采用含有二乙二醇(DEG)和乙醇胺(ETA)的双组分解交联剂降解废旧硬质聚氨酯泡沫塑料(PU硬泡),并利用降解得到的低聚物多元醇与木质素复合制备出性能增强的再生PU硬泡。通过对制备的再生PU硬泡的红外光谱、密度、吸水率、抗压强度、热稳定性、导热系数、热重曲线等进行分析测试,考察m(DEG)∶m(ETA)对再生PU硬泡性能的影响。实验结果表明:m(DEG)∶m(ETA)=1∶3时废旧PU硬泡的降解效果最好;木质素加入量为2.0%(w)时再生PU硬泡的密度低、抗压强度高、保温性能良好,达到国家标准《建筑绝热用硬质聚氨酯泡沫塑料》(GB/T 21558—2008)的品质要求。     

北京市典型废弃物焚烧源2010—2017年二NFDA1英排放特征和减排效果分析

分析2010—2017年北京市三类典型废弃物焚烧源的废气二NFDA1英排放监测数据,计算排放因子和排放量,评估减排政策成效,并分析不同排放源达标排放时同类物分布特征异同和变化规律,探讨影响排放的重要因素。结果表明: 5家焚烧源平均排放浓度为 0.008～0.069 ng/m³(以TEQ计,下同),废气二NFDA1英排放因子为 0.027～1.7 μg/t,2016年向空气中排放的二NFDA1英量为 0.002 5～0.058 g；生活垃圾、危险废物和医疗废物焚烧源的低、高氯代同类物质量分数比的平均值分别为接近于 0.5、大于0.5和小于0.5,危险废物焚烧源的 ∑PCDFs、∑PCDDs质量分数比的平均值大于2； 123478-HxCDF和123678-HxCDF质量浓度接近且线性相关,具有相近的生成机理和去除效率； I-TEQ变化趋势与∑PCDFs质量分数的变化趋势基本一致,活性炭喷射和布袋除尘的去除效率是影响二NFDA1英排放的重要因素之一；危险废物焚烧源HWI1随运行时间增加排放浓度增加,而及时更换烟道管壁有助于消除“记忆效应”的不良影响。     

不同好氧预处理方式对餐厨垃圾产甲烷的影响

为了研究不同好氧预处理方式对餐厨垃圾厌氧消化产甲烷的影响,通过建立3个模拟厌氧生物反应器,研究了传统厌氧生物反应器C1、上层好氧预处理-厌氧生物反应器C2和底部好氧预处理-厌氧生物反应器C3 3种不同操作条件下的产甲烷过程.结果表明,挥发性有机酸的累积使C1始终处于产甲烷滞后阶段;而C2、C3的好氧预处理通过加快易水解酸化组分和过量挥发性有机酸的好氧降解,有效缓解了酸性抑制,产甲烷滞后时间明显缩短至10 d内.第32天C2停止上层曝气后,在27 d内甲烷浓度达到了50％以上,同时,产甲烷速率迅速上升,并在第81天可达到峰值773 mL/(kg·d).C3在第11天停止底部曝气后,虽然经过22 d的时间甲烷浓度即上升至50％,但之后产甲烷速率经历回落阶段后再次逐渐上升,在实验结束时仅达到517 mL/(kg·d).上层曝气的好氧预处理方式所需曝气时间相对较长,但其产甲烷启动快,与底部曝气相比,其后期的甲烷化过程更稳定并可达到较高的产甲烷速率.     

酸碱度对生活垃圾焚烧厂沥滤液蒸发处理效果的影响

采用蒸发法处理城市生活垃圾焚烧厂垃圾沥滤液,着重考察了不同沥滤液初始pH值对蒸发去除COD和氨氮效果的影响,并采用GC-MS对蒸发冷凝液中有机物成分进行了分析鉴定.结果表明,生活垃圾沥滤液的初始pH对冷凝液中COD、氨氮含量及有机污染物分布产生了决定性的影响.沥滤液在酸性条件下(pH≤6)蒸发,随着pH的增加,冷凝液中COD的含量线性降低,而氨氮的含量线性增加.当沥滤液的初始pH值从6增加到11,冷凝液中COD的含量呈对数函数降低,而氨氮的含量表现出显著增加趋势.从冷凝液中鉴定出38种有机污染物,多为沸点较低的醇、酸、酚和酯类.在酸性条件下(pH=3),冷凝液中挥发性有机酸和低碳醇的相对丰度接近90％.在近中性条件下(pH=6.2),冷凝液中的有机污染物以酚、酸和杂环类化合物为主.在碱性条件下(pH =11),冷凝液中酚和杂环类化合物占比较高,而酸的含量极少.     

