钢和硬铝的加速腐蚀试验研究

目的研究45号钢和12号硬铝的温、湿度加速腐蚀情况。方法在不同的温、湿度环境下开展45号钢和12号硬铝的加速腐蚀试验,并将不同条件下的试验结果进行对比。结果得到了45号钢和12号硬铝的腐蚀速度与温、湿度条件的关系,获得了45号钢和12号硬铝分别在“40℃,RH为85％”和“70℃,RH为85％”2种温、湿度环境下的“腐蚀速度-时间”函数关系。结论45号钢和12号硬铝在温、湿度环境下的加速因子与贮存时间呈逆幂率关系。     

Feasibility of nanoscale zerovalent iron-loaded sediment-based biochar (nZVI-SBC) for simultaneous removal of nitrate and phosphate: high selectivity toward dinitrogen and synergistic mechanism

Environmental Science and Pollution Research - In the process of water treatment, excessive nitrogen and phosphorus pollutants are of great concern. Therefore, we prepared nanoscale zerovalent iron...     

Two-step harmless treatment of secondary aluminum dross (SAD) by vacuum distillation and alkaline roasting

Journal of Material Cycles and Waste Management - Secondary aluminum dross (SAD) is classified as hazardous waste by many countries in the world because it contains a large number of toxic and...     

Study on the denitrification performance of FexLayOz/activated coke for NH3-SCR and the effect of CO escaped from activated coke at mid-high temperature on catalytic activity

Currently, activated coke is widely used in the removal of multiple pollutants from industrial flue gas. In this paper, a series of novel Fe_xLa_yO_z/AC catalysts was prepared by the incipient wetness impregnation for NH₃-SCR denitrification reaction. The introduction of Fe-La bimetal oxides significantly improved the denitrification performance of activated coke at mid-high temperature, and 4% Fe_0.3La_0.7O_1.5/AC exhibited a superior NO_x conversion efficiency of 90.1% at 400 °C. The catalysts were further characterized by BET, SEM, XRD, Raman, EPR, XPS, FTIR, NH₃-TPD, H₂-TPR, et al., whose results showed that the perovskite-type oxide of LaFeO₃ and oxygen vacancies were produced on the catalysts’ surfaces during roasting. Fe-La doping enhanced the amount of acid sites (mainly Lewis and other stronger acid sites) and the content of multifarious oxygen species, which were beneficial for NO_x removal at mid-high temperature. Moreover, it was investigated that the effect of released CO from activated coke at mid-high temperature on the NO_x removal through the lifetime test, in which it was found that a large amount of CO produced by pyrolysis of activated coke could promote the NO_x removal, and long-term escaping of CO on the activated coke carrier did not have a significant negative impact on catalytic performance. The results of the TG-IR test showed that volatile matter is released from the activated coke while TG results showed that the weight loss rate of 4% Fe_0.3La_0.7O_1.5/AC only was 0.0015~0.007%/min at 300–400 °C. Hence, 4% Fe_0.3La_0.7O_1.5/AC had excellent thermal stability and denitrification performance to be continuously used at mid-high temperature. Finally, the mechanisms were proposed on the basis of experiments and characterization results.

     

聚α-烯烃合成油的清洁生产工艺

针对聚α-烯烃合成油（PAO）生产旧工艺存在的问题,介绍了以固载化AlCl3为催化剂的PAO生产新工艺,考察了各种因素对PAO收率的影响。实验结果表明,在反应温度为100℃、反应时间为8h、A1C1,与α-烯烃质量比为10：75的条件下,PAO收率为48．8％。采用新工艺后,PAO产品质量有了明显提高,黏度指数为132,碱和白土的消耗为零,且没有废渣产生,可实现清洁化生产。     

Study on Biodegradable Starch/OMMT Nanocomposites for Packaging Applications

The thermoplastic starch (TPS) and nanocomposite(TPS/OMMT) was prepared with 15% carbamide, 15% ethanolamine and different contents of organic activated montmorillonite (OMMT) by twin-screw extruder with a 130 °C barrel temperature. Fourier transforms infrared spectroscopy and wide angle X-ray diffraction shown that the alkylamine in dodecyl benzyl dimethyl ammonium bromide could react with MMT via cation exchange reaction. After treated, the d(001)space distance of MMT increased from 1.5 to 1.7 nm. Scanning electron microscope revealed that the lower contents of OMMT could disperse well in the matrixes of TPS. The carbamide, ethanolamine and the OMMT could destroy the crystallization behavior of starch, but only the OMMT restrained this behavior for long-term storing. Mechanical properties investigation indicated that the tensile strength and modulus of TPS/OMMT nanocomposites were better than those of TPS, while the elongation at break was descended with the increasing of OMMT contents. When the content of OMMT was 4%, the tensile strength and modulus of TPS was improved from 4.2 and 42 MPa to 6.0 and 76 MPa, respectively.     

