can be concluded that using GAC as the support can improve the photocatalytic efficiency.     

外负载Ce-TiO_2/活性炭复合体对亚甲基蓝光催化

用超临界流体沉积法处理过的活性炭（AC）为载体,钛酸丁酯为前驱物,硝酸铈为掺杂剂,乙醇为溶剂,制备了外负载TiO2-Ce/Csurf复合材料。在紫外灯照射下,以亚甲基蓝溶液为标准模拟降解物,研究了复合体不同热处理温度、不同浓度、不同亚甲基蓝浓度、不同铈掺杂量以及不同反应温度对光催化性能的影响。结果表明：外负载催化剂的催化性能要高于纯TiO2和体负载催化剂。铈离子掺杂能抑制TiO2晶粒生长,阻碍了TiO2由锐钛矿型向金红石型的转变。当铈离子掺杂量为1.5%,热处理温度为600℃,亚甲基蓝溶液初始浓度为5.5 mg/L,样品浓度为1.5 g/L时,光催化性能最好。     

Photocatalytic oxidation of xenobiotics in water with immobilized TiO2 on agitator

A novel photocatalytic oxidation reactor, using Degussa P-25 TiO2 as a stationary phase with a thickness of 1.5-2.0 um on the blades of agitator, was developed to study the photocatalytic oxidation of xenobiotics. Particularly in this device, separation of photocatalyst from the purified water after oxidation reaction was not necessary, and no other aeration equipment was required to supply oxygen. To examine the efficiency of this device, photocatalytic degradation of xenobiotic organics such as carbofuran was studied as an example. Results indicated that carbofuran could be degraded completely with mineralization efficiency of 20% after 6 hours of oxidation under the imposed conditions. The mineralization rate of carbofuran was found to follow the pseudo-first order reaction kinetics. Moreover, the rate constant of mineralization was found to be proportional to TiO2 film area and the square root of UV light intensity. These results implied the mineralization efficiency of carbofuran could be improved through increasing TiO2 film area and UV light intensity. Accordingly, this novel device showed potential application for degrading xenobiotics in water.     

Photocatalytic degradation of mixed gaseous carbonyl compounds at low level on adsorptive TiO2/SiO2 photocatalyst using a fluidized bed reactor

An adsorptive silica-supported titania photocatalyst TiO(2)/SiO(2) was prepared by using nanosized titania (anatase) immobilized on silica gel by the sol-gel technique with the titanium tetra isopropoxide as the main raw material and acetic acid as the acid catalyst. Meanwhile the structure and properties of the TiO(2)/SiO(2) photocatalyst were studied by means of many modern analysis techniques such as TEM, XRD, and BET. Gas-solid heterogeneous photocatalytic decomposition of four carbonyl compounds mixture at low concentration levels over ultraviolet irradiated TiO(2)/SiO(2) photocatalyst were carried out with high degradation efficiencies in a coaxial triple-cylinder-type fluidized bed photocatalytic reactor, which provided efficient continuous contact of ultraviolet photons, silica-supported titania photocatalyst, and gaseous reactants. Experimental results showed that the photocatalyst had a high adsorption performance and a good photocatalytic activity for four carbonyl compounds mixture. Some factors influencing the photocatalytic decomposition of the mixed carbonyl compounds, i.e. the gas flowrate, relative humidity, concentration of oxygen, and illumination time, were discussed in detail. It is found that the photocatalytic reaction rate of four carbonyl compounds decreased in this order: propionaldehyde, acetone, acetaldehyde and formaldehyde.