光催化氧化法处理染料中间体H酸水溶液

为了去除水中难氧化的有害染料中间体Ｈ酸,研究以ＴＩＯ２、ＺｎＯ、ＣｄＳ和Ｆｅ２Ｏ３为催化剂,采用低压汞灯为光源,对Ｈ酸水溶液进行光催化氧化实验．结果表明：ＴｉＯ２和ＣｄＳ的催化效果最好．采用ＴｉＯ２作催化剂,光催化氧化５ｈ后,Ｈ酸分解率可达９０％,反应速率遵从Ｌａｎｇｍｕｉｒ－Ｈｉｎｓｈｅｌｗｏｏｄ方程,Ｋ＝１２．３Ｌ／ｍｍｏｌ,ｋ＝２５．２×１０－６ｍｏｌ／ｈ．溶液中投加１０ｍｇ／Ｌ的Ｆｅ３＋或Ａｇ＋,可使反应时间缩短２—３ｈ．研究探讨了ｐＨ、ＴｉＯ２投加量和Ｈ酸浓度对催化氧化过程的影响．     

光催经氧化法处理染料中间体H酸水溶液

为了去除水中难氧化的有害染料中间体Ｈ酸，研究以ＴｉＯ２，ＺｎＯ，ＣｄＳ和Ｆｅ２Ｏ３为催化剂，采用低压汞灯为光源，对Ｈ酸水溶液进行光催化氧化实验。结果表明：ＴｉＯ２和ＣｄＳ的催化效果最好。采用ＴｉＯ２作催化剂，光催化氧化５ｈ后，Ｈ酸分解率可达９０％，反应速率遵大Ｌａｎｇｍｕｉｒ－Ｈｉｎｓｈｅｌｗｏｄｄ方程，Ｋ＝１２．３Ｌｍｍｏｌ，ｋ＝２５．２×１－０＾－６ｍｏｌ／ｈ。     

Fe~（2＋）－H_2O_2法处理DSD酸生产氧化母液的研究

为改善ＤＳＤ酸氧化母液的可生化降解性，将废液先用有机絮凝剂ＴＳ－１（一种季胺盐）处理，ＴＳ－１的投加量为３ｇ／Ｌ，其后用Ｆｅ２＋－Ｈ２Ｏ２法氧化，Ｆｅ２＋和Ｈ２Ｏ２的量分别为１５０ｍｇ／Ｌ，７ｇ／Ｌ，废液ＣＯＤ和色度的去除率分别可达６４％和６２％。经处理后的废水，其ＢＯＤ５／ＣＯＤ≈０．３，可以认为已达到生化处理的要求。当Ｈ２Ｏ２的投量为２ｇ／Ｌ，经Ｆｅ２＋－Ｈ２Ｏ氧化处理后的废液，再用ＦｅＣｌ３进行两级混凝处理（ＦｅＣｌ３的投加量分别为ｓｇ／Ｌ和２ｇ／Ｌ），则ＣＯＤ和色度的去除率可达９０％和９５％。     

光催化降解有机磷农药废水的可行性

在ＴｉＯ２粉末的存在下，研究光催化降解有机磷农药废水的可行性。结果表明，ＣＯＤｃｒ６５０ｍｇ／Ｌ，有机磷１９．８ｍｇ／Ｌ的有机磷农药废水在３７５Ｗ中压汞灯照射４ｈ，ＣＯＤ去除率为９０％，有机磷将完全转化为无机磷。同时还研究了光催化剂ＴｉＯ２的用量，反应液初始ｐＨ值，空气流量，外加Ｆｅ３＋浓度等多种因素对光降解的影响；并利用太阳聚光做了室外实验     