固相萃取-高效液相色谱法测定废水中的酚类化合物

建立了Supelclean ENVI-Chrom P柱固相萃取-高效液相色谱法测定废水中11种酚类化合物的分析方法,并对固相萃取条件和液相色谱条件进行了讨论。该方法分离效果良好,净化效果明显,方法检出限为2×10-3~2×10-2mg/L,平行分析(n=6)的RSD为2.7%~16.4%,废水加标回收率除2,4-二硝基酚偏低以外,其他化合物的回收率为61.4%~115.8%。     

固相萃取-气质联用法测定固体废物浸出液中的二硝基苯

建立了一种利用固相萃取法对固体废物浸出液(TCLP)中二硝基苯进行萃取,DB-5石英毛细管柱(30 m×0.25 mm×0.25μm)进行分离,质谱检测器检测二硝基苯的方法。方法在0.002 0~0.020 0 mg/L之间线性关系良好,二硝基苯三种同分异构体的检出限均为0.5μg/L,模拟样品加标回收率为93%~96%,RSD≤2%;实际固体废物样品测定的加标回收率为95%~98%。     

气相色谱-串联质谱法测定沉积物中多环芳烃

采用ASE法提取沉积物中16种多环芳烃,以固相萃取法净化提取液,用气相色谱-串联质谱法测定。通过优化测定条件,使方法在5.00μg/L~1 600μg/L范围内线性良好,方法检出限为0.15μg/kg~0.66μg/kg。空白石英砂的加标回收率为61.9%~121%,7次测定结果的RSD为2.6%~11.1%。     

Feasibility of honeycomb monolith supported sugar catalyst to produce biodiesel from palm fatty acid distillate (PFAD)

Carbon coated monolith was prepared by sucrose solution 65 wt.% via dip-coating method. Sulfonation of incomplete carbonized carbon coated monolith was carried out in order to synthesize solid acid catalyst. The textural structure characteristics of the solid acid catalyst demonstrated a low surface area and pore volume. Palm fatty acid distillate (PFAD), a by-product of palm oil refineries, was utilized as oil source in biodiesel production. The esterification reaction subjected to different reaction conditions was performed by using the sulfonated carbon coated monolith as heterogeneous catalyst. The sulfonation process had been performed by using vapour of concentrated H₂SO₄ that was much easier and efficient than liquid phase sulfonation. Total acidity value of carbon coated monolith was measured for unsulfonated sample (0.5 mmol/g) and sulfonated sample (4.2 mmol/g). The effect of methanol/oil ratio, catalyst amount and reaction time were examined. The maximum methyl ester content was 89% at the optimum condition, i.e. methanol/oil molar ratio (15:1), catalyst amount (2.5 wt.% with respect to PFAD), reaction time (240 min) and temperature 80 °C. The sugar catalyst supported on the honeycomb monolith showed comparable reactivity compared with the sugar catalyst powder. However, the catalyst reusability studies showed decrease in FFA% conversion from 95.3% to 68.8% after four cycles as well as the total acidity of catalyst dropped from the value 4.2 to 3.1 mmol/g during these cycles. This might be likely due to the leaching out of SO₃H group from the sulfonated carbon coated monolith surface. The leaching of active species reached a plateau state after fourth cycle.     

Investigation of biocatalytic potential of garbage enzyme and its influence on stabilization of industrial waste activated sludge

The decomposable waste thrown into the environment can be used to produce value added bio-product which in turn reduces the production of greenhouse gas. Garbage enzyme is one such value added product produced by fermentation of organic solid waste. In the present study enzyme activity and disinfectant potential of garbage enzyme was evaluated and its influence on reduction of total solids, suspended solids and pathogens in dairy waste activated sludge were studied. The result showed the garbage enzyme possesses protease, amylase and lipase activity and reduced 37.2% of total solids, 38.6% of suspended solids and 99% of pathogens in dairy waste activated sludge. This significant result may be helpful for researchers to compare the effectiveness of earth-friendly garbage enzyme treatment of industrial sludge with various physical and chemical pre-treatment methods to improve the biogas production from the sludge digestion unit.     

大肠杆菌吸附-化学还原法用废含金催化剂制备金纳米线

采用大肠杆菌吸附-化学还原法,以大肠杆菌(ECCs)为模板、十六烷基三甲基溴化铵为保护剂、抗坏血酸为还原剂,由废含金催化剂制备金纳米线(AuNWs)。采用XRD,SEM,TEM等技术对AuNWs进行表征。研究了AuNWs对罗丹明6G(R6G)和4-巯基苯甲酸(4-MBA)的拉曼散射信号的增强效果。实验结果表明:在制备过程中加入微生物ECCs,可使金回收率提高约20百分点;当溶液pH小于4时,反应2 h后,有大量呈线状的AuNWs聚集沉降,金回收率可达99%1以上。表征结果显示,AuNWs呈多晶结构,晶格间距为0.23 nm。表面增强拉曼散射分析表明,AuNWs对R6G和4-MBA具有良好的拉曼光谱增强性能。