Catalytic degradation of toxic organic dye using an aluminum-doped Cu0.4Zn0.6-xAlxFe2O4 (x = 0.0, 0.2, 0.4, 0.6) spinel ferrite in a photo-Fenton system

Catalytic activity of spinel ferrite in breaking down toxic dye materials are promising due to their uniqueness. In this study, aluminum-doped copper zinc ferrite, Cu_0.4Zn_0.6-xAl_xFe₂O₄ (x = 0.0, 0.2, 0.4, 0.6), a catalyst for toxic dye degradation is synthesized through chemical co-precipitation route. The formation of the spinel ferrite catalyst is initially confirmed by Fourier transform infrared spectra, which shows the frequency of metal-oxygen bond vibration at 539 and 427 cm⁻¹ attributed to the tetrahedral and octahedral sites respectively. Higher intensity sharp peak of X-ray diffraction for (311) plane is the evidence for the phase purity and the formation of spinel ferrite. The crystallite size is found to decrease with the increase of Al³⁺ ion. The surface structure of the obtained particles is investigated using a scanning electron microscope. Analyses of the material's magnetic characteristics using a vibrating sample magnetometer (VSM) revealed that it is, in fact, a soft magnet, as evidenced by the loop of its hysteresis, which is narrow. The catalytic degradation of methylene blue dye under the mechanism of the photo-Fenton process is studied with the obtained spinel ferrites and the result is found to be as high as 96.5%. The process follows pseudo-second order kinetics and the Langmuir isotherm.     

大肠杆菌吸附-化学还原法用废含金催化剂制备金纳米线

采用大肠杆菌吸附-化学还原法,以大肠杆菌(ECCs)为模板、十六烷基三甲基溴化铵为保护剂、抗坏血酸为还原剂,由废含金催化剂制备金纳米线(AuNWs)。采用XRD,SEM,TEM等技术对AuNWs进行表征。研究了AuNWs对罗丹明6G(R6G)和4-巯基苯甲酸(4-MBA)的拉曼散射信号的增强效果。实验结果表明:在制备过程中加入微生物ECCs,可使金回收率提高约20百分点;当溶液pH小于4时,反应2 h后,有大量呈线状的AuNWs聚集沉降,金回收率可达99%1以上。表征结果显示,AuNWs呈多晶结构,晶格间距为0.23 nm。表面增强拉曼散射分析表明,AuNWs对R6G和4-MBA具有良好的拉曼光谱增强性能。     

Feasibility of honeycomb monolith supported sugar catalyst to produce biodiesel from palm fatty acid distillate (PFAD)

Carbon coated monolith was prepared by sucrose solution 65 wt.% via dip-coating method. Sulfonation of incomplete carbonized carbon coated monolith was carried out in order to synthesize solid acid catalyst. The textural structure characteristics of the solid acid catalyst demonstrated a low surface area and pore volume. Palm fatty acid distillate (PFAD), a by-product of palm oil refineries, was utilized as oil source in biodiesel production. The esterification reaction subjected to different reaction conditions was performed by using the sulfonated carbon coated monolith as heterogeneous catalyst. The sulfonation process had been performed by using vapour of concentrated H₂SO₄ that was much easier and efficient than liquid phase sulfonation. Total acidity value of carbon coated monolith was measured for unsulfonated sample (0.5 mmol/g) and sulfonated sample (4.2 mmol/g). The effect of methanol/oil ratio, catalyst amount and reaction time were examined. The maximum methyl ester content was 89% at the optimum condition, i.e. methanol/oil molar ratio (15:1), catalyst amount (2.5 wt.% with respect to PFAD), reaction time (240 min) and temperature 80 °C. The sugar catalyst supported on the honeycomb monolith showed comparable reactivity compared with the sugar catalyst powder. However, the catalyst reusability studies showed decrease in FFA% conversion from 95.3% to 68.8% after four cycles as well as the total acidity of catalyst dropped from the value 4.2 to 3.1 mmol/g during these cycles. This might be likely due to the leaching out of SO₃H group from the sulfonated carbon coated monolith surface. The leaching of active species reached a plateau state after fourth cycle.     