负载型TiO2固定相光催化氧化法降解水中呋码唑酮

以高压汞灯为光源、负载在海砂上的ＴｉＯ２为催化剂，采用敞口固定床型光催化反应器对水中难降解的呋码唑酮（ＦＴＤ）进行了固定相光催化氧化实验。结果表明，反应速率可用ＬａｎｇｍｕｉｒＨｉｎｓｈｅｌｗｏｏｄ方程描述，与光分解相比，光催化氧化的突出优点是矿化程度高，相同光辐射条件下反应１００ｍｉｎ，０．１０ｍｍｏｌ／Ｌ的ＦＴＤ水溶液经光催化氧化后ＴＯＣ的去除率为８９．１％，而经光分解后ＴＯＣ的去除率仅为２８．８％；在反应体系中投加少量臭氧或过氧化氢可以显著提高ＦＴＤ的氧化效率，说明光催化氧化可以兼容Ｏ３／ＵＶ、Ｈ２Ｏ２／ＵＶ等光激发氧化工艺。制得的负载型ＴｉＯ２具有较高的机械强度和化学稳定性，可重复利用。探讨了充氧、ＦＴＤ浓度及ｐＨ值等对光催化氧化过程的影响。     

金属氧化物对CO还原NO反应的催化作用

采用固定床流动反应器,研究ＣｕＯ、Ｃｒ２Ｏ３、ＭｎＯ２、Ｆｅ２Ｏ３、Ｎｉ２Ｏ３等单元金属氧化物及它们形成的复合氧化物对ＣＯ还原ＮＯ反应的催化活性。结果表明,在５００℃８００ｍｌ／ｍ＾３ＮＯ－０．２％ＣＯ－２．０％ＣＯ２－Ｎ２气氛中ＣＯ还原ＮＯ的能力很小,稳定还原率仅为１．５０％。     

Cr(VI)离子在TiO_2表面的吸附与光催化还原消除

随着体系ｐＨ值增大，Ｃｒ（ＶＩ）离子在ＴｉＯ２表面的吸附下降．当Ｃｒ（ＶＩ）离子初始浓度为３００μｍｏｌ／Ｌ时，其在ＴｉＯ２表面具有最大值吸附．Ｈ２ＰＯ４－阴离子及乙酸的存在对Ｃｒ（ＶＩ）离子的吸附有阻抑作用，甲酸存在会提高Ｃｒ（ＶＩ）离子的吸附．Ｃｒ（ＶＩ）离子在ＴｉＯ２半导体催化剂表面的光催化还原受体系的酸度影响较大．Ｈ２ＰＯ４－阴离子或Ｍｎ２＋离子存在会降低Ｃｒ（ＶＩ）离子的光催化还原效率．在太阳光照下，Ｃｒ（ＶＩ）离子在ＴｉＯ２上的光催化还原也可实现．通过调节反应结束后水溶液的酸碱度，Ｃｒ（ＶＩ）离子得以消除．反应后催化剂经酸处理，其活性恢复并可重复使用．     

氧化氢加Fe^3＋作催化剂处理含酚废水的研究

采用Ｈ２Ｏ２／Ｆｅ＾３＋对含酚废水进行了催化氧化的研究。对于溶液ｐＨ值、过氧化氢浓度、铁离子浓度与酚、ＣＯＤ、ＴＯＣ去除的关系作了探讨。结果表明，在酸性ｐＨ值范围内，Ｆｅ＾３＋作催化剂可获得不低于Ｆｅ＾２＋作催化剂进的催化活性。对酚、ＣＯＤ和ＴＯＣ都有较好的去除率。而在初始ｐＨ＝７时，Ｆｅ＾３＋作催化剂的反应活性明显降低，自动连续控制溶液ｐＨ＝７．０±０．２时，无论是高铁或低铁离子都大幅度都大幅度     

分光光度法测定水样中铬

在ｐＨ４．４ＨＡＣ－ＮａＡｃ缓冲介质及乳化剂ＯＰ存在下，Ｃｒ６＋与二溴羟基苯基荧光酮（ＤＢＨＰＦ）显色反应生成桔红色络合物．该络合物最大吸收位于４８２ｎｍ波长处，表现摩尔吸光系数εｍａｘ＝３．４７×１０４．络合物配位比为Ｃｒ６＋：ＤＢＨＰＦ＝２：３，Ｃｒ６＋在０－１６μｇ／２５ｍＬ范围内遵守比耳定律．方法已用于水样中微量铬的测定，结果满意．     

