微波强化铁碳-双氧水体系处理填埋场渗滤液膜滤浓缩液研究

为了探讨微波(MW)/铁碳(Fe-C)/H_2O_2类芬顿反应对填埋场渗滤液膜滤浓缩液(简称"渗滤液浓缩液")中难降解有机物,系统研究了双氧水投量、Fe-C投量、初始pH值、微波输出功率和反应时间对浓缩液中有机污染物的去除规律,通过类比实验研究了MW/Fe-C/H_2O_2体系的反应协同作用;此外,采用紫外-可见和三维荧光光谱表征了浓缩液中溶解性有机物的分子结构变化;最后,利用SEM-EDS和XRD等表征对反应前后的Fe-C材料的催化机理进行了解析.结果表明,在双氧水投量为10 mL·L~(-1),Fe-C投量0.8 g·L~(-1),初始pH值为3,微波输出功率为450 W,反应时间为12 min时,其COD、腐殖质和色度的去除率达到了70.06%、94.61%和98.86%.与此同时,控制实验表明MW/Fe-C/H_2O_2具有较强的协同作用,且对有机物的降解效果远好于其他体系.经过MW/Fe-C/H_2O_2体系处理后,浓缩液中溶解性有机物的芳香性程度和腐殖质缩合度逐渐降低,并且腐殖质等大分子难降解有机物大幅去除,可生化性(BOD/COD值)也大幅提升.一方面,Fe-C材料包含了多种铁基氧化物等活性物质可与H_2O_2形成非均相芬顿反应;另一方面,在酸性条件下铁缓释淋滤产生的铁离子会与H_2O_2形成芬顿反应.并且,微波辐射作用可一定程度上强化上述过程,从而加速了有机物的去除.因此,MW/Fe-C/H_2O_2体系能够快速高效的对渗滤液浓缩液进行预处理,研究为高浓度有机废水的处理提供了借鉴.     

黄铁矿催化类Fenton反应处理阳离子红X-GRL废水

基于对天然矿物黄铁矿进行SEM、EDS表征的基础上,以黄铁矿为非均相类Fenton催化剂,以偶氮染料阳离子红X-GRL为目标污染物,考察了催化剂双氧水用量、溶液初始pH值、阳离子红X-GRL初始浓度、反应时间等因素对染料脱色效果的影响.结果表明,在H2O2浓度为26.6mg/L、矿用量1g/L、溶液初始pH值6.4左右的条件下,反应2min后,染料脱色率达95%左右.进行了黄铁矿在水溶液中的酸性氧化实验并且考察了Fe2+、SO42-浓度及溶液pH随矿重复利用次数的变化规律.初次使用的黄铁矿具有很强的酸性氧化特性,反应过程中伴随着大量Fe2+、SO42-及H+的溶出.染料的快速脱色主要是均相Fenton反应作用的结果.黄铁矿作为一种新的催化剂大大提高了类Fenton反应的催化活性,而且该新型类Fenton反应能克服传统Fenton反应适用pH范围小的局限性,拓展了Fenton反应在废水处理中的应用.     

Characteristics and mechanisms of 4A zeolite supported nanoparticulate zero-valent iron as Fenton-like catalyst to degrade methylene blue

4A zeolite supported nanoparticulate zero-valent iron (nZVI/4A zeolite), synthesized through borohydride reduction method, was used as a catalyst with H₂O₂ to build Fenton-like reaction system to degrade methylene blue (MB) in model wastewater. The characteristics and primary mechanisms of the catalyst were investigated. The results show that nZVI/4A zeolite has the potential as a Fenton-like catalyst, and (about 30 mg/L) MB was degraded completely in 3 h with 10 mM H₂O₂, 0.2 g/L catalyst, and initial pH of 3.0. The MB degradation rates were obtained at least 70% in the tests with initial pH ranged from 2.0 to 9.0 and the catalyst dose rose from 0.2 to 5.0 g/L. Importantly, the catalyst also has a distinctive ability to increase the solution pH value from its initial acidic pH and then maintain the value at close to neutrality. This ability was controlled by both the initial pH and the catalyst dose. MB degradation clarified that hydroxyl radical was the dominated active oxidative specie in the tests with initial acidic pH and low catalyst dose (less 2.5 g/L); otherwise, Fe(VI) oxidation was the main mechanism for MB degradation; and the two processes shared synergistic effect in MB degradation in the present test. The catalyst has high operational stability in both of the composites with low iron leaching (less 2%) and catalyzing ability. Therefore, nZVI/4A zeolite has great potential as a Fenton-like catalyst and is used with H₂O₂ to build Fenton-like system which could be used to degrade MB efficiently.     

钒酸铁类Fenton催化剂的制备及性能研究

在不同酸碱条件下,采用水热法制备了FeVO4催化剂,利用XRD、TEM、FTIR对产物表征,并将其作为非均相类Fenton催化剂氧化降解有机染料罗丹明B,研究了初始反应溶液pH值、类Fenton试剂中各组分的浓度、钒酸铁催化剂的制备条件等因素对类Fenton反应效率的影响.结果表明,制备的钒酸铁为FeVO4﹒1.25H2O,在优化条件下降解罗丹明B时60min内脱色率可达97%以上.与传统Fenton试剂相比,类Fenton催化剂具有更广泛的pH适用范围,易于与水分离,应用前景广阔.     

UV-Vis/Fe(Ⅲ)/H2O2体系对水中雌酮的光降解

以250W照明金属卤化物灯为光源,研究了水中雌酮（E1）在UV-Vis／Fe（Ⅲ）／H2O2体系中的光降解;考查了初始pH、Fe（Ⅲ）、H2O2、E1初始浓度对E1光降解的影响。结果表明,UV-Vis／Fe（Ⅲ）／H2O2体系能有效地光降解E1,在[Fe（Ⅲ）30-20．8μmol／L、[H2O2]0=1664μmol／L、pH=3．0时,光照160min,18．5btmol／L E1的光降解率可达98．4%;在pH3．0～8．0范围内,pH初始值越小,E1降解率越大,反应初始速率越大;实验条件下,Fe（Ⅲ）、H2O2初始浓度越大,E1降解率越大,反应初始速率越大;E1初始浓度越低,E1降解率越大,反应初始速率越小。pH=3．0,实验浓度范围内的表观动力学方程为：dCE1／dt=0．00093[H2O2]^0.47[Fe（Ⅲ）]^0.62[E1]0.24;Fe（Ⅲ）是影响反应速率的主要浓度因素。