A multi-path routing-inventory problem for a closed-loop supply chain considering the heterogeneous fleet of vehicles

In this paper, the inventory-routing problem is studied for a closed-loop supply chain. This closed-loop supply chain considers suppliers, manufacturers, whole-sellers, and disposal centers. To formulate this problem, a mixed integer linear programming model is proposed. This mathematical model minimizes the total costs of the supply chain, including the fixed and variable costs of vehicles, and holding inventory costs of final products and scraps. The proposed model considers the road roughness degree, multi-path setting and the heterogeneous fleet of vehicles, which increases its flexibility and the quality of solutions. Then, two symmetry-breaking constraints are proposed to reduce the complexity of the mathematical model. In order to evaluate the integrity of the proposed model, 20 instances of different sizes are randomly generated and solved. Finally, a comprehensive sensitivity analysis is conducted with respect to five key features of the problem, such as the impact of the symmetry-breaking constraints on the CPU time, multi-path setting, fixed cost of vehicles, heterogeneous fleet of vehicles, and lost sales. The results indicate that the consideration of multi-path setting and the heterogeneous fleet of vehicles improves the quality of solutions significantly.     

MnO2/Al2O3催化剂-微气泡臭氧体系催化降解喹啉及其机理

制备了纳米MnO₂,并以Al₂O₃为载体制备了掺杂型MnO₂/Al₂O₃颗粒催化剂.催化剂焙烧温度和时间分别为500℃和4 h、MnO₂质量分数为8%时,催化剂具有最高的臭氧催化氧化活性.SEM分析表明,纳米MnO₂均匀分布于Al₂O₃载体表面.MnO₂/Al₂O₃催化剂的比表面积（BET）为183.22 m²·g^-1,平均孔容为0.27 cm³·g^-1,平均孔径为4.87 nm.建立了MnO₂/Al₂O₃催化剂-微气泡臭氧催化反应体系,研究了该体系对喹啉的降解去除效果及其机理.臭氧微气泡的平均粒径为61.7 μm.微气泡臭氧投量为30 mg·L^-1时,反应60 min后喹啉去除率能达到95%以上;反应20 min后,MnO₂/Al₂O₃催化剂-微气泡臭氧体系对实际煤化工废水二级出水的TOC去除率可达到55%以上.以叔丁醇作为分子探针,证明了羟基自由基（·OH）氧化作用在臭氧微气泡催化氧化体系中对喹啉的降解起到主导作用.     

MnFe2O4磁性纳米棒非均相Fenton催化降解水中四环素的研究

采用水热合成法成功制备出MnFe₂O₄磁性纳米棒（s-MnFe₂O₄）,并考察了商品化的Fe₃O₄、MnFe₂O₄和合成的s-MnFe₂O₄纳米棒这3种磁性纳米颗粒作为非均相Fenton催化剂降解水中四环素抗生素的性能.同时,采用X射线衍射（XRD）、透射电镜（TEM）、N₂吸附-脱附、振动样品磁强计（VSM）及X射线光电子能谱（XPS）等技术对催化剂的理化性质进行了表征.非均相Fenton催化降解四环素的结果表明,s-MnFe₂O₄具有最高的催化活性,反应180 min,四环素的去除率可以达到87.6%,TOC的去除率达到47.5%.自由基捕获试验证实了羟基自由基（·OH）是非均相Fenton氧化过程中的主要活性物种.s-MnFe₂O₄磁性纳米棒的高催化活性归因于其表面拥有较高含量的Mn³⁺和Fe²⁺物种,它们的存在能加速界面电子的转移效率,从而促进·OH的生成.合成的s-MnFe₂O₄催化剂具有良好的稳定性,循环使用6次,四环素的去除率仅从87.6%降低到80.2%,且氧化过程中活性组分的流失很少.     