H2O2—Fe^2＋／TiO2—H2SO4体系处理废有机溶剂的研究

研究了废有机溶剂ＴＢＰ／ＯＫ在Ｈ２Ｏ２－Ｆｅ＾２＋／ＴｉＯ２－Ｈ２ＯＳ４体系中的氧化分解行为，分析Ｈ２Ｏ２用量、催化剂、温度、ＰＨ 控因素对反应进程及结果的影响。在此基础上进行的“热”实验表明，废有机溶剂氧化分解后所含放射性核素主要富集在以应残液中，基本没有二次转移或扩散。对ＴＢ．ＯＫＨ２Ｏ２经氧化机理及Ｆｅ＾２＋／ＴｉＯ２的协同催化机理进行了初步探讨。     

铁、锌、铁酸锌掺杂对纳米级二氧化钛光催化降解罗丹明B活性的影响

通过溶胶 凝胶法合成了掺杂Fe3+ 、Zn2 + 、ZnFe2 O4的纳米级TiO2 ,并进行了XRD、TEM表征 ,对罗丹明B的光催化实验表明 ,ZnFe2 O4的掺杂能明显提高TiO2 的光催化活性 ,而Zn2 + 的掺杂对TiO2 的光催化活性影响不大 ,Fe3+ 的掺杂则使TiO2 的光催化活性降低。     

TiO2纳米膜光催化深度处理城市污水的实验研究

采用溶胶-凝胶方法制备光催化性能优良的TiO2纳米膜,应用X射线衍射仪分析了TiO2纳米膜的结构,探讨了铁离子和贵金属Ag、Pt掺杂对TiO2纳米膜光催化降解性能的影响,研究了TiO2纳米膜及掺杂改性TiO2纳米膜对生物二级处理系统出水中有机物光催化去除的性能。贵金属Ag、Pt掺杂提高了TiO2纳米膜光催化性能,而铁离子掺杂则降低了其催化性能。未掺杂的TiO2纳米膜使二级出水的COD下降8.9%,而贵金属Ag、Pt掺杂的TiO2纳米膜则使COD分别下降19.4%和22.3%。实验结果表明TiO2纳米膜有优良的光催化降解性能,TiO2纳米膜有广阔的应用前景。     

Fe~(3+)及Ce~(3+)掺杂对TiO_2纳米粒子性能的影响

以溶胶-凝胶法制备纯的和分别掺杂Fe3+、Ce3+的TiO2纳米粒子,以橙黄IV的光催化氧化评价纳米粒子的紫外光与可见光活性,利用TG-DSC、XRD、BET及UV-Vis吸收光谱考察掺杂对TiO2的相变、粒径、比表面积及光吸收性能的影响,在归一化条件下探讨Fe3+及Ce3+掺杂对TiO2活性和表面性质产生影响的机制。结果表明:Fe3+及Ce3+的最佳掺杂量分别为0.2%和0.04%;Ce3+抑制TiO2由锐钛矿向金红石转变以及改善TiO2高温组织稳定性的能力均明显大于Fe3+;Fe3+和Ce3+掺杂均能提高TiO2的紫外光活性并扩展TiO2的光响应范围,但光生电子与空穴复合以及光腐蚀使它们对TiO2可见光活性的提高并不显著。Fe3+和Ce3+的半径及其相应氧化物的性质决定了两者对TiO2性能的不同影响。     

Characterization of metal doped-titanium dioxide and behaviors on photocatalytic oxidation of nitrogen oxides

A series of nanosized ion-doped TiO_2 catalysts with different ion content(between 0.1 at.% and 1.0 at.%) have been prepared by wet impregnation method and investigated with respect to their behavior for UV photocatalytic oxidation of nitric oxide.The catalytic activity was correlated with structural,electronic and surface examinations of the catalysts using X-ray diffraction analysis (XRD),ultraviolet-visible(UV-Vis)absorption spectroscopy,transmission electron microscopy(TEM),energy disperse spectrometer (EDS)and high resolution-transmission electron microscopy (HR-TEM) techniques.An enhancement of the photocatalytic activity was observed for Zn~(2 ) doping catalyst ranged from 0.1 at.% to 1.0 at.% which was attributed to the lengthened lifetime of electrons and holes.The improvement in photocatalytic activity could be also observed with the low doping concentration of Cr~(3 )(0.1 at.%). However,the doping of Fe~(3 ),Mo~(6 ),Mn~(2 ) and the high doping concentration of Cr~(3 ) had no contribution to photocatalytic activity of nitric oxide.     