Simultaneous separation of apigenin,luteolin and rosmarinic acid from the aerial parts of the copper-tolerant plant Elsholtzia splendens

Elsholtzia splendens is a copper-tolerant plant species which grows on copper deposits in China. The generation of a valuable E. splendens biomass on specific contaminated sites has become one of the promising phytotechnologies. The simultaneous separations of apigenin, luteolin, and rosmarinic acid yielded in the ethyl acetate extracts of the flowering aerial parts was achieved by the use of a macroporous resin, polyamide, and silicagel columns during chromatography. Chemical identification confirmed the structures based on the spectra of FTIR, NMR, and HPLC/ESI-MS. The isolated compounds of purity above 98.3 % were evaluated for their in vitro cytotoxic activities against human cancer cell lines including A549 (non-small lung), A431 (skin), and Bcap37 (breast). Among these compounds, luteolin and apigenin presented the best cytotoxic activities against A549, A431, and Bcap37 cells and, therefore, both could be the valuable products for the post-harvest processing of E. splendens biomass.     

Synthesis of hybrid carbon nanotubes using Brassica juncea L. application to photodegradation of bisphenol A

Hyperaccumulators contain tubular cellulose and heavy metals, which can be used as the sources of carbon and metals to synthesize nanomaterials. In this paper, carbon nanotubes (CNTs), Cu_0.05Zn_0.95O nanoparticles, and CNTs/Cu_0.05Zn_0.95O nanocomposites were synthesized using Brassica juncea L. plants, and the ultraviolet (UV)-light-driven photocatalytic degradations of bisphenol A (BPA) using them as photocatalysts were studied. It was found that the outer diameter of CNTs was around 50 nm and there were a few defects in the crystal lattice. The synthesized Cu_0.05Zn_0.95O nanocomposites had a diameter of around 40 nm. Cu_0.05Zn_0.95O nanocomposites have grown on the surface of the CNTs and the outer diameter of them was around 100 nm. The synthesized hybrid carbon nanotubes using B. juncea could enhance the efficiency of photocatalytic degradation on BPA. The complete equilibration time of adsorption/desorption of BPA onto the surface of CNTs, Cu_0.05Zn_0.95O nanoparticles, and CNTs/Cu_0.05Zn_0.95O nanocomposites was within 30, 20, and 30 min, and approximately 14.9, 8.7, and 17.4 % BPA was adsorbed by them, respectively. The combination of UV light irradiation (90 min) with CNTs, Cu_0.05Zn_0.95O nanoparticles, and CNTs/Cu_0.05Zn_0.95O nanocomposites could lead to 48.3, 75.7, and 92.6 % decomposition yields of BPA, respectively. These findings constitute a new insight for synthesizing nanocatalyst by reusing hyperaccumulators.     

交流电场联合有机物料强化东南景天修复重金属镉污染土壤

针对土壤重金属污染植物修复效率低的问题,采用盆栽实验,通过施加多种强度的交流电场(0、0.5、1.0 V·cm⁻¹)和不同种类的有机物料(黄腐酸钾、紫云英),研究了交流电场及其与有机物料联合对重金属超积累植物东南景天修复重金属镉污染土壤效率的作用。结果表明,交流电场促进了东南景天的生长和对重金属的吸收,以0.5 V·cm⁻¹作用最佳,在电场处理组20 d后东南景天地上部Cd积累量比不施加电场的处理组提高了48.1%。交流电场和有机物料联用可以进一步提升东南景天对土壤镉的累积,施加黄腐酸钾处理组有利于土壤酸可提取态Cd的提高,比对照组提高了16.35%。在交流电场为0.5 V·cm⁻¹条件下,以0.3%施用效果最佳,施加黄腐酸钾和紫云英分别是对照组(施加交流电场,不施加有机物料)的3.65倍和1.73倍。有机物料和交流电场的共同作用极大地促进了东南景天镉的积累。     

The associations of air pollution exposure during pregnancy with fetal growth and anthropometric measurements at birth: a systematic review and meta-analysis

Environmental Science and Pollution Research - Fetal growth has been demonstrated to be an important predictor of perinatal and postnatal health. Although the effects of maternal exposure to air...