电场与MnxCey催化剂在苯氧化反应中的协同效应及机理探究

挥发性有机物（VOCs）大量排放已成为日益严重的环境问题,为了实现VOCs的高效去除,本文采用自蔓延燃烧合成法制备了一系列锰铈复合氧化物催化剂,将稳恒直流电场引入典型VOCs气体苯的催化氧化过程,并基于不同电场条件下催化剂的理化性质表征结果进行机理分析.实验结果表明,Mn_xCe_y催化剂对含苯废气的去除有良好的效果,稳恒直流电场显著促进了催化剂的活性,其中Mn₁Ce₃的催化性能最佳,电流为5 mA时,Mn₁Ce₃催化剂在155℃可达到50%的苯转化率,在202.4℃可达到90%的苯转化率,对应的转化温度T₅₀和T₉₀比传统方法分别降低了62.4℃和48.3℃,且电场中的反应活化能由52.32 kJ·mol^-1降低至32.31 kJ·mol^-1.根据实验现象及表征结果,发现协同效应与活性位点的快速持续再生及活性氧物种的转化有关,由此提出苯在Mn_xCe_y催化剂上的氧化机理及电场协同催化的反应模型.     

苯醌对聚合硅酸铁多相UV-Fenton体系的增效机制

通过构建苯醌增效聚合硅酸铁多相UV-Fenton体系,讨论了体系中橙Ⅱ的脱色和降解途径.在研究苯醌浓度对聚合硅酸铁铁离子的释放、Fe²⁺与Fe³⁺之间的转化、H₂O₂分解和·OH生成影响的基础上,提出了苯醌对聚合硅酸铁多相UV-Fenton体系的增效机制.结果表明,随苯醌浓度的增加,其紫外光下光解还原聚合硅酸铁并释放Fe²⁺的程度增大、H₂O₂分解速度加快、产生·OH浓度峰值增高且出现的时间提前;苯醌增效体系释放于溶液中的Fe²⁺可以通过Fenton反应转化成Fe³⁺,反应结束后聚合硅酸铁能重新吸附Fe³⁺并使其浓度降低,避免了增效体系铁离子的二次污染.本研究将为多相催化剂催化过程的调控提供新的视角,为多相光助-芬顿反应在有机废水资源化中的应用提供理论依据和技术支持.     

Density functional theory (DFT) studies of vanadium-titanium based selective catalytic reduction (SCR) catalysts

Based on density functional theory (DFT) and basic structure models, the chemical reactions on the surface of vanadium-titanium based selective catalytic reduction (SCR) denitrification catalysts were summarized. Reasonable structural models (non-periodic and periodic structural models) are the basis of density functional calculations. A periodic structure model was more appropriate to represent the catalyst surface, and its theoretical calculation results were more comparable with the experimental results than a non-periodic model. It is generally believed that the SCR mechanism where NH₃ and NO react to produce N₂ and H₂O follows an Eley-Rideal type mechanism. NH₂NO was found to be an important intermediate in the SCR reaction, with multiple production routes. Simultaneously, the effects of H₂O, SO₂ and metal on SCR catalysts were also summarized.     

Effects of calcination temperature on physicochemical property and activity of CuSO4/TiO2 ammonia-selective catalytic reduction catalysts

CuSO_4/TiO_2 catalysts with high catalytic activity and excellent resistant to SO_2 and H_2 O,were thought to be promising catalysts used in Selective catalytic reduction of nitrogen oxides by NH_3.The performance of catalysts is largely affected by calcination temperature.Here,effects of calcination temperature on physicochemical property and catalytic activity of CuSO_4/TiO_2 catalysts were investigated in depth.Catalyst samples calcined at different temperatures were prepared first and then physicochemical properties of the catalyst were characterized by N2 adsorption-desorption,X-ray diffraction,thermogravimetric analysis,Raman spectra,Fourier-transform infrared spectroscopy,X-ray photoelectron spectroscopy,temperature-pro grammed desorption of NH_3,temperature-programmed reduction of H_2 and in situ diffuse reflectance infrared Fourier transform spectroscopy.Results revealed that high calcination temperature had three main effects on the catalyst.First,sintering and anatase transform into rutile with increase of calcination temperature,causing a decrement of specific surface area.Second,decomposition of CuSO_4 under higher calcination temperature,resulting in disappears of Br(?)nsted acid sites(S-OH),which had an adverse effect on surface acidity.Third,CuO from the decomposition of CuSO_4 changed surface reducibility of the catalyst and favored the process of NH_3 oxidation to nitrogen oxides(NO_x).Thus,catalytic activity of the catalyst calcined under high temperatures(≥600℃) decreased largely.