Formaldehyde degradation by UV/TiO2/O3process using continuous flow mode

The degradation of formaldehyde gas was studied using UV/TiO2/O3 process under the condition of continuous flow mode. The effects of humidity, initial formaldehyde concentration, residence time and ozone adding amount on degradation of formaldehyde gas were investigated. The experimental results indicated that the combination of ozonation with photocatalytic oxidation on the degradation of formaldehyde showed a synergetic action, e.g,, it could considerably increase decomposing of formaldehyde. The degradation efficiency of formaldehyde was between 73.6% and 79.4% while the initial concentration in the range of 1.84--24 mg/m^3 by O3/TiO2flJV process. The optimal humidity was about 50% in UV/TiO2/O3 processs and degradation of formaldehyde increases from 39.0% to 94.1% when the ozone content increased from 0 to 141 mg/m^3. Furthermore, the kinetics of formaldehyde degradation reaction could be described by Langmuir-Hinshelwood model. The rate constant k of 46.72 mg/（m^3.min） and Langmuir adsorption coefficient K of 0.0268 m^3/mg were obtained.     

在TiO2催化剂上菲的光催化氧化反应研究

选择TiO₂ 粉末催化剂,在发射光谱为254 nm的15 W紫外灯照射下,反应液中Al3+,Fe3+和H2O₂ 浓度增加能提高菲的降解率;TiO₂ 表面载银量的增加能提高降解速度;TiO₂ 投入量在一定范围内随投入量的增加,光催化降解菲的速度也增加,但当投入量较多时又能降低降解速率;在酸性条件下,菲易被光催化降解;菲的起始反应浓度与反应速度成负一级反应动力学关系。      

Ag掺杂改性TiO_2催化降解水体中的邻苯二甲酸二甲酯

邻苯二甲酸酯是环境中普遍存在的有机污染物(内分泌干扰物)之一。通过湿式机械混合法制备Ag掺杂改性TiO2催化剂。光催化降解实验的结果表明Ag掺杂浓度为1×10-4mol/g,焙烧温度为400℃下所得的催化剂活性较好。对降解体系的研究表明,当催化剂的投加量为0.1~0.3 g/L、pH=5~8时降解效率较高(62.0%)。相对于催化剂的降解过程而言,其吸附作用是比较小的,而是以光催化反应为主。并利用荧光光谱对催化剂的性能进行了初步表征。     

光催化降解模拟室内挥发性有机污染物研究

用浸渍-提拉法制备玻璃弹簧负载型TiO2薄膜催化剂,在自制的反应器中进行光催化降解由丙酮、甲苯、对二甲苯组成的模拟室内挥发性有机污染物VOCs研究。研究发现：催化剂中掺杂金属离子能影响催化剂的降解效果,降解效果依次为掺铈TiO2〉纯TiO2〉掺银TiO2;气体流量显著影响降解效果,丙酮、甲苯和对二甲苯的最佳降解流量分别为3、5、7L／min;混合气体中非对称性的极性分子的降解效率高于对称性分子,导致丙酮、对二甲苯组分降解率降低,甲苯降解率增高。     

Fe~(3+)掺杂TiO_2薄膜的制备及光催化降解甲醛的研究

采用溶胶-凝胶法制备Fe3+掺杂的TiO2薄膜光催化剂,进行甲醛的光催化实验,考察Fe3+掺杂量、薄膜焙烧温度及溶胶体系pH值对光催化性能的影响。结果表明,Fe3+掺杂量为1.0%,焙烧温度500℃1h,加硝酸溶胶体系pH=4时,Fe3+掺杂TiO2薄膜光催化活性最高。     

Zr/TiO2纳米颗粒的制备及其光催化活性

以钛酸丁酯,乙醇为原料,用固相合成法制备了Zr/TiO2纳米颗粒,用XRD、TEM对其组成、颗粒大小、形貌进行了表征.通过对罗丹明B的降解反应,考察了Zr/TiO2的光催化活性.结果表明,Zr/TiO2为纳米颗粒,平均粒径为12.7 nm左右,且颗粒均匀;掺杂金属离子Zr提高了TiO2光催化效率,掺杂2.0%Zr的催化剂活性最高.Zr/TiO2的光催化反应,首先是反应物在Zr/TiO2表面发生吸附作用,然后进一步发生光催化降解.